Síntese e caracterização de redes metalorgânicas baseadas em zinco e ácidos benzenodicarboxílicos

Metal Organic Frameworks (MOFs) are supramolecular structures consisted of ions or metal clusters coordinated to organic ligands which are repeated in two or three dimensions. These structures have atracted much attention due to their properties such as low density, high specific surface area and large volume of pores. In this work, MOFs consisted of zinc clusters connected by ditopic ligands, terephthalic acid (1,4- H2BDC) or isophthalic acid (1,3-H2BDC) were synthesized. To obtain the proposed materials, different routes and synthetic parameters were tested, such as the molar ratio of the precursors, the addition of template molecules, the type of solvente, the addition of organic base or the type of a counter-ion of Zn salt. It was found that the variation of these parameters led to the formation of different metalorganic structures. The solids obtained were characterized by XRD, SEM and IR. For the samples identified as MOF- 5, it was verified that the structure was composed of both interpenetrated and non interpenetrated structures. These samples showed a low stability, becoming totally transformed into another structure within less than 72 hours. The addition of the nickel and/or cobalt was found to be a promissing method for increasing the stability of MOF- 5, which in this case, still remained unconverted to another structure even after 15 days of exposure to air. The samples prepared from 1,3-H2BDC were probably new, still unknown Metal Organic Frameworks

Síntese e caracterização de materiais mesoporosos para a captura de CO2: influência do óxido de níquel

Several materials are currently under study for the CO2 capture process, like the metal oxides and mixed metal oxides, zeolites, carbonaceous materials, metal-organic frameworks (MOF's) organosilica and modified silica surfaces. In this work, evaluated the adsorption capacity of CO2 in mesoporous materials of different structures, such as MCM-48 and SBA- 15 without impregnating and impregnated with nickel in the proportions 5 %, 10 % and 20 % (m/m), known as 5Ni-MCM-48, 10Ni-MCM-48, 20Ni-MCM-48 and 5Ni-SBA-15, 10NiSBA-15, 20Ni-SBA-15. The materials were characterized by means of X-ray diffraction (XRD), thermal analysis (TG and DTG), Fourier transform infrared spectroscopy (FT-IR), N2 adsorption and desorption (BET) and scanning electron microscopy (SEM) with EDS. The adsorption process was performed varying the pressure of 100 - 4000 kPa and keeping the temperature constant and equal to 298 K. At a pressure of 100 kPa, higher concentrations of adsorption occurred for the materials 5Ni-MCM-48 (0.795 mmol g-1 ) and SBA-15 (0.914 mmol g-1 ) is not impregnated, and at a pressure of 4000 kPa for MCM-48 materials (14.89 mmol g-1) and SBA-15 (9.97 mmol g-1) not impregnated. The results showed that the adsorption capacity varies positively with the specific area, however, has a direct dependency on the type and geometry of the porous structure of channels. The data were fitted using the Langmuir and Freundlich models and were evaluated thermodynamic parameters Gibbs free energy and entropy of the adsorption system

Síntese, estrutura e propriedades de polímeros de coordenação à base de íons lantanídeos e ácidos benzenodicarboxílicos

Metal Organic Frameworks (MOFs) are hybrids materials, often crystalline, consisting of metal or metal clusters, connected by polytopic organic ligands repetitively, leading to structures, usually porous. In this work, MOFs based on lanthanide ions (La3+ and Gd3+) and dicarboxylate type of ligands (isophthalic and terephthalic acids), were synthesized by hydrothermal, solvothermal and hydro(solvo)thermal methods. The effects of the synthetic route as well as the type of heating, conventional or by microwave, on the structure and properties of MOFs were studied. The powder samples obtained were characterized by X-ray diffraction, infrared spectroscopy, thermal analysis and scanning electron microscopy. The results suggest that the addition of an organic or inorganic base is needed to promote the deprotonation of the ligand, since in the samples prepared by the hydrothermal method, without the use of a base, no formation of the metalorganic framework was observed. On the other hand, the presence of DMF as solvent or cosolvent, afforded the deprotonation of the ligand with the consequent formation of MOFs. At least two different crystalline structures were identified for the samples prepared with terephthalic acid. These samples are isostructural with those reported for phases Eu(1,3-BDC)DMF, Eu2(1,4-BDC)3 (DMF)2 and Tb(1,4-BDC)H2O. The presence of water in the reaction medium in the hydro(solvo)thermal method, provoked the growth of the structure different from that observed in the absence of water. This can be explained by the difference in the coordination mode of water and DMF to lanthanide ions. Although not identified by XRD, the samples prepared with isophthalic acid, also present metalorganic structures, which was confirmed by the presence of the characteristic displacement of the carbonyl group band in their infrared spectra, compared to the spectrum of the pure ligand. This shift was also observed in the samples prepared with terephthalic acid. Thermal analisys shows that the metal organic frameworks do not collapse occurs at a temperature below 430°C.The analysis of scanning electron microscopy suggests that the morphology of powders is highly dependent on the type of heating used, conventional or by microwave.