Avaliação espectrofotométrica do manchamento de resinas odontológicas contendo nanopartículas

Composite resins have been subjected to structural modifications aiming at improved optical and mechanical properties. The present study consisted in an in vitro evaluation of the staining behavior of two nanohybrid resins (NH1 and NH2), a nanoparticulated resin (NP) and a microhybrid resin (MH). Samples of these materials were prepared and immersed in commonly ingested drinks, i.e., coffee, red wine and acai berry for periods of time varying from 1 to 60 days. Cylindrical samples of each resin were shaped using a metallic die and polymerized during 30 s both on the bottom and top of its disk. All samples were polished and immersed in the staining solutions. After 24 hours, three samples of each resin immersed in each solution were removed and placed in a spectrofotome ter for analysis. To that end, the samples were previously diluted in HCl at 50%. Tukey tests were carried out in the statistical analysis of the results. The results revealed that there was a clear difference in the staining behavior of each material. The nanoparticulated resin did not show better color stability compared to the microhybrid resin. Moreover, all resins stained with time. The degree of staining decreased in the sequence nanoparticulated, microhybrid, nanohybrid MH2 and MH1. Wine was the most aggressive drink followed by coffee and acai berry. SEM and image analysis revealed significant porosity on the surface of MH resin and relatively large pores on a NP sample. The NH2 resin was characterized by homogeneous dispersion of particles and limited porosity. Finally, the NH1 resin depicted the lowest porosity level. The results revealed that staining is likely related to the concentration of inorganic pa rticles and surface porosity

Caracterização de compósitos Nb-20%cu obtidos por moagem de alta energia e sinterizados por fase líquida

In this work, was studied the formation of a composite of the refractory metal niobium with copper, through the process of high-energy milling and liquid phase sintering. The HEM can be used to synthesize composite powders with high homogeneity and fine size particle distribution. It may also produce the solid solubility in immiscible systems such as Nb-Cu, or extend the solubility of systems with limited solubility. Therefore, in the immiscible system Cu-Nb, the high-energy milling was successfully used to obtain the composite powder particles. Initially, the formation of composite particles during the HEM and the effect of preparation technique on the microstructure of the material was evaluated. Four loads of Nb and Cu powders containing 20%wt Cu were synthesized by MAE in a planetary type ball mill under different periods of grinding. The influence of grinding time on the metal particles is evaluated during the process by the withdrawal of samples at intermediate times of milling. After compaction under different forces, the samples were sintered in a vacuum furnace. The liquid phase sintering of these samples prepared by HEM produced a homogeneous and fine grained. The composite particles forming the sintered samples are the addition of a hard phase (Nb) with a high melting point, and a ductile phase (Cu) with low melting point and high thermal and electrical conductivities. Based on these properties, the Nb-Cu system is a potential material for many applications, such as electrical contacts, welding electrodes, coils for generating high magnetic fields, heat sinks and microwave absorbers, which are coupled to electronic devices. The characterization techniques used in this study, were laser granulometry, used to evaluate the homogeneity and particle size, and the X-ray diffraction, in the phase identification and to analyze the crystalline structure of the powders during milling. The morphology and dispersion of the phases in the composite powder particles, as well the microstructures of the sintered samples, were observed by scanning electron microscopy (SEM). Subsequently, the sintered samples are evaluated for density and densification. And finally, they were characterized by techniques of measuring the electrical conductivity and microhardness, whose properties are analyzed as a function of the parameters for obtaining the composite

Desenvolvimento de um protótipo para análise dinâmica da dureza de superfícies metálicas

In this paper we developed a prototype for dynamic and quantitative analysis of the hardness of metal surfaces by penetration tests. It consists of a micro-indenter which is driven by a gear system driven by three-rectified. The sample to be tested is placed on a table that contains a load cell that measures the deformation in the sample during the penetration of micro-indenter. With this prototype it is possible to measure the elastic deformation of the material obtained by calculating the depth of penetration in the sample from the difference of turns between the start of load application to the application of the load test and return the indenter until the complete termination of load application. To determine the hardness was used to measure the depth of plastic deformation. We used 7 types of steel trade to test the apparatus. There was a dispersion of less than 10% for five measurements made on each sample and a good agreement with the values of firmness provided by the manufacturers.

Adição de nanopartículas de Ti em matriz de Fe através da deposição por magnetron sputtering

Microalloyed steels constitute a specific class of steel with low amount of carbon and microalloying elements such as Vanadium (V), Niobium (Nb) and Titanium (Ti). The development and application of microalloyed steels and steels in general are limited to the handling of powders with particles of submicron or nanometer dimensions. Therefore, this work presents an alternative in order to construction of microalloyed steels utilizing the deposition by magnetron sputtering technique as a microalloying element addiction in which Ti nanoparticles are dispersed in an iron matrix. The advantage of that technique in relation to the conventional metallurgical processes is the possibility of uniformly disperse the microalloying elements in the iron matrix. It was carried out deposition of Ti onto Fe powder in high CH4, H2, Ar plasma atmosphere, with two deposition times. After the deposition, the iron powder with nanoparticles of Ti dispersed distributed, were compacted and sintered at 1120 ° C in resistive furnace. Characterization techniques utilized in the samples of powder before and after deposition of Ti were Granulometry, Scanning Electron Microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and X-ray diffraction (DRX). In the case of sintered samples, it was carried out characterization by SEM and Vickers Microhardness assays. The results show which the deposition technique by magnetron sputtering is practicable in the dispersion of particles in iron matrix. The EDX microanalysis detected higher percentages of Ti when the deposition were carried out with the inert gas and when the deposition process was carried out with reactive gas. The presence of titanium in iron matrix was also evidenced by the results of X-ray diffraction peaks that showed shifts in the network matrix. Given these results it can be said that the technique of magnetron sputtering deposition is feasible in the dispersion of nanoparticles of iron matrix in Ti.

Desenvolvimento e caracterização de um compósito matriz metálica (CMM): aço EUROFER97 reforçado com Carbeto de Tântalo - TaC

Steel is an alloy EUROFER promising for use in nuclear reactors, or in applications where the material is subjected to temperatures up to 550 ° C due to their lower creep resistance under. One way to increase this property, so that the steel work at higher temperatures it is necessary to prevent sliding of its grain boundaries. Factors that influence this slip contours are the morphology of the grains, the angle and speed of the grain boundaries. This speed can be decreased in the presence of a dispersed phase in the material, provided it is fine and homogeneously distributed. In this context, this paper presents the development of a new material metal matrix composite (MMC) which has as starting materials as stainless steel EUROFER 97, and two different kinds of tantalum carbide - TaC, one with average crystallite sizes 13.78 nm synthesized in UFRN and another with 40.66 nm supplied by Aldrich. In order to improve the mechanical properties of metal matrix was added by powder metallurgy, nano-sized particles of the two types of TaC. This paper discusses the effect of dispersion of carbides in the microstructure of sintered parts. Pure steel powders with the addition of 3% TaC UFRN and 3% TaC commercial respectively, were ground in grinding times following: a) 5 hours in the planetary mill for all post b) 8 hours of grinding in the mill Planetary only for steel TaC powders of commercial and c) 24 hours in the conventional ball mill mixing the pure steel milled for 5 hours in the planetary mill with 3% TaC commercial. Each of the resulting particulate samples were cold compacted under a uniaxial pressure of 600MPa, on a cylindrical matrix of 5 mm diameter. Subsequently, the compressed were sintered in a vacuum furnace at temperatures of 1150 to 1250 ° C with an increment of 20 ° C and 10 ° C per minute and maintained at these isotherms for 30, 60 and 120 minutes and cooled to room temperature. The distribution, size and dispersion of steel and composite particles were determined by x-ray diffraction, scanning electron microscopy followed by chemical analysis (EDS). The structures of the sintered bodies were observed by optical microscopy and scanning electron accompanied by EDS beyond the x-ray diffraction. Initial studies sintering the obtained steel EUROFER 97 a positive reply in relation to improvement of the mechanical properties independent of the processing, because it is obtained with sintered microhardness values close to and even greater than 100% of the value obtained for the HV 333.2 pure steel as received in the form of a bar

Adição de poliuretana em pastas de cimento para poços de petróleo como agente de correção do filtrado

Chemical admixtures, when properly selected and quantified, play an important role in obtaining adequate slurry systems for quality primary cementing operations. They assure the proper operation of a well and reduce costs attributed to corrective cementing jobs. Controlling the amount lost by filtering through the slurry to permeable areas is one of the most important requirements in an operation, commonly controlled by chemical admixtures, such as carboxymethylcellulose (CMC). However, problems related to temperature, salttolerance and the secundary retarding effect are commonly reported in the literature. According to the scenario described above, the use of an aqueous dispersion of non-ionic poliurethane was proposed to control the filter loss, given its low ionic interaction with the free ions present in the slurries in humid state. Therefore, this study aims at assessing the efficiency of poliurethane to reduce filter loss in different temperature and pressure conditions as well as the synergistic effect with other admixtures. The temperatures and pressures used in laboratory tests simulate the same conditions of oil wells with depths of 500 to 1200 m. The poliurethane showed resistance to thermal degradation and stability in the presence of salts. With the increase in the concentration of the polymer there was a considerable decrease in the volume lost by filtration, and this has been effective even with the increase in temperature

Germinação de sementes e otimização de técnicas de micropropagação de umbuzeiro (spondias tuberosa, arr.) anacardiaceae

The brazilian-plum (Spondias tuberosa, His) is a tropical fruit tree that has been consolidated in the market for agribusiness processing, due to its characteristic flavor of fruit. Accordingly, studies to optimize the propagation of plants are necessary for production of seedlings with agronomic and quality assurance measures. This study aimed at determining the efficient techniques for uniform seed germination, as brazilian-plum seed present mechanical dormancy, and establish optimal culture media for multiplication of shoots from the in vitro micropropagation. Firstly, in a greenhouse at the Universidade Federal do Rio Grande do Norte, was evaluated the influence of different methods of breaking dormancy in the emergence of seedlings of brazilian-plum and speed of germination (IVG) of seeds. After 60 days of cultivation, it was found that splay in the distal portion of the seed was the best treatment, with rates of 85.33% in germinability and 3.415 of IVG, compared with the treatment of seed-soaking in water for 12h + humus and the control group. Subsequently, new sources of seedling explants were obtained in studies of tissue culture. Laboratory of Plant Biotechnology that the university, was used stem apex, nodal segments and internodes in search of decontamination with various concentrations of calcium hypochlorite [Ca(OCl)2] and micropropagation, inoculating them in half WPM (1980) with various concentrations of 6-benzylaminopurine (BAP). We used 10 sample units with three replications for different concentrations of [Ca(OCl)2], BAP and explants type. After thirty days, which was observed for the control of contamination, during the establishment in vitro, concentrations of [Ca(OCl)2] between 0.5% and 2.0% were effective in combating exogenous contamination of the apex. In nodal segments and internodes, concentrations of [Ca(OCl)2] between 1.0% and 2.0% and 1.5% and 2.0% were respectively, sufficient to reduce the percentage of losses in these infestations explants. For micropropagation, the culture medium supplemented with 0.1 mg.L-1 BAP promotes better development of multiple shoots per explants from nodal segment. However, success does not get to shoot training in internodal segment

Testes bioquímicos para avaliação do vigor em sementes de Mimosa caesalpiniaefolia Benth

Mimosa caesalpiniaefolia Benth. is a forest species of the Mimosaceae family, recommended for recovery of degraded areas. The evaluation of vigor by biochemical tests have been an important tool in the control of seed quality programs, and the electrical conductivity and potassium leaching the most efficient in the verifying the physiological potential. The objective, therefore, to adjust the methodology of the electrical conductivity test for seeds of M. caesalpiniaefolia, for then compare the efficiency of this test with the potassium in the evaluation of seed vigor of different lots of seeds M. caesalpiniaefolia. To test the adequacy of the electrical conductivity were used different combinations of temperatures , 25 °C and 30 ºC, number of seeds , 25 and 50, periods of imbibition , 4 , 8 , 12 , 16 and 24 hours , and volumes deionized water, 50 mL and 75mL. For potassium leaching test, which was conducted from the results achieved by the methodology of the adequacy of the electrical conductivity test, to compare the efficiency of both tests , in the classification of seeds at different levels of vigor, and the period 4 hours also evaluated because the potassium leaching test can be more efficient in the shortest time . The best combination obtained in experiment of electrical conductivity is 25 seeds soaked in 50 mL deionized or distilled water for 8 hours at a temperature of 30 ° C. Data were subjected to analysis of variance, the means were compared with each other by F tests and Tukey at 5 % probability, and when necessary polynomial regression analysis was performed. The electrical conductivity test performed at period eight hour proved to be more efficient in the separation of seed lots M. caesalpiniaefolia at different levels of vigor compared to the potassium test