Análise comparativa entre as propriedades do gesso obtido de rejeito da produção de sal e gesso comerciais

The environmental impacts, caused by the solid residues generation, are an often quoted concern nowadays. Some of these residues, which are originated from different human activities, can be fully reused, reducing the effects of the poor waste management on the environment. During the salt production process, the first formed crystals are discarded as industrial waste. This is mainly made of gypsum that is a calcium sulfate dihydrate (CaSO4.2H2O). The gypsum in question may go through a calcination process due to the plaster (CaSO4.0,5H2O) production and then the application on the cement industry. Considering the necessity of development and application for these industrial wastes, this paper aims to analyze the plaster, called Salgesso, from the gypsum that was generated during the salt production, and its use viability on the civil construction industry in order to create environmental and economical benefits. For characterization, the following experiments were performed: X-ray Fluorescence (XRF), X-ray Diffraction (XRD), thermal analysis (TG/DTG) and Scanning Electron Microscopy (SEM) with EDS. The following tests were also performed to obtain the mechanical characteristics: Thinness Modulus, Unit Mass, Setting Time and Compressive Resistance. Three commercial plasters used on civil construction were taken as references. All of these tests were performed according to the current standards. It was noticed that although there were some conflicting findings between the salt and commercial plasters in all of the studied properties, the Salgesso has its values within the standard limits. However, there is the possibility to improve them by doing a more effective calcination process. Three commercial plasters, used in construction, were used as reference material. All tests were performed according to standards in force. It was observed that although some tests present conflicting findings between the salt and gypsum plasters commercial properties in all of the studied Salgesso have values within the limits imposed by the standard, but can be improved simply by calcination process more effective

Fatores litogênicos em pacientes com litíase urinária de Fortaleza, Ceará

Lithiasis is considered a public health issue due to its high prevalence and rates of recurrence. Objective: To identify risk factors for lithiasis in kidney stone patients from Fortaleza, Brazil. In the first stage of the study, the medical records of 197 patients with urinary lithiasis covering the period 1996 2006 were analyzed with regard to clinical and metabolic data. In the second stage, 340 kidney stones were submitted to morphological examination under 10x magnification. According to the external morphology and the cut surface, the stones were classified as pure or mixed, and major and minor components were identified. In addition, the stone fragments of 25 patients treated with lithotripsy were submitted to morphological analysis. In the third stage, a subsample of 50 stones was used in a double-blind comparison of morphological and chemical findings. Results were expressed as concordant, partly concordant (discordant for minor components) or discordant (discordant for major components). The average age of first symptoms was 35.8±13.3 years, with no significant difference between the genders. The male/female ratio was 1:1.7. Recurrence was reported in 53.3% of cases. The main metabolic changes observed were hypernatriuria (80.7%), hypercalciuria (48.7%), low urine volume (43.7%), hyperoxaluria (30.5%) and hyperuricosuria (17.3%). Pure stones represented 34.7% of the total sample of 340 stones. The most common route of elimination was spontaneous for pure stones (49.1%) and surgical for mixed stones (50.5%). Pure stones consisted most frequently of calcium oxalate (OxCa) (59.3%) and uric acid (UA) (23.7%), the former prevalent in women, the latter prevalent in men. The most frequently observed component in mixed stones was OxCa (67.1%), followed by carbapatite (11.2%) and struvite (7.9%). The main components were OxCa and UA for men, and carbapatite and struvite for women. Nearly half (48%) the 25 analyzed fragments were pure, consisting of calcium oxalate dihydrate (COD) (56%), calcium oxalate monohydrate (COM) (48%), phosphate (32%) and UA (20%). Four patients (16%) had infectious stones. In the chemical analysis of the subsample of 50 stones, the most 64 frequently observed major components were calcium (70%), oxalate (66%), ammonium (56%), urate (28%) and carbonate (24%). In the morphological analysis, the main components were calcium and magnesium phosphate (32%), COM (24%), UA (20%), COD (18%) and cystine (6%). Morphological and chemical findings were totally concordant for 38% of the stones, partly concordant in 52% and discordant in 10%. Conclusion: The risk factors for lithiasis in kidney stone patients from Fortaleza (Brazil) were hyperoxaluria, hypercalciuria with or without hypernatriuria, hyperuricosuria and low urine volume

Otimização do tempo e temperatura no processamento da gipsita oriunda dos cristalizadores da produção de sal para obter gesso de uso na construção civil

During the process of the salt production, the first the salt crystals formed are disposed of as industrial waste. This waste is formed basically by gypsum, composed of calcium sulfate dihydrate (CaSO4.2H2O), known as carago cru or malacacheta . After be submitted the process of calcination to produce gypsum (CaSO4.0,5H2O), can be made possible its application in cement industry. This work aims to optimize the time and temperature for the process of calcination of the gypsum (carago) for get beta plaster according to the specifications of the norms of civil construction. The experiments involved the chemical and mineralogical characterization of the gypsum (carago) from the crystallizers, and of the plaster that is produced in the salt industry located in Mossoró, through the following techniques: x-ray diffraction (XRD), x-ray fluorescence (FRX), thermogravimetric analysis (TG/DTG) and scanning electron microscopy (SEM) with EDS. For optimization of time and temperature of the process of calcination was used the planning three factorial with levels with response surfaces of compressive mechanical tests and setting time, according norms NBR-13207: Plasters for civil construction and x-ray diffraction of plasters (carago) beta obtained in calcination. The STATISTICA software 7.0 was used for the calculations to relate the experimental data for a statistical model. The process for optimization of calcination of gypsum (carago) occurred in the temperature range from 120° C to 160° C and the time in the range of 90 to 210 minutes in the oven at atmospheric pressure, it was found that with the increase of values of temperature of 160° C and time calcination of 210 minutes to get the results of tests of resistance to compression with values above 10 MPa which conform to the standard required (> 8.40) and that the X-ray diffractograms the predominance of the phase of hemidrato beta, getting a beta plaster of good quality and which is in accordance with the norms in force, giving a by-product of the salt industry employability in civil construction

Propriedades bioativas dos polissacarídeos sulfatados da alga comestível Gracilaria birdiae

Red marine algae of the genus Gracilaria synthesize sulfated polysaccharides (PS) bioactive. But many of these PS were not properly assessed, as is the case of PS synthesized by edible seaweed Gracilaria birdiae. Previous studies showed that sulfated galactans this alga has anti-inflammatory effect. In this work, a galactan (GB) of G. birdiae was obtained and evaluated by different tests. GB showed anticoagulant activity in APTT assay. GB showed no toxicity to normal cells (3T3), but inhibited the survival of cells of adenocarcinoma of the cervix (HeLa) and human pancreatic cancer (Panc-1) 80% (1.5 mg / ml). GB was not able to hijack the OH radical or the superoxide radical. However, showed activity electron donor in two different tests and presented iron chelator activity (70% and 1.0 mg / ml) and Copper (70% at 0.5 mg / ml). The presence of a higher GB promotes formation of crystals of calcium oxalate dihydrate small size, which is less aggressive, because GB is able to interact with and stabilize the crystal that form. Furthermore, GB (2.0 mg / mL) was not cytotoxic to human renal cells (HEK-293). The data lead us to propose that GB has a great potential for the treatment of urolithiasis

Análise comparativa entre as propriedades do gesso obtido de rejeito da produção de sal e gesso comerciais

The environmental impacts, caused by the solid residues generation, are an often quoted concern nowadays. Some of these residues, which are originated from different human activities, can be fully reused, reducing the effects of the poor waste management on the environment. During the salt production process, the first formed crystals are discarded as industrial waste. This is mainly made of gypsum that is a calcium sulfate dihydrate (CaSO4.2H2O). The gypsum in question may go through a calcination process due to the plaster (CaSO4.0,5H2O) production and then the application on the cement industry. Considering the necessity of development and application for these industrial wastes, this paper aims to analyze the plaster, called Salgesso, from the gypsum that was generated during the salt production, and its use viability on the civil construction industry in order to create environmental and economical benefits. For characterization, the following experiments were performed: X-ray Fluorescence (XRF), X-ray Diffraction (XRD), thermal analysis (TG/DTG) and Scanning Electron Microscopy (SEM) with EDS. The following tests were also performed to obtain the mechanical characteristics: Thinness Modulus, Unit Mass, Setting Time and Compressive Resistance. Three commercial plasters used on civil construction were taken as references. All of these tests were performed according to the current standards. It was noticed that although there were some conflicting findings between the salt and commercial plasters in all of the studied properties, the Salgesso has its values within the standard limits. However, there is the possibility to improve them by doing a more effective calcination process. Three commercial plasters, used in construction, were used as reference material. All tests were performed according to standards in force. It was observed that although some tests present conflicting findings between the salt and gypsum plasters commercial properties in all of the studied Salgesso have values within the limits imposed by the standard, but can be improved simply by calcination process more effective