Estudos de Durabilidade Frente ao Ataque Ácido de Compósitos Portland-Polímero para Cimentação de Poços de Petróleo

Portland-polymers composites are promising candidates to be used as cementing material in Northeastern oil wells of Brazil containing heavy oils submitted to steam injection. In this way, it is necessary to evaluate its degradation in the commonly acidizind agents. In addition, to identify how aggressive are the different hostile environments it is an important contribution on the decision of the acidic systems to be used in. It was investigated the performance of the Portland-polymer composites using powdered polyurethane, aqueous polyurethane, rubber tire residues and a biopolymer, those were reinforced with polished carbon steel SAE 1045 to make the electrochemical measurements. HCl 15,0 %, HCl 6,0 % + HF 1,5 % (soft mud acid), HCl 12,0 % + HF 3,0 % (regular mud acid) and HAc 10 % + HF 1,5 % were used as degrading environment and electrolytes. The more aggressive acid solution to the plain Portland hardened cement paste was the regular mud acid, that showed loss of weight around 23.0 %, followed by the soft mud acid, the showed 11.0 %, 15.0 % HCl with 7,0 % and, at last the 10.0 % HAc plus HF 1.5 % with just 1.0 %. The powdered polyurethane-composite and the aqueous polyurethane one showed larger durability, with reduction around 87.0 % on the loss of weight in regular mud acid. The acid attack is superficial and it occurs as an action layer, where the degraded layer is responsible for the decrease on the kinetic of the degrading process. This behavior can be seen mainly on the Portland- aqueous polyurethane composite, because the degraded layer is impregnated with chemically modified polymer. The fact of the acid attack does not have influence on the compressive strength or fratography of the samples, in a general way, confirms that theory. The mechanism of the efficiency of the Portland-polymers composites subjected to acid attack is due to decreased porosity and permeability related with the plain Portland paste, minor quantity of Ca+2, element preferentially leached to the acidic solution, wave effect and to substitute part of the degrading bulk for the polymeric one. The electrolyte HAc 10 % + HF 1,5 % was the least aggressive one to the external corrosion of the casing, showing open circuit potentials around +250 mV compared to -130 mV to the simulated pore solution to the first 24 hours immersion. This behavior has been performed for two months at least. Similar corrosion rates were showed between both of the electrolytes, around 0.01 μA.cm-2. Total impedance values, insipient arcs and big polarization resistance capacitive arcs on the Nyquist plots, indicating passivity process, confirm its efficiency. In this way, Portlandpolymers composites are possible solutions to be succeed applied to oilwell cementing concomitant submitted to steam injection and acidizing operation and the HAc 10,0 % + HF 1,5 % is the less aggressive solution to the external corrosion of the casing

Alquilação redutiva da quitosana a partir do glutaraldeído e 3-amino-1-pr

Chitosan derivatives were prepared by reductive alkylation using glutaraldehyde and 3-amino-1-propanol. The reducing agent used was the sodium borohydride. Tests of solubility, stability and viscosity were performed in order to evaluate these parameters effects in the reaction conditions (molar ratio of the reactants and presence of nitrogen in the reaction system). The molecular structure of commercial chitosan was determined by infrared (IR) and hydrogen nuclear magnetic resonance spectroscopy (1H NMR). The intrinsic viscosity and average molecular weight of the chitosan were determined by viscosimetry in 0.3 M acetic acid aqueous solution 0.2 M sodium acetate at 25 ºC. The derivatives of chitosan soluble in aqueous acidic medium were characterized by 1H NMR. The rheological behavior of the chitosan and of the derivative of chitosan (sample QV), which presented the largest viscosity, were studied as a function of polymer concentration, temperature and ionic strength of the medium. The results of characterization of the commercial chitosan (the degree of deacetylation obtained equal 78.45 %) used in this work confirmed a sample of low molar weight (Mv = 3.57 x 104 g/mol) and low viscosity (intrinsic viscosity = 213.56 mL/g). The chemical modification of the chitosan resulted in derivatives with thickening action. The spectra of 1H NMR of the soluble derivatives in acid aqueous medium suggested the presence of hydrophobic groups grafted into chitosan in function of the chemical modification. The solubility of the derivatives of chitosan in 0.25 M acetic acid aqueous solution decreased with increase of the molar ratio of the glutaraldehyde and 3-amino-1-propanol in relation to the chitosan. The presence of nitrogen and larger amount of reducing agent in reaction system contributed to the increase of the solubility, the stability and the viscosity of the systems. The viscosity of the polymeric suspensions in function of the shear rate increased significantly with polymer concentration, suggesting the formation of strong intermolecular associations. The chitosan presented pseudoplastic behavior with the increase in polymer concentration at a low shear rate. The derivative QV presented pseudoplastic behavior at all concentrations used and in a large range of shear rate. The viscosity of chitosan in solution decreased with an increase of the temperature and with the presence of salt. However, there was an increase of the viscosity of the chitosan solution at higher temperature (65 ºC) and ionic strength of the medium which were promoted by hydrophobic associating of the acetamide groups. The solutions of the chitosan derivatives (sample QV) were significantly more viscous than chitosan solution and showed higher thermal stability in the presence of salt as a function of the hydrophobic groups grafted into chitosan backbone

Estudos de Durabilidade Frente ao Ataque Ácido de Compósitos Portland-Polímero para Cimentação de Poços de Petróleo

Portland-polymers composites are promising candidates to be used as cementing material in Northeastern oil wells of Brazil containing heavy oils submitted to steam injection. In this way, it is necessary to evaluate its degradation in the commonly acidizind agents. In addition, to identify how aggressive are the different hostile environments it is an important contribution on the decision of the acidic systems to be used in. It was investigated the performance of the Portland-polymer composites using powdered polyurethane, aqueous polyurethane, rubber tire residues and a biopolymer, those were reinforced with polished carbon steel SAE 1045 to make the electrochemical measurements. HCl 15,0 %, HCl 6,0 % + HF 1,5 % (soft mud acid), HCl 12,0 % + HF 3,0 % (regular mud acid) and HAc 10 % + HF 1,5 % were used as degrading environment and electrolytes. The more aggressive acid solution to the plain Portland hardened cement paste was the regular mud acid, that showed loss of weight around 23.0 %, followed by the soft mud acid, the showed 11.0 %, 15.0 % HCl with 7,0 % and, at last the 10.0 % HAc plus HF 1.5 % with just 1.0 %. The powdered polyurethane-composite and the aqueous polyurethane one showed larger durability, with reduction around 87.0 % on the loss of weight in regular mud acid. The acid attack is superficial and it occurs as an action layer, where the degraded layer is responsible for the decrease on the kinetic of the degrading process. This behavior can be seen mainly on the Portland- aqueous polyurethane composite, because the degraded layer is impregnated with chemically modified polymer. The fact of the acid attack does not have influence on the compressive strength or fratography of the samples, in a general way, confirms that theory. The mechanism of the efficiency of the Portland-polymers composites subjected to acid attack is due to decreased porosity and permeability related with the plain Portland paste, minor quantity of Ca+2, element preferentially leached to the acidic solution, wave effect and to substitute part of the degrading bulk for the polymeric one. The electrolyte HAc 10 % + HF 1,5 % was the least aggressive one to the external corrosion of the casing, showing open circuit potentials around +250 mV compared to -130 mV to the simulated pore solution to the first 24 hours immersion. This behavior has been performed for two months at least. Similar corrosion rates were showed between both of the electrolytes, around 0.01 μA.cm-2. Total impedance values, insipient arcs and big polarization resistance capacitive arcs on the Nyquist plots, indicating passivity process, confirm its efficiency. In this way, Portlandpolymers composites are possible solutions to be succeed applied to oilwell cementing concomitant submitted to steam injection and acidizing operation and the HAc 10,0 % + HF 1,5 % is the less aggressive solution to the external corrosion of the casing

Obtenção de extratos da Opuntia fícus-indica L. Mill e suas aplicações em formulações cosméticas: avaliação in vivo do sensorial e da eficácia hidratante

Opuntia fícus - indica (L.) Mill is a cactacea presents in the Caatinga ecosystem and shows in its chemical c omposition flavonoids, galacturonic acid and sugars. Different hydroglicolic (EHG001 and EHG002) and hydroethanolic subsequently lyophilized (EHE001 and EHE002) extracts were developed. The EHE002 had his preliminary phytochemical composition investigated by thin layer chromatography (TLC) and we observed the predominance of flavonoids. Different formulations were prepared as emulsions with Sodium Polyacrylate (and) Hydrogenated Polydecene (and) Trideceth - 6 (Rapithix® A60), and Polyacrylamide (and) C13 - 14 I soparaffin (and) Laureth - 7 (Sepigel® 305), and gel with Sodium Polyacrylate (Rapithix® A100). The sensorial evaluation was conducted by check - all - that - apply method. There were no significant differences between the scores assigned to the formulations, howe ver, we noted a preference for those formulated with 1,5% of Rapithix® A100 and 3,0% of Sepigel® 305. These and the formulation with 3% Rapithix® A60 were tested for preliminary and accelerated stability. In accelerated stability study, samples were stored at different temperatures for 90 days. Organoleptic characteristics, the pH values and rheological behavior were assessed. T he emulsions formulated with 3,0% of Sepigel® 305 and 1,5% of Rapithix® A60 w ere stable with pseudoplastic and thixotropic behavior . The moisturizing clinical efficacy of the emulsions containing 3,0% of Sepigel® 305 containing 1 and 3% of EHG001 was performed using the capacitance method (Corneometer®) and transepidermal water lost – TEWL evaluation ( Tewameter®). The results showed t hat the formulation with 3% of EHG001 increased the skin moisturizing against the vehicle and the extractor solvent formulation after five hours. The formulations containing 1 and 3% of EHG001 increased skin barrier effect by reducing transepidermal water loss up to four hours after application.

Aproveitamento sustentável do bagaço de cana de açúcar para obtenção do acetato de celulose

The sustainable use of waste resulting from the agribusiness is currently the focus of research, especially the sugar cane bagasse (BCA), being the lignocellulosic waste produced in greater volume in the Brazilian agribusiness, where the residual biomass has been applied in production energy and bioproducts. In this paper, pulp was produced in high purity from the (BCA) by pulping soda / anthraquinone and subsequent conversion to cellulose acetate. Commercial cellulose Avicel was used for comparison. The obtained cellulose acetate was homogeneous acetylation reaction by modifying the variables, the reaction time in hours (8, 12, 16, 20 and 24) and temperature in ° C (25 and 50). FTIR spectra showed characteristic bands identical to cellulosic materials, demonstrating the efficiency of separation by pulping. The characterization of cellulose acetate was obtained and by infrared spectroscopy (FTIR), X-ray diffraction (XRD), thermogravimetric analysis (TG / DTG / DSC), scanning electron microscopy (SEM) and determining the degree of substitution (DS ) for the cellulose acetate to confirm the acetylation. The optimal reaction time for obtaining diacetates and triacetates, at both temperatures were 20 and 24 h. Cellulose acetate produced BCA presented GS between 2.57 and 2.7 at 25 ° C and 50 ° C GS obtained were 2.66 and 2.84, indicating the actual conversion of cellulose BCA of di- and triacetates. Comparative mode, commercial cellulose Avicel GS showed 2.78 and 2.76 at 25 ° C and 2.77 to 2.75 at 50 ° C. Data were collected in time of 20 h and 24 h, respectively. The best result was for the synthesis of cellulose acetate obtained from the BCA GS 2.84 to 50 ° C and 24 hours, being classified as cellulose triacetate, which showed superior result to that produced with the commercial ethyl cellulose Avicel, demonstrating converting potential of cellulose derived from a lignocellulosic residue (BCA), low cost, prospects of commercial use of cellulose acetate

O aluno surdo em classe regular: concepções e práticas dos professores

Le texte se rapporte à une recherche sur les conceptions d enseignants concernant l inclusion scolaire d élèves sourds , et leurs ralations avec les pratiques qu ils développent dans les classe régulières. Elle a été conduite dans une école publique régulière appartenant à la commune de Assu RN, et dont le choix méthodologique a été une approche qualitative, du genre ethnographyque. La construction des données devient d un processus d observation, de l application d entretiens demi-structurés et de l analyse de documents, ayant pour sujets quatre enseignants des années initiales de l enseignement fondamental. L apport théorique de base a été la théorie socio-culturelle proposée par Vygotsky (2003 ; 2005), censée traduire la compréhension de l homme dans sa dimension historique et culturelle, et mettre en évidence l interaction sociale en tant que condition pour le développement des individus. Les données font connaître que les enseignants sujets de la recherche sont favorables à l inclusion scolaire des élèves sourds dans les classes régulières, néanmoins soulignent le besoin d un changement à l école pour que l inclusion devienne une réalité. Les enseignants sont d avis que l apprentissage des élèves sourds se fait d une façon qui met trop de temps, moyennant l utilisation de recours spécifiques, tels que l usage du langage des signes (Libras). Ils signalent les difficultés qu ils doivent faire face quand il s agit de travailler pédagogiquement avec ces élèves dans le quotidien, telles que : manque d un travail collectif à l école ; besoin d une formation spécialisée ; démonstration de sentiments de peur, ou préjugés de la part de quelques uns du personnel de l école , tout celà interférant directement dans leurs attitudes et leurs actions faces aux élèves ; manque d appui des instances administratives de l école ; absence de politiques consistentes pour guider l éducation sous un regard inclusif. Quant aux pratiques pédagogiques développées à l école, la recherche laisse voir que, par rapport à la présence des élèves sourds, très peu d adaptations y ont été introduites, d où se dégage que la planification des actions éducatives à l école se tourne, prioritairement, vers les élèves qui écoutent, c est-à-dire, vers un groupe apparemment homogène. On a constaté, en plus, qu il n existe pas à l école aucun professionnel habilité pour l établissement d un processus de communication avec les élèves sourds. Malgré ces difficultés, les enseignants avouent, quand même, que travailler avec ces élèves rapporte toujours des bénéfices, tels que la collaboration et le respect mutuels chez les élèves, l acquisition de nouveaux savoirs et l amélioration de la pratique pédagogique des enseignants

Secagem do resíduo de acerola (Malphigia emarginata D.C.): estudo do processo e avaliação do impacto sobre o produto final

Brazil, one of the largest agricultural producers in the world, has managed in recent years to significantly improve its production. However, in response to this advance in the agro-industrial sector, the generation of agro-industrial residues has also increased. New technological alternatives have to be implemented in order to bring economic and rational use of this material and drying is one of the possible choices. Considering the great importance that bioactive compounds present for food science and technology, this research aims to evaluate the air-drying process of acerola residue in a tray convective drier under controlled temperature (60, 70 e 80ºC), air velocity (4.0, 5.0 e 6.0 m/s) and material width (0.5, 0.62 e 0.75 cm) by applying an experimental planning 23 + 3. Based on that, the impact on physical-chemical characteristics, color, bioactive compounds concentration and antioxidant activity of dried acerola waste was evaluated, having the in natura and freeze dried waste as control groups. Dried acerola residue presented natural pigments, mainly carotenoids (143.68 - 68.29 mg/g) and anthocyanins (290.92 - 90.11 mg/100 g), which explain the red and yellow instrumental color parameters observed. The acerola residue powder is also rich in phenolic compounds (3261.11 -2692.60 mgGAEeq/100g), proanthocyanidins (61.33-58.46 eq/100g), ascorbic acid (389.44 739.29 mg/100 g) and DPPH antioxidant activity (20.91 24.72 μg Trolox eq/g). Results show decreased concentration of phenolic compounds, anthocyanins, carotenoids, proanthocyanidins and ascorbic acid caused by the air-drying process. However, even after the observed drying losses, the acerola residue powder can be considered a high value food ingredient, considering the high bioactive compounds concentration found in the final product, as well as the colorimetric characterization and microbiological stability of the dried powder

Influência do tamoxifeno associado ao diabete melito na densidade mineral óssea

Considering that osteopenia and osteoporosis are diabetes mellitus complications, and that tamoxifen (TAM) is an anti-estrogenic drug used in breast cancer treatment, this drug may have a beneficial action preventing accentuaded bone loss associated to diabetes. Female Wistar rats (n=60) weighting 180-250g were divided in four groups: Group C, control animals (n=5); Group T, animals treated with TAM (n=5); Group D, diabetic animals (n=5); and Group DT, diabetic animals treated with TAM (n=5). Oestrus cycle was evaluated before the beggining of experimental period to select the animals with regular cycle. This evaluation continued throughout the study period and for all studied groups. Diabetes was induced by a intra perithoneal injection of streptozotocin (STZ) in a concentration of 45 mg/Kg of body weight. Those animals with serum glicose levels 250 mg/dL were considered diabetics. Animals were sacrificed in the periods of 30, 60 and 90 days after diabetes onset. Left femur histomorphometric measurements and serum biochemical analysis (glycemia, alkaline phosphatase, tartaric-resistant acid phosphatase, calcium, phosphorous, magnesium, total proteins, albumin, globulins, urea and creatinine) were done. Histomorphometric results showed a progressive bone loss in Group D animals when compared to those from Group C all over the experimental period, becoming accentuaded in the 90 days period. In relation to Groups T and DT, values approcimated to those obtained for control group were found during the whole period of study. Those data may indicate a bone mass recovery or a diminished bone loss due to diabetes when animals were treated with TAM. During the whole experimental period animals of groups D and DT maintained glycemic levels above 250 mg/dL whereas animals of groups C and T maintained those levels below 150mg/dL. Alkaline phosphatase activity was increased in all study periods for groups D and DT when compared to group C animals over the 90 days period. Tartarate-resistant acid phosphatase activity was showed unaltered in all periods of study and for all groups. Calcium and magnesium results were also unaltered, maintaining reference levels for all groups in all experimental periods. Phosphorous levels were increased in groups D and DT when compared to groups C and T in the 30 days period. However no difference was found in the periods of 60 and 90 days for this test. No difference was found for total proteins levels for groups C, T, D and DT over the study period. Albumin levels were reduced in DT group in the 60 days period and in D and DT groups in the 90 days period. Urea levels were significantly increased in the 30, 60 and 90 days study periods in groups D and DT when compared to groups C and T. Creatinine results showed a significantly increase in the 90 days period for groups D and DT when compared to groups C and T, and maintaining unaltered in the 30 and 60 days periods. These results suggest that the treatment with TAM may reduce bone loss caused by diabetes mellitus