Ação de polissacarídeos sulfatados de Fucus Vesiculosus na Hemostasia e no sistema complemento

Fucans are a family of sulfated homo and teropolysaccharides respectively, composed mainly of a- (1®2) and a- (1®3) linked by L-fucose residues. Properties such as the ability to act as an anti-contraceptive, to reduce cholesterol levels, and to act as an anti-tumor agent are much related. We have focused our attention on the anticoagulant properties, platelet aggregation, hemorrhagic activity and complement system in vitro of commercial fucoidan (F) and their purified fractions (F1, F2 and F3) from Fucus vesiculosus obtained from fractionation of the fucoidan with different concentrations of acetone 1, 2 and 3v. These compounds were chemically characterized and the fucoidan (F) was modified by desulfation. The anticoagulant activity of the compounds was assessment by activated partial thromboplastin time (APTT) and prothrombine time assay (PT) using citrated normal human plasma. The results of APPT test showed that F, F1 and F2 have high anticoagulants activities 240.0 s (5 µg). The F3 showed 73.7 s in the same concentrations. The results obtained with PT test to F, F1, F2 and F3 were 81.5 s, 120.0 s, 57.1 and 32.5 s respectively with 50 µg. The dessulfated polymer showed a decrease in the anticoagulant activity in these two tests. Platelet aggregation assay was measured turbidimetrically with platelet aggregometer by method of Born. The aggregation platelet with F and fractions F1, F2 and F3 exhibited a two-phase answer in the concentration of 5 mg/mL with maximum aggregation of 76.36 ± 10.3% ; 69.54 ± 9.40%; 75.94 ± 9.01%; 51.13 ± 9.59% respectively. However, was observed a hipoaggregate profile F (15.17 ± 5.2%), F1 (7.40 ± 3.04 %), F2 (19.1 ± 5.41%) and F3 (5.09 ± 3.02%) at 0.1 mg/mL. The hemorrhagic activity assay was carried in Wistar rats and showed that these compounds have low hemorrhagic effect when compared to heparin. The complement system ( alternative pathway was made using non-sensibilized rabbit red blood cells The results of complement system essay showed that F , F2 and F3 have action inhibitory in relation to the group control 0.544, 0.697, 0.622 and 0.958 respectively The results showed that these compounds have action on this system. Interaction of the polisaccharides with proteins C3 and C4 showed that the fraction F1 stimulated the activity assay hemolytic using red blood cells

Modificações introduzidas pelos treinamentos cardiopulmonar e neuromuscular nos níveis séricos basais de fatores de crescimento insulina símile i (igf-1), cortisol, autonomia funcional e qualidade de vida de mulheres idosas

Changes introduced by cardiopulmonar and neuromuscular training on basal serum insulin-like grow factor-1 (IGF-1) and cortisol levels, functional autonomy and quality of life in elderly women The aim of this study was to compare the effects of strength and aerobic training on basal serum IGF-1 and Cortisol levels, functional autonomy (FA) and quality of life (QoL) in elderly women after 12 weeks of training. The subjects were submitted the strength training (75-85% 1-RM) with weight exercises (SG; n=12; age=66.08 ± 3,37 years; BMI=26,77 ± 3,72 kg/m2), aerobic training with aquatic exercises (AG; n=13; age=68,69 ± 4,70 years; BMI=29,19 ± 2,96 kg/m2) and control group (CG; n=10; age=68,80 ± 5,41 years; BMI=29,70 ± 2,82 kg/m2). Fasting blood was analyzed to measure basal IGF-1 and cortisol levels by chemiluminescence method. The t-Student test showed increased IGF-1 in the SG (p<0.05) for intragroup comparison. The Repeated-measure ANOVA presented increased IGF-1 (p<0.05) in the SG compared to the other two groups. There were no differences in cortisol levels. All the FA tests (GDLAM autonomy protocol) presented decreased significant in the time marked in seconds to the SG. The same results were found in the AG, except in the rise from a sitting position test. The autonomy index presented significant improvements (p<0.05) in the SG related to the AG and CG and in the AG to the CG. The SG showed increased QoL (p<0.05) (by WHOQOL-Old questionnaire) in the facet 1 (sensorial functioning) and facet 5 (death and dying). Thus, the SG obtained positive changes on IGF-1 and FA levels when compared to the AG. This suggests that strength training can indicated to decrease the effects of ageing.

Conhecimento dos enfermeiros do Hospital Universitário Onofre Lopes sobre sistematização da assistência de Enfermagem

Nursing as a profession goes in search on quality of their care through new frameworks, trying to break postures of the health care system so fragmented in the care. To change professional practices, it is necessary to build their own knowledge grounded on Nursing Care System. The aim of this study was to analyze the influence of nurses' knowledge on care systematization in nursing in the University Hospital Natal-RN. It is an analytical descriptive study carried out at the Onofre Lopes University Hospital (HUOL), Natal-RN, 2010, the sample was composed of 40 active nurses working in hospitalization units of the hospital, the inclusion criteria were being in the monthly scale sector and agree to participate in the study. The non-participant observation and another interview were used for collecting data, statistical analysis was descriptive and inferential with reliability test, Pearson test, chi-square and Fischer, the variables that correlated were analyzed in a model Multiple logistic , calculating odds ratio. The results were: predominance of female professionals (90%), predominantly in the age range 39-46 years (37.5%), nurses who have the undergraduate degree at the Federal University of Rio Grande do Norte (80%), and who have expertise training as a minimal degree (62.5%). Among the surveyed, the knowledge showed significance with the graduation time (p = 0.018) and time working in HUOL (p = 0.036). The majority of the professionals surveyed do not know which organ is responsible for the SAE legislation (52.5%), aware of the steps needed to build the nursing diagnosis (92.5%), understand the characteristics of nursing planning (90% ). However the same professionals do not perform physical examination in patients (50.0%) did not classify the clinical findings (68.4%), and identify the problems encountered as a classification (13.2%). The planning of nursing care is carried out by verbal order of nurses (82.5%), 41% of the professionals assess only the intervention stage, in other words, the actions taken. Regarding the practical application of nursing records 53% of nurses do not realize records, 30.8% is incomplete, the other held notes (p = 0.003). The nurses know the nursing process (90% of appropriate responses), despite the actions defined by the theory are not applied in practice. Investigators believe the condition of the hospital teacher (22.5%) could positively affect the implementation of the SAE associated with the interest of professionals (20%). Of the respondents, 17.5% accept as truth the lack of facilities to assist the SAE implementation in the hospital. It was concluded that nurses know the theory that underlies the SAE and the nursing process, but do not develop the service know as well, there is need for action to boost the SAE implementation as practice of nurses in the hospital investigated

Ação de polissacarídeos sulfatados de Fucus Vesiculosus na Hemostasia e no sistema complemento

Fucans are a family of sulfated homo and teropolysaccharides respectively, composed mainly of a- (1®2) and a- (1®3) linked by L-fucose residues. Properties such as the ability to act as an anti-contraceptive, to reduce cholesterol levels, and to act as an anti-tumor agent are much related. We have focused our attention on the anticoagulant properties, platelet aggregation, hemorrhagic activity and complement system in vitro of commercial fucoidan (F) and their purified fractions (F1, F2 and F3) from Fucus vesiculosus obtained from fractionation of the fucoidan with different concentrations of acetone 1, 2 and 3v. These compounds were chemically characterized and the fucoidan (F) was modified by desulfation. The anticoagulant activity of the compounds was assessment by activated partial thromboplastin time (APTT) and prothrombine time assay (PT) using citrated normal human plasma. The results of APPT test showed that F, F1 and F2 have high anticoagulants activities 240.0 s (5 µg). The F3 showed 73.7 s in the same concentrations. The results obtained with PT test to F, F1, F2 and F3 were 81.5 s, 120.0 s, 57.1 and 32.5 s respectively with 50 µg. The dessulfated polymer showed a decrease in the anticoagulant activity in these two tests. Platelet aggregation assay was measured turbidimetrically with platelet aggregometer by method of Born. The aggregation platelet with F and fractions F1, F2 and F3 exhibited a two-phase answer in the concentration of 5 mg/mL with maximum aggregation of 76.36 ± 10.3% ; 69.54 ± 9.40%; 75.94 ± 9.01%; 51.13 ± 9.59% respectively. However, was observed a hipoaggregate profile F (15.17 ± 5.2%), F1 (7.40 ± 3.04 %), F2 (19.1 ± 5.41%) and F3 (5.09 ± 3.02%) at 0.1 mg/mL. The hemorrhagic activity assay was carried in Wistar rats and showed that these compounds have low hemorrhagic effect when compared to heparin. The complement system ( alternative pathway was made using non-sensibilized rabbit red blood cells The results of complement system essay showed that F , F2 and F3 have action inhibitory in relation to the group control 0.544, 0.697, 0.622 and 0.958 respectively The results showed that these compounds have action on this system. Interaction of the polisaccharides with proteins C3 and C4 showed that the fraction F1 stimulated the activity assay hemolytic using red blood cells

Síntese e impregnação de peneiras moleculares Fe MCM-41 derivada de sílica da casca do arroz

The mesoporous molecular sieves of the MCM-41 and FeMCM-41 type are considered promissory as support for metals used as catalysts in oil-based materials refine processes and as adsorbents for environmental protection proposes. In this work MCM-41 and FeMCM41 were synthesized using rice husk ash - RHA as alternative to the conventional silica source. Hydrothermal synthesis was the method chosen to prepare the materials. Pre-defined synthesis parameters were 100°C for 168 hours, later the precursor was calcinated at 550°C for 2 hours under nitrogen and air flow. The sieves containing different proportions of iron were produced by two routes: introduction of iron salt direct synthesis; and a modification post synthesis consisting in iron salt 1 % and 5% impregnation in the material followed by thermal decomposition. The molecular sieves were characterized by X ray diffraction XRD, Fourier transform infrared spectroscopy FT-IR, X ray fluorescence spectroscopy XFR, scanning electronic microscopy SEM, specific surface area using the BET method, Termogravimetry TG. The kinetic model of Flynn Wall was used with the aim of determining the apparent activation energy of the surfactant remove (CTMABr) in the MCM- 41 porous. The analysis made possible the morphology characterization, identifying the presence of hexagonal structure typical for mesoporous materials, as well as observation of the MCM41 and iron of characteristic bands.

Degradacao termica e catalitica da borra oleosa de Petroleo com materiais nanoestruturados al-mcm-41 e AL-SBA-15

Aiming to reduce and reuse waste oil from oily sludge generated in large volumes by the oil industry, types of nanostructured materials Al-MCM-41 and Al-SBA-15, with ratios of Si / Al = 50, were synthesized , and calcined solids used as catalysts in the degradation of oily sludge thermocatalytic oil from oilfield Canto do Amaro, in the state of Rio Grande do Norte. Samples of nanostructured materials were characterized by thermogravimetric analysis (TG / DTG), X-ray diffraction (XRD), scanning electron microscopy (SEM), absorption spectroscopy in the infrared Fourier transform (FT-IR) and adsorption nitrogen (BET). The characterization showed that the synthesized materials resulted in a catalyst nanostructure, and ordered pore diameter and surface area according to existing literature. The oily sludge sample was characterized by determining the API gravity and sulfur content and SARA analysis (saturates, aromatics, resins and asphaltenes). The results showed a material equivalent to the average oil with API gravity of 26.1, a low sulfur content and considerable amount of resins and asphaltenes, presented above in the literature. The thermal and catalytic degradation of the oily sludge oil was performed from room temperature to 870 ° C in the ratios of heating of 5, 10 and 20 ° C min-1. The curves generated by TG / DTG showed a more accelerated degradation of oily sludge when it introduced the nanostructured materials. These results were confirmed by activation energy calculated by the method of Flynn-Wall, in the presence of catalysts reduced energy, in particular in the range of cracking, showing the process efficiency, mainly for extraction of lightweight materials of composition of oily sludge, such as diesel and gasoline

Prevalência e fatores de risco à persistência de hábitos bucais de sucção não nutritiva em crianças de 3 a 5 anos de idade

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior

Síntese, caracterização e aplicação de MCM-41 funcionalizado com diisopropilamina no processo de adsorção do dióxido de carbono

Emissions of CO2 in the atmosphere have increased successively by various mechanisms caused by human action, especially as fossil fuel combustion and industrial chemical processes. This leads to the increase in average temperature in the atmosphere, which we call global warming. The search for new technologies to minimize environmental impacts arising from this phenomenon has been investigated. The capture of CO2 is one of the alternatives that can help reduce emis ions of greenhouse gases. The CO2 can be captured through the process of selective adsorption using adsorbents for this purpose. Were synthesized by hydrothermal method, materials of the type MCM-41 and Al-MCM-41 in the molar ratio Si / Al equal to 50. The synthesis of gels were prepared from a source of silicon, sodium, water and aluminum in the case of Al-MCM-41. The period of synthesis of the materials was 5 days in autoclave at 100°C. After that time materials were filtered, washed and dried in greenhouse at 100 º C for 4 hours and then calcined at 450 º C. Then the calcined material was functionalized with the Di-isopropylamine (DIPA) by the method of wet impregnation. We used 0.5 g of material mesopores to 3.5 mL of DIPA. The materials were functionalized in a closed container for 24 hours, and after this period were dried at brackground temperature for 2 hours. Were subsequently subjected to heat treatment at 250°C for 1 hour. These materials were used for the adsorption of CO2 and were characterized by XRD, FT-IR, BET / BJH, SEM, EDX and TG / DTG. Tests of adsorption of CO2 was carried out under the following conditions: 100 mg of adsorbent, temperature of 75°C under flow of 100 mL/min of CO2 for 2 hours. The desorption of CO2 was carried out by thermogravimetry from ambient temperature to 900ºC under flow of 25 mL min of He and a ratio of 10ºC/min. The difratogramas X-ray for the synthesized samples showed the characteristic peaks of MCM-41, showing that the structure of it was obtained. For samples functionalized there was a decrease of the intensities of these peaks, with a consequent reduction in the structural ordering of the material. However, the structure was preserved mesopores. The adsorption tests showed that the functionalized MCM-41 is presented as a material promising adsorbent, for CO2 capture, with a loss of mass on the desorption CO2 of 7,52%, while that in Al-MCM- 41 functionalized showed no such loss

Craqueamento termocatalítico de óleo de girassol na presença da peneira molecular SAPO-5

The catalytic cracking of triglycerides presents itself as a possible alternative to the production of biofuels with low emission of pollutants. In this work were synthesized the SAPO-5, the catalysts for the cracking reaction of soybean oil is presented. The solids were powder X-ray diffraction (XRD), thermogravimetric analysis (TG/DTG) and infrared spectroscopy (FTIR). The analyses indicated that the synthesis method has employed to obtain materials with high surface area and high acid. The soybean oil thermal and thermal catalytic cracking, realized from the room temperature to 450 ºC in a simple distillation system, has allowed obtaining two liquid fractions, each consisting of two phases, one aqueous and another organic, organic liquid (OL). The OL obtained from first fractions has shown high acid index, even in the thermal catalytic process. The products obtained in the cracking of soybean oil were analyzed by distillation, acid number, infra-red spectroscopy, density, viscosity, carbon residue, cetane number determination and characterization. The analysis of the products obtained in the presence and in the absence of the SAPO-5 permitted to conclude that all the solids tested presented catalytic activity in the deoxygenation of final products only at the second step of the cracking process

Avaliação da síntese e caracterização de zeólita ZSM-5 ausente de direcionador orgânico estrutural

The catalytic processes play a vital role in the worldwide economy, a business that handles about US$ 13 billion per year because the value of products depends on the catalytic processes, including petroleum products, chemicals, pharmaceuticals, synthetic rubbers and plastics, among others. The zeolite ZSM-5 is used as catalyst for various reactions in the area petrochemical, petroleum refining and fine chemicals, especially the reactions of cracking, isomerization, alkylation, aromatization of olefins, among others. Many researchers have studied the hydrothermal synthesis of zeolite ZSM-5 free template and they obtained satisfactory results, so this study aims to evaluate the hydrothermal synthesis and the physicochemical properties of ZSM-5 with the presence and absence of template compared with commercial ZSM-5. The methods for hydrothermal synthesis of zeolite ZSM-5 are of scientific knowledge, providing the chemical composition required for the formation of zeolitic structure in the presence and absence of template. Samples of both zeolites ZSM-5 in protonic form were obtained by heat treatment and ion exchange, according to procedures reported in the literature. The sample of commercial ZSM-5 was acquired by the company Sentex Industrial Ltda. All samples were characterized by XRD, SEM, FTIR, TG / DTG / DSC, N2 adsorption and desorption and study of acidity by thermo-desorption of probe molecule (n-butylamine), in order to understand their physicochemical properties. The efficiency of the methods applied in this work and reported in the literature has been proved by well-defined structure of ZSM-5. According as the evaluation of physicochemical properties, zeolite ZSM-5 free template becomes promising for application in the refining processes or use as catalytic support, since its synthesis reduces environmental impacts and production costs

Avaliação da remoção de hidrocarbonetos aromáticos (BTEX) em águas utilizando materiais nanoestruturados do tipo Ti-MCM-41

Volatile Organic Compounds are pollutants coming mainly from activities that use fossil fuels. Within this class are the BTEX (benzene, toluene, ethylbenzene and xylenes) compounds that are considered hazardous. Among the various existing techniques for degradation of pollutants, there is advanced oxidation using H2O2 generating hidoxil radical ( OH). In this work, the mesoporous material of MCM-41 was synthesized by hydrothermal method and then was used as support, the impregnation of titanium by the method of synthesis with excess solvent to obtain the catalyst Ti-MCM-41. The catalyst was used in the reaction catalyzed removal of BTEX in water using H2O2 as oxidant. The materials were characterized by: XRD, TG/DTG, FTIR, nitrogen adsorption-desorption and FRX-EDX, in order to verify the method of impregnation of the mesoporous titanium support was effective. Catalytic tests were carried out in reactors of 20 mL containing BTEX (100.0 μg/L), H2O2 (2.0 M) and Ti-MCM-41 (2.0 g/L) in acid medium. The reaction occurred for 5 h at 60 °C and analysis were performed by gas chromatography with photoionization detector and static headspace sampler. The characterizations have proven the effectiveness of the synthesis method used and the incorporation of titanium lt in the support. The catalytic tests showed satisfactory results with conversion of more than 95 % for the studied compounds, where the catalyst 48% Ti-MCM-41 showed a higher removal efficiency of the compounds under study

Estudo cinético da degradação térmica e catalítica de petróleo pesado usando Al-MCM-41

The mesoporous nanostructured materials have been studied for application in the oil industry, in particular Al-MCM-41, due to the surface area around 800 to 1.000 m2 g-1 and, pore diameters ranging from 2 to 10 nm, suitable for catalysis to large molecules such as heavy oil. The MCM-41 has been synthesized by hydrothermal method, on which aluminum was added, in the ratio Si/Al equal to 50, to increase the generation of active acid sites in the nanotubes. The catalyst was characterized by X-ray diffraction (XRD), surface area by the BET method and, the average pore volume BJH method using the N2 adsorption, absorption spectroscopy in the infrared Fourier Transform (FT-IR) and determination of surface acidity with application of a probe molecule - n-butylamine. The catalyst showed well-defined structural properties and consistent with the literature. The overall objective was to test the Al-MCM-41 as catalyst and thermogravimetric perform tests, using two samples of heavy oil with API º equal to 14.0 and 18.5. Assays were performed using a temperature range of 30-900 ° C and heating ratios (β) ranging from 5, 10 and 20 °C min-1.The aim was to verify the thermogravimetric profiles of these oils when subjected to the action of the catalyst Al- MCM-41. Therefore, the percentage ranged catalyst applied 1, 3, 5, 10 and 20 wt%, and from the TG data were applied two different kinetic models: Ozawa-Flynn-Wall (OFW) and Kissinger-Akahrira-Sunose (KAS).The apparent activation energies found for both models had similar values and were lower for the second event of mass loss known as cracking zone, indicating a more effective performance of Al-MCM-41 in that area. Furthermore, there was a more pronounced reduction in the value of activation energy for between 10 and 20% by weight of the oil-catalyst mixture. It was concluded that the Al-MCM-41 catalyst has applicability in heavy oils to reduce the apparent activation energy of a catalyst-oil system, and the best result with 20% by weight of Al-MCM-41

Construção de bibliotecas de cDNAs subtraídos a partir das sementes de Mamona submetidas à estresse hídrico e análise in silico de transcritos potencialmente expressos sob condições de estresse: Metalotioneina, proteína reprimida por auxina de 12.5 kDa e Glutelina tipo-A3

Estresses ambientais abióticos são fatores que causam respostas ao nível molecular, fisiológico e morfológico em plantas, dependendo também de sua intensidade e duração. É visto que algumas espécies apresentam tolerância a condições estressantes e ao mesmo tempo são fontes naturais de matéria prima para indústria. Nesse contexto encontra-se a mamona (Ricinus comunnis L.), principal fonte de óleo de rícino valorizado por suas aplicações farmacêuticas e principalmente industriais, vem sendo usada como cultura em regiões onde a disponibilidade de água é reduzida, usada como fonte de renda para agricultura da região nordeste brasileira. Visto que pouco se sabe sobre as respostas moleculares que levam essa planta a tolerar regiões secas e como as sementes, principais foco de interesse, respondem a essa escassez, nesse trabalho foram construídas duas bibliotecas de cDNAs, onde a partir de uma abordagem subtrativa, continham RNAs diferencialmente expressos em sementes de plantas mamona submetidas ao estresse hídrico durante 5 dias (biblioteca L7), e a outra RNAs diferencialmente expressos em sementes controle (biblioteca L5). A biblioteca L7 apresentou a maior variedade de transcritos com um total de 182. A maior parte das funções estabelecidas pelo sistema Gene Ontology - GO, foram direcionadas aos “Processos Metabólicos” (526), em segundo “Respostas a estímulos” (57), o terceiro termo mais abundante foram referentes a “Desenvolvimento”(26). Já na biblioteca L5, foram encontrados 91 transcritos, com maior parte de suas funções referentes a “Processos Metabólicos”(413), em segundo “Respostas a estímulos” (8) e em terceiro Regulação (6). Alguns dos transcritos da biblioteca L7 foram escolhidos para análise por repetirem-se mais de 3x e não aparecerem na biblioteca L5, o que indica uma possível regulação positiva sobre estresse. As análises sobre Metalotioneína (4x), mostraram que a sequência de proteica apresentava os domínios conservados que a caracterizava como tipo II, onde são encontrados dois domínios funcionais ricos em cisteína com posições altamente conservadas, desempenhando a função de ligar-se a metais pesados, correlacionadas assim como a atividade de eliminação EROs e defesa contra o estresse oxidativo, além de apresentar homologia com a sequência de Bruguiera gymnorhiza, uma planta de mangue adaptada a ambientes salinos. Analisamos também os transcritos da referente a proteína AUXIN-REPRESSED 12.5 KDA (3x), apontada como sendo reprimida pelo hormônio auxina e associada ao processo de dormência da semente, é descrito em uma família gênica onde vários membros pertencem as vias de resposta ao estresse. Por último, analisamos a proteína GLUTELIN TYPE-A 3 (5x), uma importante proteína de armazenamento com caráter hidrofílico, possivelmente direcionada para o vacúolo. Em nosso trabalho foi possível observar um aumento de transcritos em relação a subtração controle, possivelmente reflexo do aumento do metabolismo da semente, tanto para resposta defensiva ao estresse hídrico quanto para o amadurecimento rápido da semente onde foram observados transcritos referentes a resposta oxidativa, controle hormonal, proteínas de reserva e produção de óleo.

Síntese e impregnação de peneiras moleculares Fe MCM-41 derivada de sílica da casca do arroz

The mesoporous molecular sieves of the MCM-41 and FeMCM-41 type are considered promissory as support for metals used as catalysts in oil-based materials refine processes and as adsorbents for environmental protection proposes. In this work MCM-41 and FeMCM41 were synthesized using rice husk ash - RHA as alternative to the conventional silica source. Hydrothermal synthesis was the method chosen to prepare the materials. Pre-defined synthesis parameters were 100°C for 168 hours, later the precursor was calcinated at 550°C for 2 hours under nitrogen and air flow. The sieves containing different proportions of iron were produced by two routes: introduction of iron salt direct synthesis; and a modification post synthesis consisting in iron salt 1 % and 5% impregnation in the material followed by thermal decomposition. The molecular sieves were characterized by X ray diffraction XRD, Fourier transform infrared spectroscopy FT-IR, X ray fluorescence spectroscopy XFR, scanning electronic microscopy SEM, specific surface area using the BET method, Termogravimetry TG. The kinetic model of Flynn Wall was used with the aim of determining the apparent activation energy of the surfactant remove (CTMABr) in the MCM- 41 porous. The analysis made possible the morphology characterization, identifying the presence of hexagonal structure typical for mesoporous materials, as well as observation of the MCM41 and iron of characteristic bands.

Degradacao termica e catalitica da borra oleosa de Petroleo com materiais nanoestruturados al-mcm-41 e AL-SBA-15

Aiming to reduce and reuse waste oil from oily sludge generated in large volumes by the oil industry, types of nanostructured materials Al-MCM-41 and Al-SBA-15, with ratios of Si / Al = 50, were synthesized , and calcined solids used as catalysts in the degradation of oily sludge thermocatalytic oil from oilfield Canto do Amaro, in the state of Rio Grande do Norte. Samples of nanostructured materials were characterized by thermogravimetric analysis (TG / DTG), X-ray diffraction (XRD), scanning electron microscopy (SEM), absorption spectroscopy in the infrared Fourier transform (FT-IR) and adsorption nitrogen (BET). The characterization showed that the synthesized materials resulted in a catalyst nanostructure, and ordered pore diameter and surface area according to existing literature. The oily sludge sample was characterized by determining the API gravity and sulfur content and SARA analysis (saturates, aromatics, resins and asphaltenes). The results showed a material equivalent to the average oil with API gravity of 26.1, a low sulfur content and considerable amount of resins and asphaltenes, presented above in the literature. The thermal and catalytic degradation of the oily sludge oil was performed from room temperature to 870 ° C in the ratios of heating of 5, 10 and 20 ° C min-1. The curves generated by TG / DTG showed a more accelerated degradation of oily sludge when it introduced the nanostructured materials. These results were confirmed by activation energy calculated by the method of Flynn-Wall, in the presence of catalysts reduced energy, in particular in the range of cracking, showing the process efficiency, mainly for extraction of lightweight materials of composition of oily sludge, such as diesel and gasoline