Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos

The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet

Síntese de nanopartículas de magnetita via decomposição térmica em meio não-aquoso

This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260ºC. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface

Estudos sedimentológicos e o contexto estrutural da formação Serra do Martins, nos platôs de Portalegre, Martins e Santana/RN

This dissertation deals with sedimentological and structural framework of the siliciclastic rock of the Serra do Martins Formation (FSM) in the Portalegre, Martins and Santana plateau, located to the south of Potiguar Basin, in the southwest and central Rio Grande do Norte state. This formation, regarded as of Oligo-Miocene age based on intrusive relations of the Miocene Macau volcanics, has a still disputable age due to the lack of appropriate bio and/or chronostratigraphic markers. The FSSM deposits crop out along 650 to 750 m high plateau, as a remanescent sedimentary cover directly overlying topographically uplifted pre-cambrian crystalline rocks. During the last decades, these deposits were interpreted according to a Tertiary paleoclimatic evolutionary model, associated to pedogenetic processes. The sedimentological characterization of the FSM was done through a detailed study of its facies, petrography and diagenetic features. The facies study was based on description of field relations, textures and structures, the piling up of the strata and their lateral variations. The FSM was deposited by an anastomosing to coarse-meandering fluvial system, including deposits of lag, cannel-fill, ouver-bank and flood plain. The petrographic composition of the sediments, coupled to their facies and paleocurrent directions, suggest a rather distal sourcearea, to the south of the present plateau. The diagenetic study identified an incipient grain mechanical compaction, pronounced dissolution of the framework, matrix and/or cement components, intense precipitation of kaolinite, silic and, eventually, iron oxides, besides mechanical infiltration of the clays. Most of these events, regarded in the literature as associated to near-surface conditions (eo or telodiagenesis), indicate the FSM sediments were never deeply buried. Topographic relations along longitudinal and transversal sections reaching the Potiguar Basin to the north identified regional dips that allow to discuss stratigraphic correlations between the FSM and the basin formations. The sedimentological features of the different units and the intrusive relations of the Macau volcanics were also considered in these correlations,which support the Oligo-Miocene age previously accepted for the FSM. Concerning the tectonic framework of the FSM, this work investigated the pre-cambrian to cretaceous heritage and the cenozoic deformation, allowing the recognition of pre-, sin and post-FSM structures. The crystalline basement, belonging to the Seridó Belt, displays NE and WNW foliation trends related to the Brasiliano-age ductile shear zones. In this terrain, brittle-ductile and brittle NE- and NW-trending structures, associated with extensional joints filled with pegmatites and quartz veins, are related to an E-W compression by the end of Brasiliano Cycle. The E-W joints and NE-trending fractures were reactivated by N-S to N-S to NW extension during late Jurassic to Cretaceous times, controlling the emplacement of the Rio Ceará-Mirim basic dyke swarm and the opening of the Potiguar rift basin

Materiais a base de estruturas carbonáceas para a remoção de ácidos húmicos em soluções aquosas através da adsorção e oxidação

O presente estudo aborda a utilização de carvão ativado comercial na remoção de ácidos húmicos em meio aquoso. O objetivo principal é desenvolver e caracterizar materiais carbonáceos visando aplicações de remoção de ácidos húmicos em meio aquoso por processos de adsorção e oxidação. Testes de remoção do poluente foram desenvolvidos com a utilização do carvão comercial, carvão modificado a partir de tratamentos ácidos e compósito confeccionado com a impregnação de ferro no carvão. Espumas de carbono com dispersões de carvão ativado e óxidos de ferro também foram desenvolvidas buscando aplicações de remoção do poluente através de processos eletroquímicos. Os resultados das caracterizações demonstraram ganho de área superficial a partir do tratamento ácido, a presença dispersa de ferro em todo carvão na forma de fase maghemita com a introdução do metal, e ganho de estabilidade eletroquímica na espuma, com a presença de dispersões de carvão ativados impregnados com ferro. O processo oxidativo Fenton, foto assistido por radiação UV, demonstrou maior eficiência para remoção do ácido húmico em água.

Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos

The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet

Síntese de nanopartículas de magnetita via decomposição térmica em meio não-aquoso

This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260ºC. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface

Synthesis and characterization of lanthanum- and yttrium-doped Fe2O3 pigments

MELO, D. M. A. et al. Synthesis and charactezarion of lanthanum and yttrium doped Fe2O3 pigments. Cerâmica, São Paulo, v. 53, p. 79-82, 2007.

Dos caminhos de água aos caminhos de ferro: a construção da hegemonia de Natal através das vias de transporte (1820-1920)

At a time of changes on the territory during the 19th century, the political and socioeconomic elites of the province and later State of Rio Grande do Norte evolved a discourse in order to justify the permanence of Natal as a city holding a status of capital. In this work we analyze the means employed by the ruling classes to impose their wish to raise Natal to an outstanding position among the existing cities by intervening on the territory during a period of one hundred years (1820-1920). During that time, which was characterized by changing commercial flows and technological development, the elites interventions were essentially directed to the implementation of modes of transportation, especially the railway. We try to understand the reinforcement of Natal as a capital city not only in political and administrative terms, but mainly in a commercial and symbolic manner, through the discourse and interventions undertaken by the local administrative elites, who stimulated the creation of a set of relations on the territory that also imprinted visible marks in the capital s urban fabric. These interventions were based upon the establishment of an infrastructure for exporting the State s production, firstly through and despite the Potengi River, and later on by the construction of railways. Although the project of Natal s hegemony had been outlined before the establishment of the railway network, in both cases the ultimate objective was to reinforce and develop the capital city as a commercial urban center to the detriment of other cities

O papel modulatório do ferro sobre a resposta imune na Leishmaniose Visceral

Iron is an essential element for many cellular functions, including the immune response against intracellular pathogens. In this study, we aimed evaluate the effect of iron on IRP2, IFN-γ, TNF-α, IL-6, IL-10, MIG and IP10 expression in PBMC and assess the effect of the spleen parasite load on the expression of these genes in the spleen of L. infantum naturally infected dogs. Blood sample from 7 DTH+ donor was collected and PBMC was obtained. The cells were cultivated in absence (iron chelator desferroximane, DFO 10 μM supplemented media) or in presence of iron (hemin 6 mM) for 1 h, followed by stimulation with Leishmania infatum antigen for 4 h. 44 dog spleen samples were obtained and parasite load in this organ was determinate by qPCR. Gene expression was analyzed by qPCR and cytokine production quantified by flow cytometry. In antigen stimulated cells, genes involved in immune response are significantly more expressed in presence of iron. T CD4+ and TCD8+ lymphocytes produces IFN-γ, TNF-α and IL-10 possibly in iron dependent pathway. Monocytes antigen stimulated reduced TNF-α, IL-6 and IL-10 production in presence of iron. We found spleen of infected dogs IRP2 expression increases according to parasite load in that organ, while an inverse profile was found for IFN-γ, TNF-α e IL-10 expression. These results suggest that T lymphocytes depends on iron to produce IFN-γ, TNF-α and IL-10, while iron seems to inhibit cytokine production in monocytes. So, we propose an immunoregulatory mechanism carried out by iron during L. infantum infection in humans and dogs

Resposta de Chromobacterium Violaceum cultivada em alta concentração de ferro

The Chromobacterium violaceum is a β-proteobacterium Gram-negative widely found in tropical and subtropical regions, whose genome was sequenced in 2003 showing great metabolic versatility and biotechnological and pharmaceutical potential. Given the large number of ORFs related to iron metabolism described in the genome of C. violaceum, the importance of this metal for various biological processes and due to lack of data about the consequences of excess of iron in free-living organisms, it is important to study the response mechanism of this bacterium in a culture filled with iron. Previous work showed that C. violaceum is resistant to high concentrations of this metal, but has not yet been described the mechanism which is used to this survival. Thus, to elucidate the response of C. violaceum cultured in high concentrations of iron and expecting to obtain candidate genes for use in bioremediation processes, this study used a shotgun proteomics approach and systems biology to assess the response of C. violaceum grown in the presence and absence of 9 mM of iron. The analysis identified 531 proteins, being 71 exclusively expressed by the bacteria grown in the presence of the metal and 100 just in the control condition. The increase in expression of proteins related to the TCA cycle possibly represents a metabolic reprogramming of the bacteria caused by high concentration of iron in the medium. Moreover, we observed an increase in the activity assay of superoxide dismutase and catalase as well as in Total Antioxidant Activity assay, suggesting that the metal is inducing oxidative stress in C. violaceum that increases the levels of violacein and antioxidant enzymes to better adapt to the emerging conditions. Are also part of the adaptive response changes in expression of proteins related to transport, including iron, as well as an increased expression of proteins related to chemotaxis response, which would lead the bacteria to change the direction of its movement away from the metal. Systems Biology results, also suggest a metabolic reprogramming with mechanisms coordinated by bottleneck proteins involved in transcription (GreA), energy metabolism (Rpe and TpiA) and methylation (AhcY)

Obtenção de óxidos a base de níquel e cobalto para reação de oxidação parcial do metano

Nickel-based catalysts supported on alumina have been widely used in various reactions to obtain synthesis gas or hydrogen. Usually, higher conversion levels are obtained by these catalysts, however, the deactivation by coke formation and sintering of metal particles are still problems to be solved. Several approaches have been employed in order to minimize these problems, among which stands out in recent years the use of additives such as oxides of alkali metals and rare earths. Similarly, the use of methodologies for the synthesis faster, easier, applicable on an industrial scale and to allow control of the microstructural characteristics of these catalysts, can together provide the solution to this problem. In this work, oxides with spinel type structure AB2O4, where A represents divalent cation and B represents trivalent cations are an important class of ceramic materials investigated worldwide in different fields of applications. The nickel cobaltite (NiCo2O4) was oxides of spinel type which has attracted considerable interest due to its applicability in several areas, such as chemical sensors, flat panel displays, optical limiters, electrode materials, pigments, electrocatalysis, electronic ceramics, among others. The catalyst precursor NiCo2O4 was prepared by a new chemical synthesis route using gelatine as directing agent. The polymer resin obtained was calcined at 350°C. The samples were calcined at different temperatures (550, 750 and 950°C) and characterized by X ray diffraction, measurements of specific surface area, temperature programmed reduction and scanning electron microscopy. The materials heat treated at 550 and 750°C were tested in the partial oxidation of methane. The set of techniques revealed, for solid preparations, the presence of the phase of spinel-type structure with the NiCo2O4 NixCo1-xO solid solution. This solid solution was identified by Rietveld refinement at all temperatures of heat treatment. The catalyst precursors calcined at 550 and 750°C showed conversion levels around 25 and 75%, respectively. The reason H2/CO was around 2 to the precursor treated at 750°C, proposed reason for the reaction of partial oxidation of methane, one can conclude that this material can be shown to produce synthesis gas suitable for use in the synthesis Fischer-Tropsch process

Síntese e caracterização de óxidos de cério e cobalto obtidos por gel-combustão e Pechini aplicados às reações de oxidação de n-hexano

Oxide type spinel AB2O4 presents structure adjusted for application in the automobile industry. The spinel of cobalt has many practical applications had its excellent physical and chemical properties such as catalyst in hydrocarbon oxidation reaction. The CeO2 has been used in many of these processes because it assigns to a material with excellent thermal resistance and mechanics, high capacity of oxygen stockage (OSC) among others properties. This work deals with the synthesis, characterization and catalytic application of spinel of cobalt and CeO2 with fluorita structure, obtained for method of Pechini and method of Gel-Combustion. The process of Pechini, the puff was obtained at 300 ºC for 2 h in air. In the process of Gel-Combustion the approximately at 350 ºC material was prepared and burnt for Pyrolysis, both had been calcined at 500 ºC, 700 ºC, 900 ºC and 1050 ºC for 2 h in air. The materials of the calcinations had been characterized by TG/DTA, electronic microscopy of sweepings (MEV), spectroscopy of absorption in the infra-red ray (FTIR) and diffraction of X-rays (DRX). The obtained material reaches the phase oxide at 450 oC for Pechini method and 500 °C for combustion method. The samples were submitted catalytic reaction of n-hexane on superficies of materials. The reactor function in molar ration of 0, 85 mol.h-1.g-1 and temperature of system was 450 °C. The sample obtained for Pechini and support in alumine of superficial area of 178,63 m2.g-1 calcined at 700 ºC, give results of catalytic conversions of 39 % and the sample obtained for method of gel-combustion and support in alumina of 150 mesh calcined at 500 ºC result 13 % of conversion. Both method were selective specie C1

Degradação do PMMA através da reação despolimerização uitlizando catalisadores de óxidos mistos

In this work, mixed oxides were synthesized by two methods: polymeric precursor and gel-combustion. The oxides, Niquelate of Lanthanum, Cobaltate of Lanthanum and Cuprate of Lanthanum were synthesized by the polymeric precursor method, and treated at 300 º C for 2 hours, calcined at 800 º C for 6h in air atmosphere. In gel-combustion method were produced and oxides using urea and citric acid as fuel, forming for each fuel the following oxides Ferrate of Lanthanum, Cobaltato of Lanthanum and Ferrato of Cobalt and Lanthanum, which were submitted to the combustion process assisted by microwave power maximum of 10min. The samples were characterized by: thermogravimetric analysis, X-ray diffraction; fisisorção of N2 (BET method) and scanning electron microscopy. The reactions catalytic of depolymerization of poly (methyl methacrylate), were performed in a reactor of silica, with catalytic and heating system equipped with a data acquisition system and the gas chromatograph. For the catalysts synthesized using the polymeric precursor method, the cuprate of lanthanum was best for the depolymerization of the recycled polymer, obtaining 100% conversion in less time 554 (min), and the pure polymer, was the Niquelate of Lanthanum, with 100% conversion in less time 314 (min). By gel-combustion method using urea as fuel which was the best result obtained Ferrate of Lanthanum for the pure polymer with 100% conversion in less time 657 (min), and the recycled polymer was Cobaltate of Lanthanum with 100 % conversion in less time 779 (min). And using citric acid to obtain the best result for the pure polymer, was Ferrate of Lanthanum with 100% conversion in less time 821 (min and) for the recycled polymer, was Ferrate of Lanthanum with 98.28% conversion in less time 635 (min)

Estudo da adição do resíduo proveniente da extração de minério de ferro em argilas do Rio Grande do Norte

The mining industry is responsible for the generation of waste from their natural process of extraction. The mining impacts in urban areas are of special importance due to the high urban occupation, which are exacerbated due to the proximity of the mined areas and populated areas. Some solutions to wastedisposal have the potential to significantly reduce the environmental risks and liabilities, but represent higher costs in the stages of deployment and operation. The addition of mining waste as raw material in the development of commercial products reduces the environmental impacts, transforming the waste into a positive element in the generation of employment and income. This thesis studies the incorporation of waste iron ore in two clays, one from the ceramic industry of the City of Natal and the other from the ceramic industry of the Seridó Region, both in the State of Rio Grande do Norte, Brazil. Percentages of iron ore waste of 5%, 10% , 15%, 20%, 25% and 30% were used in the tested ceramic matrix. The two clays and the iron ore waste used as part of this investigation were characterized by X-ray diffraction tests, X-ray fluorescence tests, differential thermal analysis, thermogravimetric analysis and dilatometric analysis. The samples were sintered under temperatures of 850 °C, 950 °C and 1050°C at a heating rate of 5 °C/min with isotherms of two hours. The following tests were performed with the samples: linear shrinkage, water absorption, apparent porosity, apparent density, mass loss in fire and bending resistance in order to obtain their physical and mechanical properties. An amount of 5% of waste iron ore in the matrix clay at a temperature of 850 0C resulted in na increase of about 65% in the tensile strength of the clay samples from the Natal ceramic industry. A linear shrinkage of only 0.12% was observed for the samples, which indicates that the physical properties of the final product were not influenced by the addition of the waste

Estudo do efeito da adição da escória de aciaria no processamento e propriedades finais de telhas cerâmicas

This research presents an overview of the addition steelwork dust of ceramic shingles in order to contribute to the utilization use of such residue. The ceramic industry perspective in the Brazilian State of Piauí is quite promising. Unlike other productive sectors, the ceramic industry uses basically natural raw materials. Its final products are, in short, the result of transforming clay compounds. These raw materials are composed primarily of aluminum oxide, silicon, iron, sodium, magnesium, end calcium, among others. It was verified that steelwork dust is composed primarily of these same oxides, so that its incorporation in to structural ceramics is a very reasonable idea. Both clay and steelwork powder were characterized by AG, XRF, XRD, TGA and DTA. In addition, steelwork dust samples containing (0%, 5%, 10%, 15%, 20% and 25%) were extruded and burned at 800°C, 850°C, 900°C and 950°C. Then t echnological tests of linear shrinkage, water uptake, apparent porosity, apparent density and flexural strengthwere carried at. The results showed the possibility of using steelwork powder in ceramic shingles until 15% significant improvement in physical and mechanical properties. This behavior shows the possibility of burning at temperatures lower than 850ºC, thus promoting a product final cost reduction