The influence of heat treatment on the corrosion behaviour of as-spun amorphous Al88Ni6La6 alloy in 0.01 M NaCl solution

The effect of the heat treatment on the corrosion behaviour of amorphous Al₈₈Ni₆La₆ made by melt-spun has been investigated by electrochemical measurements. Heat treatment was carried out at 523 K and 673 K for 4 min and 15 min respectively. The evolution of the crystallization process after annealing was identified by differential scanning calorimeter (DSC) as well as X-ray diffraction. The XRD patterns show that the structure of samples heat-treated at higher temperature changes towards a crystal state. The results obtained from the polarization curves reveal that all Al₈₈Ni₆La₆ alloys exhibit spontaneously passivated behaviour. Furthermore, it is noted that the partially crystallized alloy has the best corrosion resistance in comparison with as-spun amorphous and fully crystallized alloys, while the fully crystallized sample shows deterioration in the corrosion resistance.

Preparation and characterization of graphitic carbon nitride through pyrolysis of melamine

Graphitic carbon nitride (g-C₃N₄) has been synthesized via a two-step pyrolysis of melamine (C₃H₆N₆) at 800°C for 2 h under vacuum conditions. X-ray diffraction (XRD) patterns strongly indicate that the synthesized sample is g-C₃N₄. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) morphologies indicate that the product is mainly composed of graphitic carbon nitride. The stoichiometric ratio of C:N is determined to be 0.72 by elemental analysis (EA). Chemical bonding of the sample has been investigated by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FTIR). Electron energy loss spectroscopy (EELS) verifies the bonding state between carbon and nitrogen atoms. Optical properties of the g-C₃N₄ were investigated by PL (photoluminescence) measurements and UV–Vis (ultraviolet–visible) absorption spectra. We suppose its luminescent properties may have potential application as component of optical nanoscale devices. Thermogravimetric analysis (TGA) and differential thermal analysis (DTA) were also performed.

Photo induced silver on nano titanium dioxide as an enhanced antimicrobial agent for wool

In this study an effective nanocomposite antimicrobial agent for wool fabric was introduced. The silver loaded nano TiO(2) as a nanocomposite was prepared through UV irradiation in an ultrasonic bath. The nanocomposite was stabilized on the wool fabric surface by using citric acid as a friendly cross-linking agent. The treated wool fabrics indicated an antimicrobial activity against both Staphylococcus aureus and Escherichia coli bacteria. Increasing the concentration of Ag/TiO(2) nanocomposite led to an improvement in antibacterial activities of the treated fabrics. Also increasing the amount of citric acid improved the adsorption of Ag/TiO(2) on the wool fabric surface leading to enhance antibacterial activity. The EDS spectrum, SEM images, and XRD patterns was studied to confirm the presence of existence of nanocomposite on the fabric surface. The role of both cross-linking agent and nanocomposite concentrations on the results was investigated using response surface methodology (RSM).

Reducing photoyellowing of wool using nano TiO2

Wool is the most important animal fiber used in textile industries, but its photostability is very low. Scientists have searched for new ways to increase the photostability of wool. As TiO2 nano particles have features suitable for new applications, the UV-blocking power of nano TiO2 may be used for protecting fabrics against UV rays. Treatment of wool with TiO 2 can be effective for controlling photodegradation. This study focused on protecting wool fabric against UV rays using nano TiO2. To this end, oxidized and raw wool were treated with citric acid as the cross-linking agent and different concentrations of nano TiO2. The whiteness and yellowness of wool fabric samples were reported. XRD patterns proved the existence of TiO2 nano-particles on the wool surface. Finally, the results revealed that nano TiO2 is a suitable UV absorber on wool fabric and its effect depends on concentration.