The influence of heat treatment on the corrosion behaviour of as-spun amorphous Al88Ni6La6 alloy in 0.01 M NaCl solution

The effect of the heat treatment on the corrosion behaviour of amorphous Al₈₈Ni₆La₆ made by melt-spun has been investigated by electrochemical measurements. Heat treatment was carried out at 523 K and 673 K for 4 min and 15 min respectively. The evolution of the crystallization process after annealing was identified by differential scanning calorimeter (DSC) as well as X-ray diffraction. The XRD patterns show that the structure of samples heat-treated at higher temperature changes towards a crystal state. The results obtained from the polarization curves reveal that all Al₈₈Ni₆La₆ alloys exhibit spontaneously passivated behaviour. Furthermore, it is noted that the partially crystallized alloy has the best corrosion resistance in comparison with as-spun amorphous and fully crystallized alloys, while the fully crystallized sample shows deterioration in the corrosion resistance.<br />