Wet-spinning of PEDOT:PSS/Functionalized-SWNTs Composite: a Facile Route Toward Production of Strong and Highly Conducting Multifunctional Fibers

With the aim of fabricating multifunctional fibers with enhanced mechanical properties, electrical conductivity and electrochemical performance, we develop wet-spinning of composite formulation based on functionalized PEG-SWNT and PEDOT:PSS. The method of addition and loading are directly correlated to the quality and the ease of spinnability of the formulation and to the mechanical and electrical properties of the resultant fibers. Both the fiber modulus (Y) and strength (σ) scaled linearly with PEG-SWNT volume fraction (Vf). A remarkable reinforcement rate of dY/dVf = 417 GPa and dσ/dVf = 4 GPa were obtained when PEG-SWNTs at Vf ≤ 0.02. Further increase of PEG-SWNTs loading (i.e. up to Vf 0.12) resulted in further enhancements up to 22.8 GPa and 254 MPa in Modulus and ultimate stress, respectively. We also show the enhancement of electrochemical supercapacitor performance of composite fibers. These outstanding mechanical, electrical and electrochemical performances place these fibers among the best performing multifunctional composite fibers.

Scalable One-Step Wet-Spinning of Graphene Fibers and Yarns from Liquid Crystalline Dispersions of Graphene Oxide: Towards Multifunctional Textiles

Key points in the formation of liquid crystalline (LC) dispersions of graphene oxide (GO) and their processability via wet-spinning to produce long lengths of micrometer-dimensional fibers and yarns are addressed. Based on rheological and polarized optical microscopy investigations, a rational relation between GO sheet size and polydispersity, concentration, liquid crystallinity, and spinnability is proposed, leading to an understanding of lyotropic LC behavior and fiber spinnability. The knowledge gained from the straightforward formulation of LC GO “inks” in a range of processable concentrations enables the spinning of continuous conducting, strong, and robust fibers at concentrations as low as 0.075 wt%, eliminating the need for relatively concentrated spinning dope dispersions. The dilute LC GO dispersion is proven to be suitable for fiber spinning using a number of coagulation strategies, including non-solvent precipitation, dispersion destabilization, ionic cross-linking, and polyelectrolyte complexation. One-step continuous spinning of graphene fibers and yarns is introduced for the first time by in situ spinning of LC GO in basic coagulation baths (i.e., NaOH or KOH), eliminating the need for post-treatment processes. The thermal conductivity of these graphene fibers is found to be much higher than polycrystalline graphite and other types of 3D carbon based materials.

Exploiting high quality PEDOT:PSS–SWNT composite formulations for wet-spinning multifunctional fibers

In order to exploit the inherent properties of carbon nanotubes (CNT) in any polymer composite, systematic control of carbon nanotube loading and protocols that mitigate against CNT bundling are required. If such composites are to be rendered in fiber form via wet-spinning, then CNT bundling during the coagulation process must also be avoided. Here we have achieved this by utilizing highly exfoliated single walled carbon nanotubes (SWNT) and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonicacid) (PEDOT:PSS) to obtain wet-spinnable composite formulations at various nanotube volume fractions (Vf). The addition of only 0.02 Vf of aggregate-free and individually dispersed SWNT resulted in a significant enhancement of modulus, tensile strength, electrical conductivity and two cell electrode specific capacitance of PEDOT:PSS–SWNT composite fibers to 5.2 GPa, 200 MPa, 450 S cm−1 and 59 F g−1 by the rate of dY/dVf = 89 GPa, dσ/dVf = 3.2 GPa, dS/dVf = 13 300 S cm−1 and 6 folds, respectively.

One-Step Wet-Spinning Process of Poly(3,4-ethylenedioxythiophene):Poly(styrenesulfonate) Fibers and the Origin of Higher Electrical Conductivity

A simplified wet-spinning process for the production of continuous poly (3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) fibers is reported. Conductivity enhancement of PEDOT:PSS fibers up to 223 S cm−1 has been demonstrated when these fibers are exposed to ethylene glycol as a post-synthesis processing step. In a new spinning approach it is shown that by employing a spinning formulation consisting of an aqueous blend of PEDOT:PSS and poly(ethlylene glycol), the need for post-spinning treatment with ethylene glycol is eliminated. With this approach, 30-fold conductivity enhancements from 9 to 264 S cm−1 are achieved with respect to an untreated fiber. This one-step approach also demonstrates a significant enhancement in the redox properties of the fibers. These improvements are attributed to an improved molecular ordering of the PEDOT chains in the direction of the fiber axis and the consequential enrichment of linear (or expanded-coil like) conformation to preference bipolaronic electronic structures as evidenced by Raman spectroscopy, solid-state electron spin resonance (ESR) and in situ electrochemical ESR studies.

Spinning Carbon Nanotube-Gel Fibers Using Polyelectrolyte Complexation

Biopolymer-single walled carbon nanotube (SWNT)-biopolymer fibers were prepared using a continuous flow spinning approach. Polyelectrolyte complexation was facilitated by injecting a SWNT-biopolymer dispersion into a coagulation bath containing a biopolymer of opposite charge. We showed that the ability to spin fibers and their properties depend on processing conditions such as polyelectrolyte pH, sonolysis regime (conditions employed to disperse SWNT) and the order of adding the anionic and cationic biopolymer solutions. Maximizing the ionic nature through changes in the pH increased spin-ability, while combining a sonicated dispersion with an as-prepared (non-sonicated) polyelectrolyte solution allowed us to optimize sonolysis conditions while retaining spin-ability of fibers with smooth surface morphology. Addition of the cationic biopolymer-SWNT dispersion to the anionic biopolymer solution resulted in mechanical reinforcement with the increase in SWNT loading fraction. All fibers decreased their electrical resistance upon exposure to water vapor.

Electrostatic spinning assembly

A spinneret for producing nanofibres from a viscous liquid using electrostatic spinning in an electric field is described. The spinneret includes one or more narrow annular bodies radially centred about and axially spaced along a central axis. The annular bodies may be discs, rings, or coils.

Electrostatic spinning assembly

A spinneret for producing nanofibres from a viscous liquid using electrostatic spinning in an electric field is described. The spinneret includes one or more narrow annular bodies radially centred about and axially spaced along a central axis. The annular bodies may be discs, rings, or coils.

14N overtone magic angle spinning NMR

Overtone NMR spectroscopy has the potential to provide high-resolution ¹⁴N solid-state NMR spectra. The technique was first developed during the 1980s but has only recently been successfully combined with magic angle spinning (MAS), providing improved sensitivity and resolution as well as enabling more advanced approaches such as indirect detection and signal enhancement methods. This report provides a brief background to ¹⁴N overtone NMR, describing the ways in which it differs from conventional NMR and the challenges that arise as a result. The effects of MAS on the overtone spectrum are then presented and illustrated with numerous experimental and simulated examples. Finally, several recent developments enabled by MAS are described and some potential future directions are suggested.

A facile approach to spinning multifunctional conductive elastomer fibres with nanocarbon fillers

Electrically conductive elastomeric fibres prepared using a wet-spinning process are promising materials for intelligent textiles, in particular as a strain sensing component of the fabric. However, these fibres, when reinforced with conducting fillers, typically result in a compromise between mechanical and electrical properties and, ultimately, in the strain sensing functionality. Here we investigate the wet-spinning of polyurethane (PU) fibres with a range of conducting fillers such as carbon black (CB), single-walled carbon nanotubes (SWCNTs), and chemically converted graphene. We show that the electrical and mechanical properties of the composite fibres were strongly dependent on the aspect ratio of the filler and the interaction between the filler and the elastomer. The high aspect ratio SWCNT filler resulted in fibres with the highest electrical properties and reinforcement, while the fibres produced from the low aspect ratio CB had the highest stretchability. Furthermore, PU/SWCNT fibres presented the largest sensing range (up to 60% applied strain) and the most consistent and stable cyclic sensing behaviour. This work provides an understanding of the important factors that influence the production of conductive elastomer fibres by wet-spinning, which can be woven or knitted into textiles for the development of wearable strain sensors.

Wet-spinning of multifunctional graphene fibers using graphene oxide liquid crystals

The recent discovery of liquid crystalline (LC) behavior of graphene oxide (GO) dispersions in various organic, and aqueous media brings added control to the assembly of larger structures using the chemical process approach.[1-3] The LC state can be used to direct the ordered assembly of nanocomponents in macroscopic structures via simple methods like wet-spinning. [3] Here, we developed a scaleable fabrication route to produce graphene fibers via a facile continuoes wetspinning methode. We develop solid understanding in the required criteria to correlate processability with LC behavior, aspect ratio and the dispersion concentration to provide a viable platform for spinning of LC GO. We demonstrate a striking result that highlits the importance of GO sheet size and polydispersity in generating wetspinnable LC GO dispersions from very low spinning dope concentrations (as low as 0.075 wt. %). The new knowledge gained through rheological investigations provides a sound explanation as to why continuous spinning of binder-free GO fibers is enabled by the LC behavior at this very low concentration.

Understanding key wet spinning parameters in an ionic liquid spun regenerated cellulosic fibre

The use of ionic liquid solvents for thespinning of regenerated cellulose fibres has thepotential to produce both technical and textile graderegenerated cellulose fibres. When spinning fibres,many parameters impact the material properties of thespun fibre. In this study, key wet spinning parametershave been investigated for the development of regeneratedcellulose fibres from ionic liquid solutions. Thecoagulation and associated diffusion equilibrium werecalculated for two imidazolium-based ILs, and it wasfound that the anion largely influenced the coagulationkinetics. This was likely due to the associationbetween the anion of the IL and cellulose. Theorientation of the polymer chains is known to influencethe mechanical properties greatly; previously, hotstretching was used to orientate cellulose acetate. Herewe investigated this influence on the mechanicalproperties of regenerated cellulose fibres by applying apost stretch at different stretch ratios.