Design and fabrication of an electrode for low-actuation-voltage electrowetting-on-dielectric devices

This paper presents the design and fabrication of an electrode for low-actuation-voltage electrowetting-on-dielectric (EWOD) devices. The electrode which takes advantage of a novel shape is used to develop an EWOD device. The fabrication process for the electrode and the device development includes laser exposure, wet developing, etching, and stripping. A dielectric layer of 5% (wt./wt.) Polyvinylidene difluoride (PVDF) is used for the electrode insulation. In addition, a very thin (50 nm) layer of Teflon is coated on the EWOD surface to provide hydrophobicity. It is observed that a thin and high dielectric-constant layer can reduce the actuation voltage in the EWOD device. An actuation voltage of 14.8 V was achieved by the EWOD device.

Reducing electrowetting-on-dielectric actuation voltage using a novel electrode shape and a multi-layer dielectric coating

This paper presents design and fabrication of an electrowetting-on-dielectric (EWOD) device using a novel electrode shape and a multi-layer dielectric coating that reduce the actuation voltage of the device to less than 12.6 V. The fabrication of the EWOD electrodes is carried out in several steps including laser exposure, wet developing, etching, and stripping. A high-dielectric-constant multi-layer dielectric coating containing a 770 nm thick Polyvinylidene difluoride (PVDF) layer and a 1 µm thick Cyanoethyl pullulan (CEP) layer, is deposited on the EWOD electrodes for insulation. This multi-layer dielectric structure exhibits a high capacitance per unit area, and the novel electrode shape changes the actuation force at the droplet contact line reducing the voltage required to operate the device. In addition, an overlaying Teflon layer of 50 nm is placed on top of the dielectric structure to provide a hydrophobic surface for droplet manipulation. It is observed from the experiments that the electrode shape and the dielectric structure have contributed to the reduction of the actuation voltage of the EWOD device.

Change in dielectric properties in the microwave frequency region of polypyrrole-coated textiles during aging

Complex permittivity of conducting polypyrrole (PPy)-coated Nylon-Lycra textiles ismeasured using a free space transmission measurement technique over the frequency range of1–18 GHz. The aging of microwave dielectric properties and reflection, transmission and absorptionfor a period of 18 months is demonstrated. PPy-coated fabrics are shown to be lossy over thefull frequency range. The levels of absorption are shown to be higher than reflection in the testedsamples. This is attributed to the relatively high resistivity of the PPy-coated fabrics. Both the dopantconcentration and polymerisation time affect the total shielding effectiveness and microwave agingbehaviour. Distinguishing either of these two factors as being exclusively the dominant mechanismof shielding effectiveness is shown to be difficult. It is observed that the PPy-coated Nylon-Lycrasamples with a p-toluene sulfonic acid (pTSA) concentration of 0.015 M and polymerisation times of60 min and 180 min have 37% and 26% decrease in total transmission loss, respectively, upon agingfor 72 weeks at room temperature (20 C, 65% Relative humidity (RH)). The concentration of thedopant also influences the microwave aging behaviour of the PPy-coated fabrics. The samples with ahigher dopant concentration of 0.027 mol/L pTSA are shown to have a transmission loss of 32.6% and16.5% for short and long polymerisation times, respectively, when aged for 72 weeks. The microwaveproperties exhibit better stability with high dopant concentration and/or longer polymerization times.High pTSA dopant concentrations and/or longer polymerisation times result in high microwaveinsertion loss and are more effective in reducing the transmission and also increasing the longevity ofthe electrical properties.