Effect of crystallization on corrosion resistance of Cu52.5Ti30Zr11.5Ni6 bulk amorphous alloy

The effects of crystallization on the corrosion resistance of a  Cu52.5Ti30Zr11.5Ni6 bulk amorphous alloy in 1 mol/L HCl, and 6 mol/L NaOH solutions were studied. The amorphous alloy was identified by  differential thermal analysis(DSC) and by X-ray diffraction(XRD). The partially and fully crystallized alloys were prepared by controlling the annealing  temperatures at 738 and 873 K for 1 and 12 min, respectively, and the corrosion resistances of those annealed alloys were compared with that of the amorphous alloy by immersion test and potentiodynamic measurements in 1 mol/L HCl and 6 mol/L NaOH solutions. The results show that the  partially crystallized alloy exhibits high corrosion resistance, whereas full crystallization results in deteriorated corrosion resistance compared with that of the as-cast amorphous alloy.

Exploring corrosion protection of Mg via ionic liquid pretreatment

We present the development of a 10–100 nanometer thick surface film upon pure Mg on exposure to an ionic liquid (IL) based on the bis(trifluoromethanesulfonyl)amide (TFSA) anion. This film formation is the result of the oxidative reactivity of the metal in the IL, with the subsequent effect of ultimately protecting the underlying metal from corrosion in aqueous chloride containing solution. Film formation was studied in the IL using an electrochemical droplet cell. It was seen that this film is adherent and subsequently facilitates appreciable protection against corrosion as judged by subsequent electrochemical testing in the form of potentiodynamic polarization and impedance spectroscopy, along with direct observation. The physical film morphology was studied by electron microscopy and focused ion beam.

The corrosion inhibition mechanism of new rare earth cinnamate compounds — electrochemical studies

A combination of linear polarisation resistance (LPR) and cyclic potentiodynamic polarisation (CPP) measurements demonstrated that the lanthanum-4 hydroxy cinnamate compound could inhibit both the cathodic and anodic corrosion reactions on mild steel surfaces exposed to 0.01 M NaCl solutions. However, the dominating response was shown to vary with inhibitor concentration. At the concentrations for which the highest level of protection was achieved, both REM-4 hydroxy cinnamate (REM being lanthanum and mischmetal) displayed a strong anodic behaviour for mild steel and their inhibition performance, including their resistance against localised attack, improved with time.

Electrochemical impedance spectroscopy (EIS) measurements and modelling were carried out so as to propose a simple electrical model and correlate the extracted parameters to the inhibition mechanism put forward for REM-cinnamate based compounds. The results supported the high corrosion inhibition performance of the compounds as well as the build-up of a protective film with time. Based on a two-layer model the results suggested that the upper layer of the inhibitor film seemed to offer less resistance to the diffusion of electrochemically active species than the highly resistive inner layer at the film/metal interface.

Corrosion mitigation of mild steel by new rare earth cinnamate compounds

Corrosion rate measurements based on weight loss (i.e., mild steel immersed for seven days in 0.01 M NaCl) and linear polarization resistance (LPR) techniques have shown that even low concentrations (200 ppm) of cerium and lanthanum cinnamates are able to significantly inhibit corrosion. Of all the compounds investigated in this work Ce(4-methoxycinnamate)3· 2 H2O and La(4-methoxycinnamate)3· 2 H2O compounds exhibited the greatest inhibition and, in comparison with the component inhibitors, a synergy was clearly observed. The mechanism of corrosion inhibition was investigated using cyclic potentiodynamic polarization (CPP) measurements. The results suggest that La(4-nitrocinnamate)3· 2 H2O and Ce(4-methoxycinnamate)3· 2 H2O behave as mixed inhibitors and improve the resistance of steel against localized attack.

Corrosion protection of AA2024-T3 using rare earth diphenyl phosphates

Existing corrosion protection technologies for aluminium alloys utilising chromates are environmentally damaging and extremely toxic. This paper presents a preliminary investigation into rare earth diphenyl phosphates as new environmentally benign corrosion inhibitors. Full immersion weight loss experiments, cyclic potentiodynamic polarisation measurements and Raman spectroscopy were used in this study. Results show cerium diphenyl phosphate (Ce(dpp)₃) acts as a cathodic inhibitor, decreasing cathodic current density and E_corr by passivating cathodic intermetallic particles on the alloy surface. Mischmetal diphenyl phosphate (Mm(dpp)₃) acts a mixed inhibitor, shifting E_corr to more noble values, decreasing cathodic current density, increasing the breakdown potential and suppressing pitting.

Surface modification for enhanced corrosion resistance using fluid bed reactor chemical vapour deposition (FBR-CVD)

The use of materials with otherwise desirable mechanical properties is often problematic in practice as a result of corrosion. Susceptibility may arise for a number of reasons, including an electrochemically heterogeneous surface or destabilisation of a passive film. These shortcomings have historically been overcome through the use of various coatings or claddings. However, a more robust surface layer with enhanced corrosion resistance could possibly be produced via local surface alloying using a fluidised bed. A fluidised bed treatment allows a surface to be alloyed, producing a distinct surface layer up to tens of microns thick. Surface alloying additions can be selected on the basis of whether they are known or suspected to enhance the corrosion resistance of a particular material, whilst at a minimum, surface alloying likely provides a more electrochemically homogeneous surface. Electrochemical evaluations using potentiodynamic polarisations in NaCl electrolytes have shown chromised plain carbon and stainless steel surfaces have decreased rates of corrosion, decreased passive current densities, and ennobled pitting potentials relative to untreated specimens.

Anodising AA5083 aluminium alloy using ionic liquids

Aluminium, as the current collector in lithium batteries, has shown reduced corrosion susceptibility in room temperature molten salts (1, 2). Moreover, previous studies have established that corrosion mitigation is achieved on magnesium alloys using ionic liquids pretreatments (3, 4). This paper investigated the anodisation of AA5083 aluminium alloy in Trihexyl(tetradecyl)phosphonium bis(trifluoromethylsulfony) ([P6,6,6,14][NTf2]) ionic liquid by applying a constant current followed by holding at the maximum potential for a period of time. Potentiodynamic polarisation results show that the treated surfaces were more corrosion resistant in 0.1 M sodium chloride solution compared with the control specimen. The anodising treatment was effective both in shifting the free corrosion potential to more noble values and in suppressing the corrosion current. Optical microscope and optical profilometry images indicated that an anodising film was deposited onto the alloy surface, which is thought to have inhibited corrosion in chloride environment. Further characterisation of the anodising film will be carried out in future work.

Investigating the effect of solution pH on speciation of La(4OH-cin)3 with correlation to electrochemical behaviour and corrosion efficiency

The nature of the species in solution plays a major role on the effectiveness of the corrosion inhibitor on a steel substrate. The speciation of lanthanum 4-hydroxy cinnamate (La(4OHCin) ₃) in solution has been evaluated using experimental techniques composed of potentiodynamic polarisation, immersion tests, nuclear magnetic spectroscopy and mass spectroscopy. It is evident that the species in solution are dependent on pH and this impacts the corrosion inhibition mechanism and the efficiency. It was found that at a neutral pH of 5.5 the La(4OH-Cin)₃ behaves as a strong anodic inhibitor. Whereas, when the pH shifts to low (pH2.5) and/or high (pH8) the corrosion mechanism changes.

Effect of La (40H-Cin)3 on filiform corrosion of coated steel

The potential of lanthanum 4-hydroxy cinnamate to inhibit filiform corrosion on coated mild steel (AS1020) was investigated. The effectiveness and behaviour of this rare-earth inhibitor was examined with filiform corrosion scribe tests and Potentiodynamic Polarisation. The filiform scribe tests showed that lanthanum 4-hydroxy cinnamate, as a pigment in a coating, inhibited the initiation and propagation of both delamination and filiform corrosion on coated steel. The polarisation tests demonstrated that at pH 3, no significant inhibition was observed but a secondary passivation effect was present. At pH 9, inhibition on coated steel was found to be greater than that of the inhibition found at pH 6. The models of filament initiation and growth proposed by previous authors are also discussed.

Corrosion of heat treated magnesium alloy ZE41

This paper investigates the effect of heat treatment upon the corrosion morphology and mechanism of ZE41 alloy. The results of optical and scanning electron microscopy (SEM) together with potentiodynamic polarisation reveal the importance of the microstructure in the initiation and propagation of corrosion in an aqueous environment. The corrosion of the heat-treated alloy is significantly altered due to changes in the microstructure, specifically the Zr-rich regions and the grain boundary T-phase.

Effects of corrosion inhibiting pigment lanthanum 4-hydroxy cinnamate on the filiform corrosion of coated steel

Corrosion protection by lanthanum hydroxy cinnamate (La(4OH-cin)3) in a polyurethane based varnish coating for mild steelhas been investigated. Filiform scribe tests, energy-dispersive X-ray spectroscopy (EDXS) and potentiodynamic polarisation (PP)techniques have been powerful tools to better understand the corrosion process at defects and under the coating. Filiform scribetests showed that La(4OH-cin)3, as a pigment in a coating, inhibited the initiation and propagation of both delamination and filiformcorrosion (FFC) on coated steel. The PP experiments provided an insight into the fundamental mechanism of FFC. The resultssuggest that La(4OH-cin)3 behaves as a mixed inhibitor and stifles the initiation and propagation of FFC. In this paper, the theory ofdelamination leading to FFC and the likely mechanism of inhibition by the La(4OH-cin)3 will be discussed.

Corrosion properties of a RF-magnetron-sputtered TiN coating deposited on 316L stainless steel

The effect of rf-power in the range from 100 to 200 W on the electrochemical properties of TiN coatings deposited on 316L stainless steel was investigated by using various electrochemical techniques in a 3.5-wt\% NaCl solution. Surface analyses were also conducted to analyze the coating characteristics. X-ray diffraction (XRD) and atomic force microscopy (AFM) analyses confirmed that increasing the rf-power led to a preferred orientation of the TiN(200) microstructure and decreased the surface roughness. The potentiodynamic test results confirmed the passive behavior of all of the specimens with low passive current densities and demonstrated that the effective pitting resistance of the TiN coatings increased with increasing rf-power. The electrochemical impedance spectroscopy (EIS) tests showed that the TiN films deposited with high rf-power had excellent corrosion resistance during an immersion time of 720 h due to their high total resistance and low porosity.

Effect of Ag addition on the corrosion properties of Sn-based solder alloys

Corrosion properties of three different Sn-Ag lead free solder alloys have been investigated in 0.3 wt% Na₂SO₄ solution as corrosive environment. As cast solder alloy was analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Volume fractions of the Ag₃Sn in the solders were determined by image analysis technique. Pitting potential and corrosion potential for the alloys were determined by potentiodynamic tests. Electrochemical impedance spectroscopy (EIS) was carried out to measure the film and charge transfer resistance. Alloys with lower Ag content have been found as better corrosion resistance material.

Effect of aluminum on the corrosion resistance of low-alloy steel in 10wt% sulfuric acid solution

The aqueous corrosion behavior of low-alloy steel with aluminum contents was examined in a 10 wt% H₂SO₄ (pH 0.13) solution using electrochemical techniques and surface analyses. The corrosion resistance of the new alloy steel was evaluated in terms of electrochemical parameters, such as passive current density, film, and charge transfer resistances. The results showed that a high Al content in the steel imparted better passivation behavior resulting in a lower corrosion rate. It related to the enrichment of iron carbonate and hydrocarbon by the dissolution of the carbide phase.

Corrosion properties of plasma-polymerized methylcyclohexane films using electrochemical methods

Three types of methylcyclohexane (MCH) coating were deposited as interlayer dielectrics on copper using plasma-enhanced chemical vapor deposition (PECVD) at three different RF plasma power levels. The coating performance was then evaluated by an electrochemical im pedance spectroscopy (EIS) and a potentiodynamic polarization test in 3.5 wt.% NaCl solution. An atomic force microscopy (AFM) and Fourier transform infrared reflection (FT-IR) spectroscopy were also conducted to analyze the coatings. The MCH coatings showed a lower corrosion rate than the copper substrate in the potentiodynamic tests. The EIS results showed that the corrosion resistance of the coatings increased with an increasing plasma power. Thus, the MCH films with an increasing plasma power improved the corrosion resistance due to the formation of a low-porosity coating, the enhanced formation of C−H, C−C, and C≡C stretching configurations, and the improved smooth surfaces.