Synthesis, structural characterisation and thermoelectric properties of Bi1−xPbxOCuSe

The effect of Pb2+ doping on the structure and thermoelectric properties of BiOCuSe (also known as BiCuSeO or BiCuOSe) is described. With increasing Pb2+ content, the expansion of the unit cell results in a weakening of the bonding between the [Bi2(1-x) Pb2xO2]2(1-x)+ and the [Cu2Se2]2(1-x)- layers. The electrical resistivity and Seebeck coefficient decrease in a systematic way with growing Pb2+ levels. The thermal conductivity rises due to the increase of the electronic contribution with doping. The power factor of materials with a 4-5% Pb2+ content takes values of ca. 8 W cm-1 K-2 over a wide temperature range. ZT at 673 K is enhanced by ca. 50% when compared to values found for other dopants, such as Sr2+ or Mg2+.

Thermoelectric properties of BiOCu1-xMxSe (M = Cd and Zn)

Doping of BiOCuSe at the copper site with divalent cadmium and zinc cations has been investigated. Analysis of the powder X-ray diffraction data indicates that the ZrCuSiAs structure of BiOCuSe is retained up to substitution levels of 10 and 5 at.% for Cd2+ and Zn2+, respectively. Substitution of monovalent Cu+ with divalent Cd2+ or Zn2+ leads to an increase in the magnitude of the electrical resistivity and the Seebeck coefficient. All synthesized materials behave as p-type semiconductors.

Synthesis, characterisation and thermoelectric properties of the oxytelluride Bi2O2Te

Bi2O2Te was synthesised from a stoichiometric mixture of Bi, Bi2O3 and Te by a solid state reaction. Analysis of powder X-ray diffraction data indicates that this material crystallises in the anti-ThCr2Si2 structure type (space group I4/mmm), with lattice parameters a = 3.98025(4) and c = 12.70391(16) Å. The electrical and thermal transport properties of Bi2O2Te were investigated as a function of temperature over the temperature range 300 ≤ T/K ≤ 665. These measurements indicate that Bi2O2Te is an n-type semiconductor, with a band gap of 0.23 eV. The thermal conductivity of Bi2O2Te is remarkably low for a crystalline material, with a value of only 0.91 W m-1 K-1 at room temperature.

The interplay of metal-atom ordering, Fermi leveltuning and thermoelectric properties in cobalt shandites Co3M2S2 (M = Sn, In)

A combination of structural, physical and computational techniques including powder X-ray and neutron diffraction, SQUID magnetometry, electrical and thermal transport measurements, DFT calculations and 119Sn Mössbauer and X-ray photoelec-tron spectroscopies has been applied to Co3Sn2-xInxS2 (0 ≤ x ≤ 2) in an effort to understand the relationship between metal-atom ordering and physical properties as the Fermi level is systematically varied. Whilst solid solution behavior is found throughout the composition region, powder neutron diffraction reveals that indium preferentially occupies an inter-layer site over an alternative kagome-like intra-layer site. DFT calculations indicate that this ordering, which leads to a lowering of energy, is related to the dif-fering bonding properties of tin and indium. Spectroscopic data suggest that throughout the composition range 0 ≤ x ≤ 2, all ele-ments adopt oxidation states that are significantly reduced from expectations based on formal charges. Chemical substitution ena-bles the electrical transport properties to be controlled through tuning of the Fermi level within a region of the density of states, which comprises narrow bands of predominantly Co d-character. This leads to a compositionally-induced double metal-to-semiconductor-to-metal transition. The marked increase in the Seebeck coefficient as the semiconducting region is approached leads to a substantial improvement in the thermoelectric figure of merit, ZT, which exhibits a maximum of ZT = 0.32 at 673 K. At 425 K, the figure of merit for phases in the region 0.8 ≤ x ≤ 0.85 is amongst the highest reported for sulphide phases, suggesting these materials may have applications in low-grade waste heat recovery.

Synthesis and thermoelectric properties of the new skutterudites Yb x Fe2Ni2Sb12 (0 ≤ x ≤ 0.4)

The family of materials Yb x Fe2 Ni 2Sb12 (0 ≤ x ≤ 0.4) has been prepared by solid-state synthesis from the pure elements and characterized by powder X-ray diffraction. These materials crystallize in the skutterudite structure, with the framework voids partially filled with Yb atoms. Electrical resistivity, Seebeck coefficient and thermal conductivity measurements have been performed on hot-pressed samples, and indicate that the thermoelectric performance is significantly improved by increasing the Yb content. The decomposition of the compounds under oxidizing atmosphere at elevated temperatures has also been studied by thermogravimetric analysis. The physical properties and thermal stability of the new compounds are further discussed in comparison with those of the reported isostructural and isoelectronic Yb x Co4Sb12 (0 ≤ x ≤ 0.19).

Ball milling as an effective route for the preparation of doped bornite: synthesis, stability and thermoelectric properties

Bornite, Cu5FeS4, is a naturally-occuring mineral with an ultralow thermal conductivity and potential for thermoelectric power generation. We describe here a new, easy and scalable route to synthesise bornite, together with the thermoelectric behaviour of manganese-substituted derivatives, Cu5Fe1-xMnxS4 (0 ≤ x ≤ 0.10). The electrical and thermal transport properties of Cu5Fe1-xMnxS4 (0 ≤ x ≤ 0.10), which are p-type semiconductors, were measured from room temperature to 573 K. The stability of bornite was investigated by thermogravimetric analysis under inert and oxidising atmospheres. Repeated measurements of the electrical transport properties confirm that bornite is stable up to 580 K under an inert atmosphere, while heating to 890 K results in rapid degradation. Ball milling leads to a substantial improvement in the thermoelectric figure of merit of unsusbtituted bornite (ZT = 0.55 at 543 K), when compared to bornite prepared by conventional high-temperature synthesis (ZT < 0.3 at 543 K). Manganese-substituted samples have a ZT comparable to that of unsubstituted bornite.

Thermoelectric properties of TiS2 mechanically alloyed compounds

Bulk polycrystalline samples in the series Ti1−xNbxS2 (0 ≤ x ≤ 0.075) were prepared using mechanical alloying synthesis and spark plasma sintering. X-ray diffraction analysis coupled with high resolution transmission electron microscopy indicates the formation of trigonal TiS2 by high energy ball-milling. The as-synthesized particles consist of pseudo-ordered TiS2 domains of around 20–50 nm, joined by bent atomic planes. This bottom-up approach leads, after spark plasma sintering, to homogeneous solid solutions, with a niobium solubility limit of x = 0.075. Microstructural observations evidence the formation of small crystallites in the bulk compounds with a high density of stacking faults. The large grain boundary concentration coupled with the presence of planar defects, leads to a substantial decrease in the thermal conductivity to 1.8 W/mK at 700 K. This enables the figure of merit to reach ZT = 0.3 at 700 K for x = 0.05, despite the lower electron mobility in mechanically alloyed samples due to small crystallite/grain size and structural defects.

The impact of charge transfer and structural disorder on the thermoelectric properties of cobalt intercalated TiS2

A family of phases, CoxTiS2 (0 ≤ x ≤ 0.75) has been prepared and characterised by powder X-ray and neutron diffraction, electrical and thermal transport property measurements, thermal analysis and SQUID magnetometry. With increasing cobalt content, the structure evolves from a disordered arrangement of cobalt ions in octahedral sites located in the van der Waals’ gap (x ≤ 0.2), through three different ordered vacancy phases, to a second disordered phase at x ≥ 0.67. Powder neutron diffraction reveals that both octahedral and tetrahedral inter-layer sites are occupied in Co0.67TiS2. Charge transfer from the cobalt guest to the TiS2 host affords a systematic tuning of the electrical and thermal transport properties. At low levels of cobalt intercalation (x < 0.1), the charge transfer increases the electrical conductivity sufficiently to offset the concomitant reduction in |S|. This, together with a reduction in the overall thermal conductivity leads to thermoelectric figures of merit that are 25 % higher than that of TiS2, ZT reaching 0.30 at 573 K for CoxTiS2 with 0.04 ≤ x ≤ 0.08. Whilst the electrical conductivity is further increased at higher cobalt contents, the reduction in |S| is more marked due to the higher charge carrier concentration. Furthermore both the charge carrier and lattice contributions to the thermal conductivity are increased in the electrically conductive ordered-vacancy phases, with the result that the thermoelectric performance is significantly degraded. These results illustrate the competition between the effects of charge transfer from guest to host and the disorder generated when cobalt cations are incorporated in the inter-layer space.

Layered oxychalcogenides: structural chemistry and thermoelectric properties

Layered oxychalcogenides have recently emerged as promising thermoelectric materials. The alternation of ionic oxide and covalent chalcogenide layers found in these materials often results in interesting electronic properties, and also facilitates the tuning of their properties via chemical substitution at both types of layers. This review highlights some common structure types found for layered oxychalcogenides and their interrelationships. This review pays special attention to the potential of these materials for thermoelectric applications, and provides an overview of the thermoelectric properties of materials of current interest, including BiCuSeO.

Structural stability of the synthetic thermoelectric ternary and nickel-substituted tetrahedrite phases

The purity and structural stability of the high thermoelectric performance Cu12Sb4S13 and Cu10.4Ni1.6Sb4S13 tetrahedrite phases, synthesized by solid–liquid–vapor reaction and Spark Plasma Sintering, were studied at high temperature by Rietveld refinement using high resolution X-ray powder diffraction data, DSC/TG measurements and high resolution transmission electron microscopy. In a complementary study, the crystal structure of Cu10.5Ni1.5Sb4S13 as a function of temperature was investigated by powder neutron diffraction. The temperature dependence of the structural stability of ternary Cu12Sb4S13 is markedly different to that of the nickel-substituted phases, providing clear evidence for the significant and beneficial role of nickel substitution on both sample purity and stability of the tetrahedrite phase. Moreover, kinetic effects on the phase stability/decomposition have been identified and discussed in order to determine the maximum operating temperature for thermoelectric applications. The thermoelectric properties of these compounds have been determined for high density samples (>98%) prepared by Spark Plasma Sintering and therefore can be used as reference values for tetrahedrite samples. The maximum ZT of 0.8 was found for Cu10.4Ni1.6Sb4S13 at 700 K.

A synchrotron powder X-ray diffraction study of the skutterudite-related phases AB1.5Te1.5 (A=Co, Rh, Ir; B= Ge, Sn)

X-ray resonant scattering has been exploited to investigate the crystal structure of the AB1.5Te1.5 phases (A = Co, Rh, Ir; B = Ge, Sn). Analysis of the diffraction data reveals that CoGe1.5Te1.5 and ASn1.5Te1.5 adopt a rhombohedral skutterudite-related structure, containing diamond-shape B2Te2 rings, in which the B and Te atoms are ordered and trans to each other. Anion ordering is however incomplete, and with increasing the size of both cations and anions, the degree of anion ordering decreases. By contrast, the diffraction data of IrGe1.5Te1.5 are consistent with an almost statistical distribution of the anions over the available sites, although some ordered domains may be present. The thermoelectric properties of these materials are discussed in the light of these results.

High-temperature order–disorder transitions in the skutterudites CoGe1.5Q1.5 (Q=S, Te)

The temperature dependence of anion ordering in the skutterudites CoGe1.5Q1.5 (Q=S, Te) has been investigated by powder neutron diffraction. Both materials adopt a rhombohedral structure at room temperature (space group R-3 ) in which the anions are ordered trans to each other within Ge2Q2 rings. In CoGe1.5S1.5, anion ordering is preserved up to the melting point of 950 °C. However, rhombohedral CoGe1.5Te1.5 undergoes a phase transition at 610 °C involving a change to cubic symmetry (space group Im-3). In the high-temperature modification, there is a statistical distribution of anions over the available sites within the Ge2Te2 rings. The structural transition involves a reduction in the degree of distortion of the Ge2Te2 rings which progressively transform from a rhombus to a rectangular shape. The effect of this transition on the thermoelectric properties has been investigated.

Ordered-defect sulfides as thermoelectric materials

The thermoelectric behaviour of the transition-metal disulphides n-type NiCr2S4 and p-type CuCrS2 is investigated. Materials prepared by high-temperature reaction were consolidated using cold-pressing and sintering, hot-pressing (HP) in graphite dies or spark-plasma sintering (SPS) in tungsten carbide dies. The consolidation conditions have a marked influence on the electrical transport properties. In addition to the effect on sample density, altering the consolidation conditions results in changes to the sample composition, including the formation of impurity phases. Maximum room-temperature power factors are 0.18 mW m-1 K-2 and 0.09 mW m-1 K-2 for NiCr2S4 and CuCrS2, respectively. Thermal conductivities of ca. 1.4 and 1.2 W m-1 K-1 lead to figures of merit of 0.024 and 0.023 for NiCr2S4 and CuCrS2, respectively.

Fabrication and evaluation of a skutterudite-based thermoelectric module for high-temperature applications

We report a straightforward methodology for the fabrication of high-temperature thermoelectric (TE) modules using commercially available solder alloys and metal barriers. This methodology employs standard and accessible facilities that are simple to implement in any laboratory. A TE module formed by nine n-type Yb x Co4Sb12 and p-type Ce x Fe3CoSb12 state-of-the-art skutterudite material couples was fabricated. The physical properties of the synthesized skutterudites were determined, and the module power output, internal resistance, and thermocycling stability were evaluated in air. At a temperature difference of 365 K, the module provides more than 1.5 W cm−3 volume power density. However, thermocycling showed an increase of the internal module resistance and degradation in performance with the number of cycles when the device is operated at a hot-side temperature higher than 573 K. This may be attributed to oxidation of the skutterudite thermoelements.

Synthesis, characterization and physical properties of the skutterudites YbxFe2Ni2Sb12 (0≤x≤0.4)

The skutterudites YbxFe2Ni2Sb12 (0≤x≤0.4) have been prepared by solid-state reaction and characterised by powder X-ray diffraction. The compounds crystallise in the cubic space group Im View the MathML source3¯ (a≈9.1 Å) with Yb atoms partially filling the voids in the skutterudite framework. A neutron time-of-flight diffraction experiment for Fe2Ni2Sb12 confirms the disorder of Fe and Ni atoms on the transition-metal site. Electrical resistivity, Seebeck coefficient and thermal conductivity measurements indicate that the thermoelectric performance of the skutterudites shows a marked dependence on the Yb content. Magnetic measurements over the temperature range 2≤T/K≤300 show paramagnetic behaviour for all compounds. Decomposition studies under an oxidising atmosphere at elevated temperatures have also been carried out by thermogravimetric analysis.