Mesomorphic behaviour in copoly(ester-imide)s of poly(butylene-2,6-naphthalate) (PBN)

Copolycondensation of N,N’-bis(4-hydroxybutyl)-biphenyl-3,4,3',4'-tetracarboxylic diimide at 20 and 25 mol% with bis(4-hydroxybutyl)-2,6-naphthalate produces PBN-based copoly(ester-imide)s that not only crystallise but also form a (smectic) mesophase upon cooling from the melt. Incorporation of 25 mol% imide in PBN causes the glass transition temperature (measured by DSC) to rise from 51 to 74 °C, a significant increase relative to PBN. Furthermore, increased storage- (G'), loss- (G'') and elastic (E) moduli are observed for both copoly(ester-imide)s when compared to PBN itself. Structural analysis of the 20 mol% copolymer by X-ray powder and fibre diffraction, interfaced to computational modelling, suggests a crystal structure related to that of α-PBN, in space group P-1, with cell dimensions a = 4.74, b = 6.38, c = 14.45 Å, α = 106.1, β = 122.1, γ = 97.3°, ρ = 1.37 g cm-3.

The interplay of metal-atom ordering, Fermi leveltuning and thermoelectric properties in cobalt shandites Co3M2S2 (M = Sn, In)

A combination of structural, physical and computational techniques including powder X-ray and neutron diffraction, SQUID magnetometry, electrical and thermal transport measurements, DFT calculations and 119Sn Mössbauer and X-ray photoelec-tron spectroscopies has been applied to Co3Sn2-xInxS2 (0 ≤ x ≤ 2) in an effort to understand the relationship between metal-atom ordering and physical properties as the Fermi level is systematically varied. Whilst solid solution behavior is found throughout the composition region, powder neutron diffraction reveals that indium preferentially occupies an inter-layer site over an alternative kagome-like intra-layer site. DFT calculations indicate that this ordering, which leads to a lowering of energy, is related to the dif-fering bonding properties of tin and indium. Spectroscopic data suggest that throughout the composition range 0 ≤ x ≤ 2, all ele-ments adopt oxidation states that are significantly reduced from expectations based on formal charges. Chemical substitution ena-bles the electrical transport properties to be controlled through tuning of the Fermi level within a region of the density of states, which comprises narrow bands of predominantly Co d-character. This leads to a compositionally-induced double metal-to-semiconductor-to-metal transition. The marked increase in the Seebeck coefficient as the semiconducting region is approached leads to a substantial improvement in the thermoelectric figure of merit, ZT, which exhibits a maximum of ZT = 0.32 at 673 K. At 425 K, the figure of merit for phases in the region 0.8 ≤ x ≤ 0.85 is amongst the highest reported for sulphide phases, suggesting these materials may have applications in low-grade waste heat recovery.

Solvothermal synthesis of one-dimensional chalcogenides containing group 13 elements

The solvothermal synthesis and characterisation of [C6H16N2][GaS2]2 (1), [C6H16N2][Ga2Se3(Se2)] (2), and mixed-metal phases with composition [C6H16N2][Ga2–xInxSe3(Se2)] (0 < x < 2)(3–5), is described. These materials have been characterised by single-crystal and powder X-ray diffraction, thermogravimetric analysis and UV/Vis diffuse reflectance spectroscopy. The materials contain one-dimensional anionic chains. In 1, these chains consist of edge-linked GaS4 tetrahedra, whilst in 2–5, the chains contain perselenide (Se2)2– units and comprise alternating four-membered [M2Se2] and five-membered [M2Se3] rings (where M = Ga, In). Compounds 3–5 represent the first examples of ternary mixed-metal [M2Se3(Se2)]2– chains.

Synthesis, characterization and physical properties of the skutterudites YbxFe2Ni2Sb12 (0≤x≤0.4)

The skutterudites YbxFe2Ni2Sb12 (0≤x≤0.4) have been prepared by solid-state reaction and characterised by powder X-ray diffraction. The compounds crystallise in the cubic space group Im View the MathML source3¯ (a≈9.1 Å) with Yb atoms partially filling the voids in the skutterudite framework. A neutron time-of-flight diffraction experiment for Fe2Ni2Sb12 confirms the disorder of Fe and Ni atoms on the transition-metal site. Electrical resistivity, Seebeck coefficient and thermal conductivity measurements indicate that the thermoelectric performance of the skutterudites shows a marked dependence on the Yb content. Magnetic measurements over the temperature range 2≤T/K≤300 show paramagnetic behaviour for all compounds. Decomposition studies under an oxidising atmosphere at elevated temperatures have also been carried out by thermogravimetric analysis.

Synthesis and thermoelectric properties of the new skutterudites Yb x Fe2Ni2Sb12 (0 ≤ x ≤ 0.4)

The family of materials Yb x Fe2 Ni 2Sb12 (0 ≤ x ≤ 0.4) has been prepared by solid-state synthesis from the pure elements and characterized by powder X-ray diffraction. These materials crystallize in the skutterudite structure, with the framework voids partially filled with Yb atoms. Electrical resistivity, Seebeck coefficient and thermal conductivity measurements have been performed on hot-pressed samples, and indicate that the thermoelectric performance is significantly improved by increasing the Yb content. The decomposition of the compounds under oxidizing atmosphere at elevated temperatures has also been studied by thermogravimetric analysis. The physical properties and thermal stability of the new compounds are further discussed in comparison with those of the reported isostructural and isoelectronic Yb x Co4Sb12 (0 ≤ x ≤ 0.19).