Atomic diffusion induced by stress relaxation in InGaAs/GaAs epitaxial layers

The origin of the microscopic inhomogeneities in InxGa1-xAs layers grown on GaAs by molecular beam epitaxy is analyzed through the optical absorption spectra near the band gap. It is seen that, for relaxed thick layers of about 2.8μm, composition inhomogeneities are responsible for the band edge smoothing into the whole compositional range (0.05strain inhomogeneities are dominant. This evolution in line with layer thickness is due to the atomic diffusion at the surface during growth, induced by the strain inhomogeneities that arise from stress relaxation. In consequence, the strain variations present in the layer are converted into composition variations during growth. This process is energetically favorable as it diminishes elastic energy. An additional support to this hypothesis is given by a clear proportionality between the magnitude of the composition variations and the mean strain

Relaxation and derelaxation of pure and hydrogenated amorphous silicon during thermal annealing experiments

The structural relaxation of pure amorphous silicon (a-Si) and hydrogenated amorphous silicon (a-Si:H) materials, that occurs during thermal annealing experiments, has been analyzed by Raman spectroscopy and differential scanning calorimetry. Unlike a-Si, the heat evolved from a-Si:H cannot be explained by relaxation of the Si-Si network strain but it reveals a derelaxation of the bond angle strain. Since the state of relaxation after annealing is very similar for pure and hydrogenated materials, our results give strong experimental support to the predicted configurational gap between a-Si and crystalline silicon

Quantification of the bond-angle dispersion by Raman spectroscopy and the strain energy of amorphous silicon

A thorough critical analysis of the theoretical relationships between the bond-angle dispersion in a-Si, Δθ, and the width of the transverse optical Raman peak, Γ, is presented. It is shown that the discrepancies between them are drastically reduced when unified definitions for Δθ and Γ are used. This reduced dispersion in the predicted values of Δθ together with the broad agreement with the scarce direct determinations of Δθ is then used to analyze the strain energy in partially relaxed pure a-Si. It is concluded that defect annihilation does not contribute appreciably to the reduction of the a-Si energy during structural relaxation. In contrast, it can account for half of the crystallization energy, which can be as low as 7 kJ/mol in defect-free a-Si