Microstructure and magnetic properties of Ni50 Mn37 Sn13 Heusler alloy ribbons

The Heusler alloy Ni50 Mn37 Sn13 was successfully produced as ribbon flakes of thickness around 7-10 μm melt spinning. Fracture cross section micrographs in the ribbon show the formation of a microcrystalline columnarlike microstructure, with their longer axes perpendicular to the ribbon plane. Phase transition temperatures of the martensite-austenite transformation were found to be MS =218 K, Mf =207 K, AS =224 K, and Af =232 K; the thermal hysteresis of the transformation is 15 K. Ferromagnetic L 21 bcc austenite phase shows a Curie point of 313 K, with cell parameter a=0.5971 (5) nm at 298 K, transforming into a modulated 7M orthorhombic martensite with a=0.6121 (7) nm, b=0.6058 (8) nm, and c=0.5660 (2) nm, at 150 K

Producció i caracterització d'aliatges tipus Heusler sense Gal•li

L’objecte del present treball és produir, caracteritzar i comparar aliatges tipus Heusler no estequiomètrics de base Ni-Mn-Sn-X (on X= Co, Fe per tant, es pretén generar mostres dels aliatges utilitzant els precursors amb una composició que variï de l’establerta per Heusler. La morfologia del material será en forma de cinta, ja que és la morfologia més semblant a les aplicacions industrials que voldrem aplicar a aquests aliatges