Photophysical and Electrochemical Investigations on Photoconducting Poly(6-tert-butyl-3,4-dihydro-2H- 1,3-benzoxazine)

Poly(6-tert-butyl-3,4-dihydro-2H-1,3-benzoxazine) was synthesized by thermally activated cationic ring opening polymerization. The structure of the polymer was confirmed by spectral and thermal studies. The highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) were estimated using cyclic voltammetry and optical absorption. Modulated photocurrent measurement technique was employed to study the spectral and field dependence of photocurrent. Photocurrent of the order of 1.5 micro A/m2 was obtained for polymer at a biasing electric field of 40 V/mico m.

The Effect of Glass Additives on the Microwave Dielectric Properties of Ba(Mg 1 /3Ta2/3)03 Ceramics

The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C