Selective N-monomethylation of aniline over Zn1-xNixFe2O4 (x=0, 0.2, 0.5, 0.8 and 1) type systems

The reaction of aniline with methanol was carried out over Zn1-xNixFe2O4 (x= 0, 0.2, 0.5, 0.8 and 1) type systems in a fixed-bed down-flow reactor. It was observed that systems possessing low ``x'' values are highly selective and active for mono N-alkylation of aniline leading to N-methyl aniline. Selectivity for N-methyl aniline over ZnFe2O4 was more than 99% under the optimized reaction conditions. Even at methanol to aniline molar ratio of 2, the yield of N-methyl aniline was nearly 55.5%, whereas its yield exceeded 67% at the molar ratio of 7. The Lewis acid sites of the catalysts are mainly responsible for the good catalytic performance. Cation distribution in the spinel lattice influences their acido-basic properties, and hence, these factors have been considered as helpful to evaluate the activity and stability of the systems.

Selective N-monomethylation of aniline using Zn1-x CoxFe2O4( x=0, 0.2, 0.5, 0.8 and 1.0)type systems

A series of ferrites having the general formula Zn1-xCoxFe2O4 (x=0, 0.2, 0.5, 0.8 and 1.0)were prepared by soft chemical route. The materials were characterized by adopting various physico-chemical methods. The reaction of aniline with methanol was studied in a fixed-bed reactor system as a potential source for the production of various methyl anilines. It was observed that systems possessing low ‘ x’ values are highly selective and active for N-monoalkylation of aniline leading to N-methylaniline. Reaction parameters were properly varied to optimize the reaction conditions for obtaining N-methylaniline selectively and in better yield. Among the systems Zn0.8Co0.2Fe2O4 is remarkable due to its very high activity and excellent stability. Under the optimized conditions N-methylaniline selectivity exceeded 98%. Even at a methanol to aniline molar ratio of 2, the yield of N-methylaniline was nearly 50%, whereas its yield exceeded 71% at the molar ratio of 5. ZnFe2O4, though executed better conversion than Zn0.8Co0.2Fe2O4 in the initial period of the run, deactivates quickly as the reaction proceeds. The Lewis acidity of the catalysts is mainly responsible for the good performance. Cation distribution in the spinel lattice influences their acido-basic properties and, hence, these factors have been considered as helpful parameters to evaluate the activity of the systems.

Optical and electrical properties of co-sputtered amorphous transparent conducting zinc indium tin oxide thin films

Highly conductive and transparent thin films of amorphous zinc indium tin oxide are prepared at room temperature by co-sputtering of zinc 10 oxide and indium tin oxide. Cationic contents in the films are varied by adjusting the power to the sputtering targets. Optical transmission study of 11 films showed an average transmission greater than 85% across the visible region. Maximum conductivity of 6×102 S cm−1 is obtained for Zn/In/ 12 Sn atomic ratio 0.4/0.4/0.2 in the film. Hall mobility strongly depends on carrier concentration and maximum mobility obtained is 18 cm2 V−1 s−1 13 at a carrier concentration of 2.1×1020 cm−3. Optical band gap of films varied from 3.44 eV to 3 eV with the increase of zinc content in the film 14 while the refractive index of the films at 600 nm is about 2.0.

Rotational analysis of the C1Π-X1 Σ+ system of indium monofluoride

Indium monofluoride was excited in a high-frequency discharge and the C-X system was photographed at a reciprocal dispersion of 0.3 AA mm-1 using a plane-grating spectrograph. Rotational analyses of the 0,0 1,0 2,2 3,3 4,4 2,4 3,5 4,6 and 5,7 bands have been carried out and the following molecular constants have been evaluated. Be'=0.2670(+or-3) cm-1, Be"=0.2628(+or-4) cm-1, alpha e'=0.0050(+or-4) cm-1, alpha e"=0.0020(+or-1) cm-1, De'=3.65(+or-5)*10-7 cm-1, De"=2.5(+or-3)*10-7 cm-1, beta e'=0.5(+or-2)*10-7 cm-1, beta e"=0.2(+or-1)*10-7 cm-1, re'=1.9672(+or-3) AA, re"=1.9853(+or-2) AA. The re" value agrees with the microwave absorption value 1.9854 AA.

Studies on Production of Bacterial Xylanases

Xylanases with hydrolytic activity on xylan, one of the hemicellulosic materials present in plant cell walls, have been identified long back and the applicability of this enzyme is constantly growing. All these applications especially the pulp and paper industries require novel enzymes. There has been lot of documentation on microbial xylanases, however, none meeting all the required characteristics. The characters being sought are: higher production, higher pH and temperature optima, good stabilities under these conditions and finally the low associated cellulase and protease production. The present study analyses various facets of xylanase biotechnology giving emphasis on bacterial xylanases. Fungal xylanases are having problems like low pH values for both enzyme activity and growth. Moreover, the associated production of cellulases at significant levels make fungal xylanases less suitable for application in paper and pulp industries.Bacillus SSP-34 selected from 200 isolates was clearly having xylan catabolizing nature distinct from earlier reports. The stabilities at higher temperatures and pH values along with the optimum conditions for pH and temperature is rendering Bacillus SSP-34 xylanase more suitable than many of the previous reports for application in pulp and paper industries.Bacillus SSP-34 is an alkalophilic thertmotolerant bacteria which under optimal cultural conditions as mentioned earlier, can produce 2.5 times more xylanase than the basal medium.The 0.5% xylan concentration in the medium was found to the best carbon source resulting in 366 IU/ml of xylanase activity. This induction was subjected to catabolite repression by glucose. Xylose was a good inducer for xylanase production. The combination of yeast extract and peptone selected from several nitrogen sources resulted in the highest enzyme production (379+-0.2 IU/ml) at the optimum final concentration of 0.5%. All the cultural and nutritional parameters were compiled and comparative study showed that the modified medium resulted in xylanase activity of 506 IU/ml, 5 folds higher than the basal medium.The novel combination of purification techniques like ultrafiltraton, ammonium sulphate fractionation, DEAE Sepharose anion exchange chromatography, CM Sephadex cation exchange chromatography and Gel permeation chromatography resulted in the purified xylanase having a specific activity of 1723 U/mg protein with 33.3% yield. The enzyme was having a molecular weight of 20-22 kDa. The Km of the purified xylanase was 6.5 mg of oat spelts xylan per ml and Vmax 1233 µ mol/min/mg protein.Bacillus SSP-34 xylanase resulted in the ISO brightness increase from 41.1% to 48.5%. The hydrolytic nature of the xylanase was in the endo-form.Thus the organism Bacillus SSP-34 was having interesting biotechnological and physiological aspects. The SSP-34 xylanase having desired characters seems to be suited for application in paper and pulp industries.

On tuning the orientation of grains of spray pyrolysed ZnO thin films

Effect of varying spray rate on the structure and optoelectronic properties of spray pyrolysed ZnO film is analysed. ZnO films were characterised using different techniques such as X-ray diffraction (XRD), photoluminescence, electrical resistivity measurement, and optical absorption. The XRD analysis proved that, with the increase in spray rate, orientation of the grains changed from (1 0 1) plane to (0 0 2) plane. The films exhibited luminescence in two regions—one was the ‘near band-edge’ (NBE) (∼380 nm) emission and the other one was the ‘blue-green emission’ (∼503 nm). Intensity of the blue-green emission decreased after orientation of grains shifted to (0 0 2) plane. Scanning electron microscope (SEM) analysis of the films asserts that spray rate has major role in improving the crystallographic properties of the films. Moreover resistivity of the films could be lowered to 2.4×10−2 cm without any doping or post-deposition annealing