The measured variation of the Debye-Waller factor of aluminum from 295K to 815K by using the energy dispersive x-ray diffraction technique

The Energy Dispersive X-ray Diffraction System at Brock University has been used to measure the intensities of the diffraction lines of aluminum powder sample as a function of temperature. At first, intensity measurements at high temperature were not reproducible. After some modifications have been made, we were able to measure the intensities of the diffraction lines to 815K, with good accuracy and reproducibility. Therefore the changes of the Debye-Waller factor from room temperature up to 815K for aluminum were determined with precision. Our results are in good agreement with those previously published.

X-ray diffraction studies of muscle : observations on the anterior byssus retractor muscle of Mytilus edulis and the insect flight muscle from Sarcophaga bullata

The interfilament spacing of the anterior byssus retractor muscle from Mytilus edulis was studied as the muscle was extended. It was found that variations in this spacing were very small and consistent with the hypothesis that the interfilament spacing was independent of the extension of the muscle. It was observed that the interfilament spacing was dependent on the osmolarity of the bathing medium. In concentrated solutions of the artificial seawater, the interfilament spacing decreased; while in dilute solutions of artificial seawater, it was observed that the interfilament spacing was increasing. X-ray diffraction patterns were obtained from fresh, and glutaraldehyde fixed, specimens of insect flight muscle from Sarcophaga bullata. There patterns were in general agreement with previous X-ray diffraction studies of insect flight muscle. A reflexion G at 93A was observed and interpreted as arising from diffraction in the mitochondria. Specimens of dried insect flight muscle produced a diffraction pattern consisting of arc and ring reflexions. This was interpreted as suggesting an ordered arrangement of cristae, in the mitochondria from these muscles.

X-ray diffraction from Al powder using energy dispersive technique

Using the energy dispersive x ...ray diffraction (EDXD) technique, the room temperature diffraction pattern of Al powder was obtained at diffraction angles ~ 30° and 50°. From the small angle diffraction pattern the average relative intensities (IR) of the (111), (200), and (220) lines were measured to be equal to 100, 62, and 32 respectively. From the large diffraction angle IR for the (220), (311+222), (400), (331+420), and (422) lines were measured to be 100,201,17,90, and 19.5 respectively. The diffraction pattern at those two angles were obtained at several higher temperatures to measure the change in the intensities of the Al lines. From the intensity changes the increase of the Debye- Waller temperature factor, i.e ~B(T), with respect to the value at room temperature was determined to be 0.6+0.1 at 250°C, 1.10+0.15 at 350°C, 1.45+0.20 at 450°C, and 2.20±0.35 at 550°C.

Electronic, magnetic and thermal properties of Pb₂₋x AxCrO₅ (A = K or La)

Lead chromium oxide is a photoconductive dielectric material tha t has great potential of being used as a room temperature photodetector. In this research, we made ceramic pellets of this compound as well as potassium doped compound Pb2-xKxCr05, where x=O, 0.05, 0.125. We also investigate the properties of the lanthanum doped sample whose chemical formula is Pb1.85Lao.15Cr05' The electronic, magnetic and thermal properties of these materials have been studied. Magnetization measurements of the Pb2Cr05 sample indicate a transition at about 310 K, while for the lanthanum doped sample the transition temperature is at about 295 K indicating a paramagnetic behavior. However, the potassium doped samples are showing the transition from paramagnetic state to diamagnetic state at different temperatures for different amounts of potassium atoms present in the sample. We have studied resistivity as a function of temperature in different gas environments from 300 K to 900 K. The resistivity measurement of the parent sample indicates a conducting to insulating transition at about 300 K and upon increasing the temperature further, above 450 K the sample becomes an ionic conductor. As temperature increases a decrease in resistance is observed in the lanthanum/potassium doped samples. Using Differential Scanning Calorimetry experiment an endothermic peak is observed for the Pb2Cr05 and lanthanum/potassium doped samples at about 285 K.

Crystallinity, Magnetic and Electrical Properties of Bi doped LaVO3

We report the results of crystal structure, magnetization and resistivity measurements of Bi doped LaVO3. X-ray diffraction (XRD) shows that if doping Bi in the La site is less than ten percent, the crystal structure of La1-xBixVO3 remains unchanged and its symmetry is orthorhombic. However, for higher Bi doping (>10%) composite compounds are found where the XRD patterns are characterized by two phases: LaVO3+V2O3. Energy-dispersive analysis of the x-ray spectroscopy (EDAX) results are used to find a proper atomic percentage of all samples. The temperature dependence of the mass magnetization of pure and single phase doped samples have transition temperatures from paramagnetic to antiferromagnetic region at TN=140 K. This measurement for bi-phasic samples indicates two transition temperatures, at TN=140 K (LaVO3) and TN=170 K (V2O3). The temperature dependence of resistivity reveals semiconducting behavior for all samples. Activation energy values for pure and doped samples are extracted by fitting resistivity versus temperature data in the framework of thermal activation process.