Some electrical properties of semi-conductor crystals / |nPhyu Phyu Khin. -- 260 St. Catharines, Ont. : [s. n.],

SiC and AtB 12 have been prepared and their resistivities and Hall voltages measured. The resistivities and Hall voltages were measured by the Van der Pauw's method, using spring loaded tungsten contacts. In this method, the major requirement is to have samples of plane parallel surfaces of arbitrary shape with four small contacts at the circumference. Similar measurements were made with a number of SiC crystals obtained from the Norton Research Corporation (Canada)-Ltd., Carolina Aluminum Co., Exolon Co. and Carborundum Co. It was found that resistivity, carrier concentration and mobility of ions depend on the type of impurity. AtB 12 was prepared from the melt containing At and B in the ratio of 4:1. They formed amber-colour pseudo tetragonal crystals. As the crystals obtained were small for electrical measurements, hot pressed lumps have been used to measure their resistivity.

The design of a reflectance spectrometer and its calibration using SrTiO3 /

A new Ultra-High Vacuum (UHV) reflectance spectrometer was successfully designed, making use of a Janis Industries ST-400 sample cryostat, IR Labs bolometer, and Briiker IFS 66 v/S spectrometer. Two of the noteworthy features include an in situ gold evaporator and internal reference path, both of which allow for the experiment to progress with a completely undisturbed sample position. As tested, the system was designed to operate between 4.2 K and 325 K over a frequency range of 60 - 670 cm~^. This frequency range can easily be extended through the addition of appUcable detectors. Tests were performed on SrTiOa, a highly ionic incipient ferroelectric insulator with a well known reflectance. The presence and temperatmre dependence of the lowest frequency "soft" mode were measured, as was the presence of the other two infrared modes. During the structural phase transition from cubic to tetragonal perovskite, the splitting of the second phonon mode was also observed. All of the collected data indicate good agreement with previous measurements, with a minor discrepency between the actual and recorded sample temperatures.

Magnetic and transport properties of (Ba1-xKx)Fe2As2

Single crystals of (Bal - xKx)Fe2As2 were prepared using the Sn flux method. Two heating methods were used to prepare the single crystals: the slow heating and rapid heating methods. It was found that the single crystals grown using the slow heating method were not superconducting due to a significant loss of potassium. When the rapid heating method was used, the single crystals were observed to be superconducting with the desired potassium concentration. The energy dispersive X-ray spectroscopy analysis indicated the presence of multiple phases in the single crystals. Using single crystal X-ray diffraction, the crystal structure of the single crystals was found to be 14/mmm tetragonal at room temperature. The magnetic measurements on the single crystals indicated the presence of multiple phases and magnetic impurities.

Investigation of Frustrated Quasi-One-Dimensional Quantum Spin-Chain Materials

Copper arsenite CuAs2O4 and Copper antimonite CuSb2O4 are S=1/2 (Cu2+ 3d9 electronic configuration) quasi-one-dimensional quantum spin-chain compounds. Both compounds crystallize with tetragonal structures containing edge sharing CuO6 octahedra chains which experience Jahn-Teller distortions. The basal planes of the octahedra link together to form CuO2 ribbon-chains which harbor Cu2+ spin-chains. These compounds are magnetically frustrated with competing nearest-neighbour and next-nearest-neighbour intrachain spin-exchange interactions. Despite the similarities between CuAs2O4 and CuSb2O4, they exhibit very different magnetic properties. In this thesis work, the physical properties of CuAs2O4 and CuSb2O4 are investigated using a variety of experimental techniques which include x-ray diffraction, magnetic susceptibility measurements, heat capacity measurements, Raman spectroscopy, electron paramagnetic resonance, neutron diffraction, and dielectric capacitance measurements. CuAs2O4 exhibits dominant ferromagnetic nearest-neighbour and weaker antiferromagnetic next-nearest-neighbour intrachain spin-exchange interactions. The ratio of the intrachain interactions amounts to Jnn/Jnnn = -4.1. CuAs2O4 was found to order with a ferromagnetic groundstate below TC = 7.4 K. An extensive physical characterization of the magnetic and structural properties of CuAs2O4 was carried out. Under the effect of hydrostatic pressure, CuAs2O4 was found to undergo a structural phase transition at 9 GPa to a new spin-chain structure. The structural phase transition is accompanied by a severe alteration of the magnetic properties. The high-pressure phase exhibits dominant ferromagnetic next-nearest-neighbour spin-exchange interactions and weaker ferromagnetic nearest-neighbour interactions. The ratio of the intrachain interactions in the high-pressure phase was found to be Jnn/Jnnn = 0.3. Structural and magnetic characterizations under hydrostatic pressure are reported and a relationship between the structural and magnetic properties was established. CuSb2O4 orders antiferromagnetically below TN = 1.8 K with an incommensurate helicoidal magnetic structure. CuSb2O4 is characterized by ferromagnetic nearest-neighbour and antiferromagnetic next-nearest-neighbour spin-exchange interactions with Jnn/Jnnn = -1.8. A (H, T) magnetic phase diagram was constructed using low-temperature magnetization and heat capacity measurements. The resulting phase diagram contains multiple phases as a consequence of the strong intrachain magnetic frustration. Indications of ferroelectricity were observed in the incommensurate antiferromagnetic phase.