Application of ZnO-Functionalised-Sepiolite in weaning piglet diets

The objective was to evaluate the effect of ZnO-Functionalised-Sepiolite (ZnO-Sepiolite) to fulfil Zn requirements and health status of weaning piglets. Pre-starter Basal Diet (BD, corn– soybean based, from weaning till 14 days on trial) was calculated to provide 27 mg Zn/kg feed from raw materials and had no added ZnO and no antibiotics or organic acids. Treatments during pre-starter period were: 1) BD+90% of NRC Zn requirements completed with ZnO (ZnO90); 2) BD+90% of NRC Zn requirements completed with ZnO-Sepiolite (ZnOS90); 3) BD+3000 mg ZnO/kg of diet (ZnO3000); 4) BD+150 mg added Zn/kg diet from ZnO-Sepiolite (ZnOS150). The starter feed (corn–soybean based, from 14 till 31 days on trial) was common for all piglets, and met 90% NRC Zn requirements by adding ZnO. Diarrhea affected more than 50% of the animals of ZnO90, ZnOS90 and ZnOS150, and 33% of the ZnO3000 animals. Animals from ZnOS90 tended (Pb0.10) to improve Gain to Feed ratio (G:F) compared to animals from ZnO90 (0.830 kg/kg vs. 0.811 kg/kg for G:F). Performance of animals from ZnO3000 was not significantly different from the other treatments, and was numerically similar to animals from ZnOS90. The inclusion of ZnO at 3000 mg/kg of feed in the pre-starter period numerically decreased P in serum at the end of this period, with no effect on Ca level; normal levels were restored after 2 weeks of feeding the same levels of Zn than other animals. Animals fed ZnOSepiolite diets had numerically higher serum Ca than ZnO90 and ZnO3000 at 12 days and higher than ZnO90 at 28 days. Serum Zn levels were significantly higher for ZnO3000 than the other treatments.

Reversible ferromagnetic switching in ZnO:(Co,Mn) powders

We report here on the magnetic properties of ZnO:Mn- and ZnO:Co-doped nanoparticles. We have found that the ferromagnetism of ZnO:Mn can be switched on and off by consecutive low-temperature annealings in O2 and N2, respectively, while the opposite phenomenology was observed for ZnO:Co. These results suggest that different defects (presumably n-type for ZnO:Co and p-type for ZnO:Mn) are required to induce a ferromagnetic coupling in each case. We will argue that ferromagnetism is likely to be restricted to a very thin, nanometric layer at the grain surface. These findings reveal and give insight into the dramatic relevance of surface effects to the occurrence of ferromagnetism in ZnO-doped oxides.

Size-dependent recombination dynamics in ZnO nanowires.

A deep understanding of the recombination dynamics of ZnO nanowires NWs is a natural step for a precise design of on-demand nanostructures based on this material system. In this work we investigate the influence of finite-size on the recombination dynamics of the neutral bound exciton around 3.365 eV for ZnO NWs with different diameters. We demonstrate that the lifetime of this excitonic transition decreases with increasing the surface-to-volume ratio due to a surface induced recombination process. Furthermore, we have observed two broad transitions around 3.341 and 3.314 eV, which were identified as surface states by studying the dependence of their life time and intensitiy with the NWs dimensions.

Enhancement of the photoelectrochemical properties of Cl-doped ZnO nanowires by tuning their coaxial doping profile

Arrays of vertically aligned ZnO:Cl/ZnO core-shell nanowires were used to demonstrate that the control of the coaxial doping profile in homojunction nanostructures can improve their surface charge carrier transfer while conserving potentially excellent transport properties. It is experimentally shown that the presence of a ZnO shell enhances the photoelectrochemical properties of ZnO:Cl nanowires up to a factor 5. Likewise, the ZnO shell promotes the visible photoluminescence band in highly conducting ZnO:Cl nanowires. These lines of evidence are associated with the increase of the nanowires" surface depletion layer

Gas-sensing properties of sprayed films of (CdO)x(ZnO)1-x mixed oxide

A novel NO2 sensor based on (CdO)x(ZnO)1-x mixed-oxide thin films deposited by the spray pyrolysis technique is developed. The sensor response to 3-ppm NO2 is studied in the range 50°C-350°C for three different film compositions. The device is also tested for other harmful gases, such as CO (300 ppm) and CH4 (3000 ppm). The sensor response to these reducing gases is different at different temperatures varying from the response typical for the p-type semiconductor to that typical for the n-type semiconductor. Satisfactory response to NO2 and dynamic behavior at 230°C, as well as low resistivity, are observed for the mixed-oxide film with 30% Cd. The response to interfering gas is poor at working temperature (230°C). On the basis of this study, a possible sensing mechanism is proposed.

Influence of RF power on the properties of sputtered ZnO:Al thin films

Transparent conducting, aluminium doped zinc oxide thin films (ZnO:Al) were deposited by radio frequency (RF) magnetron sputtering. The RF power was varied from 60 to 350Wwhereas the substrate temperature was kept at 160 °C. The structural, electrical and optical properties of the as-deposited films were found to be influenced by the deposition power. The X-ray diffraction analysis showed that all the films have a strong preferred orientation along the [001] direction. The crystallite size was varied from 14 to 36 nm, however no significant change was observed in the case of lattice constant. The optical band gap varied in the range 3.44-3.58 eV. The lowest resistivity of 1.2×10 -3Vcm was shown by the films deposited at 250 W. The mobility of the films was found to increase with the deposition power.

Transparent conducting thin films by the co-sputtering of ZnO-ITO targets

Transparent and conductive Zn-In-Sn-O (ZITO) amorphous thin films have been deposited at room temperature by the rf magnetron co-sputtering of ITO and ZnO targets. Co-sputtering gives the possibility to deposit multicomponent oxide thin films with different compositions by varying the power to one of the targets. In order to make ZITO films with different Zn content, a constant rf power of 50 W was used for the ITO target, where as the rf power to ZnO target was varied from 25 W to 150 W. The as deposited films showed an increase in Zn content ratio from 17 to 67 % as the power to ZnO target was increased from 25 to 150 W. The structural, electrical and optical properties of the as deposited films are reported. The films showed an average transmittance over 80% in the visible wavelength range. The electrical resistivity and optical band gap of the ZITO films were found to depend on the Zn content in the film. The ZITO films deposited at room temperature with lower Zn content ratios showed better optical transmission and electrical properties compared to ITO film.

Spatial mapping of exciton lifetimes in single ZnO nanowires

We investigate the spatial dependence of the exciton lifetimes in single ZnO nanowires. We have found that the free exciton and bound exciton lifetimes exhibit a maximum at the center of nanowires, while they decrease by 30% towards the tips. This dependence is explained by considering the cavity-like properties of the nanowires in combination with the Purcell effect. We show that the lifetime of the bound-excitons scales with the localization energy to the power of 3/2, which validates the model of Rashba and Gurgenishvili at the nanoscale.

Up-conversion effect of Er- and Yb-doped ZnO thin films

Visible up-conversion in ZnO:Er and ZnO:Er:Yb thin films deposited by RF magnetron sputtering under different O2-rich atmospheres has been studied. Conventional photoluminescence (325 nm laser source) and up-conversion (980 nm laser source) have been performed in the films before and after an annealing process at 800 °C. The resulting spectra demonstrate that the thermal treatment, either during or post-deposition, activates optically the Er3+ ions, being the latter process much more efficient. Moreover, the atmosphere during deposition was also found to be an important parameter, as the deposition under O2 flow increases the optical activity of Er+3 ions. In addition, the inclusion of Yb3+ ions into the films has shown an enhancement of the visible up-conversion emission at 660 nm by a factor of 4, which could be associated to either a better energy transfer from the 2F5/2 Yb level to the 4I11/2 Er one, or to the prevention of having Er2O3 clustering in the films.

ZnO nanorods for efficient third harmonic UV generation.

ZnO nanorods grown by both high temperature vapour phase transport and low temperature chemical bath deposition are very promising sources for UV third harmonic generation. Material grown by both methods show comparable efficiencies, in both cases an order of magnitude higher than surface third harmonic generation at the quartz-air interface of a bare quartz substrate. This result is in stark contrast to the linear optical properties of ZnO nanorods grown by these two methods, which show vastly different PL efficiencies. The third harmonic generated signal is analysed using intensity dependent measurements and interferometric frequency resolved optical gating, allowing extraction of the laser pulse parameters. The comparable levels of efficiency of ZnO grown by these very different methods as sources for third harmonic UV generation provides a broad suite of possible growth methods to suit various substrates, coverage and scalability requirements. Potential application areas range from interferometric frequency resolved optical gating characterization of few cycle fs pulses to single cell UV irradiation for biophysical studies.

Spatial mapping of exciton lifetimes in single ZnO nanowires

We investigate the spatial dependence of the exciton lifetimes in single ZnO nanowires. We have found that the free exciton and bound exciton lifetimes exhibit a maximum at the center of nanowires, while they decrease by 30% towards the tips. This dependence is explained by considering the cavity-like properties of the nanowires in combination with the Purcell effect. We show that the lifetime of the bound-excitons scales with the localization energy to the power of 3/2, which validates the model of Rashba and Gurgenishvili at the nanoscale.

Recombination dynamics in ZnO nanowires: Surfaces states versus mode quality factor

In this work, we investigate the influence of finite size on the recombinations dynamics of ZnO nanowires. We demonstrate that diameter as well as lenght of nanowires determine the lifetime of the neutral donor bound excitons. Our findings suggest that while the length is mainly responsible for different mode quality factors of the cavity-like nanowires, the diameter determines the influence of surface states as alternative recombinations channels for the optical modes trapped in the nanocavity. In addition, comparing nanowires grown using different catalyst we show that the surfaces states strongly depend on each precursor characteristics.

Estudi de la reductibilitat de catalitzadors basats en cobalt i el seu comportament en la reacció de desplaçament de gas d'aigua de CO

Projecte de recerca elaborat a partir d’una estada a la universitat d'Udine, Itàlia, entre setembre i desembre del 2006.S'han caracteritzat mitjançant la reducció a temperatura programada i tests catalítics catalitzadors en pols basats en cobalt i supostats en òxid de zinc i monòlits ceràmics funcionaliltzats també amb cobalt i òxid de zinc. L'addició de promotors (manganès, crom i ferro ) als catalitzadors en pols, preparats per impregnació i precipitació, no afecta significativament ni la temperatura a la qual té lloc la reducció ni al percentatge global de reducció. En els cicles de reducció-oxidació sí que s'observen diferències entre el primer perfil de reducció i els següents, especialment en el cas de la mostra que té ferro com a promotor, on les diferències s'accentuen en cicles successius (fins al quart). S'ha evaluat l'activitat d'aquests catalitzadors en la reacció de desplaçament de gas d'aigua, obtenint uns resultats satisfactoris. Finalment s'han realitzat reduccions a temperatura programada i tests catalítics en la reacció de desplaçament de gas d'aigua amb monòlits funcionalitzats amb cobalt i òxid de zinc (en cap d'ells s'ha introduït promotors). El nivell de conversió assolit és menor que en el cas de catalitzadors en pols, fet que s'associa a la geometria d'aquests sistemes catalítics, però la relació CH4/CO2 és més favorable que en els catalitzadors en pols, el que els converteix en sistemes molt selectius.