Influence of the (111) twinning on the formation of diamond cubic/diamond hexagonal heterostructures in Cu-catalyzed Si nanowires

The occurrence of heterostructures of cubic silicon/hexagonal silicon as disks defined along the nanowire (111) growth direction is reviewed in detail for Si nanowires obtained using Cu as catalyst. Detailed measurements on the structural properties of both semiconductor phases and their interface are presented. We observe that during growth, lamellar twinning on the cubic phase along the (111) direction is generated. Consecutive presence of twins along the (111) growth direction was found to be correlated with the origin of the local formation of the hexagonal Si segments along the nanowires, which define quantum wells of hexagonal Si diamond. Finally, we evaluate and comment on the consequences of the twins and wurtzite in the final electronic properties of the wires with the help of the predicted energy band diagram.

Surface characterization techniques for determining the root-mean-square roughness and power spectral densities of optical components

Surface topography and light scattering were measured on 15 samples ranging from those having smooth surfaces to others with ground surfaces. The measurement techniques included an atomic force microscope, mechanical and optical profilers, confocal laser scanning microscope, angle-resolved scattering, and total scattering. The samples included polished and ground fused silica, silicon carbide, sapphire, electroplated gold, and diamond-turned brass. The measurement instruments and techniques had different surface spatial wavelength band limits, so the measured roughnesses were not directly comparable. Two-dimensional power spectral density (PSD) functions were calculated from the digitized measurement data, and we obtained rms roughnesses by integrating areas under the PSD curves between fixed upper and lower band limits. In this way, roughnesses measured with different instruments and techniques could be directly compared. Although smaller differences between measurement techniques remained in the calculated roughnesses, these could be explained mostly by surface topographical features such as isolated particles that affected the instruments in different ways.

Síntesis de capas de SiC en substrato de Si mediante implantación iónica

En este trabajo se investiga la síntesis de estructuras SiC/Si mediante implantación iónica de carbono en Si. Las implantaciones se han realizado a energías entre 25 y 300 keV y las dosis en el rango lO^^ylO^^ cm , manteniendo el substrato a temperatura ambiente o 500°C. Algunas estructuras han sido recocidas a 1150°C. Los resultados indican que implantando a temperatura ambiente se forma una capa de SiC amorfa y de composición gradual, que recristaliza formando precipitados de ß-SiC con orientaciones aleatorias después del recocido. Además se forma un capa superficial rica en carbono, debida a la difusión del carbono hacia la superficie durante la implantación, y que desaparece con el recocido. Implantando a 500°C se forma directamente una capa con una muy alta densidad de precipitados de ß-SiC orientados preferencialmente con la matriz de silicio. Dada la estabilidad térmica y química de dicha capa se han realizado membranas de SiC mediante técnicas fotolitográficas y ataque químico selectivo, cuya rugosidad superficial es inferior a 6 nm. Estas membranas muestran unos gradientes de tensiones residuales, que prácticamente desaparecen después del recocido. Los resultados confirman la potencialidad de la implantación iónica para la formación de estructuras microme-cánicas de SiC sobre Si.

Cubic spline population density functions and subcentre delimitation. The case of Barcelona

The presence of subcentres cannot be captured by an exponential function. Cubic spline functions seem more appropriate to depict the polycentricity pattern of modern urban systems. Using data from Barcelona Metropolitan Region, two possible population subcentre delimitation procedures are discussed. One, taking an estimated derivative equal to zero, the other, a density gradient equal to zero. It is argued that, in using a cubic spline function, a delimitation strategy based on derivatives is more appropriate than one based on gradients because the estimated density can be negative in sections with very low densities and few observations, leading to sudden changes in estimated gradients. It is also argued that using as a criteria for subcentre delimitation a second derivative with value zero allow us to capture a more restricted subcentre area than using as a criteria a first derivative zero. This methodology can also be used for intermediate ring delimitation.

Limit cycles for cubic systems with a symmetry of order 4 and without in nite critical points

"Vegeu el resum a l'inici del document del fitxer adjunt."

Development of advanced silicon radiation detectors for high energy physics and medical imaging

The 1st chapter of this work presents the different experiments and collaborations in which I am involved during my PhD studies of Physics. Following those descriptions, the 2nd chapter is dedicated to how the radiation affects the silicon sensors, as well as some experimental measurements carried out at CERN (Geneve, Schwitzerland) and IFIC (Valencia, Spain) laboratories. Besides the previous investigation results, this chapter includes the most recent scientific papers appeared in the latest RD50 (Research & Development #50) Status Report, published in January 2007, as well as some others published this year. The 3rd and 4th are dedicated to the simulation of the electrical behavior of solid state detectors. In chapter 3 are reported the results obtained for the illumination of edgeless detectors irradiated at different fluences, in the framework of the TOSTER Collaboration. The 4th chapter reports about simulation design, simulation and fabrication of a novel 3D detector developed at CNM for ions detection in the future ITER fusion reactor. This chapter will be extended with irradiation simulations and experimental measurements in my PhD Thesis.

Engineering the thermal emission of macroporous silicon

Todos los cuerpos emiten luz espontaneamente al ser calentados. El espectro de radiacion es una funcion de la temperatura y el material. Sin embargo, la mayoria de los materiales irradia, en general, en una banda espectral amplia. Algunas matereiales, por el contrario, son capaces de concentrar la radiacion termica en una banda espectral mucho mas estrecha. Estos materiales se conocen como emisores selectivos y su uso tiene un profundo impacto en la eficiencia de sistemas sistemas tales como iluminacion y conversion de energia termofotovoltaica. De los emisores selectivos se espera que sean capaces de operar a altas temperaturas y que emitan en una banda espectral muy concisa. Uno de los metodos mas prometedores para controlar y disenar el espectro de emision termico es la utilizacion de cristales fotonicos. Los cristales fotonicos son estructuras periodicas artificiales capaces de controlar y confinar la luz de formas sin precedentes. Sin embargo, la produccion de dichas estructuras con grandes superficies y capaces de soportar altas temperaturas sigue siendo una dificil tarea. Este trabajo esta dedicada al estudio de las propiedades de emision termica de estructuras 3D de silicio macroporoso en el rango espectral mid-IR (2-30 m). En particular, este trabajo se enfoca en reducir la elevada emisividad del silicio cristalino. Las muestras estudiadas en este trabajo tienen una periodicidad de 4 m, lo que limitan los resultados obtenidos a la banda del infrarrojo medio, aunque estructuras mucho mas pequenas son tecnologicamente realizables con el metodo de fabricacion utilizado. Hemos demostrado que el silicio macroporoso 3D puede inhibir completamente la emision termica en su superficie. Mas aun, esta banda se puede ajustar en un amplio margen mediante pequenos cambios durante la formacion de los macroporos. Tambien hemos demostrado que tanto el ancho como la frecuencia de la banda de inhibicion se puede doblar mediante la aplicacion de tecnicas de postprocesado adecuadas. Finalmente hemos mostrado que es posible crear bandas de baja emisividad arbitrariamente anchas mediante estructuras macroporosas aperiodicas.

Calorimetry of dehydrogenation and dangling-bond recombination in several hydrogenated amorphous silicon materials

Differential scanning calorimetry (DSC) was used to study the dehydrogenation processes that take place in three hydrogenated amorphous silicon materials: nanoparticles, polymorphous silicon, and conventional device-quality amorphous silicon. Comparison of DSC thermograms with evolved gas analysis (EGA) has led to the identification of four dehydrogenation processes arising from polymeric chains (A), SiH groups at the surfaces of internal voids (A'), SiH groups at interfaces (B), and in the bulk (C). All of them are slightly exothermic with enthalpies below 50 meV/H atoms , indicating that, after dissociation of any SiH group, most dangling bonds recombine. The kinetics of the three low-temperature processes [with DSC peak temperatures at around 320 (A),360 (A'), and 430°C (B)] exhibit a kinetic-compensation effect characterized by a linea relationship between the activation entropy and enthalpy, which constitutes their signature. Their Si-H bond-dissociation energies have been determined to be E (Si-H)0=3.14 (A), 3.19 (A'), and 3.28 eV (B). In these cases it was possible to extract the formation energy E(DB) of the dangling bonds that recombine after Si-H bond breaking [0.97 (A), 1.05 (A'), and 1.12 (B)]. It is concluded that E(DB) increases with the degree of confinement and that E(DB)>1.10 eV for the isolated dangling bond in the bulk. After Si-H dissociation and for the low-temperature processes, hydrogen is transported in molecular form and a low relaxation of the silicon network is promoted. This is in contrast to the high-temperature process for which the diffusion of H in atomic form induces a substantial lattice relaxation that, for the conventional amorphous sample, releases energy of around 600 meV per H atom. It is argued that the density of sites in the Si network for H trapping diminishes during atomic diffusion

Oxidation of silicon: further tests for the interfacial silicon emission model

The classical description of Si oxidation given by Deal and Grove has well-known limitations for thin oxides (below 200 Ã). Among the large number of alternative models published so far, the interfacial emission model has shown the greatest ability to fit the experimental oxidation curves. It relies on the assumption that during oxidation Si interstitials are emitted to the oxide to release strain and that the accumulation of these interstitials near the interface reduces the reaction rate there. The resulting set of differential equations makes it possible to model diverse oxidation experiments. In this paper, we have compared its predictions with two sets of experiments: (1) the pressure dependence for subatmospheric oxygen pressure and (2) the enhancement of the oxidation rate after annealing in inert atmosphere. The result is not satisfactory and raises serious doubts about the model’s correctness

Vacancy and interstitial depth profiles in ion-implanted silicon

An experimental method of studying shifts between concentration-versus-depth profiles of vacancy- and interstitial-type defects in ion-implanted silicon is demonstrated. The concept is based on deep level transient spectroscopy measurements utilizing the filling pulse variation technique. The vacancy profile, represented by the vacancy¿oxygen center, and the interstitial profile, represented by the interstitial carbon¿substitutional carbon pair, are obtained at the same sample temperature by varying the duration of the filling pulse. The effect of the capture in the Debye tail has been extensively studied and taken into account. Thus, the two profiles can be recorded with a high relative depth resolution. Using low doses, point defects have been introduced in lightly doped float zone n-type silicon by implantation with 6.8 MeV boron ions and 680 keV and 1.3 MeV protons at room temperature. The effect of the angle of ion incidence has also been investigated. For all implantation conditions the peak of the interstitial profile is displaced towards larger depths compared to that of the vacancy profile. The amplitude of this displacement increases as the width of the initial point defect distribution increases. This behavior is explained by a simple model where the preferential forward momentum of recoiling silicon atoms and the highly efficient direct recombination of primary point defects are taken into account.

Gas collisions and pressure quenching of the photoluminescence of silicon nanopowder grown by plasma-enhanced chemical vapor deposition

The quenching of the photoluminescence of Si nanopowder grown by plasma-enhanced chemical vapor deposition due to pressure was measured for various gases ( H2, O2, N2, He, Ne, Ar, and Kr) and at different temperatures. The characteristic pressure, P0, of the general dependence I(P) = I0¿exp(¿P/P0) is gas and temperature dependent. However, when the number of gas collisions is taken as the variable instead of pressure, then the quenching is the same within a gas family (mono- or diatomic) and it is temperature independent. So it is concluded that the effect depends on the number of gas collisions irrespective of the nature of the gas or its temperature.

Electrical transport quantum effects in the In0.53Ga0.47As/In0.52Al0.48As heterostructure on silicon

Electrical transport in a modulation doped heterostructure of In0.53Ga0.47As/In0.52Al0.48As grown on Si by molecular beam epitaxy has been measured. Quantum Hall effect and Subnikov¿De Haas oscillations were observed indicating the two¿dimensional character of electron transport. A mobility of 20¿000 cm2/V¿s was measured at 6 K for an electron sheet concentration of 1.7×1012 cm¿2. Transmission electron microscopy observations indicated a significant surface roughness and high defect density of the InGaAs/InAlAs layers to be present due to the growth on silicon. In addition, fine¿scale composition modulation present in the In0.53Ga0.47As/In0.52Al0.48As may further limit transport properties.

Properties of nitrogen doped silicon films deposited by low-pressure chemical vapor deposition from silane and ammonia

Nitrogen doped silicon (NIDOS) films have been deposited by low-pressure chemical vapor deposition from silane SiH4 and ammonia NH3 at high temperature (750°C) and the influences of the NH3/SiH4 gas ratio on the films deposition rate, refractive index, stoichiometry, microstructure, electrical conductivity, and thermomechanical stress are studied. The chemical species derived from silylene SiH2 into the gaseous phase are shown to be responsible for the deposition of NIDOS and/or (silicon rich) silicon nitride. The competition between these two deposition phenomena leads finally to very high deposition rates (100 nm/min) for low NH3/SiH4 gas ratio (R¿0.1). Moreover, complex variations of NIDOS film properties are evidenced and related to the dual behavior of the nitrogen atom into silicon, either n-type substitutional impurity or insulative intersticial impurity, according to the Si¿N atomic bound. Finally, the use of NIDOS deposition for the realization of microelectromechanical systems is investigated.

Silicon nanocluster sensitization of erbium ions under low-energy optical excitation

The sensitizing action of amorphous silicon nanoclusters on erbium ions in thin silica films has been studied under low-energy (long wavelength) optical excitation. Profound differences in fast visible and infrared emission dynamics have been found with respect to the high-energy (shortwavelength) case. These findings point out to a strong dependence of the energy transfer process on the optical excitation energy. Total inhibition of energy transfer to erbium states higher than thefirst excited state (4I13/2) has been demonstrated for excitation energy below 1.82 eV (excitation wavelength longer than 680 nm). Direct excitation of erbium ions to the first excited state (4I13/2)has been confirmed to be the dominant energy transfer mechanism over the whole spectral range of optical excitation used (540 nm¿680 nm).

Raman scattering and photoluminescence analysis of silicon on insulator structures obtained by single and multiple oxygen implants

An analysis of silicon on insulator structures obtained by single and multiple implants by means of Raman scattering and photoluminescence spectroscopy is reported. The Raman spectra obtained with different excitation powers and wavelengths indicate the presence of a tensile strain in the top silicon layer of the structures. The comparison between the spectra measured in both kinds of samples points out the existence in the multiple implant material of a lower strain for a penetration depth about 300 nm and a higher strain for higher penetration depths. These results have been correlated with transmission electron microscopy observations, which have allowed to associate the higher strain to the presence of SiO2 precipitates in the top silicon layer, close to the buried oxide. The found lower strain is in agreement with the better quality expected for this material, which is corroborated by the photoluminescence data.