TiB2 nanostructured coating for GFRP injection moulds

In the injection moulding of polypropylene reinforced with hard glass fibres, die materials are commonly subjected to severe abrasive wear. In order to improve its wear resistance, an unbalanced magnetron sputtering PVD compositional monolayered coating has been produced. The film was composed by a nanostructured TiB2 monolayer. Microstructure characterization and thickness evaluation were conducted by scanning electron microscopy (SEM). Film topography and roughness were accessed by SEM and Atomic Force Microscopy (AFM). The phase analyse was investigated by X-ray diffraction (XRD), using Cu Kalpha radiation. Scratch tests were conducted in order to study the film adhesion to the substrate. Load-Displacement curves (nanoindentation analysis) allowed measuring the film hardness and Young's modulus. A ball-cratering tribometer was used to determine the micro-abrasion laboratorial wear resistance, under different tests conditions, using SiC particles in distilled water slurry. At the end of these tests, the worn surfaces were analyzed by SEM and Energy Dispersive X-ray Spectroscopy (EDS) in order to compare these results with some other coatings already tested in the same conditions. To test the practical wear resistance, 135000 injection cycles were done in a plastic injection industrial mould. Coated samples were put on the plastic feed canal, after a turbulent zone. In these tests, a 30% (wt) glass fibres reinforced polypropylene was used. Worn sample surfaces were analyzed by SEM after 45.000 and 90.000 cycles. Image analyses were made in order to evaluate the damage increases and to observe the wear mechanisms involved.

Prevalência de resistência a antimicrobianos em isolados ambientais de Escherichia coli e enterococos

A água é um recurso escasso e indispensável à vida, podendo ser um importante veículo de microrganismos patogénicos com origem fecal. A matéria fecal é também uma fonte de microrganismos resistentes a antimicrobianos e contribui para a sua disseminação e dos seus genes de resistência no ambiente e entre as comunidades microbianas comensais e microrganismos patogénicos humanos e animais. A qualidade microbiológica da água é monitorizada recorrendo à utilização de bioindicadores como Escherichia coli, enterococos e microrganismos totais. O presente estudo apresentou como principal objetivo determinar a prevalência de ESBLs e AmpCs e ainda avaliar a prevalência de estirpes de enterococos com resistência à vancomicina (VRE) em águas do rio Douro e da orla costeira da cidade do Porto. As amostragens de água foram realizadas em quatro locais localizados no estuário do rio Douro e orla costeira da cidade do Porto entre o mês de Abril e Julho. A deteção e quantificação dos bioindicadores foram realizadas pelo método de filtração por membrana. A suscetibilidade das estirpes de E. coli e enterococos foi testada pelo método de difusão em disco relativamente a várias classes de antimicrobianos. As contagens microbianas mais elevadas foram determinadas entre Abril e Junho e em amostras de água doce. Foram isoladas 62 estirpes de E. coli e 49 estirpes de enterococos que apresentaram prevalências de resistência a antimicrobianos de 90,3% (56/62) e 83,7% (41/49), respetivamente. As estirpes de E. coli apresentaram altas frequências de resistência à ampicilina (74,2%) e tetraciclina (61,3%). Nestas estirpes verificou-se ainda fenótipos associados a multirresistência a um mínimo de três classes de antimicrobianos em 56,5% (35/62) dos isolados. Verificou-se que as estirpes de enterococos apresentaram altos níveis de resistência à rifampicina (34,7%) e azitromicina (40,8%), detetando-se ainda a manifestação de fenótipo de resistência à vancomicina em 26,5% das estirpes. Observou-se uma prevalência de 36,7% (18/49) de estirpes de enterococos associadas a fenómenos de multirresistência antimicrobiana. Ana Martins vi Os resultados obtidos sugerem que o rio Douro e orla costeira, bem como os ambientes aquáticos, constituem reservatórios de bactérias e genes de resistência a antimicrobianos e possuem um papel preponderante na sua disseminação.

Distribuição dos receptores da adenosina no plexo mioentérico – músculo longitudinal do íleo de rato: implicações funcionais

A acetilcolina (ACh) é o neurotransmissor mais importante no controlo da motilidade gastrointestinal. A libertação de ACh dos neurónios entéricos é regulada por receptores neuronais específicos (De Man et al., 2003). Estudos prévios demonstraram que a adenosina exerce um papel duplo na libertação de ACh dos neurónios entéricos através da activação dos receptores inibitórios A1 e facilitatórios A2A (Duarte-Araújo et al., 2004). O potencial terapêutico dos compostos relacionados com a adenosina no controlo da motilidade e da inflamação intestinal, levou-nos a investigar o papel dos receptores com baixa afinidade para a adenosina, A2B e A3, na libertação de acetilcolina induzida por estimulação eléctrica nos neurónios mioentéricos. Estudos de imunolocalização mostraram que os receptores A2B exibem um padrão de distribuição semelhante ao do marcador de células gliais (GFAP). No que respeita aos receptores A1 e A3, estes encontram-se distribuídos principalmente nos corpos celulares dos neurónios ganglionares mioentéricos, enquanto os receptores A2A estão localizados predominantemente nos terminais nervosos colinérgicos. Neste trabalho mostrou-se que a modulação da libertação de ACh-[3H] (usando os antagonistas selectivos DPCPX, ZM241385 e MRS1191) é balanceada através da activação tónica dos receptores inibitórios (A1) e facilitatórios (A2A e A3) pela adenosina endógena. O antagonista selectivo dos receptores A2B, PSB603, não foi capaz de modificar o efeito inibitório da NECA (análogo da adenosina com afinidade para receptores A2). O efeito facilitatório do agonista dos receptores A3, 2-Cl-IB MECA (1-10 nM), foi atenuado pelo MRS1191 e pelo ZM241385, os quais bloqueiam respectivamente os receptores A3 e A2A. Contrariamente à 2-Cl-IB MECA, a activação dos receptores A2A pelo CGS21680C, atenuou a facilitação da libertação de ACh induzida pela activação dos receptores nicotínicos numa situação em que a geração do potencial de acção neuronal foi bloqueada pela tetrodotoxina. A localização diferencial dos receptores excitatórios A3 e A2A ao longo dos neurónios mioentéricos explica porque razão a estimulação dos receptores A3 (com 2-Cl-IB MECA) localizados nos corpos celulares dos neurónios mioentéricos exerce um efeito sinérgico com os receptores facilitatórios A2A dos terminais nervosos no sentido de aumentarem a libertação de ACh. Os resultados apresentados consolidam e expandem a compreensão actual da distribuição e função dos receptores da adenosina no plexo mioentérico do íleo de rato, e devem ser tidos em consideração para a interpretação de dados relativos às implicações fisiopatológicas da adenosina nos transtornos da motilidade intestinal.

Molecular imprinted nanoelectrodes for ultra sensitive detection of ovarian cancer marker

The relentless discovery of cancer biomarkers demands improved methods for their detection. In this work, we developed protein imprinted polymer on three-dimensional gold nanoelectrode ensemble (GNEE) to detect epithelial ovarian cancer antigen-125 (CA 125), a protein biomarker associated with ovarian cancer. CA 125 is the standard tumor marker used to follow women during or after treatment for epithelial ovarian cancer. The template protein CA 125 was initially incorporated into the thin-film coating and, upon extraction of protein from the accessible surfaces on the thin film, imprints for CA 125 were formed. The fabrication and analysis of the CA 125 imprinted GNEE was done by using cyclic voltammetry (CV), differential pulse voltammetry (DPV) and electrochemical impedance spectroscopy (EIS) techniques. The surfaces of the very thin, protein imprinted sites on GNEE are utilized for immunospecific capture of CA 125 molecules, and the mass of bound on the electrode surface can be detected as a reduction in the faradic current from the redox marker. Under optimal conditions, the developed sensor showed good increments at the studied concentration range of 0.5–400 U mL−1. The lowest detection limit was found to be 0.5 U mL−1. Spiked human blood serum and unknown real serum samples were analyzed. The presence of non-specific proteins in the serum did not significantly affect the sensitivity of our assay. Molecular imprinting using synthetic polymers and nanomaterials provides an alternative approach to the trace detection of biomarker proteins.

Metal deposition using Ionic liquids

There is an interest to create zinc/tin alloys to replace cadmium as a corrosion protective coating material. Existing aqueous electroplating systems for these alloys are commercially available but have several limitations. Dangerous and highly toxic complexing agents are uses e.g. cyanides. To overcome these problems, ionic liquids could provide a solution to obtain an alloy containing 20 to 30% of zinc. Ionic liquids (IL’s) often have wider electrochemical windows which allow the deposition of e.g. refractive metals that can not be deposited from aqueous solutions. In IL’s it is often not necessary to add complexing agents. The Zn/Sn alloy deposition from IL’s is therefore a promising application for the plating industry. Nevertheless, there are some issues with this alternative for aqueous systems. The degradation of the organic components, the control of the concentration of two metals and the risk of a two phase deposition instead of an alloy had to be overcome first. It is the main purpose of this thesis to obtain a Zn/Sn alloy with 20% zinc using IL’s as an electrolyte. First a separate study was performed on both the zinc and the tin deposition. Afterwards, an attempt to deposit a Zn/Sn alloy was made. An introduction to a study about the electrodeposition of refractive metals concludes this work. It initiated the research for oxygen-free IL’s to deposit molybdenum or tungsten. Several parameters (temperature, metal source and concentration, organic complexing agents,…) were optimized for both the zinc, tin and zinc/tin deposition. Experiments were performed both in a parallel plate cell and a Hull cell, so as to investigate the effect of current density as well. Ethaline200 was selected as electrolyte. As substrate, brass and iron were selected, while as anode a plate of the metal to deposit was chosen, tin for the alloy. The best efficiencies were always obtained on brass; however the iron substrate resulted in the best depositions. A concentration of 0.27M ZnCl2, 0.07M SnCl2 with 0.015M of K3-HEDTA as complexant resulted in a deposition containing the desired alloy with the amount of 20% zinc and 80% tin with good appearance. Refractory metals as molybdenum and tungsten cannot be electrodeposited from aqueous solutions without forming a co-deposition with Ni, Co or Fe. Here, IL’s could again provide a solution. A first requirement is the dissolution of a metal source. MoO3 could be suitable, however there are doubts about using oxides. Oxygen-free IL’s were sought for. A first attempt was the combination of ZnCl2 with chlormequat (CCC), which gave liquids below 150°C in molar ratios of 2 : 1 and 3 : 1. Unfortuna tely, MoO3 didn’t dissolve in these IL’s. Another route to design oxygen-free IL’s was the synthesis of quaternary ammonium salts. None of the methods used, proved viable as reaction time was long and resulted in very low yields. Therefore, no sufficient quantities were obtained to perform the possible electrochemical behavior of refractive metals.

Diagnóstico energético e reengenharia do processo de secagem na fábrica de revestimentos

Este trabalho surgiu no âmbito da Tese de Mestrado em Engenharia Química - Ramo Optimização Energética na Indústria Química, aliando a necessidade da Empresa Monteiro Ribas – Indústrias, S.A. em resolver alguns problemas relacionados com as estufas da unidade J da fábrica de revestimentos. Outro dos objectivos era propor melhorias de eficiência energética neste sector da empresa. Para tal, foi necessário fazer um levantamento energético de toda a unidade, o que permitiu verificar que as estufas de secagem (Recobrimento 1 e 2) seriam o principal objecto de estudo. O levantamento energético da empresa permitiu conhecer o seu consumo anual de energia de 697,9 tep, o que a classifica, segundo o Decreto-lei nº 71 de 15 de Abril de 2008, como Consumidora Intensiva de Energia (CIE). Além disso, as situações que devem ser alvo de melhoria são: a rede de termofluido, que apresenta válvulas sem isolamento, o sistema de iluminação, que não é o mais eficiente e a rede de distribuição de ar comprimido, que não tem a estrutura mais adequada. Desta forma sugere-se que a rede de distribuição de termofluido passe a ter válvulas isoladas com lã de rocha, o investimento total é de 2.481,56 €, mas a poupança pode ser de 21.145,14 €/ano, com o período de retorno de 0,12 anos. No sistema de iluminação propõe-se a substituição dos balastros normais por electrónicos, o investimento total é de 13.873,74 €, mas a poupança é de 2.620,26 €/ano, com período de retorno de 5 anos. No processo de secagem das linhas de recobrimento mediram-se temperaturas de todos os seus componentes, velocidades de ar o que permitiu conhecer a distribuição do calor fornecido pelo termofluido. No Recobrimento 1, o ar recebe entre 39 a 51% do calor total, a tela recebe cerca de 25% e na terceira estufa este é apenas de 6%. Nesta linha as perdas de calor por radiação oscilam entre 6 e 11% enquanto as perdas por convecção representam cerca de 17 a 44%. Como o calor que a tela recebe é muito inferior ao calor recebido pelo ar no Recobrimento 1, propõe-se uma redução do caudal de ar que entra na estufa, o que conduzirá certamente à poupança de energia térmica. No Recobrimento 2 o calor fornecido ao ar representa cerca de 51 a 77% do calor total e o cedido à tela oscila entre 2 e 3%. As perdas de calor por convecção oscilam entre 12 e 26%, enquanto que as perdas por radiação têm valores entre 4 e 8%. No que diz respeito ao calor necessário para evaporar os solventes este oscila entre os 4 e 13%. Os balanços de massa e energia realizados ao processo de secagem permitiram ainda determinar o rendimento das 3 estufas do Recobrimento 1, com 36, 47 e 24% paras as estufa 1, 2 e 3, respectivamente. No Recobrimento 2 os valores de rendimento foram superiores, tendo-se obtido valores próximos dos 41, 81 e 88%, para as estufas 1, 2 e 3, respectivamente. Face aos resultados obtidos propõem-se a reengenharia do processo introduzindo permutadores compactos para aquecer o ar antes de este entrar nas estufas. O estudo desta alteração foi apenas realizado para a estufa 1 do Recobrimento 1, tendo-se obtido uma área de transferência de calor de 6,80 m2, um investimento associado de 8.867,81 €. e uma poupança de 708,88 €/ano, com um período de retorno do investimento de 13 anos. Outra sugestão consiste na recirculação de parte do ar de saída (5%), que conduz à poupança de 158,02 €/ano. Estes valores, pouco significativos, não estimulam a adopção das referidas sugestões.

Simultaneous distillation–extraction of high-value volatile compounds from Cistus ladanifer L.

The present paper describes a procedure to isolate volatiles from rock-rose (Cistus ladanifer L.) using simultaneous distillation–extraction (SDE). High-value volatile compounds (HVVC) were selected and the influence of the extraction conditions investigated. The effect of the solvent nature and extraction time on SDE efficiency was studied. The best performance was achieved with pentane in 1 h operation. The extraction efficiencies ranged from 65% to 85% and the repeatability varied between 4% and 6% (as a CV%). The C. ladanifer SDE extracts were analysed by headspace solid phase microextraction (HS-SPME) followed by gas chromatography with flame ionization detection (GC-FID). The HS-SPME sampling conditions such as fiber coating, temperature, ionic strength and exposure time were optimized. The best results were achieved with an 85 µm polyacrylate fiber for a 60 min headspace extraction at 40ºC with 20% (w/v) of NaCl. For optimized conditions the recovery was in average higher than 90% for all compounds and the intermediate precision ranged from 4 to 9% (as CV %). The volatiles α-pinene (22.2 mg g−1 of extract), 2,2,6-trimethylcyclohexanone (6.1 mg g−1 of extract), borneol (3.0 mg g−1 of extract) and bornyl acetate (3.9 mg g−1 of extract) were identified in the SDE extracts obtained from the fresh plant material.

Análise de tecnologias de impermeabilização e isolamento em reabilitação da envolvente de edifícios

Neste trabalho é abordado o estágio efectuado por um período de sete meses na E.A. (Engenheiros Associados) e um estudo de caso sobre as tecnologias aplicadas no isolamento térmico de paredes exteriores. Na primeira parte deste relatório é efectuada uma breve caracterização da empresa e da sua actividade no mercado. A Engenheiros e Associados tem a sua estrutura assente nos seguintes sectores: Técnico-Comercial, de Aprovisionamento e de Gestão Administrativa; da qual foi efectuada uma descrição do trabalho desenvolvido em cada um desses sectores, nomeadamente a permanência na obra e as visitas e diligências às obras. A segunda parte deste relatório, que é a parte fulcral do trabalho desenvolvido, assenta sobre o sistema de ETICS (External Thermal Insulation Composite System), ou seja, o sistema de reboco delgado armado sobre isolamento térmico. Foi utilizado o sistema Cappotto na Obra de Requalificação da Urbanização de Vila d’Este – 1ª Fase. Após uma breve apresentação e evolução da história do ETICS ao longo do tempo, é exposta a caracterização da obra onde vai ser aplicado o sistema, que recai sobre a tipologia dos edifícios. Refira-se que, neste relatório, os edifícios por serem de construção túnel se dividem em três tipos: tipo plana ou corrente, tipo ângulo e tipo topo. Na Analise de Patologias efectuada evidenciam-se as fissuras e a humidade presentes em quase toda a extensão dos referidos edifícios antes do tratamento, tornando-as assim as principais anomalias destes edifícios. Foram elemento de foco as anomalias existentes nos edifícios, como: Deterioração do fibrocimento; Insuficiência das caleiras; Deficiências das impermeabilizações; Ausência de rufos; Deficiência das ligações; Degradação do revestimento e pintura; Fissuração do reboco; Degradação dos forros exteriores; Deterioração das padieiras; Deterioração dos peitoris; Deterioração das juntas de dilatação; Infiltrações e condensações; Ruptura das canalizações; Deslocamentos; Deficiências de ventilação; Deficiências de estanqueidade; Inexistência de Sistema de combate a incêndios. Para estas patologias são apresentadas as propostas de solução de forma a eliminar as mesmas. Sendo o ETICS escolhido por ser o sistema que elimina a maior parte destas patologias, tendo em conta uma relação de qualidade/preço, é abordada de uma forma detalhada e extensiva da aplicação do sistema antes, durante e depois da obra em si. Assim como, é feita uma descrição pormenorizada do material utilizado para a implementação do sistema. A análise dos pontos críticos refere-se a zonas sensíveis onde há a necessidade de reforço do sistema com vista a eliminar o aparecimento posterior de patologias, como por exemplo as características de suporte. Após a aplicação do sistema podem aparecer algumas patologias das quais se destaca o facto dos produtos serem preparados em obra, o erro humano nas dosagens do fabricante e no acrescento de água sem necessidade e a par das condições climatéricas, são as causas mais comuns do aparecimento de anomalias no sistema de ETICS, provocando fissurações e infiltrações, que são descritas neste relatório. É também abordada a manutenção e reparação do sistema, onde a manutenção refere-se à lavagem e à remoção de microorganismos das paredes e posterior pintura. A reparação dos danos divide-se em dois tipos, áreas até 2 cm2 e áreas maiores que 2 cm2. Por fim, são apresentados alguns rendimentos, que foram possíveis obter ao longo do desenvolvimento do trabalho, dos materiais e da mão-de-obra, dando origem aos custos directos. Sendo também abordadas as vantagens e desvantagens do sistema desde o seu início até à sua conclusão.

Instrumentação e monitorização na avaliação do comportamento de maciços e estruturas envolventes: caso de poços em meio urbano

Atualmente, a escavação de poços em locais densamente ocupados requer medidas severas para reduzir riscos e possíveis influências quer na própria obra quer em estruturas próximas. Neste campo, a instrumentação geotécnica e a sua monitorização tem um papel determinante na execução de obras geotécnicas, sendo que neste trabalho é dado um especial realce à instrumentação utilizada, às atividades de observação geotécnica, bem como à análise e interpretação das leituras para o controlo de movimentos induzidos no terreno pelas escavações. Este acompanhamento é baseado num plano de instrumentação, sendo descrito de uma forma transversal a importância do projeto e em particular das fases do processo de investigação geotécnica. O acompanhamento da execução dos poços para a futura Estação da Reboleira, permitiu validar as soluções de projeto para um determinado método construtivo, determinadas através de métodos numéricos e semi-empíricos, e abordados neste trabalho. A monitorização sistemática desde o início das escavações até ao revestimento secundário, permitiu tecer apreciações sobre os valores obtidos, apresentando-se alguns registos. Todas estas ações visam controlar e antecipar riscos de acidentes provocados pela execução de escavações, pelo que nesta tese é também realçada a importância da segurança e higiene no trabalho na prevenção dos riscos profissionais, independentemente da sua origem.

Mechanical and tribological characterization of TiB2 thin films

Titanium Diboride (TiB2) presents high mechanical and physical properties. Some wear studies were also carried out in order to evaluate its tribological properties. One of the most popular wear tests for thin films is the ball-cratering configuration. This work was focused on the study of the tribological properties of TiB2 thin films using micro-abrasion tests and following the BS EN 1071-6: 2007 standard. Due to high hardness usually patented by these films, diamond was selected as abrasive on micro-abrasion tests. Micro-abrasion wear tests were performed under five different durations, using the same normal load, speed rotation and ball. Films were deposited by unbalanced magnetron sputtering Physical Vapour Deposition (PVD) technique using TiB2 targets. TiB2 films were characterized using different methods as Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscopy (EDS), Atomic Force Microscopy (AFM), X-ray Diffraction (XRD), Electron Probe Micro-Analyser (EPMA), Ultra Micro Hardness and Scratch-test Analysis, allowing to confirm that TiB2 presents adequate mechanical and physical properties. Ratio between hardness (coating and abrasive particles), wear resistance and wear coefficient were studied, showing that TiB2 films shows excellent properties for tribological applications.

Filament wound products made with thermoplastic matrix towpregs

Cost-effective glass-reinforced thermoplastic matri x towpregs produced by a powder coating line were used to manufacture composite pipes by fi lament winding. A conventional 6 axes filament-winding equipment was adapted for processi ng such structures. The influence of the filament winding speed and mandrel temperature on t he composite final properties was studied in the present work. An optimized processin g window was established by comparing the composite theoretical expected mechanical prope rties with the experimentally obtained ones. The final properties determined on the produc ed pipes and structures and the technological changes introduced to the conventiona l filament-winding equipment will be presented and discussed. Besides the processing des cription and conditions, it will be presented the relationship between processing condi tions and mechanical properties.

Processing of continuous fibre reinforced thermoplastics

Towpregs based on different fibres and thermoplastic matrices were processed for highly demanding and more commercial applications by different composite processing technologies. In the technologies used, compression moulding and pultrusion, the final composite pr ocessing parameters were studied in order to obtain composites with adequate properties at industrial compatible production rates. The produced towpregs were tested to verify its polymer content and degree of impregnation. The obtained results have shown t hat the coating line enabled to produce, with efficiency and industrial scale speed rates, thermoplastic matrix towpregs that may be used to manufacture composites for advanced and larger volume commercial markets.

Role of abrasive material on micro-abrasion wear tests

Micro-abrasion wear tests with ball-cratering configuration are widely used. Sources of variability are already studied by different authors and conditions for testing are parameterized by BS EN 1071-6: 2007 standard which refers silicon carbide as abrasive. However, the use of other abrasives is possible and allowed. In this work, ball-cratering wear tests were performed using four different abrasive particles of three dissimilar materials: diamond, alumina and silicon carbide. Tests were carried out under the same conditions on a steel plate provided with TiB2 hard coating. For each abrasive, five different test durations were used allowing understanding the initial wear phenomena. Composition and shape of abrasive particles were investigated by SEM and EDS. Scar areas were observed by optical and electronic microscopy in order to understand the wear effects caused by each of them. Scar geometry and grooves were analyzed and compared. Wear coefficient was calculated for each situation. It was observed that diamond particles produce well-defined and circular wear scars. Different silicon carbide particles presented dissimilar results as consequence of distinct particle shape and size distribution.

Increasing the wear resistance of molds for injection of glass fiber reinforced plastics

Abrasion by glass fibers during injection molding of fiber reinforced plastics raises new challenges to the wear performance of the molds. In the last few decades, a large number of PVD and CVD coatings have been developed with the aim of minimizing abrasion problems. In this work, two different coatings were tested in order to increase the wear resistance of the surface of a mold used for glass fiber reinforced plastics: TiAlSiN and CrN/CrCN/DLC. TiAlSiN was deposited as a graded monolayer coating while CrN/CrCN/DLC was a nanostructured coating consisting of three distinct layers. Both coatings were produced by PVD unbalanced magnetron sputtering and were characterized using scanning electron microscopy (SEM) provided with energy dispersive spectroscopy (EDS), atomic force microscopy (AFM), micro hardness (MH) and scratch test analysis. Coating morphology, thickness, roughness, chemical composition and structure, hardness and adhesion to the substrate were investigated. Wear resistance was characterized through industrial tests with coated samples and an uncoated reference sample inserted in a feed channel of a plastic injection mold working with 30 wt.% glass fiber reinforced polypropylene. Results after 45,000 injection cycles indicate that the wear resistance of the mold was increased by a factor of 25 and 58, by the TiAlSiN and CrN/CrCN/DLC coatings, respectively, over the uncoated mold steel.

Influence of the abrasive particles size in the micro-abrasion wear tests of TiAlSiN thin coatings

Ball rotating micro-abrasion tribometers are commonly used to carry out wear tests on thin hard coatings. In these tests, different kinds of abrasives were used, as alumina (Al2O3), silicon carbide (SiC) or diamond. In each kind of abrasive, several particle sizes can be used. Some studies were developed in order to evaluate the influence of the abrasive particle shape in the micro-abrasion process. Nevertheless, the particle size was not well correlated with the material removed amount and wear mechanisms. In this work, slurry of SiC abrasive in distilled water was used, with three different particles size. Initial surface topography was accessed by atomic force microscopy (AFM). Coating hardness measurements were performed with a micro-hardness tester. In order to evaluate the wear behaviour, a TiAlSiN thin hard film was used. The micro-abrasion tests were carried out with some different durations. The abrasive effect of the SiC particles was observed by scanning electron microscopy (SEM) both in the films (hard material) as in the substrate (soft material), after coating perforation. Wear grooves and removed material rate were compared and discussed.