Terminal defect analysis and classification methodology for automotive industry

The impact of end customer quality complaints with direct relationship with automotive components has presented negative trend at European level for the entire automotive industry. Thus, this research proposal is to concentrate efforts on the most important items of Pareto chart and understand the failure type and the mechanism involved, link and impact of the project and parameters on the process, ending it with the development of one of the company’s most desired tool, that hosted this project – European methodology of terminals defects classification, and listing real opportunities for improvement based on measurement and analysis of actual data. Through the development of terminals defects classification methodology, which is considered a valuable asset to the company, all the other companies of the YAZAKI’s group will be able to characterize terminals as brittle or ductile, in order to put in motion, more efficiently, all the other different existing internal procedures for the safeguarding of the components, improving manufacturing efficiency. Based on a brief observation, nothing can be said in absolute sense, concerning the failure causes. Base materials, project, handling during manufacture and storage, as well as the cold work performed by plastic deformation, all play an important role. However, it was expected that this failure has been due to a combination of factors, in detriment of the existence of a single cause. In order to acquire greater knowledge about this problem, unexplored by the company up to the date of commencement of this study, was conducted a thorough review of existing literature on the subject, real production sites were visited and, of course, the actual parts were tested in lab environment. To answer to many of the major issues raised throughout the investigation, were used extensively some theoretical concepts focused on the literature review, with a view to realizing the relationship existing between the different parameters concerned. Should here be stated that finding technical studies on copper and its alloys is really hard, not being given all the desirable information. This investigation has been performed as a YAZAKI Europe Limited Company project and as a Master Thesis for Instituto Superior de Engenharia do Porto, conducted during 9 months between 2012/2013.

Adherend thickness effect on the tensile fracture toughness of a structural adhesive using an optical data acquisition method

Adhesive bonding is nowadays a serious candidate to replace methods such as fastening or riveting, because of attractive mechanical properties. As a result, adhesives are being increasingly used in industries such as the automotive, aerospace and construction. Thus, it is highly important to predict the strength of bonded joints to assess the feasibility of joining during the fabrication process of components (e.g. due to complex geometries) or for repairing purposes. This work studies the tensile behaviour of adhesive joints between aluminium adherends considering different values of adherend thickness (h) and the double-cantilever beam (DCB) test. The experimental work consists of the definition of the tensile fracture toughness (GIC) for the different joint configurations. A conventional fracture characterization method was used, together with a J-integral approach, that take into account the plasticity effects occurring in the adhesive layer. An optical measurement method is used for the evaluation of crack tip opening and adherends rotation at the crack tip during the test, supported by a Matlab® sub-routine for the automated extraction of these quantities. As output of this work, a comparative evaluation between bonded systems with different values of adherend thickness is carried out and complete fracture data is provided in tension for the subsequent strength prediction of joints with identical conditions.