Adhesion and wear behaviour of NCD coatings on Si3N4 by micro-abrasion tests

Nanocrystalline diamond (NCD) coatings offer an excellent alternative for tribological applications, preserving most of the intrinsic mechanical properties of polycrystalline CVD diamond and adding to it an extreme surface smoothness. Silicon nitride (Si3N4) ceramics are reported to guarantee high adhesion levels to CVD microcrystalline diamond coatings, but the NCD adhesion to Si3N4 is not yet well established. Micro-abrasion tests are appropriate for evaluating the abrasive wear resistance of a given surface, but they also provide information on thin film/substrate interfacial resistance, i.e., film adhesion. In this study, a comparison is made between the behaviour of NCD films deposited by hot-filament chemical vapour deposition (HFCVD) and microwave plasma assisted chemical vapour deposition (MPCVD) techniques. Silicon nitride (Si3N4) ceramic discs were selected as substrates. The NCD depositions by HFCVD and MPCVD were carried out using H2–CH4 and H2–CH4–N2 gas mixtures, respectively. An adequate set of growth parameters was chosen for each CVD technique, resulting in NCD films having a final thickness of 5 m. A micro-abrasion tribometer was used, with 3 m diamond grit as the abrasive slurry element. Experiments were carried out at a constant rotational speed (80 r.p.m.) and by varying the applied load in the range of 0.25–0.75 N. The wear rate for MPCVD NCD (3.7±0.8 × 10−5 m3N−1m−1) is compatible with those reported for microcrystalline CVD diamond. The HFCVD films displayed poorer adhesion to the Si3N4 ceramic substrates than the MPCVD ones. However, the HFCVD films show better wear resistance as a result of their higher crystallinity according to the UV Raman data, despite evidencing premature adhesion failure.

Share GFS – Games, Films & Series: sistema de recomendação

Esta dissertação incide sobre o estudo e análise de uma solução para a criação de um sistema de recomendação para uma comunidade de consumidores de media e no consequente desenvolvimento da mesma cujo âmbito inicial engloba consumidores de jogos, filmes e/ou séries, com o intuito de lhes proporcionar a oportunidade de partilharem experiências, bem como manterem um registo das mesmas. Com a informação adquirida, o sistema reúne condições para proceder a sugestões direcionadas a cada membro da comunidade. O sistema atualiza a sua informação mediante as ações e os dados fornecidos pelos membros, bem como pelo seu feedback às sugestões. Esta aprendizagem ao longo do tempo permite que as sugestões do sistema evoluam juntamente com a mudança de preferência dos membros ou se autocorrijam. O sistema toma iniciativa de sugerir mediante determinadas ações, mas também pode ser invocada uma sugestão diretamente pelo utilizador, na medida em que este não precisa de esperar por sugestões, podendo pedir ao sistema que as forneça num determinado momento. Nos testes realizados foi possível apurar que o sistema de recomendação desenvolvido forneceu sugestões adequadas a cada utilizador específico, tomando em linha de conta as suas ações prévias. Para além deste facto, o sistema não forneceu qualquer sugestão quando o histórico destas tinha provado incomodar o utilizador.

Análise dinâmica de composições musicais

A composição musical é um tema de muito interesse para a computação evolucionária dentro da área da inteligência artificial. É uma área que tem sofrido vários desenvolvimentos ao longo dos últimos anos pois o interesse em que hajam computadores que façam obras musicais é deveras aliciante. Este trabalho tem por objectivo realizar mais um passo nesse sentido. Assim, foi desenvolvida uma aplicação informática que realiza composições musicais de dois géneros distintos: Músicas Infantis e Músicas Blues. A aplicação foi implementada com recurso aos Algoritmos Genéticos, que são os algoritmos evolucionários mais populares da área da computação evolucionária. O trabalho foi estruturado em duas fases de desenvolvimento. Na primeira fase, realizou-se um levantamento estatístico sobre as características específicas de cada um dos géneros musicais. Analisaram-se quinze músicas de cada género musical, com o intuito de se chegar a uma proporção do uso que cada nota tem em cada um dos casos. Na segunda fase, desenvolveu-se o software que compõe as músicas com implementação de um algoritmo genético. Além disso, foi também desenvolvida uma interface gráfica que permite ao utilizador a escolha do género musical que pretende compor. O algoritmo genético começa por gerar uma população inicial de potenciais soluções de acordo com a escolha do utilizador, realizando, de seguida, o ciclo que caracteriza o algoritmo genético. A população inicial é constituída por soluções que seguem as regras que foram implementadas de acordo com os dados recolhidos ao longo da primeira fase. Foi também implementada uma interface de avaliação, através da qual, o utilizador pode ouvir cada uma das músicas para posterior avaliação em termos de fitness. O estado de evolução do algoritmo é apresentado, numa segunda interface, a qual facilita a clareza e justiça na avaliação ao longo de todo o processo. Esta última apresenta informação sobre a média das fitness da geração anterior e actual, sendo assim possível ter uma noção da evolução do algoritmo, no sentido de se obterem resultados satisfatórios no que diz respeito às composições musicais.

Sound levels and risk perceptions of music students during classes

It is well recognized that professional musicians are at risk of hearing damage due to the exposure to high sound pressure levels during music playing. However, it is important to recognize that the musicians’ exposure may start early in the course of their training as students in the classroom and at home. Studies regarding sound exposure of music students and their hearing disorders are scarce and do not take into account important influencing variables. Therefore, this study aimed to describe sound level exposures of music students at different music styles, classes, and according to the instrument played. Further, this investigation attempted to analyze the perceptions of students in relation to exposure to loud music and consequent health risks, as well as to characterize preventive behaviors. The results showed that music students are exposed to high sound levels in the course of their academic activity. This exposure is potentiated by practice outside the school and other external activities. Differences were found between music style, instruments, and classes. Tinnitus, hyperacusis, diplacusis, and sound distortion were reported by the students. However, students were not entirely aware of the health risks related to exposure to high sound pressure levels. These findings reflect the importance of starting intervention in relation to noise risk reduction at an early stage, when musicians are commencing their activity as students.

Preparação de biofilmes a partir de resíduos da indústria de curtumes

A indústria dos curtumes é uma das indústrias mais antigas e tradicionais de Portugal e é também uma das mais poluentes. Esta indústria produz muitos resíduos sólidos, entre os quais, está o pelo de bovino. A valorização deste resíduo permite reduzir o impacto ambiental e aumentar a eco-eficiência da indústria dos curtumes. O pelo de bovino, rico em queratina, é um bom candidato para a produção de biofilmes. O objetivo deste trabalho foi a valorização de um resíduo de indústria de curtume (pelo de bovino) através da produção de filmes à base de queratina por termocompressão. Foi estudada a melhor formulação e as condições operatórias mais favoráveis com a finalidade de melhorar as propriedades mecânicas dos filmes. O trabalho realizado durante este projeto dividiu-se em 5 partes: preparação do material, caracterização do material, seleção do pré-tratamento, produção de filmes e caracterização dos filmes. Foram produzidos filmes para a seleção do pré-tratamento e para a respetiva caracterização. Os pré-tratamentos testados foram: tratamento com detergente, tratamento com detergente e sulfureto de sódio e, tratamento com detergente e éter de petróleo. O pré-tratamento selecionado foi o tratamento com detergente. Para a produção de filmes para a posterior caracterização, foram escolhidos 4 conjuntos de condições operatórias diferentes: 160 oC – 147 kN – 8 min – 30% glicerol; 160 oC – 147 kN – 12 min – 30% glicerol; 160 oC – 147 kN – 8 min – 40% glicerol; 160 oC – 147 kN – 12 min – 40% glicerol; identificados como Conjuntos A, B, C e D, respetivamente. Na caracterização dos filmes foram analisados vários parâmetros, nomeadamente a espessura, a permeabilidade ao vapor de água ao vapor de água, as isotérmicas de sorção, a cor, a solubilidade e as propriedades mecânicas. Também foram feitas as análises de calorimetria diferencial de varrimento (DSC) e microscopia eletrónica de varrimento (SEM). Concluiu-se que os filmes do conjunto A (160 oC – 147 kN – 8 min – 30% glicerol) tiveram um melhor desempenho apresentando espessuras médias de 0,25 0,02 mm, permeabilidade ao vapor de água ao vapor de água igual a 1,20 x 10-8 6,79 x 10-10 g/(m.s.Pa), solubilidade igual a 27,9 0,4 %, tensão de rutura média igual a 9,23 1,19 N/mm2, deformação na rutura média igual a 1,9 0,2 % e módulo de elasticidade médio igual a 554 26 N/mm2. Verificou-se um bom ajuste do modelo de GAB aos resultados experimentais. A análise DSC indicou uma temperatura de fusão aos 170 ºC para a mistura de pelo e glicerol que não se verificou nos filmes formados e indicou a temperatura de degradação do material por volta dos 240-250 ºC. A análise SEM mostrou que os filmes não estão totalmente fundidos e provou a irregularidade da superfície dos mesmos. Provou-se que é possível a produção de filmes de pelo bovino sendo ainda necessário melhorar o processo de mistura do pelo com o glicerol.

Protein-responsive polymers for point-of-care detection of cardiac biomarker

This work describes a novel use for the polymeric film, poly(o-aminophenol) (PAP) that was made responsive to a specific protein. This was achieved through templated electropolymerization of aminophenol (AP) in the presence of protein. The procedure involved adsorbing protein on the electrode surface and thereafter electroploymerizing the aminophenol. Proteins embedded at the outer surface of the polymeric film were digested by proteinase K and then washed away thereby creating vacant sites. The capacity of the template film to specifically rebind protein was tested with myoglobin (Myo), a cardiac biomarker for ischemia. The films acted as biomimetic artificial antibodies and were produced on a gold (Au) screen printed electrode (SPE), as a step towards disposable sensors to enable point-of-care applications. Raman spectroscopy was used to follow the surface modification of the Au-SPE. The ability of the material to rebind Myo was measured by electrochemical techniques, namely electrochemical impedance spectroscopy (EIS) and square wave voltammetry (SWV). The devices displayed linear responses to Myo in EIS and SWV assays down to 4.0 and 3.5 μg/mL, respectively, with detection limits of 1.5 and 0.8 μg/mL. Good selectivity was observed in the presence of troponin T (TnT) and creatine kinase (CKMB) in SWV assays, and accurate results were obtained in applications to spiked serum. The sensor described in this work is a potential tool for screening Myo in point-of-care due to the simplicity of fabrication, disposability, short time response, low cost, good sensitivity and selectivity.

Myoglobin-biomimetic electroactive materials made by surface molecular imprinting on silica beads and their use as ionophores in polymeric membranes for potentiometric transduction

Myoglobin (Mb) is among the cardiac biomarkers playing a major role in urgent diagnosis of cardiovascular diseases. Its monitoring in point-of-care is therefore fundamental. Pursuing this goal, a novel biomimetic ionophore for the potentiometric transduction of Mb is presented. It was synthesized by surface molecular imprinting (SMI) with the purpose of developing highly efficient sensor layers for near-stereochemical recognition of Mb. The template (Mb) was imprinted on a silane surface that was covalently attached to silica beads by means of self-assembled monolayers. First the silica was modified with an external layer of aldehyde groups. Then, Mb was attached by reaction with its amine groups (on the external surface) and subsequent formation of imine bonds. The vacant places surrounding Mb were filled by polymerization of the silane monomers 3-aminopropyltrimethoxysilane (APTMS) and propyltrimethoxysilane (PTMS). Finally, the template was removed by imine cleavage after treatment with oxalic acid. The results materials were finely dispersed in plasticized PVC selective membranes and used as ionophores in potentiometric transduction. The best analytical features were found in HEPES buffer of pH 4. Under this condition, the limits of detection were of 1.3 × 10−6 mol/L for a linear response after 8.0 × 10−7 mol/L with an anionic slope of −65.9 mV/decade. The imprinting effect was tested by preparing non-imprinted (NI) particles and employing these materials as ionophores. The resulting membranes showed no ability to detect Mb. Good selectivity was observed towards creatinine, sacarose, fructose, galactose, sodium glutamate, and alanine. The analytical application was conducted successfully and showed accurate and precise results.

Biomimetic norfloxacin sensors made of molecularly-imprinted materials for potentiometric transduction

A biomimetic sensor for norfloxacin is presented that is based on host-guest interactions and potentiometric transduction. The artificial host was imprinted into polymers made from methacrylic acid and/or 2-vinyl pyridine. The resulting particles were entrapped in a plasticized poly(vinyl chloride) (PVC) matrix. The sensors exhibit near-Nernstian response in steady state evaluations, and detection limits range from 0.40 to 1.0 μg mL−1, respectively, and are independent of pH values at between 2 and 6, and 8 and 11, respectively. Good selectivity was observed over several potential interferents. In flowing media, the sensors exhibit fast response, a sensitivity of 68.2 mV per decade, a linear range from 79 μM to 2.5 mM, a detection limit of 20 μg mL−1, and a stable baseline. The sensors were successfully applied to field monitoring of norfloxacin in fish samples, biological samples, and pharmaceutical products.

Anomalous persistent photoconductivity in Cu2ZnSnS4 thin films and solar cells

A persistent photoconductivity effect (PPC) has been investigated in Cu2ZnSnS4 thin films and solar cells as a function of temperature. An anomalous increase of the PPC decay time with temperature was observed in all samples. The PPC decay time activation energy was found to increase when temperature rises above a crossover value, and also to grow with the increase of the sulfurization temperature and pressure. Both the anomalous behavior of the PPC decay time and the existence of two different activation energies are explained in terms of local potential fluctuations in the band edges of CZTS.

Effect of selenization conditions on the growth and properties of Cu2ZnSn(S,Se)4 thin films

The opto-electronic properties of copper zinc tin sulfide can be tuned to achieve better cell efficiencies by controlled incorporation of selenium. In this paper we report the growth of Cu2ZnSn(S,Se)4 (CZTSSe) using a hybrid process involving the sequential evaporation of Zn and sputtering of the sulfide precursors of Cu and Sn, followed by a selenization step. Two approaches for selenization were followed, one using a tubular furnace and the other using a rapid thermal processor. The effects of annealing conditions on the morphological and structural properties of the films were investigated. Scanning electron microscopy and energy dispersive spectroscopy were employed to investigate the morphology and composition of the films. Structural analyses were done using X-ray diffraction (XRD) and Raman spectroscopy. Structural analyses revealed the formation of CZTSSe. This study shows that regardless of the selenization method a temperature above 450 °C is required for conversion of precursors to a compact CZTSSe layer. XRD and Raman analysis suggests that the films selenized in the tubular furnace are selenium rich whereas the samples selenized in the rapid thermal processor have higher sulfur content.

A comparison between thin film solar cells made from co-evaporated CuIn1-xGaxSe2using a one-stage process versus a three-stage process

Until this day, the most efficient Cu(In,Ga)Se2 thin film solar cells have been prepared using a rather complex growth process often referred to as three-stage or multistage. This family of processes is mainly characterized by a first step deposited with only In, Ga and Se flux to form a first layer. Cu is added in a second step until the film becomes slightly Cu-rich, where-after the film is converted to its final Cu-poor composition by a third stage, again with no or very little addition of Cu. In this paper, a comparison between solar cells prepared with the three-stage process and a one-stage/in-line process with the same composition, thickness, and solar cell stack is made. The one-stage process is easier to be used in an industrial scale and do not have Cu-rich transitions. The samples were analyzed using glow discharge optical emission spectroscopy, scanning electron microscopy, X-ray diffraction, current–voltage-temperature, capacitance-voltage, external quantum efficiency, transmission/reflection, and photoluminescence. It was concluded that in spite of differences in the texturing, morphology and Ga gradient, the electrical performance of the two types of samples is quite similar as demonstrated by the similar J–V behavior, quantum spectral response, and the estimated recombination losses.

Exploring the long-term associations between adolescents’ music training and academic achievement

There is a positive relationship between learning music and academic achievement, although doubts remain regarding the mechanisms underlying this association. This research analyses the academic performance of music and non-music students from seventh to ninth grade. The study controls for socioeconomic status, intelligence, motivation and prior academic achievement. Data were collected from 110 adolescents at two time points, once when the students were between 11 and 14 years old in the seventh grade, and again 3 years later. Our results show that music students perform better academically than non-music students in the seventh grade (Cohen’s d = 0.88) and in the ninth grade (Cohen’s d = 1.05). This difference is particularly evident in their scores in Portuguese language and natural science; the difference is somewhat weaker in history and geography scores, and is least pronounced in mathematics and English scores (η2 p from .09 to .21). A longitudinal analysis also revealed better academic performance by music students after controlling for prior academic achievement (η2 p = .07). Furthermore, controlling for intelligence, socioeconomic status and motivation did not eliminate the positive association between music learning from the seventh to the ninth grade and students’ academic achievement (η2 p = .06). During the period, music students maintained better and more consistent academic standing. We conclude that, after controlling for intelligence, socioeconomic status and motivation, music training is positively associated with academic achievement.

Sistema de Recomendação: Share GFS Games, Films & Series

Esta dissertação incide sobre o estudo e análise de uma solução para a criação de um sistema de recomendação para uma comunidade de consumidores de media e no consequente desenvolvimento da mesma cujo âmbito inicial engloba consumidores de jogos, filmes e/ou séries, com o intuito de lhes proporcionar a oportunidade de partilharem experiências, bem como manterem um registo das mesmas. Com a informação adquirida, o sistema reúne condições para proceder a sugestões direccionadas a cada membro da comunidade. O sistema actualiza a sua informação mediante as acções e os dados fornecidos pelos membros, bem como pelo seu feedback às sugestões. Esta aprendizagem ao longo do tempo permite que as sugestões do sistema evoluam juntamente com a mudança de preferência dos membros ou se autocorrijam. O sistema toma iniciativa de sugerir mediante determinadas acções, mas também pode ser invocada uma sugestão directamente pelo utilizador, na medida em que este não precisa de esperar por sugestões, podendo pedir ao sistema que as forneça num determinado momento. Nos testes realizados foi possível apurar que o sistema de recomendação desenvolvido forneceu sugestões adequadas a cada utilizador específico, tomando em linha de conta as suas acções prévias. Para além deste facto, o sistema não forneceu qualquer sugestão quando o histórico destas tinha provado incomodar o utilizador.

Estudo electroquímico de compostos naturais e semicondutores com possível utilização em células foto voltaicas

As células foto voltaicas orgânicas ou células de Gräetzel (depois do seu descobridor) são aparelhos para a colecta de energia solar que utilizam um semicondutor inorgânico e uma molécula orgânica. Dita molécula orgânica é capaz de excitar-se na presença de radiação electromagnética e ceder esta energia através da doação de electrões a este semicondutor. Embora estas estruturas e o seu processo de fabrico sejam relativamente pouco onerosas, o aproveitamento da energia solar é ainda muito baixo. Para além desta deficiência, os corantes sintéticos sofrem de “bleaching” ou então são reduzidos ou oxidados facilmente quando não conseguem transferir a energia que foi absorvida ou quando é difícil voltar ao estado original por dificuldades no completamento de circulação de electrões. Neste trabalho pretende-se então estudar o comportamento de moléculas e misturas complexas de moléculas com capacidade para serem excitadas pela luz solar. Como a dita xcitação promove a transferência de um electrão, este processo será seguido pela técnica de Voltametria cíclica. Como substâncias absorventes de luz utilizaremos compostos naturais (principalmente flavonóides) puros, ou então na forma de complexos naturais extraídos de algumas plantas. Estas misturas de corantes serão extractos aquosos (infusões) de casca de laranja e limão assim como extractos de folhas de cerejeira, com o objectivo de proporcionar lternativas aos flavonóides utilizados neste estudo. A caracterização voltamétrica desta célula é feita em diferentes formas de iluminação. Sobre a célula assim formada faz-se incidir rimeiro luz de lâmpadas fluorescentes, depois luz ultra violeta e por fim sem qualquer tipo de luz incidente. Na base do fabrico da variante mais clássica destas células está o semicondutor óxido de itânio (TiO2), por ser uma substância muito comum e barata e com propriedades semicondutoras notáveis. Uma forma comum de melhorar a eficiência deste material é introduzir dopantes com o intuito de melhorar a eficiência do processo de transferência electrónica. Um segundo objectivo deste trabalho é o estudo de sistemas semicondutor/molécula foto activa. Semicondutores como ZnO, TiO2 e TiO2 dopado serão então estudados. O gels de TiO2 ou o TiO2 dopado serão depositados sobre lâminas de vidro comum, nas quais foi anteriormente depositado uma película de alumínio que serve de condutor (eléctrodo egativo). Uma outra variante será a utilização de óxido de zinco, um semicondutor de baixo custo que por sua vez vai ser depositado em lâminas de alumínio comercial. A nossa célula foto electroquímica será então formada por moléculas de corante, uma lâmina e um semicondutor (que funcionará como eléctrodo de trabalho), com ou sem electrólito/catalizador (solução de iodo/iodeto), e eléctrodos de referência de Ag/AgCl, e outro auxiliar de grafite. Um outro objectivo é fazer um pequeno estudo sobre influencia do catalisador I2/etilenodiamina no comportamento electroquímico da célula, de forma a poder utilizar o solvente (etilenodiamina) com menor volatilidade do que a água, que é empregada no par I2/I3.m A importância deste facto prende-se com a limitada vida destas células quando o electrólito/solvente é evaporado pelas altas temperaturas da radiação incidente.

Intervalos melódicos: diferentes estratégias de aprendizagem

O presente documento foi realizado no âmbito do Mestrado em Ensino de Música, ramo Formação Musical, na Escola Superior de Educação e Escola Superior de Música Artes e Espectáculos do Instituto Politécnico do Porto. O objectivo central deste documento visa, num primeiro capítulo, contextualizar o meio, a escola e a turma. No segundo capítulo deste documento constará a reflexão da Prática Pedagógica em Formação Musical, no Conservatório de Música de Paredes. No terceiro capítulo será apresentado o Projecto de Investigação em estudo – Intervalos melódicos: diferentes estratégias de aprendizagem. Esta investigação surge no sentido de tentar perceber quais as estratégias que surtem efeitos mais positivos para a aprendizagem de intervalos melódicos. As estratégias adoptadas foram três, são elas: aprendizagem por canções; aprendizagem por grau conjunto; aprendizagem por canções e grau conjunto. Foram seleccionados 18 indivíduos com idades compreendidas entre os 8 e os 12 anos de idade, de ambos os sexos. Todos eles têm em comum o facto de frequentarem o 1º grau de Formação Musical. A metodologia utilizada foi o estudo de caso, com abordagem quantitativa. Para testar as diferentes estratégias de aprendizagem foi realizado um teste após um período de oito semanas (8 aulas). Será feita uma revisão bibliográfica, onde serão abordadas algumas perspectivas de diferentes autores, para que possamos compreender melhor o tema desta investigação. As conclusões deste estudo revelam que a aprendizagem de intervalos melódicos utilizando a complementaridade das estratégias por canções e por grau conjunto são mais positivas, ainda que os resultados não sejam muito evidentes.