Low-Carbon Cement with Waste Oil-Cracking Catalyst Incorporation

The present paper shows preliminary results of an ongoing project which one of the goals is to investigate the viability of using waste FCC catalyst (wFCC), originated from Portuguese oil refinery, to produce low carbon blended cements. For this purpose, four blended cements were produced by substituting cement CEM I 42.5R up to 20% (w/w) by waste FCC catalyst. Initial and final setting times, consistency of standard paste, soundness and compressive strengths after 2, 7 and 28 days were measured. It was observed that the wFCC blended cements developed similar strength, at 28 days, compared to the reference cement, CEM I 42.5R. Moreover, cements with waste FCC catalyst incorporation up to 15% w/w meet European Standard EN 197-1 specifications for CEM II/A type cement, in the 42.5R strength class.

Acompanhamento dos trabalhos de reabilitação de espaços exteriores à Casa Museu dos Patudos e edifício de apoio: Câmara Municipal de Alpiarça

Relatório de Estágio para obtenção de grau de Mestre em Engenharia Civil Perfil de Edificações

Análise do sistema de tratamento de efluentes gasosos de uma central de valorização energética de resíduos sólidos urbanos

Trabalho Final de Mestrado para obtenção do grau de Mestre Em Engenharia Química e Biológica Ramo de processos Químicos

Contribuição para o estudo dos subprodutos de uma ETAR: gradados e areias

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Civil, na Área de Especialização de Hidráulica

Low-carbon cement with waste oil-craking catalyst incorporation

The present paper shows preliminary results of an ongoing project which one of the goals is to investigate the viability of using waste FCC catalyst (wFCC), originated from Portuguese oil refinery, to produce low carbon blended cements. For this purpose, four blended cements were produced by substituting cement CEM I 42.5R up to 20% (w/w) by waste FCC catalyst. Initial and final setting times, consistency of standard paste, soundness and compressive strengths after 2, 7 and 28 days were measured. It was observed that the wFCC blended cements developed similar strength, at 28 days, compared to the reference cement, CEM I 42.5R. Moreover, cements with waste FCC catalyst incorporation up to 15% w/w meet European Standard EN 197-1 specifications for CEM II/A type cement, in the 42.5R strength class.

Integração num plano municipal de segurança rodoviária: Cidade da Amadora: Freguesia da Venteira

Trabalho de Projeto para obtenção do grau de Mestre em Engenharia na Área de Especialização em Vias de Comunicação e Transportes

Implementação de um sistema de gestão municipal com recurso a sistemas de informação geográfica

Dissertação para obtenção do grau de Mestre em Engenharia Civil na Área de Especialização em Vias de Comunicação e Transportes