Wetting behaviour of femtosecond laser textured Ti-6Al-4V surfaces

The aim of the present work was to investigate the wetting behaviour of biomedical grade Ti-6Al-4V alloy surfaces textured by a femtosecond laser treatment. The material was treated in ambient atmosphere using an Yb: KYW chirped-pulse-regenerative amplification laser with a wavelength of 1030 nm and a pulse duration of 500 fs. Four main types of surface textures were obtained depending on the processing parameters and laser treatment method. These textures consist of: (1) nanoscale laser-induced periodic surface structures (LIPSS); (2) nanopillars; (3) a bimodal roughness distribution texture formed of LIPSS overlapping microcolumns; (4) a complex texture formed of LIPSS overlapping microcolumns with a periodic variation of the columns size in the laser scanning direction. The wettability of the surfaces was evaluated by the sessile drop method using distilled-deionized (DD) water and Hank's balanced salt solution (HBSS) as testing liquids. The laser treated surfaces present a hydrophilic behaviour as well as a high affinity for the saline solution, with equilibrium contact angles in the ranges 24.1-76.2. for DD water and 8.4-61.8. for HBSS. The wetting behaviour is anisotropic, reflecting the anisotropy of the surface textures. (c) 2012 Elsevier B.V. All rights reserved.

Comparative study of amine solutions used in CO2 absorption/desorption cycles

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Química

"In-vitro" corrosion behaviour of the magnesium alloy with Al and Zn (AZ31) protected with a biodegradable polycaprolactone coating loaded with hydroxyapatite and cephalexin

Mg alloys are very susceptible to corrosion in physiological media. This behaviour limits its widespread use in biomedical applications as bioresorbable implants, but it can be controlled by applying protective coatings. On one hand, coatings must delay and control the degradation process of the bare alloy and, on the other hand, they must be functional and biocompatible. In this study a biocompatible polycaprolactone (PCL) coating was functionalised with nano hydroxyapatite (HA) particles for enhanced biocompatibility and with an antibiotic, cephalexin, for anti-bacterial purposes and applied on the AZ31 alloy. The chemical composition and the surface morphology of the coated samples, before and after the corrosion tests, were studied by scanning electron microscopy (SEM) coupled with energy dispersive x-ray analysis (EDX) and Raman. The results showed that the presence of additives induced the formation of agglomerates and defects in the coating that resulted in the formation of pores during immersion in Hanks' solution. The corrosion resistance of the coated samples was studied in Hank's solution by electrochemical impedance spectroscopy (EIS). The results evidenced that all the coatings can provide corrosion protection of the bare alloy. However, in the presence of the additives, corrosion protection decreased. The wetting behaviour of the coating was evaluated by the static contact angle method and it was found that the presence of both hydroxyapatite and cephalexin increased the hydrophilic behaviour of the surface. The results showed that it is possible to tailor a composite coating that can store an antibiotic and nano hydroxyapatite particles, while allowing to control the in-vitro corrosion degradation of the bioresorbable Mg alloy AZ31. (C) 2015 Elsevier Ltd. All rights reserved.

Aryleneethynylene Trimers Bearing Calix[4]arenes: synthesis, optical properties and self-assembling studies

New homoditopic bis-calix[4]arene-carbazole conjugates, armed with hydrophilic carboxylic acid functions at their lower rims, are disclosed. Evidence for their self-association in solution was gathered from solvatochromic and thermochromic studies, as well as from gel-permeation chromatography analysis. Their ability to function as highly sensitive sensors toward polar electron-deficient aromatic compounds is demonstrated.