CVD of CrO(2): Towards a lower temperature deposition process

The deposition of highly oriented a-axis CrO(2) films onto Al(2)O(3)(0001) by atmospheric pressure (AP)CVD at temperatures as low as 330 C is reported. Deposition rates strongly depend on the substrate temperature, whereas for film surface microstructures the dependence is mainly on film thickness. For the experimental conditions used in this work, CrO(2) growth kinetics are dominated by a surface reaction mechanism with an apparent activation energy of (121.0 +/- 4.3) kJ mol(-1). The magnitude and temperature dependence of the saturation magnetization, up to room temperature, is consistent with bulk measurements.

Influence of growth temperature and carrier flux on the structure and transport properties of highly oriented CrO2 on Al2O3 (0001)

In this work we report on the structure and magnetic and electrical transport properties of CrO2 films deposited onto (0001) sapphire by atmospheric pressure (AP)CVD from a CrO3 precursor. Films are grown within a broad range of deposition temperatures, from 320 to 410 degrees C, and oxygen carrier gas flow rates of 50-500 seem, showing that it is viable to grow highly oriented a-axis CrO2 films at temperatures as low as 330 degrees C i.e., 60-70 degrees C lower than is reported in published data for the same chemical system. Depending on the experimental conditions, growth kinetic regimes dominated either by surface reaction or by mass-transport mechanisms are identified. The growth of a Cr2O3 interfacial layer as an intrinsic feature of the deposition process is studied and discussed. Films synthesized at 330 degrees C keep the same high quality magnetic and transport properties as those deposited at higher temperatures.

KrF pulsed laser deposition of chromium oxide thin films from Cr8O21 targets

Chromium oxides, CrxOy, are of great interest due to the wide variety of their technological applications. Among them, CrO2 has been extensively investigated in recent years because it is an attractive compound for use in spintronic heterostructures. However, its synthesis at low temperatures has been a difficult task due to the metastable nature of this oxide. This is indeed essential to ensure interface quality and the ability to coat thermal-sensitive materials such as those envisaged in spintronic devices. Pulsed Laser Deposition (PLD) is a technique that has the potential to meet the requirements stated above. In this work, we describe our efforts to grow chromium oxide thin films by PLD from Cr8O21 targets, using a KrF excimer laser. The as-deposited films were investigated by X-ray diffraction and Rutherford backscattering spectrometry. Structural and chemical composition studies showed that the films consist of a mixture of amorphous chromium oxides exhibiting different stoichiometries depending on the processing parameters, where nanocrystals of mainly Cr2O3 are dispersed. The analyses do not exclude the possibility of co-deposition of Cr2O3 and a low fraction of CrO2.

Electrical transport properties of CuS single crystals

Electrical resistivity, transverse magnetoresistance and thermoelectric power measurements were performed on CuS high quality single crystals in the range 1.2-300 K and under fields of up to 16 T. The zero field resistivity data are well described below 55 K by a quasi-2D model, consistent with a carrier confinement at lower temperatures, before the transition to the superconducting state. The transverse magnetoresistance develops mainly below 30 K and attains values as large as 470% for a 16 T field at 5 K, this behaviour being ascribed to a band effect mechanism, with a possible magnetic field induced DOS change at the Fermi level. The transverse magnetoresistance shows no signs of saturation, following a power law with field Delta rho/rho(0) proportional to H(1.4), suggesting the existence of open orbits for carriers at the Fermi surface. The thermoelectric power shows an unusual temperature dependence, probably as a result of the complex band structure of CuS.

KrP laser CVD of chromium oxide by photodissociation of Cr(CO)(6)

This work reports on the synthesis of chromium oxide thin films prepared by photodissociation of Cr(CO)(6) in an oxidizing atmosphere, using a pulsed UV laser (KrF, lambda = 248 nm). The experimental conditions, which should enable the synthesis of CrO2, are discussed and results on the deposition of CrxOy films on Al2O3 (0001) substrates are presented.

Structural and Microanalytical Studies of CrO2 Thin Films on c-Sapphire by High Resolution Electron Microscopy Methods

Chromium dioxide (CrO2) has been extensively used in the magnetic recording industry. However, it is its ferromagnetic half-metallic nature that has more recently attracted much attention, primarily for the development of spintronic devices. CrO2 is the only stoichiometric binary oxide theoretically predicted to be fully spin polarized at the Fermi level. It presents a Curie temperature of ∼ 396 K, i.e. well above room temperature, and a magnetic moment of 2 mB per formula unit. However an antiferromagnetic native insulating layer of Cr2O3 is always present on the CrO2 surface which enhances the CrO2 magnetoresistance and might be used as a barrier in magnetic tunnel junctions.