Fatigue Prediction on Fibrin Poly-ε-caprolactone Macroporous Scaffolds

Tissue engineering applications rely on scaffolds that during its service life, either for in-vivo or in vitro applications, are under mechanical solicitations. The variation of the mechanical condition of the scaffold is strongly relevant for cell culture and has been scarcely addressed. Fatigue life cycle of poly-ε-caprolactone, PCL, scaffolds with and without fibrin as filler of the pore structure were characterized both dry and immersed in liquid water. It is observed that the there is a strong increase from 100 to 500 in the number of loading cycles before collapse in the samples tested in immersed conditions due to the more uniform stress distributions within the samples, the fibrin loading playing a minor role in the mechanical performance of the scaffolds

Aspectos Relevantes na Implementação do Balanced Scorecard em Grandes Empresas Portuguesas

O Balanced Scorecard (BSC) aparece no panorama empresarial como uma poderosa ferramenta para enfrentar a forte concorrência. Tal constatação coloca a questão de sabermos se as empresas portuguesas estão a acompanhar esta evolução. Assim, no sentido de averiguarmos se conhecem e estão a adoptar o BSC, quais as principais motivações para a sua aplicação e como está a ser implementado, enviamos um questionário às 250 maiores empresas portuguesas. Os resultados revelam que embora exista um conhecimento elevado e correcto sobre esta ferramenta, a taxa de utilização é baixa e muito recente. À semelhança do registado em outros países, o BSC em Portugal ainda está numa fase inicial. O estudo revelou também que são essencialmente as empresas pertencentes ao sector secundário que mais utilizam o BSC. Não obstante, ao contrário de outros estudos, não obtivemos evidência empírica sobre a influência de variáveis como a localização geográfica, dimensão e internacionalização na utilização e conhecimento do BSC em Portugal.

Effect of filler content on morphology and physical-chemical characteristics of poly(vinylidene fluoride)/NaY-zeolite filled membranes

Poly(vinylidene fluoride) electrospun membranes have been prepared with different NaY zeolite contents up to 32%wt. Inclusion of zeolites induces an increase of average fiber size from ~200 nm in the pure polymer up to ~500 nm in the composite with 16%wt zeolite content. For higher filler contents, a wider distribution of fibers occurs leading to a broader size distributions between the previous fiber size values. Hydrophobicity of the membranes increases from ~115º water contact angle to ~128º with the addition of the filler and is independent on filler content, indicating a wrapping of the zeolite by the polymer. The water contact angle further increases with fiber alignment up to ~137º. Electrospun membranes are formed with ~80 % of the polymer crystalline phase in the electroactive  phase, independently on the electrospinning processing conditions or filler content. Viability of MC3T3-E1 cells on the composite membranes after 72 h of cell culture indicates the suitability of the membranes for tissue engineering applications.