Cyclic Fatigue Resistance of Rotary Nickel-Titanium Instruments Submitted to Nitrogen Ion Implantation

Introduction: The aim of this study was to assess cyclic fatigue resistance in rotary nickel-titanium instruments submitted to nitrogen ion implantation by using a custom-made cyclic fatigue testing apparatus. Methods: Thirty K3 files, size #25, taper 0.04, were divided into 3 experimental groups as follows: group A, 12 files exposed to nitrogen ion implantation at a dose of 2.5 x 10(17) ions/cm(2), accelerating voltage of 200 kV, currents of 1 mu A/cm(2), 130 degrees C temperature, and vacuum conditions of 10 x 10(-6) torr for 6 hours; group B, 12 nonimplanted files; and group C, 6 files submitted to thermal annealing for 6 hours at 130 degrees C. One extra file was used for process control. All files were submitted to a cyclic fatigue test that was performed with an apparatus that allowed the instruments to rotate freely, simulating rotary instrumentation of a curved canal (40-degree, 5-mm radius curve). An electric motor handpiece was used with a contra-angle of 16:1 at an operating speed of 300 rpm and a torque of 2 N-cm. Time to failure was recorded with a stopwatch in seconds and subsequently converted to number of cycles to fracture. Data were analyzed with the Student t test (P < .05). Results: Ion-implanted instruments reached significantly higher cycle numbers before fracture (mean, 510 cycles) when compared with annealed (mean, 428 cycles) and nonimplanted files (mean, 381 cycles). Conclusions: Our results showed that nitrogen ion implantation improves cyclic fatigue resistance in rotary nickel-titanium instruments. Industrial implementation. of this surface modification technique would produce rotary nickel-titanium instruments with a longer working life. (J Endod 2010;36:1183-1186)

Post space cleaning using a new nickel titanium endodontic drill combined with different cleaning regimens

This study compared the effect of two drills and five cleaning regimens on post space debridement. One hundred extracted premolars were instrumented and obturated with warm vertical compaction of gutta percha. The teeth were divided into two groups according to the drill used to remove gutta percha/sealer and for post space preparation: a Largo drill (Largo; Dentsply, St Quentin en Yvelines, France) or a MTwo-PF drill (Sweden&Martina, Due Carrare, Padova, Italy). The following cleaning regimens were used: EDTA, ultrasonics, ultrasonics + EDTA, phosphoric acid, and distilled water. Scanning electron microscopic images of the post spaces were taken, and the presence of debris and of open dentin tubules were evaluated. The ultrasonics + EDTA, phosphoric acid, and EDTA groups were comparable in open tubules scores for both drills and in debris scores after the use of MTwo-PF (p > 0.05). The ultrasonics and control groups performed significantly worse (p < 0.05). The MTwo-PF drill resulted as effective as the Largo drill in obtaining a good post space cleaning, especially when followed by ultrasonics + EDTA irrigant regimen.

Influence of shaft design on the shaping ability of 3 nickel-titanium rotary systems by means of spiral computerized tomography

Objective. To evaluate the influence of shaft design on the shaping ability of 3 rotary nickel-titanium (NiTi) systems. Study design. Sixty curved mesial canals of mandibular molars were used. Specimens were scanned by spiral tomography before and after canal preparation using ProTaper, ProFile, and ProSystem GT rotary instruments. One-millimeter-thick slices were scanned from the apical end point to the pulp chamber. The cross-sectional images from the slices taken earlier and after canal preparation at the apical, coronal, and midroot levels were compared. Results. The mean working time was 137.22 +/- 5.15 s. Mean transportation, mean centering ratio, and percentage of area increase were 0.022 +/- 0.131 mm, 0.21 +/- 0.11, and 76.90 +/- 42.27%, respectively, with no statistical differences (P > .05). Conclusions. All instruments were able to shape curved mesial canals in mandibular molars to size 30 without significant errors. The differences in shaft designs seemed not to affect their shaping capabilities.

Flat-Oval Root Canal Preparation with Self-Adjusting File Instrument: A Micro-Computed Tomography Study

Introduction: The aim of this study was to evaluate the root canal preparation in flat-oval canals treated with either rotary or self-adjusting file (SAF) by using micro-tomography analysis. Methods: Forty mandibular incisors were scanned before and after root canal instrumentation with rotary instruments (n = 20) or SAF (n = 20). Changes in canal volume, surface area, and cross-sectional geometry were compared with preoperative values. Data were compared by independent sample t test and chi(2) test between groups and paired sample t test within the group (alpha = 0.05). Results: Overall, area, perimeter, roundness, and major and minor diameters revealed no statistical difference between groups (P > .05). In the coronal third, percentage of prepared root canal walls and mean increases of volume and area were significantly higher with SAF (92.0%, 1.44 +/- 0.49 mm(3), 0.40 +/- 0.14 mm(2), respectively) than rotary instrumentation (62.0%, 0.81 +/- 0.45 mm(3), 0.23 +/- 0.15 mm2, respectively) (P < .05). SAF removed dentin layer from all around the canal, whereas rotary instrumentation showed substantial untouched areas. Conclusions: In the coronal third, mean increases of area and volume of the canal as well as the percentage of prepared walls were significantly higher with SAF than with rotary instrumentation. By using SAF instruments, flat-oval canals were homogenously and circumferentially prepared. The size of the SAF preparation in the apical third of the canal was equivalent to those prepared with #40 rotary file with a 0.02 taper. (J Endod 2011;37:1002-1007)

Histological evaluation of the effectiveness of increased apical enlargement for cleaning the apical third of curved canals

P>Objective To evaluate the influence of apical size on cleaning of the apical third of curved canals prepared with rotary instruments. Methodology Forty-four mesiobuccal canals of maxillary molars teeth were instrumented to different apical sizes (30, 0.02; 35, 0.02; 40, 0.02; 45, 0.02) using a crown-down technique. After canal preparation, the apical thirds of the roots were submitted to histological processing and examination. The specimens were analysed at 40x magnification and the images were submitted to morphometric analysis with an integration grid to evaluate the percentage of debris and uninstrumented root canal walls. The action of the instruments on the root canal walls was assessed based on the surface regularity, abrupt change on the continuity of root canal walls, and partial or total pre-dentine removal. The results were statistically compared using one-way anova with post hoc Tukey test. Pearson`s correlation was performed to identify potential correlations between values. Results The percentage of uninstrumented root canal dentine was higher when apical enlargement was performed with instruments 30, 0.02 taper (55.64 +/- 4.62%) and 35, 0.02 taper (49.03 +/- 5.70%) than with instruments 40, 0.02 taper (38.08 +/- 10.44%) and 45, 0.02 taper (32.65 +/- 8.51%) (P < 0.05). More debris were observed when apical enlargement was performed with instruments 30, 0.02 taper (34.62 +/- 9.49%) and 35, 0.02 taper (25.33 +/- 7.37%) (P < 0.05). There was a significant correlation between the amount of remaining debris and the perimeter of uninstrumented root canal dentine (r = 0.9130, P < 0.001). Conclusion No apical enlargement size allowed the root canal walls to be prepared completely. Apical third cleanliness could be predicted by instrument diameter.

Canal transportation and centring ability of RaCe rotary instruments

Evaluate, through computerized tomography, canal transportation and centring ability of RaCe rotary instruments after preparation of mesiobuccal root canals in maxillary molar teeth. Twenty-seven teeth were submitted to three cone beam tomographic analyses, one preoperatively, and two after preparation with file size 35, .02 taper and size 50, .02 taper. Canal transportation and centring ability were measured with reference to the distance between the noninstrumented portion of the root canals and the mesial and distal periphery of the root, compared with images obtained after the preparation with size 35 and 50 instruments. Canal transportation after preparation with the size 35 file was 0.030 +/- 0.253 mm and after the size 50 file was 0.057 +/- 0.317 mm. The centring ratio values after preparation with the size 35 file was 0.42 +/- 0.32 and after the size 50 file was 0.54 +/- 0.29, with no significant statistical difference between the groups. RaCe instruments allowed the preparation of curved root canals with preparation diameters larger than those normally used with minimal canal transportation and adequate centring ability.

Influence of Hero Apical instruments on cleaning ovoid-shaped root canals

The cleaning capacity of Hero 642 nickel-titanium files, complemented by the Hero Apical instruments in flattened roots, was determined by histological analysis, considering the area of action of the instruments on the coronal walls and the presence of remaining debris. Twenty-four single-canal, human mandibular incisors were divided into three groups and prepared as follows: GI, instrumented with Hero 642 NiTi files 30/.06, 25/.06, 20/.06, 25/.06, and 30/.06; GII, instrumented as GI followed by Hero Apical size 30/.06; GIII, instrumented as GI followed by Hero Apical sizes 30/.06 and 30/.08, then returning to 30/.06 with pendulum movements. The apical thirds were prepared for histological processing, analyzed at 40× magnification and the images were examined morphometrically. Statistical analysis showed that GIII presented the best results for removing debris (5.22% ± 4.13), with more contact between the instruments and the root canal walls (19.31% ± 0.15). This differed statistically from GI (14.04% ± 4.96 debris removal, with 42.96% ± 7.11 instrument contact) and GII (12.62% ± 5.76 debris removal, with 35.01% ± 0.15 instrument contact). Root canal preparation with Hero 642, complemented by Hero Apical instruments (30/.06 and 30/.08, then re-instrumented with Hero Apical 30/.06 using pendulum movements), was more efficient for debris removal and allowed more contact of the instruments with the root canal walls. GII presented the worst results.

Efficacy of Profile .04 taper series 29 in removing filling materials during root canal retreatment-an in vitro study

Objective. The aim of this study was to compare Profile .04 taper series 29 instruments and hand files for gutta-percha removal. Study design. Twenty maxillary central incisors with a single straight canal were instrumented and filled. The teeth were divided into 2 groups of 10 specimens each, according to gutta-percha removal techniques: Group 1- Profile series 29 and Group 2- hand files and solvent. The amount of time for gutta-percha removal and the number of fractured instruments were evaluated. Radiographs were taken and the teeth were grooved longitudinally and split. The area of residual debris was measured using computer software. Results. The time for filling material removal was significantly shorter when Profile series 29 was used (P = .00). Regarding cleanliness, there were no statistical differences in the teeth halves evaluations (P = .05). Hand instruments cleaned the canals significantly better than Profiles, in the radiographic analysis considering the whole canal. Overall, the radiographic analysis showed a smaller percentage of residual debris than the teeth halves analysis. Conclusion. The Profile series 29 instruments proved to be faster than hand instruments in removing root filling materials; however, hand instruments yielded better root canal cleanliness. Some residual debris was not visualized by radiographs. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e46-e50)

Comparative analysis of the fit of 3-unit implant-supported frameworks cast in nickel-chromium and cobalt-chromium alloys and commercially pure titanium after casting, laser welding, and simulated porcelain firings

This study compared the vertical misfit of 3-unit implant-supported nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloy and commercially pure titanium (cpTi) frameworks after casting as 1 piece, after sectioning and laser welding, and after simulated porcelain firings. The results on the tightened side showed no statistically significant differences. On the opposite side, statistically significant differences were found for Co-Cr alloy (118.64 mu m [SD: 91.48] to 39.90 mu m [SD: 27.13]) and cpTi (118.56 mu m [51.35] to 27.87 mu m [12.71]) when comparing 1-piece to laser-welded frameworks. With both sides tightened, only Co-Cr alloy showed statistically significant differences after laser welding. Ni-Cr alloy showed the lowest misfit values, though the differences were not statistically significantly different. Simulated porcelain firings revealed no significant differences.

Characterization of nickel-niobium composite electrocoatings

The electrodeposition of nickel based composites is been performed in order to improve properties of nickel layers, such as hardness, wear resistance, lubrication, corrosion resistance and catalytic activity. In the present work Nb powders (20 mu m average size) and Ni were codeposited on 1020 carbon steel by galvanostatic electrolysis of Watts bath, using 10, 20 and 40 mA/cm(2) cathodic current density and 240, 400 and 550 rpm electrolyte stirring rate. The morphology and texture of the coatings, Nb incorporated volume fraction, microhardness, adhesion to the substrate and corrosion behavior were evaluated. The Ni-Nb composite layers presented a rough morphology with randomly oriented Ni grains, whereas pure Ni coatings were smooth and showed highly preferred orientation in the [110] or [100] direction. The volume fraction of Nb in the composites determined by image analysis ranged from 8.5 to 19%. The 400 rpm stirring rate led to the highest Nb content (16 to 19016) for all current densities investigated The microhardness of the composite layers was higher than that of pure Ni coatings due to refining of Ni grains induced by incoporation of Nb particles. The adhesion of the coatings estimated qualitatively by bend test was found satisfactory. The Ni-Nb composites presented lower corrosion rate than Ni coatings in both 3% NaCl and 20% H2SO4 solutions.

Enhanced bone apposition to Brazilian microrough titanium surfaces

It has recently been reported that machined and microrough (micro) Brazilian titanium (Ti) implants have good production standards. The aim of this study was to evaluate in vivo bone formation around 2 different implant surfaces placed in dog's mandible. Thirty-two screw-typed Ti implants were used in this study. Mandibular premolars were extracted in 8 dogs and, after 12 weeks, 2 machined (Neodent Titamax, Brazil) and 2 micro implants (Neodent Titamax Porous, Brazil) were placed in each animal. Biopsies were taken at 3 and 8 weeks post-implantation and stained with Stevenel's blue and Alizarin red for histomorphometric measurements of bone-to-implant contact (BIC), bone area between threads (BABT) and bone area within the mirror area (BAMA). Data were analyzed statistically by two-way ANOVA (α=0.05). While at 3 weeks micro implants exhibited significantly more BIC than machined ones (55 ± 12.5% and 35.6 ± 15%, p<0.05), no significant difference in such parameter was detected at 8 weeks (51.2 ± 21% and 48.6 ± 18.1%, p>0.05). There were no significant differences in BABT and BAMA between the implants. Micro surfaces promoted higher contact osteogenesis. These data indicate that this commercial micro Ti implant surface enhances contact osteogenesis at an early post-implantation period when compared to the machined one.

Effect of phosphate-bonded investments on titanium reaction layer and crown fit

This study analyzed the reaction layer and measured the marginal crown fit of cast titanium applied to different phosphate-bonded investments, prepared under the following conditions (liquid concentration/casting temperature): Rema Exakt (RE) - 100%/237°C, 75%/287°C, Castorit Super C (CS)-100%/70°C, 75%/141°C and Rematitan Plus (RP)- 100%/430°C (special to titanium cast, as the control group). The reaction layer was studied using the Vickers hardness test, and analyzed by two way ANOVA and Tukey's HSD tests (α = 0.05). Digital photographs were taken of the crowns seated on the die, the misfit was measured using an image analysis system and One-way ANOVA, and Tukey's test was applied (α = 0.05). The hardness decreased from the surface (601.17 VHN) to 150 μm (204.03 VHN). The group CS 75%/141°C presented higher hardness than the other groups, revealing higher surface contamination, but there were no differences among the groups at measurements deeper than 150 μm. The castings made with CS - 100%/70°C presented the lowest levels of marginal misfit, followed by RE -100%/237°C. The conventional investments CS (100%) and RE (100%) showed better marginal fit than RP, but the CS (75%) had higher surface contamination.

Effect of laser welding on the titanium composite tensile bond strength

The aim of this study was to analyze the shear bond strength between commercially pure titanium, with and without laser welding, after airbone-particle abrasion (Al2O3) and 2 indirect composites. Sixty-four specimens were cast and divided into 2 groups with and without laser welding. Each group was divided in 4 subgroups, related to Al2O3 grain size: A - 250 µm; B - 180 µm; C- 110 µm; and D - 50 µm. Composite rings were formed around the rods and light polymerized using UniXS unit. Specimens were invested and their shear bond strength at failure was measured with a universal testing machine at a crosshead speed of 2.0 mm/min. Statistical analysis was carried out with ANOVA and Tukey's test (α=0.05). The highest bond strength means were recorded in 250 µm group without laser welding. The lowest shear bond strength means were recorded in 50 µm group with laser welding. Statistically significant differences (p<0.05) were found between all groups. In conclusion, airborne particle abrasion yielded significantly lower bond strength as the Al2O3 particle size decreased. Shear bond strength decreased in the laser welded specimens.

Effect of fluoride-containing solutions on the surface of cast commercially pure titanium

This study evaluated the effects of fluoride-containing solutions on the surface of commercially pure titanium (CP Ti) obtained by casting. CP Ti specimens were fabricated and randomly assigned to 5 groups (n=10): group 1: stored in distilled water at 37 ± 1ºC; group 2: stored in distilled water at 37 ± 1ºC and daily immersed in 0.05% NaF for 3 min; group 3: stored in distilled water at 37 ± 1ºC and daily immersed in 0.2% NaF for 3 min; group 4: stored in distilled water at 37 ± 1ºC; and immersed in 0.05% NaF every 15 days for 3 min; and group 5: stored in distilled water at 37 ± 1ºC and immersed in 0.2% NaF every 15 days for 3 min. Surface roughness was measured with a profilometer immediately after metallographic polishing of the specimens (T0) and at 15-day intervals until completing 60 days of experiment (T15, T30, T45, T60). Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). There was no statistically significant difference (p>0.05) in surface roughness among the solutions. In conclusion, fluoride-containing solutions (pH 7.0) used as mouthwashes do not damage the surface of cast CP Ti and can be used by patients with titanium-based restorations.

Retention force of T-bar clasps for titanium and cobalt-chromium removable partial dentures

The objective of this study was to evaluate the retention force of T-bar clasps made from commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) alloy by the insertion/removal test simulating 5 years use. Thirty-six frameworks were cast from CP Ti (n=18) and Co-Cr alloy (n=18) with identical prefabricated patterns on refractory casts from a distal extension mandibular hemi-arch segment. The castings were made on a vacuum-pressure machine, under vacuum and argon atmosphere. Each group was subdivided in three, corresponding to 0.25 mm, 0.50 mm and 0.75 mm undercuts, respectively. No polishing procedures were performed to ensure uniformity. The specimens were subjected to an insertion/removal test and data was analyzed statistically to compare CP Ti and Co-Cr alloy in the same undercut (Student's t-test for independent samples) and each material in different undercuts (one-way ANOVA) (p=0.05). Comparisons between materials revealed significant differences (p=0.017) only for the 0.50-mm undercut. No significant differences (p>0.05) were found when comparing the same material for the undercuts. It may be concluded that for different undercuts, both Co-Cr alloy and CP Ti had no significant differences for T-bar clasps; CP Ti showed the lowest retention force values when compared to Co-Cr alloy in each undercut, but with significant difference only for the 0.50-mm undercut; and both materials maintained the retentive capacity during the simulation test.