Luminescence and defect centres in Tb(3+) doped LaMgAl(11)O(19) phosphors

Terbium (Tb) doped LaMgAl(11)O(19) phosphors have been prepared by the combustion of corresponding metal nitrates (oxidizer) and urea (fuel) at furnace temperature as low as 500 C Combustion synthesized powder phosphor was characterized by X-ray diffraction and field emission scanning electron microscopy techniques LaMgAl(11)O(19) doped with trivalent terbium ions emit weakly in blue and orange light region and strongly in green light region when excited by the ultraviolet light of 261 nm Electron Spin Resonance (ESR) studies were carried out to study the defect centres Induced in the phosphor by gamma irradiation and also to identify the defect centres responsible for the thermally stimulated luminescence (TSL) process Room temperature ESR spectrum of irradiated phosphor appears to be a superposition of at least two defect centres One of the centres (centre I) with principal g-values g(parallel to) = 2 0417 and g(perpendicular to) = 2 0041 is identified as O(2)(-) ion while centre II with an axially symmetric g-tensor with principal values g(parallel to) = 19698 and g(perpendicular to) = 1 9653 is assigned to an F(+) centre (singly ionized oxygen vacancy) An additional defect centre is observed during thermal annealing experiments and this centre (assigned to F(+) centre) seems to originate from an F centre (oxygen vacancy with two electrons) The F centre and also the F+ centre appear to correlate with the observed high temperature TSL peak in LaMgAl(11)O(19) Tb phosphor (C) 2010 Elsevier Masson SAS All rights reserved

Persistent luminescence of Eu(2+) and Dy(3+) doped barium aluminate (BaAl(2)O(4):Eu(2+),Dy(3+)) materials

Polycrystalline Eu(2+) and Dy(3+) doped barium aluminate materials, BaAl(2)O(4):Eu(2+),Dy(3+), were prepared with solid state reactions at temperatures between 700 and 1500 degrees C. The influence of the thermal treatments on the stability, homogeneity and structure as well as to the UV-excited and persistent luminescence of the materials was investigated by X-ray powder diffraction, SEM imaging and infrared spectroscopies as well as by steady state luminescence spectroscopy and persistent luminescence decay curves, respectively. The IR spectra of the materials prepared at 250, 700, and 1500 degrees C follow the formation of BaAl(2)O(4) composition whereas the X-ray powder diffraction of compounds revealed how the hexagonal structure was obtained. The morphology of the materials at high temperatures indicated important aggregation due to sintering. The luminescence decay of the quite narrow Eu(2+) band at ca. 500 nm shows the presence of persistent luminescence after UV irradiation. The dopant (Eu(2+)) and co-clopant (Dy(3+)) concentrations affect the crystallinity and luminescence properties of the materials. (C) 2009 Elsevier B.V. All rights reserved.

Effects of a novel calcium aluminate cement on the early events of the progression of osteogenic cell cultures

The present study evaluated the progression of osteogenic cell cultures exposed to a novel calcium aluminate cement (CAC+) in comparison with the gold standard mineral trioxide aggregate (MTA). Cells were enzimatically isolated from newborn rat calvarial bone, plated on glass coverslips containing either CAC+ or a control MTA samples in the center, and grown under standard osteogenic conditions. Over the 10-day culture period, roundening of sample edges was clearly noticed only for MTA group. Although both cements supported osteogenic cell adhesion, spreading, and proliferation, CAC+-exposed cultures showed significantly higher values in terms of total cell number at days 3 and 7, and total protein content and alkaline phosphatase activity at day 10. The present in vitro results indicate that the exposure to CAC+ supports a higher differentiation of osteogenic cells compared with the ones exposed to MTA. Further experimental studies should consider CAC+ as a potential alternative to MTA when the repair of mineralized tissues is one of the desired outcomes in endodontic therapy.

Cerium-based phosphors: blue luminescent properties for applications in optical displays

In this paper, we describe the blue photoluminescence (PL) observed in the multi-component oxosalt phosphor GdVO(4)center dot Ce(3+). Different doping concentrations (0.25-1 mol%) and heat treatment (900-1100 degrees C) were used to evaluate which conditions would lead to the most suitable blue phosphor for optimal display performance. The cerium doping concentration influences the profile of the emission spectrum (broad peak at 412 nm under UV excitation at 330 nm), as reflected on the values of chromaticity coordinates. On the basis of luminescent properties, we can conclude that, among the phosphors prepared in this work the most adequate for a blue display is the one obtained via the combustion method using glycine as fuel, a 0.50 mol% cerium doping concentration, and heat treatment at 1000 degrees C.

Hydroalumination of Thioacetylenes: A Versatile Generation and Reactions of -Aluminate Sulfides Intermediates

Hydroalumination of thioacetylenes using DIBAL-H and lithium di-(isobutyl)-n-(butyl)-aluminate hydride (Zweifel`s reagent), followed by addition of water, furnished exclusively the (Z)- and (E)-vinyl sulfides, respectively. The regio- and stereochemistry of the intermediates generated, (Z)- and (E)-phenylthio vinyl alanates, were determined by capture with iodine, which afforded the corresponding (E)- and (Z)-1-iodo-1-phenylthio-2-organoyl ethenes. Reactions of the (E)-iodo(thio)ketene acetals with n-BuLi followed by addition of hexanal afforded the (Z)-phenylthio allylic alcohol, while the (Z)-iodo(thio)ketene acetals under similar reactions conditions gave the (E)-phenylthio allylic alcohol exclusively.

Red, green, and blue lanthanum phosphate phosphors obtained via surfactant-control led hydrothermal synthesis

A new solution route for the obtainment of highly pure luminescent rare-earth orthophosphates in hydrothermal conditions was developed. By starting from soluble precursors (lanthanide tripolyphosphato complexes. i.e. with P(3)O(10)(5) as a complexing agent and as in orthophosphate source) and by applying surfactants in a water/toluene medium, the precipitations are confined to reverse micelle structures, thus yielding nanosized and homogeneous orthophosphates The method was employed to obtain lanthanide-activated lanthanum phosphates, which can be applied as red (LaPO(4):Eu(3+)), green (LaPO(4):Ce(3+), Tb(3+)) and blue (LaPO(4):Tm(3+)) phosphors The produced materials were analyzed by powder X-ray diffractometry, scanning electron microscopy, infrared spectroscopy and luminescence spectroscopy (emission, excitation, lifetimes and chromaticity coordinates) (C) 2009 Elsevier B V All rights reserved

Radiopacity Evaluation of Calcium Aluminate Cement Containing Different Radiopacifying Agents

Introduction: The aim of this study was to evaluate the radiopacity of calcium aluminate cement (Endo Binder) with 3 different radiopacifiers (bismuth oxide, zinc oxide, or zirconium oxide) in comparison with gray mineral trioxide aggregate (GMTA), white MTA, and dental structures (enamel and dentin). Methods: Eighteen test specimens of each cement with thicknesses of 0.5, 1.0, 1.5, 2.0, 2.5, and 3.0 mm (n = 3) were made by using a stainless steel matrix and were adapted to a standardizing device (8 x 7 cm) with a graduated aluminum stepwedge varying from 2.0-16.0 mm in thickness. To compare the radiopacity of the cements with that of dental structures, slices of first molars with a thickness increasing from 0.5-3.0 mm were obtained and placed on the standardizing device. One occlusal radiograph for each tested cement was taken, with exposure time of 0.1 seconds and focus-film distance of 20 cm. Films were processed in an automatic device, and the mean radiopacity values were obtained by using a photodensitometer. Results: Mean values showed that the thicker the specimen was, the greater was its radiopacity. Only EndoBinder + bismuth oxide (EBBO) and GMTA demonstrated radiopacity values greater than 3.0 mm of the aluminum scale for all thicknesses. When zinc oxide was used as radiopacifier agent, EndoBinder only reached the desired radiopacity with a thickness of 2.0 mm, and with zirconium oxide it was 2.5 mm. Conclusions: Bismuth oxide was the most efficient radiopacifier for EndoBinder, providing adequate radiopacity in all studied thicknesses, as recommended by ISO 6876, being similar to GMTA. (J Endod 2011;37: 67-71)

Characterization, photoluminescence, thermally stimulated luminescence and electron spin resonance studies of Eu(3+) doped LaAlO(3) phosphor

Europium-doped lanthanum aluminate (LaAlO(3)) powder was prepared by using a combustion method. The crystallization, surface morphology, specific surface area and luminescence properties of the samples have been investigated. Photoluminescence studies of Eu doped LaAlO(3) showed orange-reddish emission due to Eu(3+) ions. LaAlO(3):Eu(3+) exhibits one thermally stimulated luminescence (TSL) peak around 400 degrees C. Room temperature electron spin resonance spectrum of irradiated phosphor appears to be a superposition of two centres. One of them (centre I) with principal g-value 2.017 is identified as an O(-) centre while centre II with an isotropic g-value 2.011 is assigned to an F(+) centre (singly ionized oxygen vacancy). An additional defect centre observed during thermal annealing around 300 degrees C grows with the annealing temperature. This centre (assigned to F(+) centre) originates from an F-centre (oxygen vacancy with two electrons) and the F-centre along with the associated F(+) centre appear to correlate with the observed TSL peak in LaAlO(3):Eu(3+) phosphor. The activation energy for this peak has been determined to be 1.54 eV from TSL data. (C) 2010 Elsevier Masson SAS. All rights reserved.

Infrared emission and defect centres in Er and Yb codoped Y(3)Al(5)O(12) phosphors

YAG phosphor powders doped/codoped with Er(3+)/(Er(3+) + Yb(3+)) have been synthesised by using the solution combustion method. The effect of direct pumping into the (4)I(11/2) level under 980 nm excitation of doped/codoped Er(3+)/Yb(3+)-Er(3+) in Y(3)Al(5)O(12) (YAG) phosphor responsible for an infrared (IR) emission peaking at similar to 1.53 mu m corresponding to the (4)I(13/2)->(4)I(15/2) transition has been studied. YAG exhibits three thermally-stimulated luminescence (TSL) peaks at around 140A degrees C, 210A degrees C and 445A degrees C. Electron spin resonance (ESR) studies were carried out to identify the centres responsible for the TSL peaks. The room temperature ESR spectrum of irradiated phosphor appears to be a superposition of two distinct centres. One of the centres (centre I) with principal g-value 2.0176 is identified as O(-) ion, while centre II with an isotropic g-factor 2.0020 is assigned to an F(+) centre (singly ionised oxygen vacancy). An additional defect centre is observed during thermal-annealing experiments and this centre (assigned to F(+) centre) seems to originate from an F-centre (oxygen vacancy with two electrons) and these two centres appear to correlate with the observed high-temperature TSL peak in YAG phosphor.

Luminescence and defect centres in MgSrAl(10)O(17):Sm(3+) phosphor

An efficient reddish orange emission MgSrAl(10)O(17):Sm(3+) phosphor was prepared by the combustion method. The phosphor has been characterized by X-ray diffraction, scanning electron microscopy, thermogravimetric analysis measurements. Photoluminescence spectrum revealed that samarium ions are present in trivalent oxidation states. The phosphor exhibits two thermally stimulated luminescence (TSL) peaks at 210 degrees C and 450 degrees C. Electron spin resonance studies were carried out to identify the defect centres responsible for the TSL process in MgSrAl(10)O(17):Sm(3+) phosphor. Three defect centres have been identified in irradiated phosphor and these centres are tentatively assigned to an O(-) ion and F(+) centres. O(-) ion (hole centre) correlates with the 210 degrees C TSL peak while one of the F+ centres (electron centre) appears to relate to the 450 degrees C TSL peak. (C) 2010 Elsevier B.V. All rights reserved.

Luminescent nanoparticles of MgAl(2)O(4):Eu, Dy prepared by citrate sol-gel method

MgAl(2)O(4):Eu, Dy nanoparticles were prepared by citrate sol-gel method and thermally treated at 600, 700, 800 and 900 degrees C. The trivalent europium ion is partially reduced to the divalent state at 700 and 800 degrees C. Infrared spectra of the phosphors showed bands around 700 and 520 cm(-1) corresponding to the AlO(6) groups. X-ray diffraction patterns present sharp reflections of samples heated from 700 to 900 degrees C indicating the MgAl(2)O(4) spinel phase. Grain size in the range 20-30 nm were observed by measurement of transmission electron microscopy (TEM). The emission spectra of the phosphors show a broadened band at 480 nm assigned to the 4f(G)5d -> 4f(7) ((8)S(7/2)) transition of Eu(2+) ion overlapped to the (4)F(9/2) -> (6)H(15/2) transition of the Dy(3+) ion. Besides, the (4)F(9/2) -> (6)H(13/2) transition (579 nm) of Dy(3+) ion is overlapped with the (5)D(0) -> (7)F(0) (578 nm) and (5)D(0) -> (7)F(1) (595 nm) transitions from the Eu(3+) ion. Excitation spectra of the sample heated at 900 degrees C monitoring the excitation at 615 nm of (5)D(0) -> (7)F(2) transition of Eu(3+) ion exhibit a broad band assigned to the O -> Eu(3+) ligand-to-metal charge-transfer states (LMCT) around 280 nm. The samples present green persistent luminescence after exposure to UV radiation. The chromaticity coordinates were obtained from the luminescence emission spectrum. (C) 2008 Elsevier B.V. All rights reserved.

Ethanol steam reforming for production of hydrogen on magnesium aluminate-supported cobalt catalysts promoted by noble metals

The performance of noble metal (Pt, Ru, Ir)-promoted Co/MgAl(2)O(4) catalysts for the steam reforming of ethanol was investigated. The catalysts were characterized by energy-dispersive X-ray spectroscopy, Xray diffraction, UV-vis diffuse reflectance spectroscopy, temperature-programmed reduction, temperature-programmed oxidation and X-ray absorption near edge structure (XANES). The results showed that the formation of inactive cobalt aluminate was suppressed by the presence of a MgAl(2)O(4) spinel phase. The effects of the noble metals included a marked lowering of the reduction temperatures of the cobalt surface species interacting with the support. It was seen that the addition of noble metal stabilized the Co sites in the reduced state throughout the reaction. Catalytic performance was enhanced in the promoted catalysts, particularly CoRu/MgAl(2)O(4), which showed the highest selectivity for H(2) production. (C) 2009 Elsevier B.V. All rights reserved.

Structural models for yttrium aluminium borate laser glasses: NMR and EPR studies of the system (Y(2)O(3))(0.2)-(Al(2)O(3))(x)-(B(2)O(3))(0.8-x)

The structure of laser glasses in the system (Y(2)O(3))(0.2){(Al(2)O(3))(x))(B(2)O(3))(0.8-x)} (0.15 <= x <= 0.40) has been investigated by means of (11)B, (27)Al, and (89)Y solid state NMR as well as electron spin echo envelope modulation (ESEEM) of Yb-doped samples. The latter technique has been applied for the first time to an aluminoborate glass system. (11)B magic-angle spinning (MAS)-NMR spectra reveal that, while the majority of the boron atoms are three-coordinated over the entire composition region, the fraction of three-coordinated boron atoms increases significantly with increasing x. Charge balance considerations as well as (11)B NMR lineshape analyses suggest that the dominant borate species are predominantly singly charged metaborate (BO(2/2)O(-)), doubly charged pyroborate (BO(1/2)(O(-))(2)), and (at x = 0.40) triply charged orthoborate groups. As x increases along this series, the average anionic charge per trigonal borate group increases from 1.38 to 2.91. (27)Al MAS-NMR spectra show that the alumina species are present in the coordination states four, five and six, and the fraction of four-coordinated Al increases markedly with increasing x. All of the Al coordination states are in intimate contact with both the three-and the four-coordinate boron species and vice versa, as indicated by (11)B/(27)Al rotational echo double resonance (REDOR) data. These results are consistent with the formation of a homogeneous, non-segregated glass structure. (89)Y solid state NMR spectra show a significant chemical shift trend, reflecting that the second coordination sphere becomes increasingly ""aluminate-like'' with increasing x. This conclusion is supported by electron spin echo envelope modulation (ESEEM) data of Yb-doped glasses, which indicate that both borate and aluminate species participate in the medium range structure of the rare-earth ions, consistent with a random spatial distribution of the glass components.

Intermolecular energy transfer and photostability of luminescence-tuneable multicolour PMMA films doped with lanthanide-beta-diketonate complexes

It is reported in this work the preparation, characterisation and photoluminescence study of poly(methylmethacrylate) (PMMA) thin films co-doped with [Eu(tta)(3)(H(2)O)(2)] and [Tb(acac)(3)(H(2)O)(3)] complexes. Both the composition and excitation wavelength may be tailored to fine-tune the emission properties of these Ln(3+)-beta-diketonate doped polymer films, exhibiting green and red primary colours, as well as intermediate colours. In addition to the ligand-Ln(3+) intramolecular energy transfer, it is observed an unprecedented intermolecular energy transfer process from the (5)D(4) emitting level of the Tb(3+) ion to the excited triplet state T(1) of the tta ligand coordinated to the Eu(3+) ion. The PMMA polymer matrix acts as a co-sensitizer and enhances the overall luminescence intensity of the polymer films. Furthermore, it provides considerable UV protection for the luminescent species and improves the photostability of the doped system.