Substrate orientation effect on potential fluctuations in multiquantum wells of GaAs/AlGaAs

The photoluminescence (PL) technique as a function of temperature and excitation intensity was used to study the optical properties of multiquantum wells (MQWs) of GaAs/Al(x)Ga(1-x)As grown by molecular beam epitaxy on GaAs substrates oriented in the [100], [311]A, and [311]B directions. The asymmetry presented by the PL spectra of the MQWs with an apparent exponential tail in the lower-energy side and the unusual behavior of the PL peak energy versus temperature (blueshift) at low temperatures are explained by the exciton localization in the confinement potential fluctuations of the heterostructures. The PL peak energy dependence with temperature was fitted by the expression proposed by Passler [Phys. Status Solidi B 200, 155 (1997)] by subtracting the term sigma(2)(E)/k(B)T, which considers the presence of potential fluctuations. It can be verified from the PL line shape, the full width at half maximum of PL spectra, the sigma(E) values obtained from the adjustment of experimental points, and the blueshift maximum values that the samples grown in the [311]A/B directions have higher potential fluctuation amplitude than the sample grown in the [100] direction. This indicates a higher degree of the superficial corrugations for the MQWs grown in the [311] direction. (C) 2008 American Institute of Physics.

The influence of crystallographic orientation on the generation of multiple structural phases generation in Silicon by cyclic microindentation

A Raman scattering study on multiple phase generation in silicon submitted to successive Vickers microindentation cycles, in different crystallographic orientations, was performed. The microindentations were perfon-ned in a virgin single crystal (100)-oriented surface, in the [001] and [011] directions. The results indicated that the formation of multiple phases by cyclic microindentation may depend on the crystallographic direction and number of successive cycles: the onset of several different structural phases was detected after the third cycle for the [001] direction and only after 15 cycles for the [011] direction, indicating that there is a crystallographic orientation dependence for multiple phase generation. (C) 2007 Elsevier B.V. All rights reserved.

Living Our Lives on the Edge: Power, Space and Sexual Orientation in Cape Town Townships, South Africa

Much of social science literature about South African cities fails to represent its complex spectrum of sexual practices and associated identities. The unintended effects of such representations are that a compulsory heterosexuality is naturalised in, and reiterative with, dominant constructions of blackness in townships. In this paper, we argue that the assertion of discreet lesbian and gay identities in black townships of a South African city such as Cape Town is influenced by the historical racial and socio-economic divides that have marked urban landscape. In their efforts to recoup a positive sense of gendered personhood, residents have constructed a moral economy anchored in reproductive heterosexuality. We draw upon ethnographic data to show how sexual minorities live their lives vicariously in spaces they have prised open within the extant sex/gender binary. They are able to assert the identities of moffie and man-vrou (mannish woman) without threatening the dominant ideology of heterosexuality.

Discovery of VVV CL001 A low-mass globular cluster next to UKS 1 in the direction of the Galactic bulge

Context. It is not known how many globular clusters may remain undetected towards the Galactic bulge. Aims. One of the aims of the VISTA Variables in the Via Lactea (VVV) Survey is to accurately measure the physical parameters of the known globular clusters in the inner regions of the Milky Way and search for new ones, hidden in regions of large extinction. Methods. From deep near-infrared images, we derive deep JHK(S)-band photometry of a region surrounding the known globular cluster UKS 1 and reveal a new low-mass globular cluster candidate that we name VVV CL001. Results. We use the horizontal-branch red clump to measure E(B-V) similar to 2.2 mag, (m - M)(0) = 16.01 mag, and D = 15.9 kpc for the globular cluster UKS 1. On the basis of near-infrared colour-magnitude diagrams, we also find that VVV CL001 has E(B-V) similar to 2.0, and that it is at least as metal-poor as UKS 1, although its distance remains uncertain. Conclusions. Our finding confirms the previous projection that the central region of the Milky Way harbours more globular clusters. VVV CL001 and UKS 1 are good candidates for a physical cluster binary, but follow-up observations are needed to decide if they are located at the same distance and have similar radial velocities.

Near infrared polarimetry of a sample of YSOs

Aims. Our goal is to study the physical properties of the circumstellar environment of young stellar objetcs (YSOs). In particular, the determination of the scattering mechanism can help us to constrain the optical depth of the disk and/or envelope in the near infrared. Methods. We used the IAGPOL imaging polarimeter along with the CamIV infrared camera at the LNA observatory to obtain near infrared polarimetry measurements in the H band of a sample of optically visible YSOs, namely, eleven T Tauri stars and eight Herbig Ae/Be stars. An independent determination of the disk (or jet) orientation was obtained for twelve objects from the literature. The circumstellar optical depth could then be estimated by comparing the integrated polarization position angle (PA) with the direction of the major axis of the disk projected onto the plane of the sky. Optically thin disks have, in general, a polarization PA that is perpendicular to the disk plane. In contrast, optically thick disks have polarization PAs parallel to the disks. Results. Among the T Tauri stars, three are consistent with having optically thin disks (AS 353A, RY Tau and UY Aur) and five with optically thick disks (V536 Aql, DG Tau, DO Tau, HL Tau and LkH alpha 358). Among the Herbig Ae/Be stars, two stars exhibit evidence of optically thin disks (Hen 3-1191 and VV Ser) and two of optically thick disks (PDS 453 and MWC 297). Our results seem consistent with optically thick disks at near infrared bands, which are more likely to be associated with younger YSOs. Marginal evidence of polarization reversal is found in RY Tau, RY Ori, WW Vul, and UY Aur. In the first three cases, this feature can be associated with the UXOR phenomenon. Correlations with the IRAS colors and the spectral index yielded evidence of an evolutionary segregation in which the disks tend to be optically thin when they are older.

Angular dependence of the thermal-lens effect on LiSrAlF(6) and LiSrGaF(6) single crystals

We apply thermal-lens (TL) spectrometry to measure the angular dependence of the TL effect on colquiriite single crystals. The experiments were performed with LiSrAlF(6) and LiSrGaF(6) using a two-beam mode-mismatched configuration. The results show that it is possible to minimize the TL effect by selecting the appropriate crystal orientation. Our data also show that the anisotropy of the linear thermal expansion coefficient drives the amplitude of the TL effect, including the inversion from focusing to defocusing as the crystal orientation angle tends to the c-axis direction. The results may be useful for those working to develop a high-power laser using LiSrAlF(6)(:Cr) and LiSrGaF(6)(:Cr) single crystals, allowing for optimization of the designed laser cavity. (C) 2008 Optical Society of America.

Regional scale analysis of landform configuration with base-level (isobase) maps

Base-level maps (or ""isobase maps"", as originally defined by Filosofov, 1960), express a relationship between valley order and topography. The base-level map can be seen as a ""simplified"" version of the original topographic surface, from which the ""noise"" of the low-order stream erosion was removed. This method is able to identify areas with possible tectonic influence even within lithologically uniform domains. Base-level maps have been recently applied in semi-detail scale (e.g., 1:50 000 or larger) morphotectonic analysis. In this paper, we present an evaluation of the method's applicability in regional-scale analysis (e.g., 1:250 000 or smaller). A test area was selected in northern Brazil, at the lower course of the Araguaia and Tocantins rivers. The drainage network extracted from SRTM30_PLUS DEMs with spatial resolution of approximately 900 m was visually compared with available topographic maps and considered to be compatible with a 1:1,000 000 scale. Regarding the interpretation of regional-scale morphostructures, the map constructed with 2nd and 3rd-order valleys was considered to present the best results. Some of the interpreted base-level anomalies correspond to important shear zones and geological contacts present in the 1:5 000 000 Geological Map of South America. Others have no correspondence with mapped Precambrian structures and are considered to represent younger, probably neotectonic, features. A strong E-W orientation of the base-level lines over the inflexion of the Araguaia and Tocantins rivers, suggest a major drainage capture. A N-S topographic swath profile over the Tocantins and Araguaia rivers reveals a topographic pattern which, allied with seismic data showing a roughly N-S direction of extension in the area, lead us to interpret this lineament as an E-W, southward-dipping normal fault. There is also a good visual correspondence between the base-level lineaments and geophysical anomalies. A NW-SE lineament in the southeast of the study area partially corresponds to the northern border of the Mosquito lava field, of Jurassic age, and a NW-SE lineament traced in the northeastern sector of the study area can be interpreted as the Picos-Santa Ines lineament, identifiable in geophysical maps but with little expression in hypsometric or topographic maps.

Woodgrain defect on tinned steel Flandres foil

Tin electrocoated steel strip, also referred to as Flandres foil, is largely used for manufacturing food containers. Tinplates must have good corrosion resistance, workability, weldability, as well as a bright appearance. The woodgrain defect, a not yet fully understood defect that occurs on tinplates and accounts for their high scrap rate, consists of alternate bands of bright/dull reflectivity and resembles longitudinally cut wood. Observations of the woodgrain defect by scanning electron microscopy showed that the molten tin spreads irregularly during both the melting and solidification stages. X-ray diffraction analyses showed that the metallic tin tended to crystallize in the (200) direction for coupons with and without the woodgrain defect. Nevertheless, the preferential orientation degree decreased for coupons with the woodgrain defect. The rocking curves, also known as omega-scan, showed that the tin grains were uniformly aligned parallel to the strip surface for coupons with no defects, whereas for tinplates with woodgrain, the tin grains were not uniformly oriented, probably due to the misalignment of the grains in relation to the surface. (C) 2011 Elsevier Inc. All rights reserved.

Characterization of nickel-niobium composite electrocoatings

The electrodeposition of nickel based composites is been performed in order to improve properties of nickel layers, such as hardness, wear resistance, lubrication, corrosion resistance and catalytic activity. In the present work Nb powders (20 mu m average size) and Ni were codeposited on 1020 carbon steel by galvanostatic electrolysis of Watts bath, using 10, 20 and 40 mA/cm(2) cathodic current density and 240, 400 and 550 rpm electrolyte stirring rate. The morphology and texture of the coatings, Nb incorporated volume fraction, microhardness, adhesion to the substrate and corrosion behavior were evaluated. The Ni-Nb composite layers presented a rough morphology with randomly oriented Ni grains, whereas pure Ni coatings were smooth and showed highly preferred orientation in the [110] or [100] direction. The volume fraction of Nb in the composites determined by image analysis ranged from 8.5 to 19%. The 400 rpm stirring rate led to the highest Nb content (16 to 19016) for all current densities investigated The microhardness of the composite layers was higher than that of pure Ni coatings due to refining of Ni grains induced by incoporation of Nb particles. The adhesion of the coatings estimated qualitatively by bend test was found satisfactory. The Ni-Nb composites presented lower corrosion rate than Ni coatings in both 3% NaCl and 20% H2SO4 solutions.

Composition and orientation effects on the final recrystallization texture of coarse-grained Nb-containing AISI 430 ferritic stainless steels

Composition and orientation effects on the final recrystallization texture of three coarse-grained Nb-containing AISI 430 ferritic stainless steels (FSSs) were investigated. Hot-bands of steels containing distinct amounts of niobium, carbon and nitrogen were annealed at 1250 degrees C for 2h to promote grain growth. In particular, the amounts of Nb in solid solution vary from one grade to another. For purposes of comparison, the texture evolution of a hot-band sheet annealed at 1030 degrees C for 1 min (finer grain structure) was also investigated. Subsequently, the four sheets were cold rolled up to 80% reduction and then annealed at 800 degrees C for 15 min. Texture was determined using X-ray diffraction and electron backscatter diffraction (EBSD). Noticeable differences regarding the final recrystallization texture and microstructure were observed in the four investigated grades. Results suggest that distinct nucleation mechanisms take place within these large grains leading to the development of different final recrystallization textures. (c) 2011 Elsevier B.V. All rights reserved.

Intragranular formation of austenite during delta ferrite decomposition in a duplex stainless steel

A Fe-22.5%Cr-4.53%Ni-3.0%Mo duplex stainless steel was solution treated at 1,325 A degrees C for 1 h, quenched in water and isothermally treated at 900 A degrees C for 5,000 s. The crystallography of austenite was studied using EBSD technique. Intragranular austenite particles formed from delta ferrite are shown to nucleate on inclusions, and to be subdivided in twin-related sub-particles. Intragranular austenite appears to have planar-only orientation relationships with the ferrite matrix, close to Kurdjumov-Sachs and Nishyiama-Wassermann, but not related to a conjugate direction. Samples treated at 900 A degrees C underwent sparse formation of sigma phase and pronounced growth of elongated austenite particles, very similar to acicular ferrite.

Hygroexpansivity profiles on a commercial paper machine

Paper products show dimensional changes when subjected to moisture content modification. Hygroexpansivity was investigated in a commercial paper machine operating at 1256 m/min by a set of measurements on 75 g/m(2) reprographic bleached eucalyptus pulp paper samples. The present work shows hygroexpansivity development in different sections of the paper machine along the manufacturing direction. The measurement results demonstrate the effects of papermaking process operations on paper hygroexpansivity and lead to the confirmation of fiber orientation degree, drying restraint and shrinkage and paper tension as significant influencing factors. Structural, strength and elastic properties of paper were also measured as a function of machine direction position and presented for discussion purposes.

Influence of the sidewall crystal orientation, HfSiO nitridation and TiN metal gate thickness on n-MuGFETs under analog operation

This work characterizes the analog performance of SOI n-MuGFETs with HfSiO gate dielectric and TiN metal gate with respect to the influence of the high-k post-nitridation. TiN thickness and device rotation. A thinner TiN metal gate is found favorable for improved analog characteristics showing an increase in intrinsic voltage gain. The devices where the high-k material is subjected to a nitridation step indicated a degradation of the Early voltage (V(EA)) values which resulted in a lower voltage gain. The 45 degrees rotated devices have a smaller V(EA) than the standard ones when a HfSiO dielectric is used. However, the higher transconductance of these devices, due to the increased mobility in the (1 0 0) sidewall orientation, compensates this V(EA) degradation of the voltage gain, keeping it nearly equal to the voltage gain values of the standard devices. (C) 2011 Elsevier Ltd. All rights reserved.

Personal Values as Basis for Strategic Segmentation: a study with Professionals from Sao Paulo

An important segmentation basis used by firms is related to consumers` personal values which are investigated in this study. It was used a descriptive research with the survey method of data collection in a sample of executives from Sao Paulo who are considered to be potential buyers of high value and innovative goods. An exploratory factor analysis was employed in order to reduce the values scale used and a cluster analysis was performed to identify the groups of executives according to the importance attached to different person values. Concluding, it was observed that there was a similarity among the three personal values dimensions, named as Civility (concerns about having a good conduct before society according to social rules of interaction), Self-Direction (intellectual aspects and practical orientation in their conducts) and Conformity (restriction of actions, inclinations and impulses, that are likely to harm others and would violate expectations) and the ones reported in the theory Rokeach`s theory about instrumental personal values. Furthermore, three groups of executives were identified (good conduct group, low restriction group and high restriction group). The differences observed in the importance of personal values here presented by the dimensions called Civility, Self-Direction and Conformity can lead to different buying behaviors and product preferences. From the results found in this study the companies could adapt their current and new products offers, as well as their communication in order to better serve these segments of executives from Sao Paulo.

Nest site selection by a neotropical swarm-founding wasp: seasonal alternation of nest orientation

Nest orientation in social insects has been intensively studied in warmer and cooler climates, particularly in the northern hemisphere. Previous studies have consistently shown that species subjected to these climatic conditions prefer to select mostly southern locations where the nests can gain direct sunlight. However, very little is known on nest orientation in tropical and subtropical social insects. We studied nest orientations initiated by swarms throughout a year in a Brazilian swarm-founding wasp, Polybia paulista von Ihering (Hymenoptera: Polistinae). Swarms selected various orientations as nest sites, but there was a particular trend in that swarms in the winter period (May-August) preferred to build northward-facing nests. This preference is opposite from that of social wasps observed in the northern hemisphere. Colonies of this species can potentially last for many years with continuous nesting, but nesting activities of colonies during the winter are severely limited due to cool temperature and a shortened day length. Northward-facing nests are warmer through the gain of direct solar heat during the winter period; consequently, choosing northward-facing sites may be advantageous for swarms in terms of a shortened brood development and shortened time needed to increase metabolic rates during warm-up for flight.