EXERGOECONOMIC COMPARISON OF ABSORPTION REFRIGERATION SYSTEMS INCLUDING A HIBRID ABSORPTION-EJECTO COMPRESSION CHILLER

The study of absorption refrigeration systems has had increasing importance in recent years due to the fact that the primary energy that is used in an absorption system can be heat available from a residual source or even a renewable one. Therefore, these systems not only use energy that would be rejected by the environment, but also they avoid the consumption of expensive fossil or electrical energies. The production cost of the mechanical work necessary to obtain a kW of refrigeration for mechanical compression cycle is normally higher than the cost for recovering the needed heat to obtain the same kW in an absorption cycle. Also, the use of these systems reduces impact on the environment by decreasing the emission of CO(2). We intend to show the performance of a hybrid absorption-ejecto compression chiller compared to conventional double- and single-effect water/lithium bromide systems, by means of an exergetic and exergoeconomic analysis of these configurations in order to calculate the exergy-based cost of a final product. The vapor compression refrigeration system is included in the results, as a comparisson to the performance of the absorption refrigeration systems analyzed.

Stability Testing of Spray- and Spouted Bed-Dried Extracts of Passiflora alata

The aim of this research was to perform a stability testing of spray- and spouted bed-dried extracts of Passiflora alata Dryander (Passion flower) under stress storage conditions. Spouted bed- and spray-dried extracts were characterized by determination of the average particle diameter (dP), apparent moisture content (XP), total flavonoid content (TF), and vitexin content. Smaller and more irregular particles were generated by the spouted bed system due to a higher attrition rate (surface erosion) inside the dryer. The SB dryer resulted in an end product with higher concentration of flavonoids (approximate to 10%) and lower moisture content (1.6%, dry basis) than the spray dryer, even with both dryers working at similar inlet drying air temperature and ratio between the extract feed flow rate to drying air flow rate (Ws/Wg). Samples of the spouted bed- and spray-dried extracts were stored at two different temperatures (34 and 45 degrees C) and two different relative humidities (52 and 63% RH for 34 degrees C; 52 and 60% RH for 45 degrees C) in order to perform the stability testing. The dried extracts were stored for 28 days and were analyzed every 4 days. The flavonoid vitexin served as the marker compound, which was assayed during the storage period. Results revealed shelf lives ranging from 9 to 184 days, depending on the drying process and storage conditions.

Effect of treadmill exercise on lumbar vertebrae in ovariectomized rats: anthropometrical and mechanical analyses

The purpose of this study was to examine the preventive effect of exercise on lumbar vertebrae in ovariectomized rats. Three-month-old female Wistar rats were divided into 3 groups: control group (A, n = 10); non-exercised ovariectomized group (B, n = 7) and exercised ovariectomized group (C, n = 7). The rats from group C were subjected to treadmill exercise (15 m/minute in the initial six weeks and 19 m/minute in the next six weeks, 1 hour/day, 4 days/week) for 12 weeks. At death, the fourth lumbar vertebrae were removed and an anthropometrical analysis by a paquimeter and a mechanical compression test by a universal test machine were performed. After 12 weeks, the ovariectomy decreased the superior-inferior vertebral height and the maximal braking load in group B compared to group A, while the exercise increased the vertebral mass in group C compared to both groups A and B (p < 0.01) and the stiffness compared to group B. We concluded the physical activity has an important role to prevent the osteopenia in lumbar vertebrae.

Low-Intensity Pulsed Ultrasound Accelerates Healing in Rat Calcaneus Tendon Injuries

STUDY DESIGN: Controlled laboratory study. OBJECTIVE: To evaluate the effect of low-intensity therapeutic ultrasound on the murine calcaneus tendon healing process. BACKGROUND: Therapeutic ultrasound promotes formation and maturation of scar tissue. METHODS: Calcaneus tendon tenotomy and tenorrhaphy was performed on 28 Wistar rats. After the procedure, the animals were randomly divided into 2 groups. The animals in the experimental group received a 5-minute ultrasound application, once a day, at a frequency of 1 MHz, a spatial average temporal average intensity of 0.1 W/cm(2), and a spatial average intensity of 0.52 W/cm(2) at a 16-Hz frequency pulse mode (duty cycle, 20%). Data for the injured side were normalized in relation to the data from the contralateral healthy calcaneus tendon (relative values). The animals in the control group received sham treatment. After a 28-day treatment period, the animals were sacrificed and their tendons surgically removed and subjected to mechanical stress testing. The parameters analyzed were cross-sectional area (mm(2)), ultimate load (N), tensile strength (MPa), and energy absorption (mJ). RESULTS: A significant difference between groups was found for the relative values of ultimate load and tensile strength. The mean +/- SD ultimate load of the control group was -3.5% +/- 32.2% compared to 33.3% +/- 26.8% for the experimental group (P = .005). The mean tensile strength of the control group was -47.7% +/- 19.5% compared to -28.1% +/- 24.1% for the experimental group (P = .019). No significant difference was found in cross-sectional area and energy absorption. CONCLUSION: Low-intensity pulsed ultrasound produced by a conventional therapeutic ultrasound unit can positively influence the calcaneus tendon healing process in rats. J Ort hop Sports Phys Ther 2011;41(7):526-531, Epub 2 February 2011. doi:10.2519/jospt.2011.3468

Development and mechanical testing of a short intramedullary nail for fixation of femoral rotational osteotomy in cerebral palsy patients

Background: Rotational osteotomy is frequently indicated to correct excessive femoral anteversion in cerebral palsy patients. Angled blade plate is the standard fixation device used when performed in the proximal femur, but extensile exposure is required for plate accommodation. The authors developed a short locked intramedullary nail to be applied percutaneously in the fixation of femoral rotational osteotomies in children with cerebral palsy and evaluated its mechanical properties. Methods: The study was divided into three stages. In the first part, a prototype was designed and made based on radiographic measurements of the femoral medullary canal of ten-year-old patients. In the second, synthetic femoral models based on rapid-prototyping of 3D reconstructed images of patients with cerebral palsy were obtained and were employed to adjust the nail prototype to the morphological changes observed in this disease. In the third, rotational osteotomies were simulated using synthetic femoral models stabilized by the nail and by the AO-ASIF fixed-angle blade plate. Mechanical testing was done comparing both devices in bending-compression and torsion. Results: The authors observed proper adaptation of the nail to normal and morphologically altered femoral models, and during the simulated osteotomies. Stiffness in bending-compression was significantly higher in the group fixed by the plate (388.97 +/- 57.25 N/mm) than in that fixed by the nail (268.26 +/- 38.51 N/mm) as torsional relative stiffness was significantly higher in the group fixed by the plate (1.07 +/- 0.36 Nm/degrees) than by the nail (0.35 +/- 0.13 Nm/degrees). Conclusions: Although the device presented adequate design and dimension to fit into the pediatric femur, mechanical tests indicated that the nail was less stable than the blade plate in bending-compression and torsion. This may be a beneficial property, and it can be attributed to the more flexible fixation found in intramedullary devices.

Validation of an experimental polyurethane model for biomechanical studies on implant-supported prosthesis: compression tests

OBJECTIVES: The complexity and heterogeneity of human bone, as well as ethical issues, most always hinder the performance of clinical trials. Thus, in vitro studies become an important source of information for the understanding of biomechanical events on implant-supported prostheses, although study results cannot be considered reliable unless validation studies are conducted. The purpose of this work was to validate an artificial experimental model based on its modulus of elasticity, to simulate the performance of human bone in vivo in biomechanical studies of implant-supported prostheses. MATERIAL AND METHODS: In this study, fast-curing polyurethane (F16 polyurethane, Axson) was used to build 40 specimens that were divided into five groups. The following reagent ratios (part A/part B) were used: Group A (0.5/1.0), Group B (0.8/1.0), Group C (1.0/1.0), Group D (1.2/1.0), and Group E (1.5/1.0). A universal testing machine (Kratos model K - 2000 MP) was used to measure modulus of elasticity values by compression. RESULTS: Mean modulus of elasticity values were: Group A - 389.72 MPa, Group B - 529.19 MPa, Group C - 571.11 MPa, Group D - 470.35 MPa, Group E - 437.36 MPa. CONCLUSION: The best mechanical characteristics and modulus of elasticity value comparable to that of human trabecular bone were obtained when A/B ratio was 1:1.

Evaluation of rock mechanical behaviors under uniaxial compression with reference to assessed weathering grades

A weathering classification for granitic rock materials from southeastern Brazil was framed based on core characteristics. The classification was substantiated by a detailed petrographic study. Indirect assessment of weathering grades by density, ultrasonic and Schmidt hammer index tests was performed. Rebound values due to Schmidt hammer multiple impacts at one representative point were more efficient in predicting weathering grades than averaged single impact rebound values, P-wave velocities and densities. Uniaxial compression tests revealed that a large range of uniaxial compressive strength (214-153 MPa) exists in Grade I category where weathering does not seem to have played any role. It was concluded that variability in occurrences of quartz intragranular cracks and in biotite percentage, distribution and orientation might have played a key role in accelerating or decelerating the failure processes of the Grade I specimens. Deterioration of uniaxial compressive strength and elastic modulus and increase in Poisson`s ratio with increasing weathering intensity could be attributed to alteration of minerals, disruption of rock skeleton and microcrack augmentation. A crude relation between failure modes and weathering grades also emerged.

Mechanical Testing of Indirect Composite Materials Directly Applied on Implant Abutments

Purpose: To test the strength to failure and fracture mode of three indirect composite materials directly applied onto Ti-6Al-4V implant abutments vs cemented standard porcelain-fused-to-metal (PFM) crowns. Materials and Methods: Sixty-four locking taper abutments were randomly allocated to four groups and were cleaned in ethanol in an ultrasonic bath for 5 min. After drying under ambient conditions, the abutments were grit blasted and a custom 4-cusp molar crown mold was utilized to produce identical crowns (n = 16 per group) of Tescera (Bisco), Ceramage (Shofu), and Diamond Crown (DRM) according to the manufacturer`s instructions. The porcelain-fused-to-metal crowns were fabricated by conventional means involving the construction and a wax pattern and casting of a metallic coping followed by sintering of increasing layers of porcelain. All crowns were loaded to failure by an indenter placed at one of the cusp tips at a 1 mm/min rate. Subsequently, fracture analysis was performed by means of stereomicroscopy and scanning electron microscopy. One-way ANOVA at 95% level of significance was utilized for statistical analysis. Results: The single load to failure (+/- SD) results were: Tescera (1130 +/- 239 N), Ceramage (1099 +/- 257 N), Diamond Crown (1155 +/- 284 N), and PFM (1081 +/- 243 N). Stereomicroscopy analysis showed two distinct failure modes, where the loaded cusp failed either with or without abutment/metallic coping exposure. SEM analysis of the fractures showed multiple crack propagation towards the cervical region of the crown below a region of plastic deformation at the indenter contact region. Conclusion: The three indirect composites and PFM systems fractured at loads higher than those typically associated with normal occlusal function. Although each material had a different composition and handling technique, no significant differences were found concerning their single load to fracture resistance among composite systems and PFM.

Thermal/mechanical simulation and laboratory fatigue testing of an alternative yttria tetragonal zirconia polycrystal core-veneer all-ceramic layered crown design

This study evaluated the stress levels at the core layer and the veneer layer of zirconia crowns (comprising an alternative core design vs. a standard core design) under mechanical/thermal simulation, and subjected simulated models to laboratory mouth-motion fatigue. The dimensions of a mandibular first molar were imported into computer-aided design (CAD) software and a tooth preparation was modeled. A crown was designed using the space between the original tooth and the prepared tooth. The alternative core presented an additional lingual shoulder that lowered the veneer bulk of the cusps. Finite element analyses evaluated the residual maximum principal stresses fields at the core and veneer of both designs under loading and when cooled from 900 degrees C to 25 degrees C. Crowns were fabricated and mouth-motion fatigued, generating master Weibull curves and reliability data. Thermal modeling showed low residual stress fields throughout the bulk of the cusps for both groups. Mechanical simulation depicted a shift in stress levels to the core of the alternative design compared with the standard design. Significantly higher reliability was found for the alternative core. Regardless of the alternative configuration, thermal and mechanical computer simulations showed stress in the alternative core design comparable and higher to that of the standard configuration, respectively. Such a mechanical scenario probably led to the higher reliability of the alternative design under fatigue.

Comparison of physical and mechanical properties of microwave-polymerized acrylic resin after disinfection in sodium hypochlorite solutions

This study evaluated the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin after immersion in sodium hypochlorite (NaOCl), simulating 20 min of disinfection daily during 180 days. Forty disk-shaped (15 x 4 mm) and 40 rectangular (65 x 10 x 3 mm) specimens were prepared with a microwave-polymerized acrylic resin (Onda-Cryl). Specimens were immersed in either 0.5% NaOCl, 1% NaOCl, Clorox/Calgon and distilled water (control). Color measurements were determined by a portable colorimeter. Three parallel lines, separated by 1.0 mm, were registered on each specimen before and after immersion procedures to analyze the surface roughness. The flexural strength was measured using a 3-point bending test in a universal testing machine with a 50 kgf load cell and a crosshead speed of 1 mm/min. Data were analyzed statistically by ANOVA and Tukey's test (?=0.05). There was no statistically significant differences (p>0.05) among the solutions for color, surface roughness and flexural strength. It may be concluded that immersion in NaOCl solutions simulating short-term daily use during 180 days did not influence the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin.

Comparative study of chemical and mechanical retentive systems for bonding of indirect composite resin to commercially pure titanium

This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (a=5%). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.

Mechanical strength and thermal conductivity of low-porosity gypsum plates

The thermal conductivity and mechanical strength of gypsum and gypsum-cellulose plates made from commercial plaster by a new process have been measured. The gypsum parts made by the new process, 'novogesso', have high mechanical strength and low porosity. The gypsum strength derives from both the high aspect ratio of the gypsum crystals and the strong adhesion among them by nano-flat layers of confined water, which behaves as supercooled water. Another contribution to the strength comes from the nano-flatness of the lateral surfaces of the gypsum single crystals. The bending and compression strengths, σB and σc, of gypsum plates prepared by this new technique can be as high as 30 and 100 MPa, respectively. The way gypsum plates have been assembled as well as their low thermal conductivity allowed for the construction of a low-cost experimental house with thermal and acoustic comfort.

Texture and mechanical properties evolution of a deep drawing medium carbon steel during cold rolling and subsequent recrystallization

Medium carbon steels are mostly used for simple applications; however, new applications have been developed for which good sheet metal formability is required. These types of steels have an inherent low formability. A medium-carbon hot-rolled SAE 1050 steel was selected for this study. It has been cold rolled with thickness reductions varying between 7 and 80%. The samples obtained were used to evaluate the strain hardening curve. For samples with a 50 and 80% thickness reduction, an annealing heat treatment was performed to achieve recrystallization. The material was characterized in the ""as-received"", cold rolled and annealed conditions using several methods: optical metallography, X-ray diffraction (texture), Vickers hardness, and tensile testing. For large thickness reductions, the SAE 1050 steel presented low elongation, less than 2%, and yield strength (YS) and tensile strength (TS) around 1400 MPa. Texture in the ""as-received"" condition showed strong components on the {001} plane, in the < 100 >, < 210 > and (110) directions. After cold rolling, the texture did not present any significant changes for small thickness reductions, however. It changed completely for large ones, where gamma, < 111 >//ND, alpha, < 110 > HRD, and gamma prime, < 223 >//ND, fibres were strengthened. After annealing, the microstructure of the SAE 1050 steel was characterized by recrystallized ferrite and globular cementite. There was little change in the alpha fibre for the 50% reduction, whereas for the 80% reduction, its intensity increased. Both gamma and gamma prime fibres vanished upon annealing for 50 and 80% reductions alike. (c) 2008 Elsevier B.V. All rights reserved.

Medium carbon steel deep drawing: A study on the evolution of mechanical properties, texture and simulations, from cold rolling to the end product

Medium carbon steels are mostly used for simple applications; nevertheless new applications have been developed for which good sheet formability is required. This class of steels has an inherent low formability. A medium carbon hot rolled SAE 1050 steel has been selected for this study. It has been cold rolled with reductions in the 7-80% range. Samples have been used to assess the cold work hardening curve. For samples with a 50 and 80% thickness reduction, an annealing heat treatment has been performed to obtain recrystallization. The material has been characterized in the ""as received"", cold rolled and annealed conditions, using several methods: optical microscopy, X-ray diffraction (texture), Vickers hardness and tensile testing. The 50% cold rolled and recrystallized material has been further studied in terms of sheet metal formability and texture evolution during the actual stamping of a steel toecap that has been used to validate the finite element simulations. (C) 2008 Elsevier B.V. All rights reserved.

Instrumented indentation testing of an epoxy adhesive used in automobile body assembling

Instrumented indentation has been used to investigate the mechanical properties of BETAMATE 1496 (R) Epoxy adhesive. The properties of the adhesive were analyzed by measuring its hardness and its Young`s modulus in samples extracted from six different positions of the front door of a commercial passenger vehicle in two phases of processing: after application of the adhesive in the door assembling (""pre-cured"" state) and after final cure in the painting oven (""cured"" state). Special attention was given to setting the optimal parameters (""creep"" time and unloading time step) for the instrumented indentation testing for the present application. Young`s modulus values around 1.1 +/- 0.2 GPa and hardness values around 0.15 +/- 0.05 GPa were obtained for all samples, irrespective of the variation of the indentation parameters in the testing procedure and of the relative position of the adhesive in the door frame in both states. (C) 2008 Elsevier Ltd. All rights reserved.