Knoop Microhardness and FT-Raman Spectroscopic Evaluation of a Resin-Based Dental Material Light-Cured by an Argon Ion Laser and Halogen Lamp: An in Vitro Study

Objective: The purpose of this study was to evaluate in vitro the Knoop microhardness (Knoop hardness number [KHN]) and the degree of conversion using FT-Raman spectroscopy of a light-cured microhybrid resin composite (Z350-3M-ESPE) Vita shade A3 photopolymerized with a halogen lamp or an argon ion laser. Background Data: Optimal polymerization of resin-based dental materials is important for longevity of restorations in dentistry. Materials and Methods: Thirty specimens were prepared and inserted into a disc-shaped polytetrafluoroethylene mold that was 2.0 mm thick and 3 mm in diameter. The specimens were divided into three groups (n = 10 each). Group 1 (G1) was light-cured for 20 sec with an Optilux 501 halogen light with an intensity of 1000 mW/cm(2). Group 2 (G2) was photopolymerized with an argon laser with a power of 150 mW for 10 sec, and group 3 (G3) was photopolymerized with an argon laser at 200 mW of power for 10 sec. All specimens were stored in distilled water for 24 h at 37 degrees C and kept in lightproof containers. For the KHN test five indentations were made and a depth of 100 mu m was maintained in each specimen. One hundred and fifty readings were obtained using a 25-g load for 45 sec. The degree of conversion values were measured by Raman spectroscopy. KHN and degree of conversion values were obtained on opposite sides of the irradiated surface. KHN and degree of conversion data were analyzed by one-way ANOVA and Tukey tests with statistical significance set at p < 0.05. Results: The results of KHN testing were G1 = 37.428 +/- 4.765; G2 = 23.588 +/- 6.269; and G3 = 21.652 +/- 4.393. The calculated degrees of conversion (DC%) were G1 = 48.57 +/- 2.11; G2 = 43.71 +/- 3.93; and G3 = 44.19 +/- 2.71. Conclusions: Polymerization with the halogen lamp ( G1) attained higher microhardness values than polymerization with the argon laser at power levels of 150 and 200 mW; there was no difference in hardness between the two argon laser groups. The results showed no statistically significant different degrees of conversion for the polymerization of composite samples with the two light sources tested.

Collimated scanning LS-INAA for testing trace elements homogeneity in Brazilian coffee beans

The degree of homogeneity is normally assessed by the variability of the results of independent analyses of several (e.g., 15) normal-scale replicates. Large sample instrumental neutron activation analysis (LS-INAA) with a collimated Ge detector allows inspecting the degree of homogeneity of the initial batch material, using a kilogram-size sample. The test is based on the spatial distributions of induced radioactivity. Such test was applied to samples of Brazilian whole (green) coffee beans (Coffea arabica and Coffea canephora) of approximately I kg in the frame of development of a coffee reference material. Results indicated that the material do not contain significant element composition inhomogeneities between batches of approximately 30-50 g, masses typically forming the starting base of a reference material.

Testing motor fitness in karate

Background and Study Aim: Evaluation of sport skills test can be very useful tool for coach practice. The aim of the present paper was: (a) to evaluate the reliability and accuracy of the Specific Physical Fitness Tests (SPFT) (b) to review the results of karate athletes who represent different weight categories, and who are at different stages of schooling; (c) to establish grading criteria of physical fitness preparation. Material/Methods: The reseach was conducted among 219 Kyokushin karate players, whose profiles were presented as (chi) over bar +/- SD and their main characteristics were the following: age 26.8 +/- 4.67 (19-39) years, body mass 75.2 +/- 8.35 (50-97) kg and body height 176.4 +/- 5.67 (160-196) cm. The value of the BMI amounted to 24.1 +/- 2.17 (17.9-29.4) kg/m(2). All the subjects of the research had training experience of 10.5 +/- 3.71 (4-20) years and their degree of proficiency ranged from 4(th) kyu to 3(rd) dan. The physical fitness trials proposed by Story (1989) included: hip turning speed, speed punches, flexibility, rapid kicks, agility, and evasion actions. It was supplemented by a test of local strength endurance, composing a battery of the SPFT, which was implemented by first of the authors between 1991 and 2006. Results: SPFT is characterized by high reliability and it can be used to diagnose the physical fitness preparation and monitor the individual results of training. It discriminates accurately competitors with different sports level and it is characterized by very high accuracy, it is correlated with the test results of motor general physical fitness abilities and coordination abilities as well as it is connected with the somatic build of the athlete. The performance classification table was developed on the basis of our research. Discussion: Results obtained in SPFT were shortly discussed. Conclusions: The collected results of our research allowed us to come to, the conclusion: The table can be applied not only to assess karate fighters, but also adepts in taekwondo, kick-boxing, ju-jitsu, hapkido or other mixed martial arts.

Study of the influence of simultaneous variation of magnetic material microstructural features on domain wall dynamics

The magnetic Barkhausen noise (MBN) is a phenomenon sensitive to several kinds of magnetic material microstructure changes, as well as to variations in material plastic deformation and stress. This fact stimulates the development of MBN-based non-destructive testing (NDT) techniques for analyzing magnetic materials, being the proposition of such a method, the main objective of the present study. The behavior of the MBN signal envelope, under simultaneous variations of carbon content and plastic deformation, is explained by the domain wall dynamics. Additionally, a non-destructive parameter for the characterization of each of these factors is proposed and validated through the experimental results. (C) 2010 Elsevier B.V. All rights reserved.

Use of diamond-like carbon with tungsten (W-DLC) films as biocompatible material

Diamond-like carbon (DLC), also known as amorphous hydrogenated carbon (a-C:H), are a class of materials with excellent mechanical, tribological and biological properties. When the DLC films are enhanced with other elements, all of these properties can be changed within a certain range. In this work, reactive magnetron sputtering was used to deposit W-DLC (hydrogenated tungsten carbide) films on Ti6A14V (implant material). Many films were made using pure tungsten (99.99%) target and different plasmas processes, with different ratio among argon and methane. It was possible to change the films composition (from pure amorphous carbon to carbon enhanced with tungsten) according to ratio of argon and methane plasma. Between all films processed, the carbon films enhanced with tungsten showed good results in the ""in vitro"" cytotoxicity testing. Raman spectroscopy was used to analyze the chemical bonds kinds and the chemical bonds quantities. The Rutherford Back Scattering (RBS) was used to analyze the films compositions. The chemical inertness was analyzed by scanning voltametry. W-DLC thin films obtained in these processes have low roughness, high chemical resistance, good adhesion and show a high biocompatibility, when compared with common DLC thin films. Hence we have concluded that the tungsten concentrations in the DLC films make an important role to improve the properties of the DLC layers. (C) 2007 Elsevier B.V. All rights reserved.

Mechanical Testing of Indirect Composite Materials Directly Applied on Implant Abutments

Purpose: To test the strength to failure and fracture mode of three indirect composite materials directly applied onto Ti-6Al-4V implant abutments vs cemented standard porcelain-fused-to-metal (PFM) crowns. Materials and Methods: Sixty-four locking taper abutments were randomly allocated to four groups and were cleaned in ethanol in an ultrasonic bath for 5 min. After drying under ambient conditions, the abutments were grit blasted and a custom 4-cusp molar crown mold was utilized to produce identical crowns (n = 16 per group) of Tescera (Bisco), Ceramage (Shofu), and Diamond Crown (DRM) according to the manufacturer`s instructions. The porcelain-fused-to-metal crowns were fabricated by conventional means involving the construction and a wax pattern and casting of a metallic coping followed by sintering of increasing layers of porcelain. All crowns were loaded to failure by an indenter placed at one of the cusp tips at a 1 mm/min rate. Subsequently, fracture analysis was performed by means of stereomicroscopy and scanning electron microscopy. One-way ANOVA at 95% level of significance was utilized for statistical analysis. Results: The single load to failure (+/- SD) results were: Tescera (1130 +/- 239 N), Ceramage (1099 +/- 257 N), Diamond Crown (1155 +/- 284 N), and PFM (1081 +/- 243 N). Stereomicroscopy analysis showed two distinct failure modes, where the loaded cusp failed either with or without abutment/metallic coping exposure. SEM analysis of the fractures showed multiple crack propagation towards the cervical region of the crown below a region of plastic deformation at the indenter contact region. Conclusion: The three indirect composites and PFM systems fractured at loads higher than those typically associated with normal occlusal function. Although each material had a different composition and handling technique, no significant differences were found concerning their single load to fracture resistance among composite systems and PFM.

In vitro evaluation of an alternative method to bond molar tubes

Despite the advances in bonding materials, many clinicians today still prefer to place bands on molar teeth. Molar bonding procedures need improvement to be widely accepted clinically. OBJECTIVE: The purpose of this study was to evaluate the shear bond strength when an additional adhesive layer was applied on the occlusal tooth/tube interface to provide reinforcement to molar tubes. MATERIAL AND METHODS: Sixty third molars were selected and allocated to the 3 groups: group 1 received a conventional direct bond followed by the application of an additional layer of adhesive on the occlusal tooth/tube interface, group 2 received a conventional direct bond, and group 3 received a conventional direct bond and an additional cure time of 10 s. The specimens were debonded in a universal testing machine. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). RESULTS: Group 1 had a significantly higher (p<0.05) shear bond strength compared to groups 2 and 3. No difference was detected between groups 2 and 3 (p>0.05). CONCLUSIONS: The present in vitro findings indicate that the application of an additional layer of adhesive on the tooth/tube interface increased the shear bond strength of the bonded molar tubes.

Novo protocolo para as ações de saúde bucal coletiva: padronização no armazenamento, distribuição e uso do material de higiene bucal

Este trabalho avaliou o material de higiene bucal usado em escolas para estabelecer um protocolo às ações de higiene bucal coletiva. O estudo foi dividido em duas etapas: 1ª- 20 responsáveis pelos procedimentos coletivos com escolares de Bauru e São José dos Campos - SP responderam a dois questionários sobre o uso de cinco kits de higiene bucal coletiva. A análise estatística foi realizada através do teste Wilcoxon (p < 0,05); 2ª - 178 escolares de 4 a 8 anos de Bauru e Bariri-SP dispensaram na escova uma quantidade de creme dental e dentifrício líquido para a prática da escovação, a qual foi pesada através de uma balança portátil. A análise estatística foi obtida através do coeficiente de correlação de Pearson e a análise de covariância (p< 0,05). O kit 5 obteve graus de satisfação e muita satisfação quando comparado aos kits 1 a 4. A quantidade de creme dental dispensada pelos escolares foi em média 0,41g (Bauru) e 0,48g (Bariri). Não houve diferença estatística entre os escolares de Bauru e Bariri em relação ao dentifrício líquido (média de 0,15g). O dentifrício líquido, através da "técnica da gota", foi considerado prático, dispensando uma pequena quantidade padronizada. O kit 5 demonstrou ser uma boa alternativa ao estabelecimento de um protocolo de ações em saúde bucal coletiva no SUS.

Validation of an experimental polyurethane model for biomechanical studies on implant-supported prosthesis: compression tests

OBJECTIVES: The complexity and heterogeneity of human bone, as well as ethical issues, most always hinder the performance of clinical trials. Thus, in vitro studies become an important source of information for the understanding of biomechanical events on implant-supported prostheses, although study results cannot be considered reliable unless validation studies are conducted. The purpose of this work was to validate an artificial experimental model based on its modulus of elasticity, to simulate the performance of human bone in vivo in biomechanical studies of implant-supported prostheses. MATERIAL AND METHODS: In this study, fast-curing polyurethane (F16 polyurethane, Axson) was used to build 40 specimens that were divided into five groups. The following reagent ratios (part A/part B) were used: Group A (0.5/1.0), Group B (0.8/1.0), Group C (1.0/1.0), Group D (1.2/1.0), and Group E (1.5/1.0). A universal testing machine (Kratos model K - 2000 MP) was used to measure modulus of elasticity values by compression. RESULTS: Mean modulus of elasticity values were: Group A - 389.72 MPa, Group B - 529.19 MPa, Group C - 571.11 MPa, Group D - 470.35 MPa, Group E - 437.36 MPa. CONCLUSION: The best mechanical characteristics and modulus of elasticity value comparable to that of human trabecular bone were obtained when A/B ratio was 1:1.

Impact and fracture resistance of an experimental acrylic polymer with elastomer in different proportions

The purpose of this study was to evaluate the impact and fracture resistance of acrylic resins: a heat-polymerized resin, a high-impact resin and an experimental polymethyl methacrylate with elastomer in different proportions (10, 20, 40 and 60%). 120 specimens were fabricated and submitted to conventional heat-polymerization. For impact test, a Charpy-type impact tester was used. Fracture resistance was assessed with a 3-point bending test by using a mechanical testing machine. Ten specimens were used for each test. Fracture (MPa) and impact resistance values (J.m-1) were submitted to ANOVA - Bonferroni's test - 5% significance level. Materials with higher amount of elastomer had statistically significant differences regarding to impact resistance (p < 0.05). Fracture resistance was superior (p < 0.01) for high-resistance acrylic resin. The increase in elastomer concentration added to polymethyl methacrylate raised the impact resistance and decreased the fracture resistance. Processing the material by injection decreased its resistance to impact and fracture.

Comparative study of two commercially pure titanium casting methods

The interest in using titanium to fabricate removable partial denture (RPD) frameworks has increased, but there are few studies evaluating the effects of casting methods on clasp behavior. OBJECTIVE: This study compared the occurrence of porosities and the retentive force of commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) removable partial denture circumferential clasps cast by induction/centrifugation and plasma/vacuum-pressure. MATERIAL AND METHODS: 72 frameworks were cast from CP Ti (n=36) and Co-Cr alloy (n=36; control group). For each material, 18 frameworks were casted by electromagnetic induction and injected by centrifugation, whereas the other 18 were casted by plasma and injected by vacuum-pressure. For each casting method, three subgroups (n=6) were formed: 0.25 mm, 0.50 mm, and 0.75 mm undercuts. The specimens were radiographed and subjected to an insertion/removal test simulating 5 years of framework use. Data were analyzed by ANOVA and Tukey's to compare materials and cast methods (α=0.05). RESULTS: Three of 18 specimens of the induction/centrifugation group and 9 of 18 specimens of plasma/vacuum-pressure cast presented porosities, but only 1 and 7 specimens, respectively, were rejected for simulation test. For Co-Cr alloy, no defects were found. Comparing the casting methods, statistically significant differences (p<0.05) were observed only for the Co-Cr alloy with 0.25 mm and 0.50 mm undercuts. Significant differences were found for the 0.25 mm and 0.75 mm undercuts dependent on the material used. For the 0.50 mm undercut, significant differences were found when the materials were induction casted. CONCLUSION: Although both casting methods produced satisfactory CP Ti RPD frameworks, the occurrence of porosities was greater in the plasma/vacuum-pressure than in the induction/centrifugation method, the latter resulting in higher clasp rigidity, generating higher retention force values.

Effect of temporary cements on the shear bond strength of luting cements

OBJECTIVE: The purpose of this study was to evaluate, by shear bond strength (SBS) testing, the influence of different types of temporary cements on the final cementation using conventional and self-etching resin-based luting cements. Material and Methods: Forty human teeth divided in two halves were assigned to 8 groups (n=10): I and V (no temporary cementation); II and VI: Ca(OH)2-based cement; III and VII: zinc oxide (ZO)-based cement; IV and VIII: ZO-eugenol (ZOE)-based cement. Final cementation was done with RelyX ARC cement (groups I to IV) and RelyX Unicem cement (groups V to VIII). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. RESULTS: Means were (MPa): I - 3.80 (±1.481); II - 5.24 (±2.297); III - 6.98 (±1.885); IV - 6.54 (±1.459); V - 5.22 (±2.465); VI - 4.48 (±1.705); VII - 6.29 (±2.280); VIII - 2.47 (±2.076). Comparison of the groups that had the same temporary cementation (Groups II and VI; III and VII; IV and VIII) showed statistically significant difference (p<0.001) only between Groups IV and VIII, in which ZOE-based cements were used. The use of either Ca(OH)2-based (Groups II and VI) or ZO-based (Groups III and VII) cements showed no statistically significant difference (p>0.05) for the different luting cements (RelyX TM ARC and RelyX TM Unicem). The groups that had no temporary cementation (Groups I and V) did not differ significantly from each other either (p>0.05). CONCLUSION: When temporary cementation was done with ZO- or ZOE-based cements and final cementation was done with RelyX ARC, there was an increase in the SBS compared to the control. In the groups cemented with RelyX Unicem, however, the use of a ZOE-based temporary cement affected negatively the SBS of the luting agent used for final cementation.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1% NaOCl/17% EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% EDTA produced similar bond strength to that of untreated dentin.

Influence of ferrule preparation with or without glass fiber post on fracture resistance of endodontically treated teeth

OBJECTIVE: This study evaluated the effect of ferrule preparation (Fp) on the fracture resistance of endodontically treated teeth, restored with composite resin cores with or without glass fiber posts. MATERIAL AND METHODS: Forty-four bovine teeth were sectioned 19 or 17 mm (2 mm ferrule) from the apex, endodontically treated and assigned to four groups (n = 11): Group 1: Fp and post; Group 2: Fp and without post; Group 3: without Fp and with post; Group 4: without Fp and without post. All specimens were restored with composite resin core and metal crown. Specimens were subjected to fracture resistance testing in a universal testing machine at a crosshead speed of 0.5 mm/min. The data were analyzed by two-way ANOVA and Tukey's tests (α=0.05). RESULTS: The mean fracture resistance values were as follows: Group 1: 573.3 N; Group 2: 552.5 N; Group 3: 275.3 N; Group 4: 258.6 N. Significantly higher fracture resistance was found for the groups with Fp (p<0.001). CONCLUSION: There was no statistically significant interaction between the "Fp" and "post" factors (p = 0.954). The ferrule preparation increased the fracture resistance of endodontically treated teeth. However, the use of glass fiber post showed no significant influence on the fracture resistance.

Microhardness assessment of different commercial brands of resin composites with different degrees of translucence

Owing to improvements in its mechanical properties and to the availability of shade and translucence resources, resin composite has become one of the most widely used restorative materials in present day Dentistry. The aim of this study was to assess the relation between the surface hardness of seven different commercial brands of resin composites (Charisma, Fill Magic, Master Fill, Natural Look, Opallis, Tetric Ceram, and Z250) and the different degrees of translucence (translucid, enamel and dentin). Vickers microhardness testing revealed significant differences among the groups. Z250 was the commercial brand that showed the best performance in the hardness test. When comparing the three groups assessed within the same brand, only Master Fill and Fill Magic presented statistically significant differences among all of the different translucencies. Natural Look was the only one that showed no significant difference among any of the three groups. Charisma, Opallis, Tetric Ceram and Z250 showed significant differences among some of the tested groups. Based on the results found in this study, it was not possible to establish a relation between translucence and the microhardness of the resin composites assessed. Depending on the material assessed, however, translucence variation did affect the microhardness values of the resin composites.