Corrosion behavior of carbon steel protected with single and bi-layer of silane films filled with silica nanoparticles

The electrochemical behaviour of carbon steel coated with bis-[trimethoxysilylpropyl]amine (BTSPA) filled with silica nanoparticles in naturally aerated 0.1 mol L-1 NaCl solutions was evaluated. The coating was prepared by adding different concentrations of silica nanoparticles (100, 200, 300, 400 and 500 ppm) to the hydrolysis solution and then a second layer without silica nanoparticles was applied. The electrochemical behavior of the coated steel was evaluated by means of open-circuit potential (E-OC), electrochemical impedance spectroscopy (EIS) and polarization curves. Surface characterization was made by atomic force microscopy (AFM), and its hydrophobicity assessed by contact angle measurements. EIS diagrams have shown an improvement of the barrier properties of the silane layer with the silica addition, which was further improved on the bi-layer system. However, a dependence on the filler concentration was verified, and the best electrochemical response was obtained for samples modified with 300 ppm of silica nanoparticles. AFM images have shown a homogeneous distribution of the silica nanoparticles on the sample surface; however particles agglomeration was detected, which degraded the corrosion protection performance. The results were explained on the basis of the improvement of the barrier properties of the coating due to the filler addition and on the onset of defective regions on the more heavily filled coatings allowing easier electrolyte penetration. (C) 2007 Elsevier B.V. All rights reserved.

Distribution and storage characterization of soil solution for drip irrigation

The increased use of marginal quality water with drip irrigation requires sound fertigation practices that reconcile environmental concerns with viable crop production objectives. We conducted experiments to characterize dynamics and patterns of soil solution within wet bulb formed by drip irrigation. Time-domain reflectometry probes were used to monitor the distribution of potassium nitrate (KNO(3)) and water distribution from drippers discharging at constant flow rates of 2, 4 and 8 L h(-1) in soil-filled containers. Considering results from different profiles, we observed greater solute storage near the dripper decreasing gradually towards the wetting front. About half of the applied KNO(3) solution (48%) was stored in the first layer (0-0.10 m) for all experiments, 29% was stored in the next layer (0.10-0.20 m). Comparing different dripper flow rates, we observed higher solution storage for 4 L h(-1), with 45, 53 and 47% of applied KNO(3) solution accumulating in the first layer (0-0.10 m) for dripper flow rates of 2, 4 and 8 L h(-1), respectively. The results suggest that based on the volume and frequency used in this experiment, it would be advantageous to apply small amounts of solution at more frequent intervals to reduce deep percolation losses of applied water and solutes.

Macroscopic root water uptake distribution using a matric flux potential approach

Hydrological models featuring root water uptake usually do not include compensation mechanisms such that reductions in uptake from dry layers are compensated by an increase in uptake from wetter layers. We developed a physically based root water uptake model with an implicit compensation mechanism. Based on an expression for the matric flux potential (M) as a function of the distance to the root, and assuming a depth-independent value of M at the root surface, uptake per layer is shown to be a function of layer bulk M, root surface M, and a weighting factor that depends on root length density and root radius. Actual transpiration can be calculated from the sum of layer uptake rates. The proposed reduction function (PRF) was built into the SWAP model, and predictions were compared to those made with the Feddes reduction function (FRF). Simulation results were tested against data from Canada (continuous spring wheat [(Triticum aestivum L.]) and Germany (spring wheat, winter barley [Hordeum vulgare L.], sugarbeet [Beta vulgaris L.], winter wheat rotation). For the Canadian data, the root mean square error of prediction (RMSEP) for water content in the upper soil layers was very similar for FRF and PRF; for the deeper layers, RMSEP was smaller for PRF. For the German data, RMSEP was lower for PRF in the upper layers and was similar for both models in the deeper layers. In conclusion, but dependent on the properties of the data sets available for testing,the incorporation of the new reduction function into SWAP was successful, providing new capabilities for simulating compensated root water uptake without increasing the number of input parameters or degrading model performance.

Collagen Fiber and Versican Distribution Within the Lamina Propria of Fetal Vocal Folds

Objectives: To analyze the presence and distribution of collagen fibers and versican in human vocal fold lamina propria of fetal larynges. Study Design: Cross sectional analysis of cadaveric vocal folds of human fetuses. Methods: Seven fetal larynges obtained from 28- to 36-week-old fetuses were analyzed with the Picrosirius-polarization method, immunohistochemistry, and image analysis. Results: Collagen fibers within the lamina propria exhibited a monolaminar distribution pattern and spatial arrangement in ""wicker basket."" Versican distribution was larger in the superficial and intermediate layers when compared to the deep layer. Conclusion: Our findings suggest that collagen and versican distribution and arrangement within the lamina propria in the developing fetus are important for vocalization at birth.

Influence of Post and Resin Cement on Stress Distribution of Maxillary Central Incisors Restored with Direct Resin Composite

The current study evaluated the influence of two endodontic post systems and the elastic modulus and film thickness of resin cement on stress distribution in a maxillary central incisor (MCI) restored with direct resin composite using finite element analysis (FEA). A three-dimensional model of an MCI with a coronary fracture and supporting structures was performed. A static chewing pressure of 2.16 N/mm(2) was applied to two areas on the palatal surface of the composite restoration. Zirconia ceramic (ZC) and glass fiber (GF) posts were considered. The stress distribution was analyzed in the post, dentin and cement layer when ZC and GF posts were fixed to the root canals using resin cements of different elastic moduli (7.0 and 18.6 GPa) and different layer thicknesses (70 and 200 mu m). The different post materials presented a significant influence on stress distribution with lesser stress concentration when using the GF post. The higher elastic modulus cement created higher stress levels within itself. The cement thicknesses did not present significant changes.

Thickness and Annealing Temperature Effects on the Optical Properties and Surface Morphology of Layer-by-Layer Poly(p-phenyline vinylene) plus Dodecylbenzenesulfonate Films

The fabrication of controlled molecular architectures is essential for organic devices, as is the case of emission of polarized light for the information industry. In this study, we show that optimized conditions can be established to allow layer-by-layer (LbL) films of poly(p-phenylene vinylene) (PPV)+dodecylbenzenesulfonate (DBS) to be obtained with anisotropic properties. Films with five layers and converted at 110 degrees C had a dichroic ratio delta = 2.3 and order parameter r = 34%, as indicated in optical spectroscopy and emission ellipsometry data. This anisotropy was decreased with the number of layers deposited, with delta = 1.0 for a 75-layer LbL PPV + DBS film. The analysis with atomic force microscopy showed the formation of polymer clusters in a random growth process with the normalized height distribution being represented by a Gaussian function. In spite of this randomness in film growth, the self-covariance function pointed to a correlation between clusters, especially for thick films. In summary, the LbL method may be exploited to obtain both anisotropic films with polarized emission and regular, nanostructured surfaces. (c) 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 49: 206-213, 2011

Microbial distribution in the root canal system after periapical lesion induction using different methods

The aim of this study was to evaluate the microbial distribution in the root canal system after periapical lesion induction in dogs' teeth using different methods. Fifty-two root canals were assigned to 4 groups (n=13). Groups I and II: root canals were exposed to the oral cavity for 180 days; groups III and IV: root canals were exposed for 7 days and then the coronal openings were sealed for 53 days. The root apices of groups I and III were perforated, while those of groups II and IV remained intact. After the experimental periods, the animals were euthanized and the anatomic pieces containing the roots were processed and stained with the Brown & Brenn method to assess the presence and distribution of microorganisms. The incidence of microorganisms at different sites of the roots and periapical lesions was analyzed statistically by the chi-square test at 5% significance level. All groups presented microorganisms in the entire root canal system. A larger number of microorganisms was observed on the root canal walls, apical delta and dentinal tubules (p<0.05), followed by cementum and cemental resorption areas. In spite of the different periods of exposure to the oral environment, the methods used for induction of periapical periodontitis yielded similar distribution of microorganisms in the root canal system.

Effect of phosphate-bonded investments on titanium reaction layer and crown fit

This study analyzed the reaction layer and measured the marginal crown fit of cast titanium applied to different phosphate-bonded investments, prepared under the following conditions (liquid concentration/casting temperature): Rema Exakt (RE) - 100%/237°C, 75%/287°C, Castorit Super C (CS)-100%/70°C, 75%/141°C and Rematitan Plus (RP)- 100%/430°C (special to titanium cast, as the control group). The reaction layer was studied using the Vickers hardness test, and analyzed by two way ANOVA and Tukey's HSD tests (α = 0.05). Digital photographs were taken of the crowns seated on the die, the misfit was measured using an image analysis system and One-way ANOVA, and Tukey's test was applied (α = 0.05). The hardness decreased from the surface (601.17 VHN) to 150 μm (204.03 VHN). The group CS 75%/141°C presented higher hardness than the other groups, revealing higher surface contamination, but there were no differences among the groups at measurements deeper than 150 μm. The castings made with CS - 100%/70°C presented the lowest levels of marginal misfit, followed by RE -100%/237°C. The conventional investments CS (100%) and RE (100%) showed better marginal fit than RP, but the CS (75%) had higher surface contamination.

Evaluation of in vitro human gingival fibroblast seeding on acellular dermal matrix

The acellular dermal matrix (ADM) was introduced in periodontology as a substitute for the autogenous grafts, which became restricted because of the limited source of donor's tissue. The aim of this study was to investigate, in vitro, the distribution, proliferation and viability of human gingival fibroblasts seeded onto ADM. ADM was seeded with human gingival fibroblasts for up to 21 days. The following parameters were evaluated: cell distribution, proliferation and viability. Results revealed that, at day 7, fibroblasts were adherent and spread on ADM surface, and were unevenly distributed, forming a discontinuous single cell layer; at day 14, a confluent fibroblastic monolayer lining ADM surface was noticed. At day 21, the cell monolayer exhibited a reduction in cell density. At 7 days, about to 90% of adherent cells on ADM surface were cycling while at 14 and 21 days this proportion was significantly reduced. A high proportion of viable cell was detected on AMD surface both on 14 and 21 days. The results suggest that fibroblast seeding onto ADM for 14 days can allow good conditions for cell adhesion and spreading on the matrix; however, migration inside the matrix was limited.

Distribution of biotypes and leukotoxic activity of Aggregatibacter actinomycetemcomitans isolated from Brazilian patients with chronic periodontitis

Aggregatibacter actinomycetemcomitans is an important etiologic agent of the periodontitis and is associated with extra-oral infections. In this study, the detection of the ltxA gene as well as the ltx promoter region from leukotoxic A. actinomycetemcomitans isolated from 50 Brazilian patients with periodontitis and 50 healthy subjects was performed. The leukotoxic activity on HL-60 cells was also evaluated. Leukotoxic activity was determined using a trypan blue exclusion method. The 530 bp deletion in the promoter region was evaluated by PCR using a PRO primer pair. A. actinomycetemcomitans was detected by culture and directly from crude subgingival biofilm by PCR using specific primers. By culture, A. actinomycetemcomitans was detected in nine (18%) of the periodontal patients and one (2%) healthy subject. However, by PCR, this organism was detected in 44% of the periodontal patients and in 16% of the healthy subjects. It was verified a great discrepancy between PCR detection of the ltx operon promoter directly from crude subgingival biofilm and from bacterial DNA. Only one periodontal sample harbored highly leukotoxic A. actinomycetemcomitans. Moreover, biotype II was the most prevalent and no correlation between biotypes and leukotoxic activity was observed. The diversity of leukotoxin expression by A. actinomycetemcomitans suggests a role of this toxin in the pathogenesis of periodontal disease and other infectious diseases.

Inequalities in the distribution of dental caries among 12-year-old Brazilian schoolchildren

We assessed the inequality in the distribution of dental caries and the association between indicators of socioeconomic status and caries experience in a representative sample of schoolchildren. This study followed a cross-sectional design, with a sample of 792 schoolchildren aged 12 years, representative of this age group in Santa Maria, RS, Brazil. Guardians answered questions on socioeconomic status and a dental examination provided information on the dental caries experience (DMF-T). Inequality in dental caries distribution was measured by the Gini coefficient and the Significant Caries Index (SiC). The assessment of association used Poisson regression models. Socioeconomic factors were associated with prevalence of dental caries for the whole sample and also for individuals with a high-caries level. Children from low-income households had the highest prevalence of dental caries. The Gini coefficient was 0.7 and the SiC Index 2.5. The percentage of caries prevalence was 39.3% (95% CI: 35.8%-42.8%) and the mean for DMF-T was 0.9 (± SD 1.5). Inequalities in the distribution of dental caries were observed and socioeconomic factors were found to be strong predictors of the prevalence of oral disease in children of this age group.

Use of flowable composite as intermediary layer in non-carious cervical lesions restored with composite resin: 48-month follow-up

PURPOSE: In this case report, the clinical performance of a microhybrid resin composite placed with or without a flowable resin composite was compared, over a 48-month period. CASE DESCRIPTION: The patient of this case report presented 2 pairs of equivalent cervical abfraction lesions, under occlusion. Four restorations were placed in teeth 34, 35, 44 and 45. The restorations were divided into groups (Single Bond + Filtek-Flow + Filtek Z250 or Single Bond + Filtek Z250) and the materials were applied according to the manufactures instructions. Two previously calibrated operators placed the restorations and two other independent examiners evaluated the restorations at baseline and after 48 months, according to the USPHS criteria and modified criteria for color match. CONCLUSION: After 48 months of evaluation the lesions restored with Filtek-Flow as a liner under Filtek Z250 did not show better clinical performance than the restorations without Filtek-Flow. All restorations showed a trend toward dark yellowing after 48 months.

Study of the equatorial Atlantic Ocean mixing layer using a one-dimensional turbulence model

The General Ocean Turbulence Model (GOTM) is applied to the diagnostic turbulence field of the mixing layer (ML) over the equatorial region of the Atlantic Ocean. Two situations were investigated: rainy and dry seasons, defined, respectively, by the presence of the intertropical convergence zone and by its northward displacement. Simulations were carried out using data from a PIRATA buoy located on the equator at 23º W to compute surface turbulent fluxes and from the NASA/GEWEX Surface Radiation Budget Project to close the surface radiation balance. A data assimilation scheme was used as a surrogate for the physical effects not present in the one-dimensional model. In the rainy season, results show that the ML is shallower due to the weaker surface stress and stronger stable stratification; the maximum ML depth reached during this season is around 15 m, with an averaged diurnal variation of 7 m depth. In the dry season, the stronger surface stress and the enhanced surface heat balance components enable higher mechanical production of turbulent kinetic energy and, at night, the buoyancy acts also enhancing turbulence in the first meters of depth, characterizing a deeper ML, reaching around 60 m and presenting an average diurnal variation of 30 m.

A new species of the genus Pimelerodius Vanin from the Amazon Region, with notes on the geografic distribution of Pimelerodius motacilla (Boheman) (Coleoptera, Curculionidae, Otidocephalini)

Pimelerodius punctiventris sp. nov. (type locality Brazil, Amazonas, Itacoatiara) is described and illustrated. The new taxon is compared with similar species, being distinguished from the other 12 known species of the genus by the presence of punctures in ventrite I. The available published key for identification of species of Pimelerodius is adapted to include the new species. A modification of the generic description of the aedeagus of Pimelerodius is provided, a necessity due to the differences observed in the aedeagus of the new species. The occurrence of P. motacilla (Boheman, 1843) in the Amazon Region, recorded in sympatry with P. punctiventris in Itacoatiara, AM, is discussed and confirmed, based on the study of 41 available specimens.

Glycosaminoglycan distribution in the rat uterine cervix during the estrous cycle

OBJECTIVE: To analyze the amount of glycosaminoglycans in the uterine cervix during each phase of the rat estrous cycle. DESIGN: Based on vaginal smears, forty female, regularly cycling rats were divided into four groups (n = 10 for each group): GI - proestrous, GII - estrous, GIII - metaestrous and GIV - diestrous. Animals were sacrificed at each phase of the cycle, and the cervix was immediately removed and submitted to biochemical extraction and determination of sulfated glycosaminoglycans and hyaluronic acid. The results were analyzed by ANOVA followed by the Bonferroni post-hoc test. RESULTS: The uterine cervix had the highest amount of total sulfated glycosaminoglycans and dermatan sulfate during the estrous phase (8.90 ± 0.55 mg/g of cetonic extract, p<0.001; and 8.86 ± 0.57 mg/g of cetonic extract, p<0.001). In addition, there was more heparan sulfate at the cervix during the proestrous phase (0.185 ± 0.03 mg/g of cetonic extract) than during any other phase (p<0.001). There were no significant changes in the concentration of hyaluronic acid in the uterine cervix during the estrous cycle. CONCLUSION: Our data suggest that the amount of total sulfated glycosaminoglycans may be influenced by hormonal fluctuations related to the estrous cycle, with dermatan sulfate and heparan sulfate being the glycosaminoglycans most sensitive to hormonal change.