The purpose of this study was to compare the polymerization shrinkage stress of composite resins (microfilled, microhybrid and hybrid) photoactivated by quartz-tungsten halogen light (QTH) and light-emitting diode (LED). Glass rods (5.0 mm x 5.0 cm) were fabricated and had one of the surfaces air-abraded with aluminum oxide and coated with a layer of an adhesive system, which was photoactivated with the QTH unit. The glass rods were vertically assembled, in pairs, to a universal testing machine and the composites were applied to the lower rod. The upper rod was placed closer, at 2 mm, and an extensometer was attached to the rods. The 20 composites were polymerized by either QTH (n=10) or LED (n=10) curing units. Polymerization was carried out using 2 devices positioned in opposite sides, which were simultaneously activated for 40 s. Shrinkage stress was analyzed twice: shortly after polymerization (t40s) and 10 min later (t10min). Data were analyzed statistically by 2-way ANOVA and Tukey's test (a=5%). The shrinkage stress for all composites was higher at t10min than at t40s, regardless of the activation source. Microfilled composite resins showed lower shrinkage stress values compared to the other composite resins. For the hybrid and microhybrid composite resins, the light source had no influence on the shrinkage stress, except for microfilled composite at t10min. It may be concluded that the composition of composite resins is the factor with the strongest influence on shrinkage stress.

Prevalência do HPV em mulheres rastreadas para o câncer cervical

OBJETIVO: Analisar a prevalência da infecção genital por papilomavírus humano (HPV) de alto risco por faixa etária e fatores associados. MÉTODOS: Estudo transversal com amostra de 2.300 mulheres (15-65 anos) que buscaram rastreamento para o câncer cervical entre fevereiro de 2002 e março de 2003 em São Paulo e Campinas, estado de São Paulo. Aplicou-se questionário epidemiológico e realizou-se coleta cervical para citologia oncológica e teste de captura híbrida II. As análises estatísticas empregadas foram teste de qui-quadrado de Pearson e análise multivariada pelo método forward likelihood ratio. RESULTADOS: A prevalência total da infecção genital por HPV de alto risco foi de 17,8%, distribuída nas faixas etárias: 27,1% (<25 anos), 21,3% (25-34 anos), 12,1% (35-44 anos), 12,0% (45-54 anos) e de 13,9% (55-65 anos). Participantes com maior número de parceiros sexuais durante a vida apresentaram maior freqüência da infecção. Relacionamento estável, idade de 35 a 44 anos e ex-fumantes foram associados à proteção da infecção. A infecção genital por HPV de alto risco ocorreu em 14,3% das citologias normais, em 77,8% das lesões escamosas de alto grau e nos dois (100%) casos de carcinoma. CONCLUSÕES: A prevalência da infecção genital por HPV de alto risco na amostra estudada foi alta. Houve predomínio de casos abaixo dos 25 anos e tendência a um novo aumento após os 55 anos, com maior freqüência naqueles com maior número de parceiros sexuais durante a vida