Tensile bond strength of cast commercially pure titanium and cast gold-alloy posts and cores cemented with two luting agents

Statement of problem. In vitro studies on the retentive strengths of various cements used to retain posts have reported conflicting results. Purpose. The purpose of this study was to compare the tensile strength of commercially pure titanium and type III cast gold-alloy posts and cores cemented with zinc phosphate or resin cement. Material and methods. Forty-two extracted human canines were endoclontically treated. The root preparations were accomplished using Largo reamers (10 mm in depth and 1.7 mm in diameter). Acrylic resin patterns for the posts and cores were made, and specimens were cast in commercially pure titanium and in type III gold alloy (n=7). Fourteen titanium cast posts and cores were submitted to surface treatment with Kroll acid solution and to scanning electron microscopy (SEM), before and after acid etching. The groups (n=7) were cemented with zinc phosphate cement or resin cement (Panavia F). Tensile strengths were measured in a universal testing machine at a crosshead speed of 0.5 mm/min. The results (Kgf) were statistically analyzed by 2-way ANCIVA (alpha=.05). Results. The 2-way ANOVA indicated that there were no significant differences among the groups tested. Retentive means for zinc phosphate and Panavia F cements were statistically similar. The bond strength was not Influenced by the alloy, the luting material, or the etching treatment. SEM analysis indicated that the etched surfaces were smoother than those that did not receive surface treatment, but this fact did not influence the results. Conclusions. Commercially pure titanium cast posts and cores cemented with zinc phosphate and resin cements demonstrated similar mean tensile retentive values. Retentive values were also similar to mean values recorded for cast gold-alloy posts and cores cemented with zinc phosphate cement and resin cements.

Energy-dispersive X-ray fluorescence analysis of a pre-Columbian funerary gold mask from the Museum of Sican, Peru

A funerary gold mask from the Museum of Sican, Ferranafe, Peru was analyzed in 30 different areas using a portable equipment using energy-dispersive X-ray fluorescence. It was deduced from the measurements that the main sheet of the mask and the majority of the pendants have a similar composition and are made of tumbaga, which means a poor gold alloy enriched at the surface by depletion gilding, and have a similar `equivalent` gilding thickness of about 5 mu m. The nose, also on tumbaga, has different composition and a thickness of about 8 mu m. The clamps are on gilded or on silvered copper. The red pigment dispersed on the surface of the mask is cinnabar. Copyright (C) 2009 John Wiley & Sons, Ltd.

Wear of Ball Attachments After 1 to 8 Years of Clinical Use: A Qualitative Analysis

The purpose of this study was to analyze and compare scanning electron microscopy (SEM) observations of ball attachments that had been worn by patients during three periods of clinical use. One hundred forty-four specimens of ball anchor attachments (gold alloy matrix and titanium patrix) were studied by SEM after periods of approximately 1, 3.5, and 8 years of clinical use. Twenty new attachment components were examined as controls. SEM images revealed signs of mechanical wear for the ball attachments studied. The surfaces of the titanium patrix were associated primarily with roughening after short-term use, whereas surfaces of the gold alloy matrix showed wear, roughening, and loss of microscopic material in the form of flakes. Severe mechanical wear on both surfaces was noted after longer periods of use. The mechanical changes were not correlated with patient-mediated observations regarding the time-dependent retentive efficacy of the attachments. One year of clinical wear appeared to have limited effect on the ball attachment tested. Conversely, longer periods of use led to marked modifications in shape of the matrix and patrix components. Int J Prosthodont 2011;24:270-272.

Ex Situ Scanning Electrochemical Microscopy (SECM) Investigation of Bismuth- and Bismuth/Lead Alloy Film-Modified Gold Electrodes in Alkaline Medium

Scanning electrochemical microscopy (SECM) in feedback mode was employed to characterise the reactivity and microscopic peculiarities of bismuth and bismuth/lead alloys plated onto gold disk substrates in 0.1 molL(-1) NaOH solutions. Methyl viologen was used as redox mediator, while a platinum microelectrode was employed as the SECM tip. The metal films were electrodeposited ex situ from NaOH solutions containing either bismuth ions only or both bismuth and lead ions. Approach curves and SECM images indicated that the metal films were conductive and locally reactive with oxygen to provide Bi(3+) and Pb(2+) ions. The occurrence of the latter chemical reactions was verified by local anodic stripping voltammetry (ASV) at the substrate solution interface by using a mercury-coated platinum SECM tip. The latter types of measurements allowed also verifying that lead was not uniformly distributed onto the bismuth film electrode substrate. These findings were confirmed by scanning electron microscopy images. The surface heterogeneity produced during the metal deposition process, however, did not affect the analytical performance of the bismuth coated gold electrode in anodic stripping voltammetry for the determination of lead in alkaline media, even in aerated aqueous solutions. Under the latter conditions, stripping peak currents proportional to lead concentration with a satisfactory reproducibility (within 5% RSD) were obtained.