Influence of specimens' design and manufacturing process on microtensile bond strength to enamel: laboratory and FEA comparison

This study evaluated the effect of specimens' design and manufacturing process on microtensile bond strength, internal stress distributions (Finite Element Analysis - FEA) and specimens' integrity by means of Scanning Electron Microscopy (SEM) and Laser Scanning Confocal Microscopy (LCM). Excite was applied to flat enamel surface and a resin composite build-ups were made incrementally with 1-mm increments of Tetric Ceram. Teeth were cut using a diamond disc or a diamond wire, obtaining 0.8 mm² stick-shaped specimens, or were shaped with a Micro Specimen Former, obtaining dumbbell-shaped specimens (n = 10). Samples were randomly selected for SEM and LCM analysis. Remaining samples underwent microtensile test, and results were analyzed with ANOVA and Tukey test. FEA dumbbell-shaped model resulted in a more homogeneous stress distribution. Nonetheless, they failed under lower bond strengths (21.83 ± 5.44 MPa)c than stick-shaped specimens (sectioned with wire: 42.93 ± 4.77 MPaª; sectioned with disc: 36.62 ± 3.63 MPa b), due to geometric irregularities related to manufacturing process, as noted in microscopic analyzes. It could be concluded that stick-shaped, nontrimmed specimens, sectioned with diamond wire, are preferred for enamel specimens as they can be prepared in a less destructive, easier, and more precise way.

Determination of the minimum value of the safety factor from geodesic Alfven eigenmodes in Joint European Torus

An analysis of the experimental conditions under which low-frequency (70-150 kHz) Alfven eigertmodes (AE) are excited during the monster sawtooth in Joint European Torus [F Romanelli et al, Proceedings of the 22nd IAEA Fusion Energy Conference, Geneva, Switzerland, 2008] is presented for the specific case of a discharge with ion cyclotron heating (5 MW) Using a simplified AE model for modes excited at the Alfven wave continuum maximum with geodesic corrections taken into account, the temporal evolution of the value of the safety factor q(0) at the magnetic axis is determined We describe a new scheme to determine the time variation of q(0) that works under conditions in which other standard diagnostics, such as the motional Stark effect do not give reliable results such as during a monster sawtooth [doi 10 1063/1 3494212]

A geometrical approach of 3-D FEA for educational purposes applied to electrostatic fields

A geometrical approach of the finite-element analysis applied to electrostatic fields is presented. This approach is particularly well adapted to teaching Finite Elements in Electrical Engineering courses at undergraduate level. The procedure leads to the same system of algebraic equations as that derived by classical approaches, such as variational principle or weighted residuals for nodal elements with plane symmetry. It is shown that the extension of the original procedure to three dimensions is straightforward, provided the domain be meshed in first-order tetrahedral elements. The element matrices are derived by applying Maxwell`s equations in integral form to suitably chosen surfaces in the finite-element mesh.

The suitability of different FEA models for studying root fractures caused by wedge effect

Finite element analysis (FEA) utilizing models with different levels of complexity are found in the literature to study the tendency to vertical root fracture caused by post intrusion (""wedge effect""). The objective of this investigation was to verify if some simplifications used in bi-dimensional FEA models are acceptable regarding the analysis of stresses caused by wedge effect. Three plane strain (PS) and two axisymmtric (Axi) models were studied. One PS model represented the apical third of the root entirely, in dentin (PS-nG). The other models included gutta-percha in the apical third, and differed regarding dentin-post relationship: bonded (PS-B and Axi-B) or nonbonded (PS-nB and Axi-nB). Mesh discretization and material properties were similar for all cases. Maximum principal stress (sigma(max)) was analyzed as a response to a 165 N longitudinal load. Stress magnitude and orientation varied widely (PS-nG: 10.3 MPa; PS-B: 0.8 MPa; PS-nB: 10.4 MPa; Axi-13: 0.2 MPa, Axi-nB: 10.8 MPa). Axi-nB was the only model where all (sigma(max) vectors at the apical third were perpendicular to the model plane. Therefore, it is adequate to demonstrate the tendency to vertical root fractures caused by wedge effect. Axi-13 showed only part of the (sigma(max) perpendicular to the model plane while PS models showed sigma(max) on the model plane. In these models, sigma(max) orientation did not represent a situation where vertical root fracture would occur due to wedge effect. Adhesion between post and dentin significantly reduced (c) 2007 Wiley Periodicals, Inc.

Descentralização e financiamento da educação brasileira: uma análise comparativa, 1930-1964

Entre 1930 e 1964, um período de rápido crescimento econômico no Brasil, a expansão do ensino primário foi muito aquém do suficiente para superar o relativo atraso educacional. Este artigo sustenta não apenas que houve pouco interesse dos governos, como também que a estrutura administrativa e de financiamento da educação primária foi também responsável pela manutenção do atraso. A administração do ensino primário era de responsabilidade estadual, mas o governo federal, que detinha grande parte da receita tributária, não financiava adequadamente os estados. A comparação com o caso dos Estados Unidos parece apoiar as conclusões desse trabalho.

Trade unions and the economic performance of brazilian establishments

Este artigo analisa, pela primeira vez na literatura, o impacto dos sindicatos de trabalhadores em vários indicadores de desempenho econômico de firmas industriais brasileiras. Realizou-se uma pesquisa retrospectiva sobre a densidade sindical de 1000 estabelecimentos industriais brasileiros e seus resultados foram combinados aos indicadores de desempenho econômico da Pesquisa Industrial Anual (PIA) de 1990 a 2000. Os resultados indicam que a relação entre a densidade sindical na firma e seus salários, emprego e produtividade, é não-linear, ou seja, um aumento no grau de sindicalização leva a um melhor desempenho, porém a taxas decrescentes. Observou-se, também, uma relação negativa entre sindicalização e rentabilidade. Finalmente, estabelecimentos que introduziram mecanismos de 'participação nos lucros' aumentaram sua produtividade e rentabilidade no período e pagaram maiores salários nas firmas onde o grau de sindicalização era maior.

Aspectos estratégicos e econômicos da política de bonificação em quantidade de produto

ste trabalho objetiva identificar a percepção dos gestores de controladoria de indústrias sobre os aspectos estratégicos e econômicos da decisão de bonificação em quantidade de produto. A premissa é que os resultados econômicos gerados pela decisão de desconto no preço e de bonificação em quantidade de produto são iguais, considerando a mesma quantidade de produto entregue ao cliente. Com base no banco de dados da FIPECAFI- FEA-USP, analisaram-se 91 questionários encaminhados a controllers atuantes em diversos setores. Os resultados revelam: 1) um número muito significativo de empresas da amostra selecionada adota a bonificação em produtos; 2) a área comercial é a principal responsável por essa decisão; e 3) identificação da percepção dos controllers sobre aspectos decisórios de bonificação em quantidade de produtos.

Failure analysis of low velocity impact on thin composite laminates: Experimental and numerical approaches

The dynamic behavior of composite laminates is very complex because there are many concurrent phenomena during composite laminate failure under impact load. Fiber breakage, delaminations, matrix cracking, plastic deformations due to contact and large displacements are some effects which should be considered when a structure made from composite material is impacted by a foreign object. Thus, an investigation of the low velocity impact on laminated composite thin disks of epoxy resin reinforced by carbon fiber is presented. The influence of stacking sequence and energy impact was investigated using load-time histories, displacement-time histories and energy-time histories as well as images from NDE. Indentation tests results were compared to dynamic results, verifying the inertia effects when thin composite laminate was impacted by foreign object with low velocity. Finite element analysis (FEA) was developed, using Hill`s model and material models implemented by UMAT (User Material Subroutine) into software ABAQUS (TM), in order to simulate the failure mechanisms under indentation tests. (C) 2007 Elsevier Ltd. All rights reserved.

Power Factor Calculation by the Finite Element Method

The use of finite element analysis (FEA) to design electrical motors has increased significantly in the past few years due the increasingly better performance of modern computers. Even though the analytical software remains the most used tool, the FEA is widely used to refine the analysis and gives the final design to be prototyped. The power factor, a standard data of motor manufactures data sheet is important because it shows how much reactive power is consumed by the motor. This data becomes important when the motor is connected to network. However, the calculation of power factor is not an easy task. Due to the saturation phenomena the input motor current has a high level of harmonics that cannot be neglected. In this work the FEA is used to evaluate a proposed (not limitative) methodology to estimate the power factor or displacement factor of a small single-phase induction motor. Results of simulations and test are compared.

Toward Optimal Design of Piezoelectric Transducers Based on Multifunctional and Smoothly Graded Hybrid Material Systems

This work explores the design of piezoelectric transducers based on functional material gradation, here named functionally graded piezoelectric transducer (FGPT). Depending on the applications, FGPTs must achieve several goals, which are essentially related to the transducer resonance frequency, vibration modes, and excitation strength at specific resonance frequencies. Several approaches can be used to achieve these goals; however, this work focuses on finding the optimal material gradation of FGPTs by means of topology optimization. Three objective functions are proposed: (i) to obtain the FGPT optimal material gradation for maximizing specified resonance frequencies; (ii) to design piezoelectric resonators, thus, the optimal material gradation is found for achieving desirable eigenvalues and eigenmodes; and (iii) to find the optimal material distribution of FGPTs, which maximizes specified excitation strength. To track the desirable vibration mode, a mode-tracking method utilizing the `modal assurance criterion` is applied. The continuous change of piezoelectric, dielectric, and elastic properties is achieved by using the graded finite element concept. The optimization algorithm is constructed based on sequential linear programming, and the concept of continuum approximation of material distribution. To illustrate the method, 2D FGPTs are designed for each objective function. In addition, the FGPT performance is compared with the non-FGPT one.

Tailoring vibration mode shapes using topology optimization and functionally graded material concepts

Tailoring specified vibration modes is a requirement for designing piezoelectric devices aimed at dynamic-type applications. A technique for designing the shape of specified vibration modes is the topology optimization method (TOM) which finds an optimum material distribution inside a design domain to obtain a structure that vibrates according to specified eigenfrequencies and eigenmodes. Nevertheless, when the TOM is applied to dynamic problems, the well-known grayscale or intermediate material problem arises which can invalidate the post-processing of the optimal result. Thus, a more natural way for solving dynamic problems using TOM is to allow intermediate material values. This idea leads to the functionally graded material (FGM) concept. In fact, FGMs are materials whose properties and microstructure continuously change along a specific direction. Therefore, in this paper, an approach is presented for tailoring user-defined vibration modes, by applying the TOM and FGM concepts to design functionally graded piezoelectric transducers (FGPT) and non-piezoelectric structures (functionally graded structures-FGS) in order to achieve maximum and/or minimum vibration amplitudes at certain points of the structure, by simultaneously finding the topology and material gradation function. The optimization problem is solved by using sequential linear programming. Two-dimensional results are presented to illustrate the method.

Bending fatigue of stainless steel shear pins belonging to a hydroelectric plant

Coaracy Nunes was the first hydroelectric power plant in the Amazon region, being located in Araguari River, Amapa State, Brazil. The plant operates since 1976, presenting now a nominal capacity of 78 MW. The shear pins, which are installed in the turbine hydraulic arms to control the wicket gate and regulate the water flow into the turbine blades, suffered several breakdowns since 2004. These shear pins are made of an ASTM 410 stainless steel and were designed to break by a shear overload of 120 kN. Fractographic investigation of the pins, however, revealed two types of fracture topographies: a region of stable crack propagation area, with non-pronounced striation and secondary cracks; and a region of unstable propagation, featuring elongated dimples. These results indicated that the stable crack propagation occurred by fatigue (bidirectional bending), which was nucleated at machining marks under high nominal load. Finite element analysis was carried out using two loading conditions (pure shear and a combination of shear and bending) and the results indicated that the presence of a bending stress strongly increased the stress concentration factor (85% rise in the shear stress and 130% rise in the Von Mises stress). Misalignment during shear pins assembly associated with vibration might have promoted the premature failure of the shear by bending fatigue. (C) 2008 Elsevier Ltd. All rights reserved.

Brazilian Network of Food Data Systems and LATINFOODS Regional Technical Compilation Committee: Food composition activities (2006-2009)

The Brazilian Network of Food Data Systems (BRASILFOODS) has been keeping the Brazilian Food Composition Database-USP (TBCA-USP) (http://www.fcf.usp.br/tabela) since 1998. Besides the constant compilation, analysis and update work in the database, the network tries to innovate through the introduction of food information that may contribute to decrease the risk for non-transmissible chronic diseases, such as the profile of carbohydrates and flavonoids in foods. In 2008, data on carbohydrates, individually analyzed, of 112 foods, and 41 data related to the glycemic response produced by foods widely consumed in the country were included in the TBCA-USP. Data (773) about the different flavonoid subclasses of 197 Brazilian foods were compiled and the quality of each data was evaluated according to the USDAs data quality evaluation system. In 2007, BRASILFOODS/USP and INFOODS/FAO organized the 7th International Food Data Conference ""Food Composition and Biodiversity"". This conference was a unique opportunity for interaction between renowned researchers and participants from several countries and it allowed the discussion of aspects that may improve the food composition area. During the period, the LATINFOODS Regional Technical Compilation Committee and BRASILFOODS disseminated to Latin America the Form and Manual for Data Compilation, version 2009, ministered a Food Composition Data Compilation course and developed many activities related to data production and compilation. (C) 2010 Elsevier Inc. All rights reserved.

A critical view on biaxial and short-beam uniaxial flexural strength tests applied to resin composites using Weibull, fractographic and finite element analyses

Objective. To evaluate the biaxial and short-beam uniaxial strength tests applied to resin composites based upon their Weibull parameters, fractographic features and stress distribution. Methods. Disk- (15 mm x 1 mm) and beam-shaped specimens (10 mm x 2 mm x 1 mm) of three commercial composites (Concept/Vigodent, CA; Heliomolar/Ivoclar-Vivadent, HE; Z250/3M ESPE, FZ) were prepared. After 48h dry storage at 37 degrees C, disks and beams were submitted to piston-on-three-balls (BI) and three-point bending (UNI) tests, respectively. Data were analyzed by Weibull statistics. Fractured surfaces were observed under stereomicroscope and scanning electron microscope. Maximum principal stress (sigma(1)) distribution was determined by finite element analysis (FEA). Maximum sigma(1-BI) and sigma(1-UNI) were compared to FZ strengths calculated by applying the average failure loads to the analytical equations (sigma(a-BI) and sigma(a-UNI)). Results. For BI, characteristic strengths were: 169.9a (FZ), 122.4b (CA) and 104.8c (HE), and for UNI were: 160.3a (FZ), 98.2b (CA) and 91.6b (HE). Weibull moduli ( m) were similar within the same test. CA and HE presented statistically higher m for BI. Surface pores ( BI) and edge flaws ( UNI) were the most frequent fracture origins. sigma(1-BI) was 14% lower than sigma(a-BI.) sigma(1-UNI) was 43% higher than sigma(a-UNI). Significance. Compared to the short-beam uniaxial test, the biaxial test detected more differences among composites and displayed less data scattering for two of the tested materials. Also, biaxial strength was closer to the material`s strength estimated by FEA. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.