Production, microstructural characterization and mechanical properties of as-cast Ti-10Mo-xNb alloys

Beta titanium (Ti) alloys are one of the most promising groups of Ti alloys for biomedical applications. This work presents the production, microstructural characterization, and mechanical properties of as-cast Ti-10Mo-xNb (x = 0, 3, 6, 9, 20, and 30) alloys. They were produced via arc melting and characterized by scanning electron microscopy and X-ray diffraction. The density of each alloy was measured by the Archimedes method and the mechanical characterization was carried out by using the Vickers microhardness test and Young`s modulus measurements. The results show a near beta microstructure for niobium (Nb) contents lower or equal to 9 wt% while beta single-phase microstructure was obtained for higher Nb additions. The microhardness values decreased with the increase of Nb content in the alloys. The elastic modulus values of Ti-10Mo-3Nb and Ti-10Mo-20Nb alloys were lower than those of cp Ti and Ti-6Al-4V.

Efficacy and Tolerability of Lodenafil Carbonate for Oral Therapy in Erectile Dysfunction: A Phase II Clinical Trial

Oral treatment with phosphodiesterase type 5 inhibitor (PDE5) is considered the first-line treatment for patients with erectile dysfunction (ED). Lodenafil carbonate (LC) is a novel PDE5. This is a phase II, prospective, randomized, double-blind, and placebo controlled clinical trial of LC. Efficacy end points were International Index of Sexual Function (IIEF) erectile domain, IIEF questions 3 and 4, and Sexual Encounter Profile (SEP) questions 2 and 3, before and after the use of LC or placebo. Seventy-two men older than 18 years, with ED for at least 6 months with stable sexual relationship were enrolled. Patients were randomized to placebo or LC 80 mg, 40 mg, or 20 mg and followed for 4 weeks. IIEF erectile domain scores before and after the use of medications were (mean +/- standard deviation [SD]): placebo: 11.9 +/- 3.4 and 12.6 +/- 5.5; LC 20 mg: 15.8 +/- 4.1 and 18.9 +/- 6.6; LC 40 mg: 11.9 +/- 4.4 and 15.4 +/- 8.1; LC 80 mg: 14.2 +/- 4.7 and 22.8 +/- 6.0 (anova P < 0.01). The SEP-2 scores before and after the use of medications were (Mean +/- SD): placebo: 71.0 +/- 33.1 and 51.2 +/- 43.1; LC 20 mg 70.3 +/- 34.2 and 75.5 +/- 31.5; LC 40 mg: 48.4 +/- 42.1 and 60.8 +/- 42.5; LC 80 mg: 68.6 +/- 33.5 and 89.6 +/- 26.0. The SEP-3 scores were: placebo 23.3 +/- 27.6 and 33.6 +/- 42.3; LC 20 mg: 32.3 +/- 38.9 and 51.2 +/- 41.7; LC 40 mg: 39.7 +/- 44.7 and 46.7 +/- 41.1; LC 80 mg* 17.2 +/- 29.5 and 74.3 +/- 36.4 (*P < 0.05 for difference to placebo). The drug was well tolerated. Adverse reactions were mild and self-limited and included headache, rhinitis, flushing, color visual disorders, and dyspepsia. This study showed that the dosage of 80 mg of LC was significantly more efficacious than placebo and well tolerated. Glina S, Toscano I, Gomatzky C, de Goes PM, Junior AN, de Almeida Claro JF, and Pagani E. Efficacy and tolerability of lodenafil carbonate for oral therapy in erectile dysfunction: A phase II clinical trial. J Sex Med 2009;6:553-557.

Comparison between multislice and cone-beam computerized tomography in the volumetric assessment of cleft palate

The aim of this study was to determine the applicability of multislice and cone-beam computerized tomography (CT) in the assessment of bone defects in patients with oral clefts. Bone defects were produced in 9 dry skulls to mimic oral clefts. All defects were modeled with wax. The skulls were submitted to multislice and cone-beam CT. Subsequently, physical measurements were obtained by the Archimedes principle of water displacement of wax models. The results demonstrated that multislice and cone-beam CT showed a high efficiency rate and were considered to be effective for volumetric assessment of bone defects. It was also observed that both CT modalities showed excellent results with high reliability in the study of the volume of bone defects, with no difference in performance between them. The clinical applicability of our research has shown these CT modalities to be immediate and direct, and they is important for the diagnosis and therapeutic process of patients with oral cleft. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011; 112: 249-257)

Effect of temperature and heating rate on the sintering of leucite-based dental porcelains

The aim of this work was to determine the effect of temperature and heating rate on the densification of four leucite-based dental porcelains: two low-fusion (Dentsply Ceramco and Ivoclar) and two high-fusion commercial porcelains (Dentsply Ceramco). Porcelain powders were characterized by differential thermal analysis (DTA), X-ray diffraction (XRD), particle size distribution, helium picnometry, and by scanning electron microscopy. Test specimens were sintered from 600 to 1050 degrees C, with heating rates of 55 degrees C/min and 10 degrees C/min. The bulk density of the specimens was measured by the Archimedes method in water, and microstructures of fracture surfaces were analyzed by scanning electron microscopy (SEM). The results showed that densification of specimens increased with the increase in temperature. The increase in the heating rate had no effect on the densification of the porcelains studied. Both high-fusion materials and one of the low-fusing porcelains reached the maximum densification at a temperature that was 50 degrees C lower than that recommended by the manufactures. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Tailoring of physical properties in highly filled experimental nanohybrid resin composites

Objectives. To assess the elastic modulus (EM), volumetric shrinkage (VS), and polymerization shrinkage stress (PSS) of experimental highly filled nanohybrid composites as a function of matrix composition, filler distribution, and density. Methods. One regular viscosity nanohybrid composite (Grandio, VOCO, Germany) and one flowable nanohybrid composite (Grandio Flow, VOCO) were tested as references along with six highly filled experimental nanohybrid composites (four Bis-GMA-based, one UDMA-based, and one Ormocer (R) -based). The experimental composites varied in filler size and density. EM values were obtained from the ""three-point bending"" load-displacement curve. VS was calculated with Archimedes` buoyancy principle. PSS was determined in 1-mm thick specimens placed between two (poly) methyl methacrylate rods (empty set = 6 mm) attached to an universal testing machine. Data were analyzed using oneway ANOVA, Tukey`s test (alpha = 0.05), and linear regression analyses. Results. The flowable composite exhibited the highest VS and PSS but lowest EM. The PSS was significantly lower with Ormocer. The EM was significantly higher among experimental composites with highest filler levels. No significant differences were found between all other experimental composites regarding VS and PSS. Filler density and size did not influence EM, VS, or PSS. Significance. Neither the filler configuration nor matrix composition in the investigated materials significantly influenced composite shrinkage and mechanical properties. The highest filled experimental composite seemed to increase EM by keeping VS and PSS low; however, matrix composition seemed to be the determinant factor for shrinkage and stress development. The Ormocer, with reduced PSS, deserves further investigation. Filler size and density did not influence the tested parameters. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.