Chemical characterization of a high nitrogen stainless steel by optimized electron probe microanalysis

The distribution of Cr and N in a high-temperature gas-nitrided stainless steel was measured by using a scanning electron microscope-coupled wavelength-dispersive X-ray spectrometer and the results were related to the microhardness profile of the hardened case. The experimental spectrometric procedure was optimized to consistently measure N contents varying between 0.1 and 0.8 wt.% in martensite and between 18.3 and 21.6 wt.% in nitrides, as well as Cr contents ranging from 11.5 to 17.0 wt.%. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Assessment of the cavitation erosion resistance in high nitrogen austenitic stainless steels: study of the wear mechanisms

Specimens of a UNS S31803 steel were submitted to high temperature gas nitriding and then to vibratory pitting wear tests. Nitrided samples displayed fully austenitic microstructures and 0.9 wt. % nitrogen contents. Prior to pitting tests, sample texture was characterized by electron backscattering diffraction, EBSD. Later on, the samples were tested in a vibratory pit testing equipment using distilled water Pitting tests were periodically interrupted to evaluate mass loss and to characterize the surface wear by SEM observations. At earlier pit erosion, stages intense and highly heterogeneous plastic deformation inside individual grains was observed. Later on, after the incubation period, mass loss by debris detachment was observed. Initial debris micro fracturing was addressed to low cycle fatigue. Damage started at both sites, inside the grains and grain boundaries. The twin boundaries were the most prone to mass-loss incubation. Grains with (101) planes oriented near parallel to the sample surface displayed higher wear resistance than grains with other textures. This was attributed to lower resolved stresses for plastic deformation inside the grains with (101)

High temperature flexural strength and fracture toughness of AlN with Y(2)O(3) ceramic

The effects of temperature on the fast fracture behavior of aluminum nitride with 5 wt% Y(2)O(3) ceramic were investigated. Four-point flexural strength and fracture toughness were measured in air at several temperatures (30-1,300 A degrees C). The flexural strength gradually decreased with the increase of temperature up to 1,000 A degrees C due to the change in the fracture mode from transgranular to intergranular, and then became almost constant up to 1,300 A degrees C. Two main flaw types as fracture origin were identified: small surface flaw and large pores. The volume fraction of the large pores was only 0.01%; however, they limited the strength on about 50% of the specimens. The fracture toughness decreased slightly up to 800 A degrees C controlled by the elastic modulus change, and then decreased significantly at 1,000 A degrees C due to the decrease in the grain-boundary toughness. Above 1,000 A degrees C, the fracture toughness increased significantly, and at 1,300 A degrees C, its value was close to that measured at room temperature.

High Carbon Ferro-Chromium by Self-Reducing Process

This paper discusses the effects of temperature, addition of ferro-silicon and fluxing agents for the production of high carbon ferro-chromium by self-reducing process. The use of self-reducing agglomerates for ferro-alloys production is becoming an emerging processing technology due to lowering the electric energy consumption and improving the metal recovery in comparison with traditional ones. The self-reducing pellets were composed by chromite, petroleum coke, cement and small (0.1% - 2%) addition of ferro-silicon. The slag composition was adjusted by addition of fluxing agents. The reduction of pellets was carried out at 1773K (1500 degrees C), 1823K (1550 degrees C) and 1873K (1600 degrees C) by using induction furnace. The products obtained, containing slag and metallic phases, were analyzed by scanning electron microscopy and chemical analyses (XEDS). By increasing temperature from 1773K to 1823K large effect on the reduction time was observed. It decreased from 30 minutes to 10 minutes, for reaching around 0.98 reduction fraction. No significant effect on reduction time was observed when the reduction temperature was increased from 1823K to 1873K. At 1773K, the addition of 2% of ferro-silicon in the pellet resulted in an increasing reaction rate of around 6 times, in comparison with agglomerate without this addition. The addition of fluxing agents (silica and hydrated lime) has effect on reduction time (inverse relationship) and the pellets become less porous after reduction.

Mesoscale plasticity anisotropy at the earliest stages of cavitation-erosion damage of a high nitrogen austenitic stainless steel

A high nitrogen austenitic stainless steel (0.9wt% N) and an ordinary 304 austenitic stainless steel were submitted to cavitation-erosion tests in a vibratory apparatus operating at a frequency of 20 kHz. The high nitrogen stainless steel was obtained by high temperature gas nitriding a 1-mm thick strip of an UNS 31803 duplex stainless steel. The 304 austenitic stainless steel was used for comparison purposes. The specimens were characterized by scanning electron microscopy and Electron Back Scatter Diffraction. The surface of the cavitation damaged specimens was analyzed trying to find out the regions where cavitation damage occurred preferentially. The distribution of sites where cavitation inception occurred was extremely heterogeneous, concentrating basically at (i) slip lines inside some grains and (ii) Sigma-3 coincidence site lattice (CSL) boundaries (twin boundaries). Furthermore, it was observed that the CE damage spread faster inside those grains which were more susceptible to damage incubation. The damage heterogeneity was addressed to plasticity anisotropy. Grains in which the crystallographic orientation leads to high resolved shear stress show intense damage at slip lines. Grain boundaries between grains with large differences in resolved shear stress where also intensely damaged. The relationship between crystallite orientation distributions, plasticity anisotropy and CE damage mechanisms are discussed. (C) 2009 Elsevier B.V. All rights reserved.

High-resolution transmission electron microscopy and electron backscatter diffraction in nanoscaled ferritic and ferritic-martensitic oxide dispersion strengthened-steels

For specific blanket and divertor applications in future fusion power reactors a replacement of presently considered reduced activation ferritic martensitic (RAFM) steels as a structural material by suitable oxide dispersion strengthened ferritic martensitic steels would allow a substantial increase of the operating temperature from similar to 823 to about 923 K. Due to this reason the RAFM-alloy ODS-Eurofer has already been developed and produced with industrial partners. In the He-cooled modular divertor concept, where temperatures above 923 K will arise, an ODS-steel with a purely ferritic matrix is advantageous, because of missing phase transitions. Due to this reason, a special ferritic ODS-steel is being manufactured as well. In this work the microstructures of these two ODS-alloy types, analysed mainly by high resolution TEM are compared, with respect to different manufacturing processes. In addition first results of high resolution EBSD scans together with determined orientation maps of the RAFM steel ODS-Eurofer will also be presented. (C) 2008 Elsevier B.V. All rights reserved.

Numerical modeling of ductile crack extension in high pressure pipelines with longitudinal flaws

This study examines the applicability of a micromechanics approach based upon the computational cell methodology incorporating the Gurson-Tvergaard (GT) model and the CTOA criterion to describe ductile crack extension of longitudinal crack-like defects in high pressure pipeline steels. A central focus is to gain additional insight into the effectiveness and limitations of both approaches to describe crack growth response and to predict the burst pressure for the tested cracked pipes. A verification study conducted on burst testing of large-diameter, precracked pipe specimens with varying crack depth to thickness ratio (a/t) shows the potential predictive capability of the cell approach even though both the CT model and the CTOA criterion appear to depend on defect geometry. Overall, the results presented here lend additional support for further developments in the cell methodology as a valid engineering tool for integrity assessments of pipelines with axial defects. (C) 2011 Elsevier Ltd. All rights reserved,

Influence of substrate surface topography in the deposition of nanostructured diamond-like carbon films by high density plasma chemical vapor deposition

In this work, we have studied the influence of the substrate surface condition on the roughness and the structure of the nanostructured DLC films deposited by High Density Plasma Chemical Vapor Deposition. Four methods were used to modify the silicon wafers surface before starting the deposition processes of the nanostructured DLC films: micro-diamond powder dispersion, micro-graphite powder dispersion, and roughness generation by wet chemical etching and roughness generation by plasma etching. The reference wafer was only submitted to a chemical cleaning. It was possible to see that the final roughness and the sp(3) hybridization degree strongly depend on the substrate surface conditions. The surface roughness was observed by AFM and SEM and the hybridization degree of the DLC films was analyzed by Raman Spectroscopy. In these samples, the final roughness and the sp(3) hybridization quantity depend strongly on the substrate surface condition. Thus, the effects of the substrate surface on the DLC film structure were confirmed. These phenomena can be explained by the fact that the locally higher surface energy and the sharp edges may induce local defects promoting the nanostructured characteristics in the DLC films. (C) 2008 Elsevier B.V. All rights reserved.

Porous silicon optical cavity structure applied to high sensitivity organic solvent sensor

The present work reports the thermal annealing process, the number of layer and electrochemical process effect in the optical response quality of Bragg and microcavity devices that were applied as organic solvent sensors. These devices have been obtained by using porous silicon (PS) technology. The optical characterization of the Bragg reflector, before annealing, showed a broad photonic band-gap structure with blue shifted and narrowed after annealing process. The electrochemical process used to obtain the PS-based device imposes the limit in the number of layers because of the chemical dissolution effect. The interface roughness minimizations in the devices have been achieved by using the double electrochemical cell setup. The microcavity devices showed to have a good sensibility for organic solvent detection. The thermal annealed device showed better sensibility feature and this result was attributed to passivation of the surface devices. (c) 2007 Elsevier Ltd. All rights reserved.

Improved moisture and hydrocarbons barrier of epoxy resin-based coating

To improve the surface characteristics of epoxy resin coatings, a treatment by fluorine-containing plasma was used to develop a coating with low surface free energy and improved chemical resistance. Through the coating analysis it was possible to verify information about the CF(n) bond formation and the fluorination depth. The best plasma process parameters presented the best fluorination depth, 90 nm, and fluorine concentration was nearly 30%. The improvement in contact angle of water was 50% and of raw petroleum was 130%. Salt spray test proves that the coating fluorination decreases the chance of substrate corrosion.

High frequency tendon reflexes in the human soleus muscle

Tendon reflexes have been often used in studies of the human nervous system in health and disease. They have been investigated either in response to single tendon taps or to long duration vibrations. Tendon reflexes are described here in response to a high frequency vibration burst (3 cycles of a 100 Hz sine wave) applied to the Achilles tendon of standing subjects, either in quiet stance or during a forward leaning posture. The electromyogram from the soleus muscle usually showed three components separated by 10 ms which were interpreted as being three reflexes, each reflex induced by each of the three cycles in a burst. This result indicates that soleus tendon reflexes can respond in fast succession in a phasic manner when a brief high frequency vibration is applied to the Achilles tendon. This occurs in spite of possible depression of the la to motoneuron synapses and the long after hyperpolarization of the motoneurons. An interpretation of the results is that motoneurons from different subsets of the motoneuron pool respond to different cycles of the sinusoidal vibratory burst. (c) 2008 Elsevier Ireland Ltd. All rights reserved.

Sensory Stability of Ultra-High Temperature Milk in Polyethylene Bottle

The objective of this study was to evaluate the sensory stability of ultra-high temperature (UHT) milk subjected to different heat treatments and stored at room temperature in white high density polyethylene bottles (HDPE) pigmented with titanium dioxide. Two lots of 300 units each were processed, respectively, at 135 and 141 degrees C/10 s using indirect heating and subsequently aseptically filled in an ISO class 7 clean room. These experimental lots were evaluated for appearance, aroma, flavor, and overall appreciation and compared to samples of commercial UHT milk purchased from local commercial stores. The time-temperature combinations investigated did not affect either the acceptability or the shelf life of the milk. Despite the limited light barrier properties of HDPE bottles, the product contained in the package tested exhibited good stability, with a shelf life ranging from 4 to 11 wk. Within this time period, the acceptability of the experimental lots was similar to that of the commercial products. The results achieved in this study contribute to turn the low-cost UHT system investigated into a technically viable option for small-size dairy processing plants.

The synergism between high superficial roughness and corrosive atmosphere in the fatigue behavior of the SAE 1045 steel

The fatigue behavior of the SAE 1045 steel in four different conditions is reported in this paper. Four treatments were tested: polished surface, corrosive atmosphere (sugar cane juice), low quality roughness (typical equivalent surface of the shaft cane mill) and the combined condition of the two last treatments involved. Fatigue tests were performed in rotating bending conditions and the values of fatigue strength for the different situations from tests were obtained. The diminution in fatigue strength for the synergy condition of rough surface and corrosive atmosphere was of 8.7%, result statistically representative with less than 0.01% of uncertainty.

Toward sustainable soil and water resources use in China`s highly erodible semi-arid loess plateau

The water-wind crisscross region of the Loess Plateau in China is comprised of 17.8 million hectares of highly erodible soil under limited annual rainfall. This requires a sustainable water balance for the restoration of dryland ecosystems to reduce and manage soil erosion. In this region, alfalfa has been one of the main legumes grown to minimize soil erosion. However, alfalfa yields were significantly lower in years of reduced rainfall suggesting that high water use and deep rooting alfalfa make it an unsustainable crop due to the long-term decline in soil water storage and productivity. Our objectives in this Study were to evaluate the soil water balance of Loess Plateau soils during vegetative restoration and to evaluate practices that prevent soil desiccation and promote ecosystem restoration and sustainability. Field observations of soil moisture recovery and soil erosion were carried out for five years after alfalfa was replaced with different crops and with bare soil. Soil water content changes in cropland, rangeland, and bare soil were tracked over several years, using a water balance approach. Results indicate that growing forages significantly reduced runoff and sediment transport. A forage-food-crop rotation is a better choice than other cropping systems for achieving sustainable productivity and preventing soil erosion and desiccation. However, economic considerations have prevented its widespread adoption by local farmers. Alternatively, this study recommends consideration of grassland crops or forest ecosystems to provide a sustainable water balance in the Loess Plateau of China. (C) 2009 Elsevier B.V. All rights reserved.

Changes in wood-water relationship due to heat treatment assessed on micro-samples of three Eucalyptus species

Wood-water relationship of untreated and heat-treated wood was studied. Specimens of Eucalyptus grandis, E saligna, and E citriodora were submitted to five conditions of heat treatment: 180 degrees C and 220 degrees C with air; 220 degrees C, 250 degrees C, and 280 degrees C with N(2). The wood-water relationships were accurately studied in a special device, in which the moisture content (MC) of the sample was measured with a highly sensitive electronic microbalance placed in a climatic chamber. The dimensions of the sample were collected continuously without contact by means of two high-speed laser scan micrometers. Sorption curves and shrinkage-MC relationships were observed. To study the effects of heat treatment, the following parameters were also determined: fiber saturation point (FPS), wood anisotropy (T/R ratio), shrinkage slope, reduction in hygroscopicity, and anti-shrink efficiency (ASE). The physical properties were significantly affected only at 220 degrees C and above. At heat temperature levels higher than 220 degrees C, the reduction in hygroscopicity and ASE are higher than 40% and continue to be reduced with increasing temperature level. This work also demonstrates that heat treatment does not change the slope of the curves shrinkage vs. MC, proving that heat treatment affects the domain of alterations in wood properties, but not the behavior within this domain.