Evaluation of the physical and chemical properties of two commercial and three experimental root-end filling materials

Objective. The aim of this study was to evaluate the pH, calcium release, setting time, and solubility of two commercially available mineral trioxide aggregate (MTA) cements (white MTA Angelus and MTA Bio), and of three experimental cements (light-cured MTA, Portland cement with 20% bismuth oxide and 5% calcium sulfate, and an epoxy resin-based cement). Study design. For evaluation of pH and calcium ion release, polyethylene tubes with 1.0 mm internal diameter and 10.0 mm length were filled with the cements and immediately immersed in flasks containing 10 mL deionized water. After 3, 24, 72, and 168 hours, the tubes were removed and the water from the previous container was measured for its pH and calcium content with a pH meter and an atomic absorption spectrophotometer. For analysis of the setting time, Gilmore needles weighing 100 g and 456.5 g were used, in accordance with the American Society for Testing and Materials specification no. C266-03. Solubility of each cement was also tested. Results. All the cements were alkaline and released calcium ions, with a declining trend over time. After 3 hours, Portland cement + bismuth oxide and MTA Bio had the highest pH and light-cured MTA the lowest. After 1 week, MTA Bio had the highest pH and light-cured MTA and epoxy resin-based cement the lowest. Regarding calcium ion release, after 3 hours, Portland cement + bismuth oxide showed the highest release. After 1 week, MTA Bio had the highest. Epoxy resin-based cement and light-cured MTA had the lowest calcium release in all evaluation periods. Regarding setting times, white MTA Angelus and MTA Bio had the shortest, Portland cement + bismuth oxide had an intermediate setting time, and the epoxy resin-based cement had the longest. The materials that showed the lowest solubility values were the epoxy resin-based cement, Portland cement + bismuth oxide, and light-cured MTA. The highest solubility values were presented in white MTA Angelus and MTA Bio. Conclusions. The white MTA Angelus and MTA Bio had the shortest setting times, higher pH and calcium ion release, and the highest solubility. In contrast, the epoxy resin-based cement and light-cured MTA showed lower values of solubility, pH, and calcium ion release. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010; 110: 250-256)

Evaluation of the radiopacity of some commercial and experimental root-end filling materials

Objective. The aim of the present study was to evaluate the radiopacity of 5 root end filling materials (white MTA Angelus, MTA Bio, light-cured MTA, Sealepox RP, and Portland cement clinker with bismuth oxide and calcium sulfate). Method. Five specimens, 10 mm in diameter and 1 mm in thickness according to specification ISO 6876: 2001 were fabricated from each material and radiographed using Insigth occlusal films close to a graduated aluminum step-wedge (2 to 16 mm in thickness). Radiographs were digitized and compared to the aluminum step-wedge. The radiographic density data were converted into millimeters of aluminum (mm Al), using the Digora 1.51 software. Results were evaluated statistically using the analysis of variance (ANOVA) followed by Tukey test. The level of significance was set at 5% (P<.05%). Results. Radiopacity values ranged from 1.21 mm Al (light-cured MTA) to 6.45 mm Al (MTA Angelus). Comparison between materials showed significant difference (P<.05) between MTA Angelus and all other materials, between Sealepox RP and MTA Bio, and between light-cured MTA and Portland cement clinker. Light-cured MTA was significantly less radiopaque than all other materials. No significant difference (P>.05) was found between MTA Bio and Portland cement clinker. Conclusions. All retrograde filling materials evaluated showed greater radiopacity than dentin. All the materials, except light-cured MTA met the minimum radiopacity standards of 3 mm Al recognized by the ISO 6876: 2001 and ADA n.57. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e35-e38)

Evaluation of pH and Calcium Ion Release of Root-end Filling Materials Containing Calcium Hydroxide or Mineral Trioxide Aggregate

Introduction: To evaluate calcium ion release and pH of Sealer 26 (S26) (Dentsply, Rio de Janeiro, RJ, Brazil), white mineral trioxide aggregate (MTA), Endo CPM Sealer (CPM1) (EGEO SRL Bajo licencia MTM Argentina SA, Buenos Aires, Argentina), Endo CPM Sealer in a thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE). Methods: Material samples (n = 10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 3, 6,12,24, and 48 hours and 7,14, and 28 days, the water pH was determined with a pH meter, and calcium release was assessed by atomic absorption spectrophotometry. An empty tube was used as the control group. Results: The control group presented a pH value of 6.9 at all studied periods and did not show the presence of calcium ion. S26 presented greater hydroxyl ion release up to 12 hours (p < 0.05). From 24 hours until 28 days, S26, MTA, CPM1, and CPM2 had similar results. in ail periods, ZOE presented the lowest hydroxyl ion release. CPM1, followed by CPM2, released the most calcium ions until 24 hours (p < 0.05). Between 48 hours and 7 days, CPM1 and CPM2 had the highest release. A greater calcium ion release was observed for CPM2, followed by CPM1 at 14 days and for S26, CPM1, and CPM2 at 28 days. ZOE released the least calcium ions in all periods. Conclusion: Sealer 26, MTA, and Endo CPM sealer at normal or thicker consistency release hydroxyl and calcium ions. Endo CPM sealer may be an alternative as root-end filling material. (J Endod 2009;35:1418-1421)

Evaluation of pH and calcium ion release of new root-end filling materials

Objective. The purpose of this study was to evaluate the pH and calcium ion release of 6 materials used for root-end filling and perforation repair. Study design. Gray ProRoot MTA, gray MTA-Angelus, white MTA-Angelus, and CPM were compared to 2 experimental ones: MTA-exp, also based in Portland cement with a modified mixing liquid, and MBPc, an epoxy-resin based cement containing calcium hydroxide. After 3, 24, 72, and 168 hours the water in which each sample had been immersed was tested to determine the ph and calcium ion release. Results. All the analyzed materials showed alkaline pH and capacity to release calcium ions; however, a tendency of reduction of these characteristics was noted for all the analyzed materials, except for the MBPc, which showed a slight increase of pH among the 3 initial periods. Conclusion. The results suggest that all materials investigated presented alkaline pH and ability of release of calcium ions. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: 135-139)

Mineral trioxide aggregate with or without calcium chloride in pulpotomy

The aim of this study was to evaluate the reaction of the pulp tissue against mineral trioxide aggregate (MTA) with or without 10% calcium chloride (CaCl2). Pulpotomies were performed in 4 canines and 8 premolars of two 8-month-old dogs. MTA with or without CaCl2 was applied on the pulp tissue. The animals were killed after 90 days, and the specimens were processed for the microscopic analysis. Pulp tissue response was similar for MTA with and without CaCl2 Pulp vitality was present in all specimens, along with pulp repair with formation of mineralized tissue bridging. The addition of CaCl2 to MTA did not change its biologic properties in formation of mineralized barrier after pulpotomy.

Radiopacity Evaluation of Calcium Aluminate Cement Containing Different Radiopacifying Agents

Introduction: The aim of this study was to evaluate the radiopacity of calcium aluminate cement (Endo Binder) with 3 different radiopacifiers (bismuth oxide, zinc oxide, or zirconium oxide) in comparison with gray mineral trioxide aggregate (GMTA), white MTA, and dental structures (enamel and dentin). Methods: Eighteen test specimens of each cement with thicknesses of 0.5, 1.0, 1.5, 2.0, 2.5, and 3.0 mm (n = 3) were made by using a stainless steel matrix and were adapted to a standardizing device (8 x 7 cm) with a graduated aluminum stepwedge varying from 2.0-16.0 mm in thickness. To compare the radiopacity of the cements with that of dental structures, slices of first molars with a thickness increasing from 0.5-3.0 mm were obtained and placed on the standardizing device. One occlusal radiograph for each tested cement was taken, with exposure time of 0.1 seconds and focus-film distance of 20 cm. Films were processed in an automatic device, and the mean radiopacity values were obtained by using a photodensitometer. Results: Mean values showed that the thicker the specimen was, the greater was its radiopacity. Only EndoBinder + bismuth oxide (EBBO) and GMTA demonstrated radiopacity values greater than 3.0 mm of the aluminum scale for all thicknesses. When zinc oxide was used as radiopacifier agent, EndoBinder only reached the desired radiopacity with a thickness of 2.0 mm, and with zirconium oxide it was 2.5 mm. Conclusions: Bismuth oxide was the most efficient radiopacifier for EndoBinder, providing adequate radiopacity in all studied thicknesses, as recommended by ISO 6876, being similar to GMTA. (J Endod 2011;37: 67-71)