Investigation of the electrical and electrochemical properties of nanocomposites from V2O5, polypyrrole, and polyaniline

In this work, an investigation of the electrical and electrochemical properties responsible for the energy storage capability of nanocomposites has been carried out. We demonstrate that, in the case of the V2O5 xerogel and the nanocomposites polypyrrole (Ppy)/V2O5 and polyaniline (PANI)/V2O5, the quadratic logistic equation (QLE) can be used to fit the inverse of the resistance values as a function of the injected charge in non-steady-state conditions. This contributes to a phenomenological understanding of the lithium ion and electron transport. The departure of the experimental curve from the fitting observed for the V2O5 xerogel can be attributed to the trapping sites formed during the lithium electroinsertion, which was observed by electrochemical impedance spectroscopy. The amount of trapping sites was obtained on the basis of the QLE. Similar values used to fit the inverse of the resistance were also used to fit the absorbance changes, which is also associated with the small polaron hopping from the V(IV) to the V(V) sites. On the other hand, there was good agreement between the experimental and the theoretical data when the profile of the inverse of the resistance as a function of the amount of inserted lithium ions of the nanocomposites Ppy/V2O5 and PANI/ V2O5 was concerned. We suggest that the presence of the conducting polymers is responsible for the different electrical profile of the V2O5 xerogel compared with those of the nanocomposites. In the latter case, interactions between the lithium ions and oxygen atoms from V2O5 are shielded, thus decreasing the trapping effect of lithium ions in the V2O5 sites. The different values of the lithium ion diffusion coefficient into these intercalation materials are in agreement with this hypothesis.

Electrical and optical properties of poly(2-dodecanoylsulfanyl-p-phenylenevnylene) and its application in electroluminescent devices

We describe the optical and electrical characterization of a poly(p-phenylenevinylene) derivative: poly(2-dodecanoylsulfanyl-p-phenylenevinylene) (12COS-PPV). The electrical characterization was carried out on devices with the FTO\PEDOT:PSS\12COS-PPV/Al structure. Positive charge carrier mobility mu(h) of similar to 1.0 x 10(-6) cm(2) V(-1) s(-1) and barrier height phi of similar to 0.1 eV for positive charge carrier injection at the PEDOT:PSS/12COS-PPV interface were obtained using a thermionic injection model. FTO\PEDOT:P55\12COS-PPV/Ca devices exhibited green-yellow electroluminescence with maximum emission at lambda = 540 nm.

Evaluation of physico-chemical properties of Portland cements and MTA

The purpose of this study was to evaluate the hydrogenionic potential and electrical conductivity of Portland cements and MTA, as well as the amount of arsenic and calcium released from these materials. In Teflon molds, samples of each material were agitated and added to plastic flasks containing distilled water for 3, 24, 72 and 168 h. The results were analyzed with a Kruskal-Wallis non-parametric test for global comparisons and a Dunn-Tukey test for pairwise comparisons. The results revealed no significant differences in the pH of the materials (p > 0.05). The electrical conductivity of the cements were not statistically different (p > 0.05). White non-structural cement and MTA BIO released the largest amount of calcium ions into solution (p < 0.05), while arsenic release was insignificant in all of the materials (p > 0.05). The results indicated that the physico-chemical properties of Portland cements and MTA were similar. Furthermore, all materials produced an alkaline environment and can be considered safe for clinical use because arsenic was not released. The electrical conductivity and the amount of calcium ions released into solution increased over time.

Comparison of the Effects of Electrical Field Stimulation and Low-Level Laser Therapy on Bone Loss in Spinal Cord-Injured Rats

Objective: This study investigated the effects of low-level laser therapy (LLLT) and electrical stimulation (ES) on bone loss in spinal cord-injured rats. Materials and Methods: Thirty-seven male Wistar rats were divided into four groups: standard control group (CG); spinal cord-injured control (SC); spinal cord-injured treated with laser (SCL; GaAlAs, 830 nm, CW, 30mW/cm, 250 J/cm(2)); and spinal cord-injured treated with electrical field stimulation (SCE; 1.5 MHz, 1: 4 duty cycles, 30 mW, 20 min). Biomechanical, densitometric, and morphometric analyses were performed. Results: SC rats showed a significant decrease in bone mass, biomechanical properties, and morphometric parameters (versus CG). SCE rats showed significantly higher values of inner diameter and internal and external areas of tibia diaphyses; and the SCL group showed a trend toward the same result (versus SC). No increase was found in either mechanical or densitometric parameters. Conclusion: We conclude that the mentioned treatments were able to initiate a positive bone-tissue response, maybe through stimulation of osteoblasts, which was able to determine the observed morphometric modifications. However, the evoked tissue response could not determine either biomechanical or densitometric modifications.

Study of the influence of indium segregation on the optical properties of InGaAs/GaAs quantum wells via split-operator method

In the case of quantum wells, the indium segregation leads to complex potential profiles that are hardly considered in the majority of the theoretical models. The authors demonstrated that the split-operator method is useful tool for obtaining the electronic properties in these cases. Particularly, they studied the influence of the indium surface segregation in optical properties of InGaAs/GaAs quantum wells. Photoluminescence measurements were carried out for a set of InGaAs/GaAs quantum wells and compared to the results obtained theoretically via split-operator method, showing a good agreement.

Effect of Mn concentration and atomic structure on the magnetic properties of Ge thin films

This work reports on the magnetic properties of Ge(100-x)Mn(x) (x=0-24 at. %) films prepared by cosputtering a Ge+Mn target and submitted to cumulative thermal annealing treatments up to 500 degrees C. Both as-deposited and annealed films were investigated by means of compositional analysis, Raman scattering spectroscopy, magnetic force microscopy, superconducting quantum interference device magnetometry, and electrical resistivity measurements. All as-deposited films (either pure or containing Mn) exhibit an amorphous structure, which changes to crystalline as the annealing treatments are performed at increasing temperatures. In fact, the magnetic properties of the present Ge(100-x)Mn(x) films are very sensitive to the Mn content and whether their atomic structure is amorphous or crystalline. More specifically: whereas the amorphous Ge(100-x)Mn(x) films (with high x) present a characteristic spin glass behavior at low temperature; after crystallization, the films (with moderate Mn contents) are ferromagnetic at room temperature. Moreover, the magnetic behavior of the films scales with their Mn concentration and tends to be more pronounced after crystallization. Finally, the semiconducting behavior of the films, experienced by previous optical studies, was confirmed through electrical measurements, which also indicate the dependence of the resistivity with the atomic composition of the films. (C) 2010 American Institute of Physics. [doi: 10.1063/1.3520661]

Electrical and Magnetic Characterization of BSCCO and YBCO HTS Tapes for Fault Current Limiter Application

Several high temperature superconductor (HTS) tapes have been developed since the late eighties. Due to the new techniques applied for their production, HTS tapes are becoming feasible and practical for many applications. In this work, we present the test results of five commercial HTS tapes from the BSCCO and YBCO families (short samples of 200 mm). We have measured and analyzed their intrinsic and extrinsic properties and compared their behaviors for fault current limiter (FCL) applications. Electrical measurements were performed to determine the critical current and the n value through the V-I relationship under DC and AC magnetic fields. The resistance per unit length was determined as a function of temperature. The magnetic characteristics were analyzed through susceptibility curves as a function of temperature. As transport current generates a magnetic field surrounding the HTS material, the magnetic measurements indicate the magnetic field supported by the tapes under a peak current 1.5 times higher than the critical current, I(c). By pulsed current tests the recovery time and the energy/volume during a current fault were also analyzed. These results are in agreement with the data found in the literature giving the most appropriate performance conductor for a FCL device (I(peak) = 4 kA) to be used in a 220 V-60 Hz grid.

Influence of alumina content on green machined electrical porcelain

The effect of alumina content on the mechanical strength of electrical porcelain manufactured by green machining of isostatically pressed blanks was examined with a view to attaining optimal mechanical properties at low sintering temperatures. Porcelain compositions were formulated with four different alumina contents, maintaining the same proportion of the other materials (kaolin, clay and feldspar). Test specimens were isostatically pressed at 70 MPa and machined at high speed into cylindrical test specimens using controlled machining parameters. These specimens were sintered at several temperatures to determine the optimal sintering temperature for each composition, after which their mechanical properties were analyzed by the flexural bend test. The results indicated a correlation between the alumina content and the sintering temperature, and between the flexural strength and its influence on the green machining conditions. An average tensile strength of 786 MPa was attained for the composition with an added content of 30 wt% of commercial alumina sintered at 1250 degrees C, pressed and machined under industrial conditions.

Embrittlement of electrical steel laminations by nitrogen pick-up during heat treatment

Heat treated electrical steel laminations have shown evidence of low ductility behavior, characterized by a small number of bends till fracture, on repeated bending tests. The laminations were produced using a new grade of electrical steel with much lower aluminum content than usual. The problem happens when the oxygen potential (measured by the dew point of the atmosphere) of the heat treatment atmosphere is abnormally high. Furthermore, ductility can be restored by a low-oxygen potential heat treatment. Although the heat treatment resulted in a loss of ductility, the magnetic properties were not deteriorated. The low ductility samples always show intergranular fracture, whereas the un-treated laminations fracture by cleavage. The low ductility is associated with the formation of silicon manganese nitride precipitates formed at grain boundaries, although they are not the cause of the low ductility. Ductility could be restored by a low dew point heat treatment but the inclusions remained in the grain boundaries. The low ductility and its recovery must be ascribed to the presence of nitrogen atoms segregated to the grain boundaries when the heat treatment atmosphere has a high oxygen potential. The lack of aluminum in the composition of the steel hinders the scavenging effect of this element on nitrogen atoms in solution in the steel. (C) 2009 Elsevier Ltd. All rights reserved.

Impact of plastic deformation on magnetoacoustic properties of Fe-2%Si alloy

The paper presents the results of a complementary study including magnetic hysteresis loops B(H), magnetic Barkhausen noise (MBN) and magnetoacoustic emission (MAE) signals measurements for plastically deformed Fe-2%Si samples. The investigated samples had been plastically deformed with plastic strain level (epsilon(p)) up to 8%. The properties of B(H) loops are quantified using the coercivity H(C) and maximum differential permeability mu(rmax) as parameters. The MBN and MAE voltage signals were analysed by means of rms-like voltage (Ub and Ua, respectively) envelopes, plotted as a function of applied field strength. Integrals of the Ub and Ua voltages over half of a period of magnetization were then calculated. It has been found that He and integrals of Ub increase, while mu(rmax) decreases monotonically with increasing epsilon(p). The MAE (Ua) peak voltage at first decreases, then peaks at epsilon(p) approximate to 1.5% and finally decreases again. The integral of the Ua voltage at first increases for low epsilon(p) and then decreases for epsilon(p) > 1.5%. All those various dependence types suggest the possibility of detection of various stages of microstructure change. The above-mentioned results are discussed qualitatively in the paper. Some modelling of the discussed dependency is also presented. (C) 2008 Elsevier Ltd. All rights reserved.

An In-Depth Study of the Barkhausen Emission Signal Properties of the Plastically Deformed Fe-2%Si Alloy

This paper presents the results of the in-depth study of the Barkhausen effect signal properties for the plastically deformed Fe-2%Si samples. The investigated samples have been deformed by cold rolling up to plastic strain epsilon(p) = 8%. The first approach consisted of time-domain-resolved pulse and frequency analysis of the Barkhausen noise signals whereas the complementary study consisted of the time-resolved pulse count analysis as well as a total pulse count. The latter included determination of time distribution of pulses for different threshold voltage levels as well as the total pulse count as a function of both the amplitude and the duration time of the pulses. The obtained results suggest that the observed increase in the Barkhausen noise signal intensity as a function of deformation level is mainly due to the increase in the number of bigger pulses.

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

This work investigates the influence of the addition of cerium (IV) ions on the anticorrosion properties of organic-inorganic hybrid coatings applied to passivated tin coated steel. In order to evaluate the specific effect of cerium (IV) addition on nanostructural features of the organic and inorganic phases of the hybrid coating, the hydrolytic polycondensation of silicon alkoxide and the radical polymerization of the methyl methacrylate (MMA) function were induced separately. The corrosion resistance of the coatings was evaluated by means of linear polarization, Tafel type curves and electrochemical impedance measurements. The impedance results obtained for the hybrid coatings were discussed based on an electrical equivalent circuit used to fit the experimental data. The electrochemical results clearly showed the improvement of the protective properties of the organic-inorganic hybrid coating mainly when the cerium (IV) was added to the organic phase solution precursor, which seemed to be due to the formation of a more uniform and densely reticulated siloxane-PMMA film. (C) 2010 Elsevier Ltd. All rights reserved.

Relationship between surface segregation and rapid propane electrical response in Cd-doped SnO2 nanornaterials

Controlling the surface properties of nanoparticles using ionic dopants prone to be surface segregated has emerged as an interesting tool for obtaining highly selective and sensitive sensors. In this work, the surface segregation of Cd cations on SnO2 nanopowders prepared by the Pechini`s method was studied by infrared spectroscopy, X-ray diffraction, and specific surface area analysis. We observed that the surface chemistry modifications caused by the surface segregation of Cd and the large specific surface area were closely responsible for a rapid and regular electrical response of 5 mol% Cd-doped SnO2 films to 100 ppm propane and NO, diluted in dry air at relatively low temperature (100 degrees C). (c) 2008 Elsevier B.V. All rights reserved.

Spectral properties of chaotic signals generated by the skew tent map

Chaotic signals have been considered potentially attractive in many signal processing applications ranging from wideband communication systems to cryptography and watermarking. Besides, some devices as nonlinear adaptive filters and phase-locked loops can present chaotic behavior. In this paper, we derive analytical expressions for the autocorrelation sequence, power spectral density and essential bandwidth of chaotic signals generated by the skew tent map. From these results, we suggest possible applications in communication systems. (C) 2009 Elsevier B.V. All rights reserved.

Experimental and theoretical study of transport properties in uniaxially pressed (Bi, Pb)(2)Sr(2)Ca(2)Cu(3)O(10+delta) ceramic samples

Experimental and theoretical studies on the magnetic field dependence of the electrical resistance R(B(a)) and the transport noise (TN) in polycrystalline high-T(c) superconductors subjected to different uniaxial compacting pressures were conducted. X-ray diffraction rocking curves were performed in different surfaces of the samples in order to investigated the degree of texture The results indicated an improvement of the degree of texture with increasing the uniaxial compacting pressure In theoretical simulations of the data, the polycrystalline superconductors were described as a series-parallel array of Josephson devices The intergranular magnetic field is described within the framework of the intragranular flux-trapping model and the distribution of the grain-boundary angles is assumed to follow the Rayleigh statistical function The proposed model describes well the experimental magnetoresistance R(B(a)) data We have found that the behavior of the R(B(a)) curves changes appreciably when different uniaxially compacting pressures are applied to the sample and such a changes are reproduced by the model when different grain-boundary angles distributions are used In addition, changes in the R(B(a)) dependence have their counterparts in the experimental transport noise signals (C) 2009 Elsevier B.V. All rights reserved