Bond Strength of Fiber Posts to Weakened Roots After Resin Restoration With Different Light-Curing Times

Introduction: This study evaluated the bond strength of translucent fiber posts to experimentally weakened radicular dentin restored with composite resin and polymerized with different light-exposure time. Methods: Roots of 60 maxillary incisors were used. Twenty-four hours after obturation, the filling materials of root canals were removed to a depth of 12 mm, and 4 groups were randomly formed. In 3 groups, root dentin was flared to produce a space between fiber post and canal walls. In the control group, the roots were not experimentally weakened. The flared roots were bulk restored with composite resin, which was light-activated through the translucent post for 40, 80, or 120 seconds. Posts were cemented, and after 24 hours, all roots were sectioned transversely in the coronal, middle, and apical regions, producing 1-mm-thick slices. Push-out test was performed, and failure modes were observed. Results The quantitative analysis showed significant statistical difference only among groups (P <.001). Comparing the weakened/restored groups, composite light-exposure time did not influence the results. Overall, adhesive failures occurred more frequently than other types of failures. Cohesive failures occurred only in the weakened/restored roots. Conclusions Intracanal root restoration with composite resin and translucent fiber posts provided similar or higher bond strength to dentin than the control group, regardless of the light-exposure time used for polymerization. (J Endod 2009;35:1034-1039)

Solubility of Epiphany Endodontic Sealer Prepared with Resinous Solvent

Purpose: To evaluate in vitro the solubility of the Epiphany endodontic filling material Epiphany (Pentron Clinical Technologies, Wallingford, CT) prepared with its resinous solvent. Methods: The specimens were prepared in the following experimental conditions: (1) GI, epiphany without photoactivation; (2) GII, Epiphany prepared with resinous solvent without photoactivation; (3) Gill, Epiphany followed by photoactivation; and (4) GIV, Epiphany prepared with resinous solvent followed by photoactivation. Ten specimens of each group were obtained from Teflon molds with 80% reduction in volume of the specimen`s dimensions based on American National Standard Institute/American Dental Association (ANSI/ADA) Specification No. 57. The samples were weighted and immersed in distilled water for 7 days. After this period, they were removed, dried, and weighed again. Solubility was calculated by using samples weight loss (%). The immersion liquid was evaluated through atomic absorption spectrometry. Results: The sealers without photoactivation were statistically similar (p > 0.05) between themselves (GI = 6.93% and GII = 6.39%) and different from the uncured sealers, which were statistically different between themselves (p < 0.05) (GIII = 3.56% and GIV = 0.47%). Only the Epiphany sealer prepared with resinous solvent followed by photoactivation presented solubility values within ANSI/ADA requirements, liberating the following amounts of ions: 114.43 mu g of Ca(2+)/mL, 2.4 mu g of Mg(2+)/mL, 0.33 mu g of Fe(2+)/mL, 0.11 mu 4g of Zn(2+)/mL, 1.31 mu g of Ni(2+)/mL, and 7.1 mu g of Na(+)/mL. Conclusion: The association of resinous solvent to the Epiphany sealer followed by photoactivation resulted in a filling material with low solubility and expressive liberation of calcium ions. (J Endod 2009;35:715-718)

A New Periapical Index Based on Cone Beam Computed Tomography

The purpose of this study was to evaluate a new periapical index based on cone beam computed tomography (CBCT) for identification of apical periodontitis (AP). The periapical index proposed in this study (CBCTPAI) was developed on the basis of criteria established from measurements corresponding to periapical radiolucency interpreted on CBCT scans. Radiolucent images suggestive of periapical lesions were measured by using the working tools of Planimp software on CBCT scans in 3 dimensions: buccopalatal, mesiodistal, and diagonal. The CBCTPAI was determined by the largest lesion extension. A 6-point (0-5) scoring system was used with 2 additional variables, expansion of cortical bone and destruction of cortical bone. A total of 1014 images (periapical radiographs and CBCT scans) originally taken from 596 patients were evaluated by 3 observers by using the CBCTPAI criteria. AP was identified in 39.5% and 60.9% of cases by radiography and CBCT, respectively (P<.01). The CBCTPAI offers an accurate diagnostic method for use with high-resolution images, which can reduce the incidence of false-negative diagnosis, minimize observer interference, and increase the reliability of epidemiologic studies, especially those referring to AP prevalence and severity. (J Endod 2008;34:1325-1331)

Effects of light exposure time on composite resin hardness after root reinforcement using translucent fibre post

Objectives: The purpose of this in vitro study was to evaluate the Vickers hardness (VHN) of a Light Core (Bisco) composite resin after root reinforcement, according to the light exposure time, region of intracanal reinforcement and lateral distance from the light-transmitting fibre post. Methods: Forty-five 17-mm long roots were used. Twenty-four hours after obturation, the root canals were emptied to a depth of 12 mm and the root dentine was artificially flared to produce a 1 mm space between the fibre post and the canal walls. The roots were bulk restored with the composite resin, which was photoactivated through the post for 40 s (G1, control), 80 s (G2) or 120 s (G3). Twenty-four hours after post-cementation, the specimens were sectioned transversely into three slices at depths of 2, 6 and 10 mm, corresponding to the coronal, middle and apical regions of the reinforced root. Composite VHN was measured as the average of three indentations (100 g/15 s) in each region at lateral distances of 50, 200 and 350 mu m from the cement/post-interface. Results: Three-way analysis of variance (alpha = 0.05) indicated that the factors time, region and distance influenced the hardness and that the interaction time x region was statistically significant (p = 0.0193). Tukey`s test showed that the mean VHN values for G1 (76.37 +/- 8.58) and G2 (74.89 +/- 6.28) differed significantly from that for G3 (79.5 +/- 5.18). Conclusions: Composite resin hardness was significantly lower in deeper regions of root reinforcement and in lateral areas distant from the post. Overall, a light exposure time of 120 s provided higher composite hardness than the shorter times (40 and 80 s). (C) 2008 Elsevier Ltd. All rights reserved.

Influence of Filling Materials on the Bonding Interface of Thin-walled Roots Reinforced with Resin and Quartz Fiber Posts

Introduction: A common complication during the restoration of severely destroyed teeth is the loss of coronal root dentine. The aim of this study was to evaluate the influence of different sealers on the bonding interface of weakened roots reinforced with resin and fiber posts. Methods: Sixty extracted maxillary canines were used. The crowns were removed, and the thickness of root dentine was reduced in the experimental (n = 40) and positive control (n = 10) groups. The specimens of experimental group were assigned to four subgroups (n = 10) according to the filling material: gutta-percha + Grossmann`s sealer, gutta-percha + AH Plus (Dentsply De Trey Gmbh, Konstanz, Germany), gutta-percha + Epiphany (Pentron Clinical Technologies, Wallingford, CT), and Resilon (Resilon Research LLC, Madison, CT) + Epiphany. In the negative control group (n = 10), canals were not filled. After post space preparation, the roots were restored with composite resin light-activated through a translucent fiber post. After 24 hours, specimens were transversally sectioned into 1-mm-thick slices. Push-out test and scanning electron microscopic (SEM) analyses of different regions were performed. Data from push-out test were analyzed by using Tukey post hoc multiple comparison tests. The percentage of failure type was calculated. Data from SEM analysis were compared by Friedman and Kruskal-Wallis tests (alpha = 0.05). Results: The mean bond strength was significantly higher in the negative control group as compared with the other groups (P < .05). In all groups, the most frequent type of failure was adhesive. Overall, apical and middle regions presented a lower density of resin tags than the coronal region (P < .05). Conclusions: The push-out bond strength was not affected by sealer or region. The canal region affected significantly the resin tag morphology and density at the bonding interface. (J Endod 2011;37:531-537)

Study on the potential inhibition of root dentine wear adjacent to fluoride-containing restorations

The purpose of this in vitro study was to determine whether the vicinity of root dentine that had been restored with fluoride-releasing materials was at reduced risk for erosive/abrasive wear compared to root dentine restored with a non-fluoride-containing material. According to a randomized complete block design, standardized cavities prepared on the surface of 150 bovine root dentine slabs were restored with glass-ionomer cement, resin-modified glass ionomer, polyacid-modified resin composite, fluoride-containing or conventional composite. Specimens were coated with two layers of an acid-resistant nail varnish exposing half of the dentine surface and half of the restoration. Subsequently, specimens were either eroded in an acidic drink or left uneroded, then exposed to artificial saliva and abraded in a toothbrushing machine. Wear depth in the vicinity of restorations was quantified by a stylus profilometer, based on the nonabraded areas surrounding the erosion/abrasion region. Two-way ANOVA did not demonstrate significant interaction between restoratives and eroded-uneroded dentine (p = 0.5549) nor significant difference among restorative materials (p = 0.8639). Tukey`s test ascertained that the wear depth was higher for eroded than for uneroded groups. Fluoride-releasing materials seemed to negligibly inhibit wear in the vicinity of restored root dentine subjected to erosive/abrasive challenges.

Deposition of Lead and Cadmium Released by Cigarette Smoke in Dental Structures and Resin Composite

Cigarette smoke is a significant source of cadmium, lead, and toxic elements, which are absorbed into the human organism. In this context, the aim of this study was to investigate in vitro the presence of toxic elements, cadmium, and lead deriving from cigarette smoke in the resin composite, dentine, and dental enamel. Eight cylindrical specimens were fabricated from resin composite, bovine enamel, and root dentin fragments that were wet ground and polished with abrasive paper to obtain sections with 6-mm diameter and 2-mm thickness. All specimens were exposed to the smoke of 10 cigarettes/day during 8 days. After the simulation of the cigarette smoke, the specimens were examined with scanning electron microscopy (SEM) and the energy-dispersive X-ray analysis. In the photomicrographic analysis in SEM, no morphological alterations were found; however, the microanalysis identified the presence of cadmium, arsenic, and lead in the different specimens. These findings suggest that the deposition of these elements derived from cigarette smoke could be favored by dental structures and resin composite. Microsc. Res. Tech. 74:287-291, 2011. (C) 2010 Wiley-Liss, Inc.

Microtensile Bond Strength of Glass Fiber Posts Cemented with Self-adhesive and Self-etching Resin Cements

Purpose: To evaluate the bond strength of glass fiber posts to intraradicular dentin when cemented with self-etching and self-adhesive resin cements. Materials and Methods: Forty-eight single-rooted human teeth were decoronated, endodontically treated, post-space prepared and divided into 8 groups (n = 6). The glass fiber posts used were: Exacto (EA) (Angelus) and everStick (ES) (StichTeck), which were cemented with two self-adhesive resin cements: BisCem (BIS) (Bisco) and Rely-X Unicem (UNI) (3M/ESPE), and two self-etching resin cements: Esthetic Cementing System NAC100 (NAC) (Kuraray) and Panavia-F (PAN) (Kuraray). Specimens were thermocycled between 5 degrees C and 55 degrees C for 1000 cycles and stored in water at 37 degrees C for 1 month. Four 1-mm-thick (in cross section) rods were obtained from the cervical region of the roots. Specimens were then subjected to microtensile testing in a special machine (BISCO; Schaumburg, IL, USA) at a crosshead speed of 0.5 mm/min. Microtensile bond strength (mu TBS) data were analyzed with two-way ANOVA and Tukey`s tests. Results: Means (and SD) of mu TBS (MPa) were: EA/PAN: 10.3 (4.1), EA/NAC: 14 (5.1) EA/BIS: 16.4 (4.8), EA/UNI: 19.8 (5.1), ES/PAN: 25.9 (6.1), ES/NAC: 29.1 (7), ES/BIS: 28.9 (6), ES/UNI: 30.5 (6.6). ANOVA indicated significant differences among the groups (p < 0.001). Mean mu TBS values obtained with ES post were significantly higher than those obtained with EA (p < 0.001). For EA, Tukey`s test indicated that higher mu TBS means were obtained with the self-adhesive resin cements (BIS and UNI), which were statistically significantly different (p < 0.05) from values obtained with the self-etching resin cements (PAN and NAC). Different cements had no significant effects on the bond strength values of ES post (p > 0.05). mu TBS values obtained with ES post were significantly higher than those obtained with EA post irrespective of the resin cement used. Conclusion: everStick posts resulted in the highest mean mu TBS values with all cements. Self-adhesive cements performed well in terms of bond strength.

Photoelastic Stress Analysis of Different Designs of Cement-Retained Fixed Partial Dentures on Morse Taper Oral Implants

There is no consensus in literature regarding the best plan for prosthetic rehabilitation with partial multiple adjacent implants to minimize stress generated in the bone-implant interface. The aim of this study was to evaluate the biomechanical behavior of cemented fixed partial dentures, splinted and nonsplinted, on Morse taper implants and with different types of coating material (ceramic and resin), using photoelastic stress analysis. A photoelastic model of an interposed edentulous space, missing a second premolar and a first molar, and rehabilitated with 4 different types of cemented crowns and supported by 2 adjacent implants was used. Groups were as follows: UC, splinted ceramic crowns; IC, nonsplinted ceramic crowns; UR, splinted resin crowns; and IR, nonsplinted resin crowns. Different vertical static loading conditions were performed: balanced occlusal load, 10 kgf; simultaneous punctiform load on the implanted premolar and molar, 10 kgf; and alternate punctiform load on the implanted premolar and molar, 5 kgf. Changes in stress distribution were analyzed in a polariscope, and digital photographs were taken of each condition to allow comparison of stress pattern distribution around the implants. Cementation of the fixed partial dentures generated stresses between implants. Splinted restorations distributed the stresses more evenly between the implants than nonsplinted when force was applied. Ceramic restorations presented better distribution of stresses than resin restorations. Based on the results obtained, it was concluded that splinted ceramic restorations promote better stress distribution around osseointegrated implants when compared with nonsplinted crowns; metal-ceramic restorations present less stress concentration and magnitude than metal-plastic restorations.

Use of resin-bonded extracoronal attachments with removable partial denture: case report

Introduction: Resin-bonded extracoronal attachments may be indicated for the abutment teeth of removable partial dentures, especially for anterior teeth when a cingulum rest must be provided. This type of treatment has a series of advantages such as minimal tooth reduction, supragingival margins, favourable stress distribution, and improved aesthetic appearance. Objective: To report a clinical case of oral rehabilitation using a combination of resin-bonded extracoronal attachments joined by a Dolder bar with a removable partial denture. Case report: A 60-year-old male patient with only the canines in the maxillary arch was restored with a combination of resin-bonded extracoronal attachments joined by a Dolder bar and a removable partial denture. Conclusion: Dentures with resin-bonded extracoronal attachments can have a number of advantages over traditional clasp-retained removable partial dentures.

The Effect of Coating Patterns with Spinel-Based Investment on the Castability and Porosity of Titanium Cast into Three Phosphate-Bonded Investments

Purpose: This study evaluated the effect of pattern coating with spinel-based investment Rematitan Ultra (RU) on the castability and internal porosity of commercially pure (CP) titanium invested into phosphate-bonded investments. The apparent porosity of the investment was also measured. Materials and Methods: Square patterns (15 x 15 x 0.3 mm(3)) were either coated with RU, or not and invested into the phosphate-bonded investments: Rematitan Plus (RP), Rema Exakt (RE), Castorit Super C (CA), and RU (control group). The castings were made in an Ar-arc vacuum-pressure machine. The castability area (mm(2)) was measured by an image-analysis system (n = 10). For internal porosity, the casting (12 x 12 x 2 mm(3)) was studied by the X-ray method, and the projected porous area percentage was measured by an image-analysis system (n = 10). The apparent porosity of the investment (n = 10) was measured in accordance with the ASTM C373-88 standard. Results: Analysis of variance (One-way ANOVA) of castability was significant, and the Tukey test indicated that RU had the highest mean but the investing technique with coating increased the castability for all phosphate-bonded investments. The analysis of the internal porosity of the cast by the nonparametric test demonstrated that the RP, RE, and CA with coating and RP without coating did not differ from the control group (RU), while the CA and RE casts without coating were more porous. The one-way ANOVA of apparent porosity of the investment was significant, and the Tukey test showed that the means of RU (36.10%) and CA (37.22%) were higher than those of RP (25.91%) and RE (26.02%). Conclusion: Pattern coating with spinel-based material prior to phosphate-bonded investments can influence the castability and the internal porosity of CP Ti.

Evaluation of the Abrasiveness of Dentifrices for Complete Dentures

Purpose: This study analyzed the surface roughness and weight loss in Plex Glass specimens caused by dentifrices, one conventional (Sorriso) and three specific for dentures. Materials and Methods: Specimens (n = 6) of Plex Glass were divided into 5 groups including: negative control (water); positive control 1 (Sorriso) and 2 (Corega Brite); Experimental 1 (containing Chloramine T, antimicrobial agent); and Experimental 2 (containing Zonyl, detergent). Brushing was performed in a toothbrushing machine (Pepsodent) with a soft brush and a suspension of toothpaste and distilled water for 300 minutes, representing 6 years of brushing. Weight was measured initially and after the trial period; roughness was measured after the trial period only. The results of roughness and weight loss were analyzed using ANOVA and Tukey tests at 5%. Results: The negative control (2.82 +/- 4.41 mg) showed the lowest weight loss. Experimental 1 (13.62 +/- 4.29 mg) and Experimental 2 (15.4 +/- 5.80 mg) were equal statistically, and Sorriso (23.22 +/- 7.23 mg) and Corega (28.83 +/- 6.34 mg) produced the greatest weight loss. Concerning roughness, the negative control group (0.03 +/- 0.01 mu m) showed the lowest value. No significant differences were found between Corega (13.43 +/- 1.65 mu m), Experimental 1 (12.28 +/- 0.85 mu m), and Experimental 2 (10.68 +/- 2.56 mu m). The Sorriso toothpaste produced the greatest amount of surface roughness (19.15 +/- 2.36 mu m). Conclusion: Of the tested dentifrices, the experimental preparations proved to be the least abrasive and resulted in the lowest weight loss after brushing of the acrylic. Based on these findings, the use of these experimental dentifrices is advocated. Further evaluation based on the ability of these preparations to remove biofilms is required.

Biocompatibility Evaluation of Epiphany/Resilon Root Canal Filling System in Subcutaneous Tissue of Rats

Introduction: The purpose of this study was to evaluate the biocompatibility of the root canal filling system Epiphany/Resilon in connective tissue of rats. Methods: Fifteen rats were used, separated into 3 groups in accordance with its period of death (7, 21, 42 days). Four filled dentin tubes were implanted with the tested materials as follows: ERSP group, Epiphany/Resilon with Self-etch Primer; ER group, Epiphany/Resilon without primer; EG group, Endofill/gutta-percha points; and ET group, empty tube. After 7, 21, and 42 days, animals were killed, obtaining 5 samples per group. A grade from I-IV was used to graduate the inflammatory reaction. Results: Results showed that Epiphany/Resilon (ERSP and ER groups) induced a slight (II) inflammatory reaction after 42 days. However, in ER group, in which the self-etch primer was not applied, severe (IV) to moderate (III) inflammatory reactions were observed between 7 and 21 days. When compared with the EG and ET groups, it was observed that these groups presented tissue reaction ranging from slight (II, 7 and 21 days) to no inflammation (I, 42 days). Conclusions: Epiphany/Resilon root canal filling system presented satisfactory tissue reaction. It was biocompatible when tested in connective tissue of rats. (J Endod 2010;36:110-114)

Effects of Ethanol on the Surface and Bulk Properties of a Microwave-Processed PMMA Denture Base Resin

Purpose: This study evaluated the effect of different concentrations of ethanol on hardness, roughness, flexural strength, and color stability of a denture base material using a microwave-processed acrylic resin as a model system. Materials and Methods: Sixty circular (14 x 4 mm) and 60 rectangular microwave-polymerized acrylic resin specimens (65 x 10 x 3 mm(3)) were employed in this study. The sample was divided into six groups according to the ethanol concentrations used in the immersion solution, as follows: 0% (water), 4.5%, 10%, 19%, 42%, and 100%. The specimens remained immersed for 30 days at 37 degrees C. The hardness test was performed by a hardness tester equipped with a Vickers diamond penetrator, and a surface roughness tester was used to measure the surface roughness of the specimens. Flexural strength testing was carried out on a universal testing machine. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 30 days. Variables were analyzed by ANOVA/Tukey`s test (alpha = 0.05). Results: For the range of ethanol-water solutions for immersion (water only, 4.5%, 10%, 19.5%, 42%, and 100%), the following results were obtained for hardness (13.9 +/- 2.0, 12.1 +/- 0.7, 12.9 +/- 0.9, 11.2 +/- 1.5, 5.7 +/- 0.3, 2.7 +/- 0.5 VHN), roughness (0.13 +/- 0.01, 0.15 +/- 0.07, 0.13 +/- 0.05, 0.13 +/- 0.02, 0.23 +/- 0.05, 0.41 +/- 0.19 mu m), flexural strength (90 +/- 12, 103 +/- 18, 107 +/- 16, 90 +/- 25, 86 +/- 22, 8 +/- 2 MPa), and color (0.8 +/- 0.6, 0.8 +/- 0.3, 0.7 +/- 0.4, 0.9 +/- 0.3, 1.3 +/- 0.3, 3.9 +/- 1.5 Delta E) after 30 days. Conclusions: The findings of this study showed that the ethanol concentrations of tested drinks affect the physical properties of the investigated acrylic resin. An obvious plasticizing effect was found, which could lead to a lower in vivo durability associated with alcohol consumption.

Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Purpose: This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Materials and Methods: Ninety-six disk-shaped (14-mm diameter x 4-mm thick) and 30 rectangular (65 x 10 x 3.3 mm(3)) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (alpha = 0.05). Results: The following mean results (+/-SD) were obtained for hardness (A: 15.6 +/- 0.6, B: 14.6 +/- 1.7, C: 14.8 +/- 0.8 VHN; ANOVA: p = 0.061), flexural strength (A: 111 +/- 17, B: 105 +/- 12, C: 88 +/- 12 MPa; ANOVA: p = 0.008), and roughness (A: 0.20 +/- 0.11, B: 0.20 +/- 0.11, C: 0.24 +/- 0.08 mu m; ANOVA: p = 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 +/- 3.1, B: 14.8 +/- 7.5, C: 13.3 +/- 6.1 Delta E; ANOVA: p < 0.05). Conclusions: The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance.