Evaluation of the radiopacity of some commercial and experimental root-end filling materials

Objective. The aim of the present study was to evaluate the radiopacity of 5 root end filling materials (white MTA Angelus, MTA Bio, light-cured MTA, Sealepox RP, and Portland cement clinker with bismuth oxide and calcium sulfate). Method. Five specimens, 10 mm in diameter and 1 mm in thickness according to specification ISO 6876: 2001 were fabricated from each material and radiographed using Insigth occlusal films close to a graduated aluminum step-wedge (2 to 16 mm in thickness). Radiographs were digitized and compared to the aluminum step-wedge. The radiographic density data were converted into millimeters of aluminum (mm Al), using the Digora 1.51 software. Results were evaluated statistically using the analysis of variance (ANOVA) followed by Tukey test. The level of significance was set at 5% (P<.05%). Results. Radiopacity values ranged from 1.21 mm Al (light-cured MTA) to 6.45 mm Al (MTA Angelus). Comparison between materials showed significant difference (P<.05) between MTA Angelus and all other materials, between Sealepox RP and MTA Bio, and between light-cured MTA and Portland cement clinker. Light-cured MTA was significantly less radiopaque than all other materials. No significant difference (P>.05) was found between MTA Bio and Portland cement clinker. Conclusions. All retrograde filling materials evaluated showed greater radiopacity than dentin. All the materials, except light-cured MTA met the minimum radiopacity standards of 3 mm Al recognized by the ISO 6876: 2001 and ADA n.57. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e35-e38)

Radiopacity of Portland Cement Associated With Different Radiopacifying Agents

This study evaluated the radiopacity of Portland cement associated with the following radiopacifying agents: bismuth oxide, zinc oxide, lead oxide, bismuth subnitrate, bismuth carbonate, barium sulfate, iodoform, calcium tungstate, and zirconium oxide. A ratio of 20% radiopacifier and 80% white Portland cement by weight was used for analysis. Pure Portland cement and dentin served as controls. Cement/radiopacifier and dentin disc-shaped specimens were fabricated, and radiopacity testing was performed according to the ISO 6876/2001 standard for dental root sealing materials. Using Insight occlusal films, the specimens were radiographed near to a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The radiographs were digitized and radiopacity compared with the aluminum stepwedge using Digora software (Orion Corporation Soredex, Helsinki, Finland). The radiographic density data were converted into mmAl and analyzed statistically by analysis of variance and Tukey-Kramer test (alpha = 0.05). The radiopacity of pure Portland cement was significantly lower (p < 0.05) than that of dentin, whereas all cement/radiopacifier mixtures were significantly more radiopaque than dentin and Portland cement alone (p < 0.05). Portland cement/bismuth oxide and Portland cement/lead oxide presented the highest radiopacity values and differed significantly from the other materials (p < 0.05), whereas Portland cement/zinc oxide presented the lowest radiopacity values of all mixtures (p < 0.05). All tested substances presented higher radiopacity than that of dentin and may potentially be added to the Portland cement as radiopacifying agents. However, the possible interference of the radiopacifiers with the setting chemistry, biocompatibility, and physical properties of the Portland cement should be further investigated before any clinical recommendation can be done. (J Endod 2009,35:737-740)

Radiopacity Evaluation of Calcium Aluminate Cement Containing Different Radiopacifying Agents

Introduction: The aim of this study was to evaluate the radiopacity of calcium aluminate cement (Endo Binder) with 3 different radiopacifiers (bismuth oxide, zinc oxide, or zirconium oxide) in comparison with gray mineral trioxide aggregate (GMTA), white MTA, and dental structures (enamel and dentin). Methods: Eighteen test specimens of each cement with thicknesses of 0.5, 1.0, 1.5, 2.0, 2.5, and 3.0 mm (n = 3) were made by using a stainless steel matrix and were adapted to a standardizing device (8 x 7 cm) with a graduated aluminum stepwedge varying from 2.0-16.0 mm in thickness. To compare the radiopacity of the cements with that of dental structures, slices of first molars with a thickness increasing from 0.5-3.0 mm were obtained and placed on the standardizing device. One occlusal radiograph for each tested cement was taken, with exposure time of 0.1 seconds and focus-film distance of 20 cm. Films were processed in an automatic device, and the mean radiopacity values were obtained by using a photodensitometer. Results: Mean values showed that the thicker the specimen was, the greater was its radiopacity. Only EndoBinder + bismuth oxide (EBBO) and GMTA demonstrated radiopacity values greater than 3.0 mm of the aluminum scale for all thicknesses. When zinc oxide was used as radiopacifier agent, EndoBinder only reached the desired radiopacity with a thickness of 2.0 mm, and with zirconium oxide it was 2.5 mm. Conclusions: Bismuth oxide was the most efficient radiopacifier for EndoBinder, providing adequate radiopacity in all studied thicknesses, as recommended by ISO 6876, being similar to GMTA. (J Endod 2011;37: 67-71)