Effect of Test Environment and Microstructure on the Flexural Strength of Dental Porcelains

Purpose: The objective of this study was to verify the influence of test environment on the flexural strength of dental porcelains with distinct microstructures. Material and Methods: Disk-shaped specimens from three dental porcelains with distinct leucite content (VM: zero; CE: 12; NS: 22 vol%) were manufactured and tested for biaxial flexural strength in air and immersed in artificial saliva. The results were analyzed by means of two-way ANOVA and Tukey`s test (alpha = 0.05). Results: The flexural strength (MPa) obtained for ambient air and artificial saliva environments, respectively, were: 110.0 +/- 16.0 and 81.5 +/- 10.8 for VM; 51.9 +/- 4.0 and 42.0 +/- 4.7 for CE; 72.0 +/- 11.5 and 63.6 +/- 5.8 for NS. A numerical decrease in the mean flexural strength was observed for all groups when specimens were tested under artificial saliva; however, the difference was only statistically significant for VM. Conclusions: The results indicate that the effect of water immersion on the flexural strength of dental porcelains varies according to their leucite content, as only the material without leucite in its microstructure (VM) showed significant strength degradation when tested under water.

The Erosive Potential of 1% Citric Acid Supplemented by Different Minerals: An In Vitro Study

Purpose: The objective of the present in vitro study was to evaluate the effect of different minerals in combination with 1% citric acid on dental erosion. Materials and Methods: Ninety enamel samples were randomly allocated to nine groups (G1. pure 1% citric acid solution [control]. G2. with 1 mM Ca: G3 with 0 047 mM F, G4. with 1 mM Fe. G5. with 1 mM P, G6 with 1 mM Ca and 0 047 mM F. G7. with 1 mM Ca and 1 mM P: G8: with 1 mM Fe and 0.047 mM F, G9. with 1 mM Ca, 1 mM P. 0 047 rnM F and 1.0 mM Fe) The samples were subjected to six pH cycles, each consisting of immersion in pure or modified 1% citric acid (1 min) followed by storage in artificial saliva (59 min) Enamel wear was assessed using profilometry. Results: Data were analysed using analysis of variance and Tukey test (P < 0 05) Enamel loss (mean +/- SD) amounted to between 0 87 +/- 0 30 and 1 74 +/- 0 74 mu m but did not significantly differ among the groups Conclusions: The modification of 1% citric acid with different minerals did not have a protective effect on enamel erosion

Proteomic analysis of kidney in rats chronically exposed to fluoride

Two-dimensional gel electrophoresis (2-DE) was used to better understand alterations in renal metabolism induced by fluoride (F). Three groups of weanling male Wistar rats were treated with drinking water containing 0 (control), 5, or 50 ppm F for 60 days (n=6/group). Kidneys were collected for proteomic and histological (HE) analysis. After protein isolation, renal proteome profiles were examined using 2-DE and Colloidal Coomassie Blue staining. Protein spots with a 2-fold significant difference as detected by quantitative intensity analysis (image Master Platinum software) and t-test (p < 0.05) were excised and analyzed by MALDI-TOF MS (matrix assisted laser desorption ionization-time-of-flight mass spectrometry). The histological analysis revealed no damage in kidneys induced by F, except for a vascular congestion in the 50 ppm F group. Between control vs 50 ppm F, and control vs 5 ppm F groups, 12 and 6 differentially expressed proteins were detected, respectively. Six proteins, mainly related with metabolism, detoxification and housekeeping, were successfully identified. At the high F group, pyruvate carboxylase, a protein involved in the formation of oxaloacetate was found to be downregulated, while enoyl coenzyme A hydratase, involved in fatty acids oxidation, was found to be upregulated. Thus, proteomic analysis can provide new insights into the alterations in renal metabolism after F exposure, even in low doses. (C) 2009 Elsevier Ireland Ltd. All rights reserved.

Effect of different concentrations of fluoride in dentifrices on dentin erosion subjected or not to abrasion in situ/ex vivo

This in situ/ex vivo study assessed the effect of different concentrations of fluoride in dentifrices on dentin subjected to erosion or to erosion plus abrasion. Ten volunteers took part in this crossover and double-blind study performed in 3 phases (7 days). They wore acrylic palatal appliances containing 4 bovine dentin blocks divided in two rows: erosion and erosion plus abrasion. The blocks were subjected to erosion by immersion ex vivo in a cola drink (60 s, pH 2.6) 4 times daily. During this step, the volunteers brushed their teeth with one of three dentifrices D (5,000 ppm F, NaF, silica); C (1,100 ppm F, NaF, silica) and placebo (22 ppm F, silica). Then, the respective dentifrice slurry (1: 3) was dripped on dentin surfaces. While no further treatment was performed in one row, the other row was brushed using an electric toothbrush for 30 s ex vivo. The appliances were replaced in the mouth and the volunteers rinsed with water. Dentin loss was determined by profilometry and analyzed by 2-way ANOVA/Bonferroni test (alpha = 0.05). Dentin loss after erosive-abrasive wear was significantly greater than after erosion alone. Wear was significantly higher for the placebo than for the D and C dentifrices, which were not significantly different from each other. It can be concluded that the presence of fluoride concentrations around 1,100 ppm in dentifrices is important to reduce dentin wear by erosion and erosion + abrasion, but the protective effect does not increase with fluoride concentration. Copyright (C) 2008 S. Karger AG, Basel.

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Objective: As resin-modified glass-ionomer cement (RMGIC) is an adhesive material, its association to dentin bonding agents (DBAs) was previously proposed. This study investigated the adjunctive behavior of an RMGIC with etch-and-rinse bonding systems under in situ/ex vivo cariogenic challenge. Method and Materials: Bovine enamel blocks (3 3 2 mm) were randomly assigned to group VP, Vitremer + its own primer (3M ESPE); group VSB, Vitremer + Single Bond (3M ESPE); and group VPB, Vitremer + Prime & Bond 2.1 (Dentsply). Two blocks of each group were randomly placed in an acrylic palatal appliance, so each appliance included six blocks. Volunteers (n = 10) wore these appliances according to given instructions to promote a sucrose challenge eight times/day for 15 days. After this period, the blocks were removed from the devices and cleaned, and demineralization was assessed through longitudinal microhardness analysis (Knoop indenter, 25 g/5 s). Data were submitted to three-way ANOVA and Tukey test (P < .05). Results: No treatment was able to completely avoid demineralization. All materials showed a statistically significant difference in mineral loss when the microhardness on the outer enamel was compared with deeper regions (P < .05). Conclusion: Association of the tested RMGICs with etch-and-rinse DBAs did not seem to be more beneficial against caries than the conventional treatment with RMGIC. (Quintessence Int 2010; 41: e192-e199)

The role of surface sealants in the roughness of composites after a simulated toothbrushing test

Objectives: To evaluate the influence of two surface sealants (BisCover/Single Bond) and three application techniques (unsealed/conventional/co-polymerization) on the roughness of two composites (Filtek Z250/Z350) after the toothbrushing test. Methods: Seventy-two rectangular specimens (5 mm x 10 mm x 3 mm) were fabricated and assigned into 12 groups (n = 6). Each sample was subjected to three random roughness readings at baseline, after 100,000 (intermediate), and 200,000 (final) toothbrushing strokes. Roughness (R) at each stage was obtained by the arithmetic mean of the reading of each specimen. Sealant removal was qualitatively examined (optical microscope) and classified into scores (0-3). Data were analyzed by Student`s paired t-test, two-way ANOVA/Tukey`s test, and by Wilcoxon, Kruskal-Wallis and Miller`s test (alpha = 0.05). Results: Z250 groups at baseline did not differ statistically from each other. Unsealed Z350 at baseline had lower R values. All the unsealed groups presented gradual decrease in R from baseline to final brushing. From baseline to the inter-mediate stage, Z250 co-polymerized groups presented a significant reduction in R (score 3). Conventionally sealed groups had no significant changes in R (scores 2-0.8). From baseline to the intermediate stage, the conventionally sealed Z350 Single Bond group had an increase in R (score 1.5). In the final stage, all the conventionally sealed groups presented a reduction in R (scores 0.7-0). Co-polymerized Single Bond groups had a significant reduction in R (scores 2.5-2.7), and co-polymerized BisCover groups an increase in R (scores 2.8-3). Conclusions: At any brushing stage, sealed composites presented superior performance when compared with unsealed composites. (C) 2009 Elsevier Ltd. All rights reserved.

Evaluation of the radiopacity of some commercial and experimental root-end filling materials

Objective. The aim of the present study was to evaluate the radiopacity of 5 root end filling materials (white MTA Angelus, MTA Bio, light-cured MTA, Sealepox RP, and Portland cement clinker with bismuth oxide and calcium sulfate). Method. Five specimens, 10 mm in diameter and 1 mm in thickness according to specification ISO 6876: 2001 were fabricated from each material and radiographed using Insigth occlusal films close to a graduated aluminum step-wedge (2 to 16 mm in thickness). Radiographs were digitized and compared to the aluminum step-wedge. The radiographic density data were converted into millimeters of aluminum (mm Al), using the Digora 1.51 software. Results were evaluated statistically using the analysis of variance (ANOVA) followed by Tukey test. The level of significance was set at 5% (P<.05%). Results. Radiopacity values ranged from 1.21 mm Al (light-cured MTA) to 6.45 mm Al (MTA Angelus). Comparison between materials showed significant difference (P<.05) between MTA Angelus and all other materials, between Sealepox RP and MTA Bio, and between light-cured MTA and Portland cement clinker. Light-cured MTA was significantly less radiopaque than all other materials. No significant difference (P>.05) was found between MTA Bio and Portland cement clinker. Conclusions. All retrograde filling materials evaluated showed greater radiopacity than dentin. All the materials, except light-cured MTA met the minimum radiopacity standards of 3 mm Al recognized by the ISO 6876: 2001 and ADA n.57. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e35-e38)

Evaluation of the temperature of different refrigerant sprays used as a pulpal test

The temperature of different refrigerant sprays (Endo-Ice, Endo-Frost, Coolermatic and Sprayon Contact and Tuner Cleaner) used as pulpal tests were evaluated in vitro. A thermocouple placed inside the pulp chamber of a maxillary central incisor was used to register the temperature changes when the refrigerant sprays were applied with a cotton swab, for 10 s. Results indicate that Endo-Ice and Endo-Frost presented the lowest temperatures among the refrigerant sprays tested. Temperatures measured inside the pulp chamber, however, were statistically similar in all groups.

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling. Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05). Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps. Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

Enamel Wetness Effects on Bond Strength Using Different Adhesive Systems

Objective: To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. Methods: This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive systems (Clearfil SE Bond; and Xeno IV). Flat bovine enamel surfaces were either air-dried for 30 seconds or blotted with absorbent paper after acid-etching for the conventional bonding agents or before the application of self-etching bonding agents. The resin composite EsthetX was bonded to flat surfaces that had been treated with one of the adhesives, following the manufacturer`s instructions. After being stored in water at 37 degrees C for one week, bonded specimens were broken in shear. Data were evaluated with two-way analysis of variance (ANOVA) and Student-Newman-Keuls tests (alpha=0.05). For comparing each condition individually, regardless of the adhesive or wetness condition, a one-way ANOVA and a Student-Newman-Keuls test (alpha=0.05) were applied. Results: The two-way ANOVA showed significant differences among adhesive systems. An interaction effect was also observed (p < 0.05), but wetness did not influence shear bond strength (p=0.98). The one-way ANOVA showed that the all-in-one adhesive was the only material influenced by the presence of water at the enamel`s surface. Conclusion: The all-in-one adhesive behaved differently depending on whether the enamel surface was dry or wet.

Preventive effect of an iron varnish on bovine enamel erosion in vitro

Objective: The aim of this study was to evaluate, in vitro, the effect of an experimental varnish containing iron on the dissolution of bovine enamel by carbonated beverage. Methods: Eighty specimens were randomly allocated to four groups (n = 20 per group), according to the following treatments: Fe varnish (FeV, 10 mmoL/L Fe), F varnish (FV, 2.71% F), placebo varnish (PV) and control (not treated, NT). The varnishes were applied in a thin layer and removed after 6 h. Then, the samples were submitted to six cycles, alternating re- and demineralisation (only 1 day). Demineralisation was performed with the beverage Coca-Cola (R) (10 min, 30 mL/block) and remineralisation with artificial saliva for I h. In order to determine the amount of enamel dissolved, the wear was analysed by profilometry. Data were analysed by ANOVA and Tukey`s test (p < 0.05). Results: The mean wear (+/- S.E.) was significantly lesser for the FeV (0.451 +/- 0.018 mu m) when compared to the other treatments. The FV caused significantly less wear (0.554 +/- 0.022 mu m) when compared to PV (0.991 +/- 0.039 mu m) and NT (1.014 +/- 0.033), which did not significantly differ from each other. Conclusions: The results suggest that the iron varnish can interfere with the dissolution of dental enamel in the presence of acidic beverages. (C) 2008 Elsevier Ltd. All rights reserved.

Six-year evaluation of the atraumatic restorative treatment approach in permanent-tooth Class III restorations

Purpose: The aim of this study was to assess the 6-year performance of the ART (atraumatic restorative treatment) approach in Class III restorations in permanent teeth. Materials and Methods: A total of 127 ART Class III restorations, using Ketac-Molar (3M ESPE) ionomer cement, was performed in 58 adult patients by one experienced operator in 1998. After a 6 years, 34 patients and 65 restorations were evaluated according to ART criteria. Two calibrated examiners carried out the evaluation. Data were analyzed by exact 95% Confidence Interval and Survival Analysis using the Jackknife method for standard error determination. Results: Among assessed restorations, 73.8% (95% CI = 61.5% to 86.2%) were in good condition and classified as successful, with a 67.6% (95% CI = 54.4% to 80.7%) cumulative survival rate. Failed restorations included 13.9% completely or partially missing restorations, 9.2% restorations that had been replaced by other treatment, 1.5% restorations with a large defect at the margin, and 1.5% restorations that presented high wear on the surface. No caries was observed even in those teeth in which restorations were absent. Conclusion: The 6-year success rate of the ART approach in anterior permanent teeth (Class III) was considered high.

Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).

SEM observation of the bond integrity of fiber-reinforced composite posts cemented into root canals

Objectives. To test the null hypothesis that continuity of resin cement/dentin interfaces is not affected by location along the root canal walls or water storage for 3 months when bonding fiber posts into root canals. Methods. Fiber posts were luted to bovine incisors using four resinous luting systems: Multilink, Variolink II, Enforce Dual and Enforce PV. After cementation, roots were longitudinally sectioned and epoxy resin replicas were prepared for SEM analysis (baseline). The original halves were immersed in solvent, replicated and evaluated. After 3 months water storage and a second solvent immersion, a new set of replicas were made and analyzed. The ratio (%) between the length (mm) of available bonding interface and the actual extension of bonded cement/dentin interface was calculated. Results. Significant lower percent values of bond integrity were found for Multilink (8.25%) and Variolink 11 (10.08%) when compared to Enforce Dual (25.11%) and Enforce PV (27.0%) at baseline analysis. The same trend was observed after immersion in solvent, with no significant changes. However, bond integrity was significantly reduced after 3 months water storage and a second solvent immersion to values below 5% (Multilink = 3.31%, Variolink=1.87%, Enforce Dual=1.20%, and Enforce PV=0.75%). The majority of gaps were depicted at the apical and middle thirds at baseline and after immersion in solvent. After 3 months, gaps were also detected at the cervical third. Significance. Bond integrity at the cement/dentin interface was surprisingly low after cementation of fiber posts to root canals with all resin cements. That was not significantly altered after immersion in solvent, but was further compromised after 3 months water storage. Gaps were mainly seen at middle and apical thirds throughout the experiment and extended to the cervical third after water storage for 3 months. Bond integrity of fiber posts luted to root canals was affected both by location and water storage. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.