BisGMA/TEGDMA ratio and filler content effects on shrinkage stress

Objective. To investigate the contributions of BisGMA:TEGDMA and filler content on polymerization stress, along with the influence of variables associated with stress development, namely, degree of conversion, reaction rate, shrinkage, elastic modulus and loss tangent for a series of experimental dental composites. Methods. Twenty formulations with BisGMA: TEGDMA ratios of 3: 7, 4: 6, 5: 5, 6: 4 and 7: 3 and barium glass filler levels of 40, 50, 60 or 70 wt% were studied. Polymerization stress was determined in a tensilometer, inserting the composite between acrylic rods fixed to clamps of a universal test machine and dividing the maximum load recorded by the rods cross-sectional area. Conversion and reaction rate were determined by infra-red spectroscopy. Shrinkage was measured by mercury dilatometer. Modulus was obtained by three-point bending. Loss tangent was determined by dynamic nanoindentation. Regression analyses were performed to estimate the effect of organic and inorganic contents on each studied variable, while a stepwise forward regression identified significant variables for polymerization stress. Results. All variables showed dependence on inorganic concentration and monomeric content. The resin matrix showed a stronger influence on polymerization stress, conversion and reaction rate, whereas filler fraction showed a stronger influence on shrinkage, modulus and loss tangent. Shrinkage and conversion were significantly related to polymerization stress. Significance. Both the inorganic filler concentration and monomeric content affect polymerization stress, but the stronger influence of the resin matrix suggests that it may be possible to reduce stress by modifying resin composition without sacrificing filler content. The main challenge is to develop formulations with low shrinkage without sacrificing degree of conversion. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Activity of Matrix Metalloproteinases in Bovine versus Human Dentine

Metalloproteinases (MMPs) have been implicated with metabolism of collagen in physiological and pathological processes in human dentine. As bovine teeth have been used as a substitute for human teeth in laboratory analysis, this study evaluated the activity of MMP-2 and -9 in bovine versus human dentine. Bovine and human dentine fragments, from crowns and roots, were powderized. Protein extraction was performed by two protocols: a neutral extraction with guanidine-HCl/EDTA (pH 7.4) and an acidic extraction with citric acid (pH 2.3). Gelatinolytic activities of extracts were revealed by zymography. MMP-2 and -9 were detected in crown and root dentine from bovine and human teeth. Total activities of MMP-2 were 11.4 +/- 2.2, 14.6 +/- 2.0, 9.7 +/- 1.2 and 12.4 +/- 0.9 ng/ml for bovine root, human root, bovine crown and human crown dentine, respectively. Corresponding activities for MMP-9 were 14.9 +/- 2.0, 15.3 +/- 1.3, 15.4 +/- 1.3 and 15.5 +/- 1.3 ng/ml, respectively. Bovine dentine was found to be a reliable substrate for studies involving the activity of MMP-2 and -9. Copyright (C) 2011 S. Karger AG, Basel

Effect of Iron on Matrix Metalloproteinase Inhibition and on the Prevention of Dentine Erosion

It is known that some metal salts can inhibit matrix metalloproteinase (MMP) activity, but the effect of iron has not been tested yet. On the other hand, it has recently been suggested that MMP inhibition might influence dentine erosion. Based on this, the aims of this study were: (1) to test in vitro the effect of FeSO(4) on MMP-2 and -9 activity, and (2) to evaluate in situ the effect of FeSO(4) gel on dentine erosion. MMP-2 and -9 activities were analysed zymographically in buffers containing FeSO(4) in concentrations ranging between 0.05 and 1.5 mmol/l or not. Volunteers (n = 10) wore devices containing bovine dentine blocks (n = 60) previously treated with the following gel treatments: FeSO(4) (1 mmol/l FeSO(4)), F (NaF 1.23%; positive control) and placebo (negative control). The gels were applied once and removed after 1 min. Erosion was performed extraorally with Coca-Cola 4 times per day for 5 min over 5 days. Dentine wear was evaluated by profilometry. The data were analysed by Kruskal-Wallis and Dunn`s tests (p < 0.05). FeSO(4) inhibited both MMP-2 (IC(50) = 0.75 mmol/l) and MMP-9 (IC(50) = 0.50 mmol/l) activities. In the in situ experiment, the mean wear (+/- SD) found for the F gel (0.79 8 +/- 0.08 mu m) was significantly reduced in more than 50% when compared to the placebo gel (1.77 +/- 0.33 mu m), but the FeSO(4) gel completely inhibited the wear (0.05 +/- 0.02 mu m). Since FeSO(4) was able to inhibit MMP in vitro, it is possible that the prevention of dentine wear by the FeSO(4) gel in situ might be due to MMP inhibition, which should be investigated in further studies. Copyright (C) 2010 S. Karger AG, Basel

A direct composite resin stratification technique for restoration of the smile

Composite resins can be used to improve the esthetics of the smile at a low cost and with relatively high clinical performance, The aim of this article was to describe an approach to restore and enhance the esthetic appearance of the anterior dentition through vital tooth whitening and the direct layering of composite resin during predictable esthetic procedures, (Quintessence lot 2011;42205-211)

Expression analysis of matrix metalloproteinase-9 in epithelialized and nonepithelialized apical periodontitis lesions

Objective. The objective of this study was to determine the expression of matrix metalloproteinase-9 (MMP-9) in apical periodontitis lesions. Study design. Nineteen epithelialized and 18 nonepithelialized apical periodontitis lesions were collected after periapical surgery. After histological processing, serial sectioning, H&E staining, and microscopic analysis, 10 epithelialized and 10 nonepithelialized lesions were selected for immunohistochemical analysis for MMP-9 and CD 68. At least one third of each specimen collected was frozen at -70 degrees C for further mRNA isolation and reverse transcription into cDNA for real-time-PCR procedures. Geometric averaging of multiple housekeeping genes normalized MMP-9 mRNA expression level. Results. Polymorphonuclear neutrophils, macrophages and lymphocytes presented MMP-9 positive immunostaining in both types of lesions. When present, epithelial cells were also stained. The number and the ratio of MMP-9(+)/total cells were greater in nonepithelialized than epithelialized lesions (P = .0001) presenting a positive correlation to CD68(+)/total cells (P = .045). Both types of lesions presented increased MMP-9 expression (P < .0001) when compared to healthy periapical ligaments. However, no significant differences were observed for MMP-9 mRNA expression between ephithelized and nonephithelized lesions. Conclusion. The present data suggest the participation of several inflammatory cells, mainly CD68(+) cells, in the MMP-9 expression in apical periodontitis lesions. MMP-9 could be actively enrolled in the extracellular matrix degradation in apical periodontitis lesions. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 107: 127-132)

Influence of curing rate on softening in ethanol, degree of conversion, and wear of resin composite

Purpose: To investigate the effect of curing rate on softening in ethanol, degree of conversion, and wear of resin composites. Methods: With a given energy density and for each of two different light-curing units (QTH or LED), the curing rate was reduced by modulating the curing mode. Thus, the irradiation of resin composite specimens (Filtek Z250, Tetric Ceram, Esthet-X) was performed in a continuous curing mode and in a pulse-delay curing mode. Wallace hardness was used to determine the softening of resin composite after storage in ethanol. Degree of conversion was determined by infrared spectroscopy (FTIR). Wear was assessed by a three-body test. Data were submitted to Levene`s test, one and three-way ANOVA, and Tukey HSD test (alpha= 0.05). Results: Immersion in ethanol, curing mode, and material all had significant effects on Wallace hardness. After ethanol storage, resin composites exposed to the pulse-delay curing mode were softer than resin composites exposed to continuous cure (P< 0.0001). Tetric Ceram was the softest material followed by Esthet-X and Filtek Z250 (P< 0.001). Only the restorative material had a significant effect on degree of conversion (P< 0.001): Esthet-X had the lowest degree of conversion followed by Filtek Z250 and Tetric Ceram. Curing mode (P= 0.007) and material (P< 0.001) had significant effect on wear. Higher wear resulted from the pulse-delay curing mode when compared to continuous curing, and Filtek Z250 showed the lowest wear followed by Esthet-X and Tetric Ceram. (Am J Dent 2011;24:115-118).

Expression of matrix metalloproteinases-2 and-9 and RECK during alveolar bone regeneration in rat

MMPs are endopeptidases that play a pivotal role in ECM turnover. RECK is a single membrane-anchored MMP-regulator. Here, we evaluated the temporal and spatial expression of MMP-2, MMP-9, and RECK during alveolar bone regeneration. The maxillary central incisor of Wistar rats was extracted and the animals were killed at 1, 3, 7, 10, 14, 21, 28, and 42 days post-operatively (n = 3/period). The hemimaxillae were collected, demineralized and embedded in paraffin. Immunohistochemical analysis was performed by the immunoperoxidase technique with polyclonal antibodies. On day 1, polymorphonuclear cells in the blood clot presented mild immunolabeling for MMPs. During bone remodeling, osteoblasts facing new bone showed positive staining for gelatinases and RECK in all experimental periods. MMPs were also found in the connective tissue and endothelial cells. Our results show for the first time that inactive and/or active forms of MMP-2, MMP-9 and RECK are differentially expressed by osteogenic and connective cells during several events of alveolar bone regeneration. This may be important for the replacement of the blood clot by connective tissue, and in the formation, maturation and remodeling of new bone.

The Effect of Framework Design on Fracture Resistance of Metal-Ceramic Implant-Supported Single Crowns

This study evaluated the effect of framework design on the fracture resistance of metal-ceramic implant-supported crowns. Screw-retained molar crowns with a screw access hole composed of metal or porcelain were compared to a cement-retained crown (control). For each group (n = 10), five crowns were subjected to dynamic loading (1,200,000 x 100 N x 2 Hz at 37 degrees C). Afterward, all specimens were loaded to failure using a universal testing machine. Significant differences could be established between the cement-and screw-retained groups (P <= .05), but no difference was found between the screw-retained groups and the specimens subjected to dynamic loading. Occlusal discontinuity of screw-retained crowns affects their resistance, and the metallic support on the screw access hole did not reinforce the crowns. Int J Prosthodont 2010;23:350-352.

Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).

Fracture resistance of endodontically treated teeth with different heights of crown ferrule restored with prefabricated carbon fiber post and composite resin core by intermittent loading

This study evaluated the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber posts and varying quantities of coronal dentin. Sixty freshly extracted upper canines were randomly divided into groups of 10 teeth each. The specimens were exposed to 250,000 cycles in a controlled chewing simulator. All intact specimens were subjected to a static load (N) in a universal testing machine at 45 degrees to the long axis. Data were analyzed by 1-way analysis of variance and Tukey test (alpha = .05). Significant differences (P < .001) were found among the mean fracture forces of the test groups (positive control, 0 mm, 1 mm, 2 mm, 3 mm, and negative control groups: 1022.82 N, 1008.22 N, 1292.52 N, 1289.19 N, 1255.38 N, and 1582.11, respectively). These results suggested that the amount of coronal dentin did not significantly increase the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber post and composite resin core. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2008;106:e52-e57)

SEM observation of the bond integrity of fiber-reinforced composite posts cemented into root canals

Objectives. To test the null hypothesis that continuity of resin cement/dentin interfaces is not affected by location along the root canal walls or water storage for 3 months when bonding fiber posts into root canals. Methods. Fiber posts were luted to bovine incisors using four resinous luting systems: Multilink, Variolink II, Enforce Dual and Enforce PV. After cementation, roots were longitudinally sectioned and epoxy resin replicas were prepared for SEM analysis (baseline). The original halves were immersed in solvent, replicated and evaluated. After 3 months water storage and a second solvent immersion, a new set of replicas were made and analyzed. The ratio (%) between the length (mm) of available bonding interface and the actual extension of bonded cement/dentin interface was calculated. Results. Significant lower percent values of bond integrity were found for Multilink (8.25%) and Variolink 11 (10.08%) when compared to Enforce Dual (25.11%) and Enforce PV (27.0%) at baseline analysis. The same trend was observed after immersion in solvent, with no significant changes. However, bond integrity was significantly reduced after 3 months water storage and a second solvent immersion to values below 5% (Multilink = 3.31%, Variolink=1.87%, Enforce Dual=1.20%, and Enforce PV=0.75%). The majority of gaps were depicted at the apical and middle thirds at baseline and after immersion in solvent. After 3 months, gaps were also detected at the cervical third. Significance. Bond integrity at the cement/dentin interface was surprisingly low after cementation of fiber posts to root canals with all resin cements. That was not significantly altered after immersion in solvent, but was further compromised after 3 months water storage. Gaps were mainly seen at middle and apical thirds throughout the experiment and extended to the cervical third after water storage for 3 months. Bond integrity of fiber posts luted to root canals was affected both by location and water storage. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fatigue life and failure modes of crowns systems with a modified framework design

Objectives: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. Methods: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n = 10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n = 10 each). Fatigue loading was delivered with a spherical steel indenter (3.18 mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300 N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. Results: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. Conclusions: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system. (C) 2010 Elsevier Ltd. All rights reserved.

Failure modes of Y-TZP crowns at different cusp inclines

Objectives To compare the reliability of the disto-facial (DF) and mesio-lingual (ML) cusps of an anatomically correct zirconia (Y-TZP) crown system The research hypotheses tested were (1) fatigue reliability and failure mode are similar for the ML and DF cusps, (2) failure mode of one cusp does not affect the failure of the other Methods The average dimensions of a mandibular first molar crown were imported into CAD software, a tooth preparation was modelled by 1 5 mm marginal high reduction of proximal walls and occlusal surface by 2 0 mm The CAD-based tooth preparation was milled and used as a die to fabricate crowns (n = 14) with porcelain veneer on a 0 5 mm Y-TZP core. Crowns were cemented on composite reproductions of the tooth preparation The crowns were step-stress mouth motion fatigued with sliding (0 7 mm) a tungsten-carbide indenter of 6 25 mm diameter down on the inclines of either the DF or ML cusps Use level probability Weibull curve with use stress of 200 N and the reliability for completion of a mission of 50,000 cycles at 200 N load were calculated Results Reliability for a 200 N at 50,000 cycles mission was not different between tested cusps SEM imaging showed large cohesive failures within the veneer for the ML and smaller for the DF Fractures originated from the contact area regardless of the cusp loaded Conclusion No significant difference on fatigue reliability was observed between the DF compared to the ML cusp Fracture of one cusp did not affect the other (c) 2010 Elsevier Ltd All rights reserved

Monolithic CAD/CAM Lithium Disilicate Versus Veneered Y-TZP Crowns: Comparison of Failure Modes and Reliability After Fatigue

Purpose: The aim of this research was to evaluate the fatigue behavior and reliability of monolithic computer-aided design/computer-assisted manufacture (CAD/CAM) lithium disilicate and hand-layer-veneered zirconia all-ceramic crowns. Materials and Methods: A CAD-based mandibular molar crown preparation, fabricated using rapid prototyping, served as the master die. Fully anatomically shaped monolithic lithium disilicate crowns (IPS e.max CAD, n = 19) and hand-layer-veneered zirconia-based crowns (IPS e.max ZirCAD/Ceram, n = 21) were designed and milled using a CAD/CAM system. Crowns were cemented on aged dentinlike composite dies with resin cement. Crowns were exposed to mouth-motion fatigue by sliding a WC-indenter (r = 3.18 mm) 0.7 mm lingually down the distobuccal cusp using three different step-stress profiles until failure occurred. Failure was designated as a large chip or fracture through the crown. If no failures occurred at high loads (> 900 N), the test method was changed to staircase r ratio fatigue. Stress level probability curves and reliability were calculated. Results: Hand-layer-veneered zirconia crowns revealed veneer chipping and had a reliability of < 0.01 (0.03 to 0.00, two-sided 90% confidence bounds) for a mission of 100,000 cycles and a 200-N load. None of the fully anatomically shaped CAD/CAM-fabricated monolithic lithium disilicate crowns failed during step-stress mouth-motion fatigue (180,000 cycles, 900 N). CAD/CAM lithium disilicate crowns also survived r ratio fatigue (1,000,000 cycles, 100 to 1,000 N). There appears to be a threshold for damage/bulk fracture for the lithium disilicate ceramic in the range of 1,100 to 1,200 N. Conclusion: Based on present fatigue findings, the application of CAD/CAM lithium disilicate ceramic in a monolithic/fully anatomical configuration resulted in fatigue-resistant crowns, whereas hand-layer-veneered zirconia crowns revealed a high susceptibility to mouth-motion cyclic loading with early veneer failures. Int J Prosthodont 2010; 23: 434-442.

Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.