Microhardness of resin cements in the intraradicular environment: Effects of water storage and softening treament

Objectives. To analyze the microhardness of four dual-cure resin cements used for cementing fiber-reinforced posts under the following conditions: after 7 days of storage in water, after additional 24 h of immersion in 75% ethanol, and after 3 months of storage in water. Hardness measurements were taken at the cervical, middle and apical thirds along the cement line. Methods. Root canals of 40 bovine incisors were prepared for post space. Fibrekor (R) glass fiber-reinforced posts (Jeneric/Pentron) of 1 mm in diameter were cemented using Panavia F 2.0 (Kuraray), Variolink (Ivoclar-Vivadent), Rely X Unicem (3M ESPE) or Duolink (Bisco) (N = 10). After 7 days of water storage at 37 degrees C, half the sample (N = 5) was longitudinally sectioned and the initial microhardness measured along the cement line from cervical to apex. These same samples were further immersed in 75% ethanol for 24 h and reassessed. The remaining half (N = 5) was kept unsectioned in deionized water at 37 degrees C for 3 months, followed by sectioning and measuring. Data were analyzed by a series of two-way ANOVA and Tukey tests at alpha = 5%. Results. Statistically significant differences were identified among the cements, thirds and conditions. Significant interactions were also observed between cements and thirds and between cements and conditions. Panavia F exhibited significantly higher initial microhardness than the other three cements, which showed no statistical difference among themselves. Variolink and Duolink showed significantly higher microhardness values in the cervical third, without significant difference among the thirds for the other cements. Immersion in ethanol significantly reduced the hardness values for all cements, regardless of the thirds. Storage in water for 3 months had no influence on the hardness of most of the cements, with the exception of Unicem that showed a significant increase in the hardness values after this period. Results showed heterogeneity in the microhardness of the cements inside the canal. All cements presented some degree of softening after ethanol treatment, which suggests instability of the polymer. The quality of curing of resin cements in the root canal environment seems unpredictable and highly material dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical stability of adhesives under water storage

Objectives. To evaluate the effects of storage condition (wet or dry) and storage time (24 h and 3 months) on the ultimate tensile strength (UTS) of Single Bond (SB), 3M-ESPE; Opti Bond Solo Plus (OB), Kerr; One Step (OS), Bisco, and Prime & Bond NT (PB), Dentsply adhesive resins. Methods. Hourglass-shaped specimens were obtained from a metallic matrix. Each adhesive was dispensed to fill the molds completely and left undisturbed in a dark chamber for 4 min at 37 degrees C for solvent evaporation. They were individually light-cured for 80 s at 500 mW/cm(2) and randomly divided into three groups: 24 h of water storage; 3 months of water storage; 3 months of dry storage. The specimens were tested in tension at 0.5 mm/min using the microtensile method and data were analyzed by two-way ANOVA and SNK tests for each material. Results. Water storage for 3 months did not cause significant changes in the UTS of any of the adhesives (p-value). Values for water storage ranged from 25.9 MPa for Single Bond at 24 h to 32.7 MPa for Prime & Bond NT after 3 months. Dry storage for 3 months yielded significantly higher UTS for most adhesives, which ranged from approximately 20% for Opti Bond to 160% higher values for Single Bond compared to their 3 months wet storage values. Conclusion. The effects of storage condition and time on the UTS of adhesives were material-dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Direct and transdentinal antibacterial activity of chlorhexidine

Purpose: To evaluate the antibacterial effect of different chlorhexidine (CHX) concentrations against Streptococcus mutans using the agar-diffusion method with and without human dentin discs placed between the bacteria and the test substances. Methods: For the direct application (agar-well technique), a base layer containing 15 mL of BHI agar and 300 mu L. of S. mutans inoculum (10(9) cfu/mL) was prepared in Petri dishes. Six wells per dish were made at equidistant points and immediately filled with CHX gels (0.12%, 0.2%, 1% and 2%), 35% phosphoric acid and pure natrosol (n=6 wells/substance). Paper discs soaked in sterile distilled water served as control group (n=6). For the indirect application (transdentinal diffusion), 0.2 mm- and 0.5 mm-thick human dentin discs (36 discs/thickness) had the hydraulic conductance determined, which allowed the homogeneous allocation of them to the experimental and control groups. The discs were placed at equidistant points on the Petri dishes containing BHI with the S. mutans inoculum (six discs per dish; one per substance) with the pulpal side in contact with the bacteria. In the discs treated with CHX gels, dentin surface was etched with H(3)PO(4) and rinsed with distilled water before CHX gel application for 1 minute. After both direct and indirect application, the dishes were incubated for 24 hours and the bacterial growth inhibition zones formed around the wells and dentin discs were measured. Data were analyzed statistically by the non-parametric Kruskal-Wallis and Mann-Whitney tests at 5% significance level. Results: In the direct test, all CHX concentrations presented a dose-dependent antibacterial activity against S. mutans. In the indirect test, there were statistically significant differences (P< 0.05) among all groups and the largest microbial growth inhibition zones were observed when 2% CHX was applied on 0.2 mm-thick discs (P< 0.05). It was concluded that all evaluated CHX gels exhibited both direct and transdentinal antibacterial activity against S. mutans. This effect of CHX was strongly influenced by the CHX concentration as well as the dentin barrier thickness. (Am J Dent 2010;23:255-259).

Bacterial leakage evaluation of root canals filled with different endodontic sealers

Objective. The objective of this study was to evaluate the sealing ability of AH Plus, Epiphany, Acroseal, Endofill, and Polifil after active lateral condensation technique, by using a bacterial test, during 64 days. Study design. One hundred bovine incisors were cleaned and shaped; then they were filled with the endodontic sealers and adapted into a microcentrifuge tube. The setup root/microcentrifuge tube was added to glass flasks containing Brain Heart Infusion broth. A culture of Enterococcus faecalis was inserted into the upper chamber of each assembly. Daily leakage was evaluated through the broth turbidity. Results. The results were submitted to statistical analysis (Kaplan-Meier method, Kruskal-Wallis and Dunn tests). Conclusions. AH Plus and Endofill had the worst sealing ability when compared with Polifil, which showed the least leakage. Acroseal and Epiphany showed a tendency toward having an intermediate behavior; however, there was no significant difference among Acroseal, Epiphany, and the other sealers. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e56-e60)

Bond strength of AH Plus and Epiphany sealers on root dentine irradiated with 980 nm diode laser

Aim To evaluate the bond strength of AH Plus and Epiphany sealers to human root canal dentine irradiated with a 980 nm diode laser at different power and frequency parameters, using the push-out test. Methodology Sixty canine roots were sectioned below the cementoenamel junction to provide 4-mm-thick dentine discs that had their root canals prepared with a tapered bur and irrigated with sodium hypochlorite, ethylenediaminetetraacetic acid and distilled water. The specimens were assigned to five groups (n = 12): one control (no laser) and four experimental groups that were submitted to 980 nm diode laser irradiation at different power (1.5 and 3.0 W) and frequency (continuous wave and 100 Hz) parameters. Half of specimens in each group had their canals filled with AH Plus sealer and half with Epiphany. The push-out test was performed and data (MPa) were analysed statistically by ANOVA and Tukey`s test (P < 0.05). The specimens were split longitudinally and examined under SEM to assess the failure modes after sealer displacement. Results The specimens irradiated with the diode laser and filled with AH Plus had significantly higher bond strength values (8.69 +/- 2.44) than those irradiated and filled with Epiphany (3.28 +/- 1.58) and the nonirradiated controls (3.86 +/- 0.60). The specimens filled with Epiphany did not differ significantly to each other or to the control (1.75 +/- 0.69). There was a predominance of adhesive failures at Epiphany-dentine interface (77%) and mixed failures at AH Plus-dentine interface (67%). Conclusions The 980 nm diode laser irradiation of root canal dentine increased the bond strength of AH Plus sealer, but did not affect the adhesion of Epiphany sealer.

Temperature variation at the external root surface during 980-nm diode laser irradiation in the root canal

Objective: To assess the temperature variation in the cervical, middle and apical thirds of root external wall, caused by 980-nm diode laser irradiation with different parameters. Methods: The roots of 90 canines, had their canals instrumented and were randomly distributed into 3 groups (n = 30) according to the laser potency (1.5 W, 3.0 W and 5.0 W). Each group was subdivided into 3 (n = 10) according to the frequency (CM, 100 Hz and 1000 Hz), and each subgroup divided into 2 (n = S): dried canal or filled with distilled water. The maximum temperature values were collected by 3 thermocouples located at each third of the root external wall and recorded by digital thermometers. Results: The groups irradiated in the continuous mode (CM) presented the highest values (11.82 +/- 5.78), regardless of the canals were dry or not, which were statistically different (p < 0.01) from those obtained with 100 Hz (6.22 +/- 3.64) and 1000 Hz (6.00 +/- 3.36), which presented no statistical difference between them (p > 0.01). The groups irradiated with 5.0 W presented the greatest temperature variation (12.15 +/- 5.14), followed by 3.0 W (7.88 +/- 3.92) and 1.5 W (4.02 +/- 2.16), differing between them (p < 0.01). The cervical third of the root presented the highest temperature rises (9.68 +/- 5.80), followed by the middle (7.66 +/- 4.87) and apical (6.70 +/- 4.23), with statistical difference among them (p < 0.01). After 30 s from the end of irradiation, all the specimens presented temperature variation lower than 10 degrees C. Conclusions: Application of 980-nm diode laser in the root, at 1.5 W in all operating modes, and 3.0 W, in the pulsed mode, for 20 s, can safely be used in endodontic treatment, irrespective of the presence of humidity. (C) 2008 Elsevier Ltd. All rights reserved.