Photoinitiator content in restorative composites: Influence on degree of conversion, reaction kinetics, volumetric shrinkage and polymerization stress

Purpose: To determine the influence of rate of polymerization, degree of conversion and volumetric shrinkage on stress development by varying the amount of photoinitiators in a model composite. Methods: Volumetric shrinkage (with a mercury dilatometer), degree of conversion, maximum rate of reaction (RP(max)) (with differential scanning calorimetry) and polymerization stress (with a controlled compliance device) were evaluated. Bis-GMA/TEGDMA (equal mass ratios) were mixed with a tertiary amine (EDMAB) and camphorqpinone, respectively, in three concentrations (wt%): high= 0.8/1.6; intermediate= 0.4/0.8 and low= 0.2/0.4. 80 wt% filler was added. Composites were photoactivated (400 mW/cm(2) x 40 seconds; radiant exposure=16J/cm(2)). A fourth experimental group was included in which the low concentration formulation was exposed for 80 seconds (32 J/cm(2)). Results: For the same radiant exposure, conversion, RP(max) and stress increased with photoinitiator concentration (P< 0.001). When the low concentration group exposed to 32 J/cm(2) was compared with the high and intermediate groups (exposed to 16 J/cm(2)), RPmax Still increased with the photoinitiator concentration between all levels (P< 0.001) but conversion and stress did not vary (P> 0.05). Shrinkage did not vary regardless of the photoinitiator concentration or radiant exposure. For the photoinitiator concentrations used in this study. Polymerization stress was influenced by conversion but not by rate of reaction. (Am J Dent 2009;22:206-210).

Roughness of Human Enamel Surface Submitted to Different Prophylaxis Methods

The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber clip and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Industria e Comercio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi A dante Indtistrias Medico Odontologicas Ltda, Ribeirao Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel stuface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.

Untreated Dental Caries in a Brazilian Paediatric AIDS Patient Population

Purpose: The objective of the present study was to assess the prevalence of untreated caries in a Brazilian paediatric acquired immunodeficiency syndrome (AIDS) patient population and its association with sociodemographic, behavioural and clinical characteristics. Materials and Methods: The study group was comprised of 125 HIV-infected patients (aged 3 to 15 years) who had already manifested AIDS and were assisted in a specialised health care unit. Dental examinations followed the World Health Organization`s guidelines for oral health surveys. Family caregivers provided information about the socioeconomic standing and the behaviour of their children. Patients` medical records in the hospital provided information on the clinical status of patients. A Poisson regression analysis was used for assessing the covariates for the prevalence of untreated dental caries, as adjusted by age. Results: The prevalence of untreated caries was 58%; a higher prevalence was found in younger children with primary and mixed dentition. The prevalence of untreated caries associated significantly with lower socioeconomic status (household crowding and schooling of the caregiver), dietary habits (higher frequency of sugar consumption) and poorer clinical status (HIV viral load and symptom severity). Conclusions: The high burden of untreated caries on paediatric AIDS patients reinforced the importance of integrating the clinician with the interdisciplinary health care team that assisted these children. The identification of socioeconomic and behavioural factors associated with caries experience reinforced the importance of the attention that children with AIDS received within their own households for the prevention of dental disease, particularly a proper nutritional advisement and monitoring of dental hygiene.

Emerging technologies for the prevention of dental caries. Are current methods of prevention sufficient for the high risk patient?

Fluorides and chlorhexidine are technologies that are 65 and 40 years old, respectively. This overview argues that current methods of caries prevention are not effective for the high caries risk patient. In this review examples, arguments and recommendations are provided to address the high caries risk patient that include: failure of comprehensive chemical modalities treatments to address the high caries risk patient; ecological alteration - would this be an effective approach?; and biomaterials and oral microbiome research to address the high caries risk patient.

Physical Properties and Interfacial Adaptation of Three Epoxy Resin-based Sealers

Introduction: The aim of the study was to evaluate the radiopacity, solubility, flow, film thickness, setting time, and adaptation to the root canal walls of 3 epoxy resin based sealers: AH Plus, Acroseal, and Adseal. Methods: Physical tests were performed following American National Standards Institute/American Dental Association`s requirements. For interfacial adaptation analysis, 30 maxillary canines were shaped by using Pro Taper instruments. The specimens were divided into 3 groups (n = 10): group 1, AH Plus; group 2, Acroseal; and group 3, Adseal. The sealers were mixed with rhodamine B dye, and the canals were filled by using the lateral compaction technique. The percentage of gaps and voids area was calculated at 2, 4, and 6 mm levels from the apex. Statistical evaluation was performed by using analysis of variance for physical analysis and nonparametric Kruskal-Wallis and Dunn tests for interfacial adaptation (P<.05). Results: No statistical differences were found for adaptation, percentage of voids, solubility, flow, and film thickness among the sealers (P>.05). AH Plus was significantly more radiopaque (P<.05). For the setting time, there were statistical differences among all the studied sealers (P<.05). Conclusions: AH Plus, Acroseal, and Adseal presented similar root canal adaptation, solubility, flow, and film thickness. Statistical differences were found for radiopacity and setting time (P<.05). (J Endod 2011;37:1417-1421)

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling. Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05). Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps. Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

Influence of rapid palatal expansion on maxillary incisor alignment stability

Introduction: The purpose of this retrospective study was to compare the long-term stability of maxillary incisor alignment in patients treated with and without rapid maxillary expansion (RME). Methods: The sample comprised 48 subjects with Class I and Class II malocclusions, treated without extractions with fixed edgewise appliances, divided into 2 groups according to the treatment protocol: group 1 comprised 25 patients (15 girls, 10 boys) at a mean initial age of 13.53 years (SD, 1.63), who had RME during orthodontic treatment. Group 2 comprised 23 patients (13 girls, 10 boys) at a mean initial age of 13.36 years (SD, 1.81 years), treated with fixed appliances without RME. Maxillary dental cast measurements were obtained at the pretreatment, posttreatment, and long-term posttreatment stages. Variables assessed were the irregularity index and maxillary arch dimensions. Intergroup comparisons were made with independent t tests. Results: Greater transverse increases were found during treatment in the group treated with RME. However, during the long-term posttreatment period, no significant difference was observed in the amount of incisor crowding relapse between the groups. Conclusions: RME did not influence long-term maxillary anterior alignment stability. (Am J Orthod Dentofacial Orthop 2010; 137: 164. e1-164.e6)

Microtensile vs Microshear Bond Strength of All-in-One Adhesives to Unground Enamel

Purpose To determine the bond strength to unground enamel of all in one adhesives in comparison with an etch and rinse system and to compare the reliability of microtensile and microshear methods in providing such measurements Materials and Methods The bonding procedure was performed on enamel of 64 extracted molars The tested all in one adhesives were Bond Force (Tokuyama), AdheSE One (Ivoclar Vivadent) and Xeno V (Dentsply) Prime&Bond NT (Dentsply) served as control Microtensile specimens were obtained from 4 teeth per group Twelve teeth per group were used for microshear testing Microtensile specimens that failed prior to testing were included in statistical calculations, they were assigned the lowest value measured in the respective group Failure modes were observed under light microscope and classified (cohesive within substrates, adhesive mixed) Statistically significant differences in bond strength were assessed among the adhesives within each testing method and between microshear and microtensile data for each adhesive Failure mode distributions were compared using the chi square test Results All in-one adhesives had similar microshear and microtensile bond strengths In both testing methods, the etch and rinse system achieved the strongest bond For all adhesives significantly higher bond strengths were measured with the microshear test In microtensile testing specimens bonded with the etch and rinse adhesive exhibited a significantly different distribution of failure modes The coefficients of variation were extremely high for microtensile bond strength data, particularly of all in one adhesives Conclusion The adhesive potential to intact enamel of recently introduced all in-one adhesives was inferior to that of an etch and rinse system When testing bond strength to enamel of all in one adhesives, microshear testing may be a more accurate method than microtensile

Influence of endodontic sealers on the bond strength of carbon fiber posts

Objective: The aim of this study was to verify the influence of endodontic sealers on the bond strength of an adhesive system and a resin cement used for carbon posts cementation. Methods: Thirty extracted human premolars were instrumented and randomly divided into three groups according to the tested sealer: EndoFill, Sealapex, or EndoREZ. Specimens were stored at 37 degrees C. After 48 h, half of specimens were prepared to receive the post and the others after 7 days. The posts were cemented with Adper Single Bond/Rely X ARC and stored in distilled water at 37 degrees C for 7 days. After this period, the specimens were sectioned in three slices (coronal, middle, and apical). The push-out test was performed in a universal machine and the debonded area was examined in a stereomicroscope. Results: Data were submitted ANOVA and Tukey test (alpha = 0.05). The EndoFill showed lower bond strength than other sealers (p < 0.01). The EndoREZ sealer was statistically greater than other groups for coronal and middle portions and similar for apical portion (P > 0.05). Coronal and middle portions showed the best results for all groups, mainly when the canal preparation was performed after 48 h (p < 0.01). Mixed failure occurs with more frequency (55.6%) followed by failure in adhesive-dentin interface (34.4%) and adhesive-post interface (10.0%). Conclusion: The use of EndoREZ sealer promoted higher bond strength in root coronal and middle portions when carbon post was fixed with a resin cement. (C) 2007 Wiley Periodicals, Inc.

An in vitro study of non-axial forces upon the retention of an O-ring attachment

Objective The purpose of this study was to evaluate the retention force of an O-ring attachment system in different inclinations to the ideal path of insertion, using devices to compensate angulations. Material and methods Two implants were inserted into an aluminum base, and ball attachments were screwed to implants. Cylinders with O-rings were placed on ball attachments and connected to the test device using positioners to compensate implant angulations (0 degrees, 7 degrees, and 14 degrees). Plexiglass bases were used to simulate implant angulations. The base and the test device were positioned in a testing apparatus, which simulated insertion/removal of an overdenture. A total of 2900 cycles, simulating 2 years of overdenture use, were performed and 36 O-rings were tested. The force required for each cycle was recorded with computer software. Longitudinal sections of ball attachment-positioner-cylinder with O-rings of each angulation were obtained to analyze the relationship among them, and O-ring sections tested in each angulation were compared with an unused counterpart. A mixed linear model was used to analyze the data, and the comparison was performed by orthogonal contrasts (alpha=0.05). Results At 0 degrees, the retention force decreased significantly over time, and the retention force was significantly different in all comparisons, except from 12 to 18 months. When the implants were positioned at 7 degrees, the retention force was statistically different at 0 and 24 months. At 14 degrees, significant differences were found from 6 and 12 to 24 months. Conclusions Within the limitations of this study, it was concluded that O-rings for implant/attachments perpendicular to the occlusal plane were adequately retentive over the first year and that the retentive capacity of O-ring was affected by implant inclinations despite the proposed positioners. To cite this article:Rodrigues RCS, Faria ACL, Macedo AP, Sartori IAM, de Mattos MGC, Ribeiro RF. An in vitro study of non-axial forces upon the retention of an O-ring attachment.Clin. Oral Impl. Res. 20, 2009; 1314-1319.doi: 10.1111/j.1600-0501.2009.01742.x.