Effect of carbon fibres on the mechanical properties and corrosion levels of reinforced portland cement mortars

The changes in mechanical properties of portland cement mortars due to the addition of carbon fibres (CF) to the mix have been studied. Compression and flexural strengths have been determined in relation to the amount of fibres added to the mix, water/binder ratio, curing time and porosity. Additionally, the corrosion level of reinforcing steel bars embedded in portland cement mortars containing CF and silica fume (SF) have also been investigated and reinforcing steel corrosion rates have been determined. As a consequence of the large concentration of oxygen groups in CF surface, a good interaction between the CF and the water of the mortar paste is to be expected. A CF content of 0.5% of cement weight implies an optimum increase in flexural strength and an increase in embedded steel corrosion.

Effect of the stabilisation time of pitch fibres on the molecular sieve properties of carbon fibres

The stabilisation of pitch fibres (PFs) is the most important step for their subsequent use in the preparation of carbon fibres (CFs) and their resulting characteristics. The present work studies the influence that the stabilisation time has on the porosity of the CFs, and on the subsequent properties as carbon molecular sieve (CMS). The increase of the stabilisation time carried out at 573 K, from 2 to 8 h favours their CMS properties producing a decrease in the microposity accessible to N2, which gets completely blocked after 6 and 8 h, while the narrow microporosity (V-DR CO2) remains accessible. Adsorption kinetic studies with CH4 and CO2 were performed to assess the possibility of using these CFs as CMS by comparing them with Takeda 3A CMS. The results suggest that there is an optimal stabilisation time which allows the preparation of CFs from an abundant raw precursor with properties similar to Takeda 3A CMS.

Stabilisation of low softening point petroleum pitch fibres by HNO3

This paper deals with the stabilisation of low softening point pitch fibres obtained from petroleum pitches using HNO3 as oxidising agent. This method presents some advantages compared with conventional methods: pitches with low softening point (SP) can be used to prepare carbon fibres (CF), the stabilisation time has been reduced, the CF yields are similar to those obtained after general methods of stabilisation, and the initial treatments to increase SP when low SP pitches are used to prepare CF, are avoided. The parent pitches were characterised by different techniques such as diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), elemental analysis and solvent extraction with toluene and quinoline. The interaction between HNO3 and the pitch fibres, as well as the changes occurring during the heat treatment, have been followed by DRIFTS.

Activated carbon fibre monoliths

Activated carbon fibre monoliths were prepared by physical activation of carbon fibre monoliths derived from two kinds of pitch-based carbon fibre (CF) (carbon fibres from a coal tar pitch and carbon fibres derived from a petroleum pitch). The monoliths were conformed using a coal tar pitch binder. The carbon fibre monoliths and the activated carbon fibre monoliths were studied by scanning electron microscopy (SEM) and gas adsorption (i.e. N2 at 77 K and CO2 at 273 K). The results obtained reveal that monoliths perform a good activation process that produce a quite high development of microporosity (BET surface areas around 2600 m2/g and N2 micropore volume of 1.23 cm3/g). On the other hand, it is remarkable that the activation process used allow to easily control the degree of activation and hence to select the adsorption capacities of the activated carbon fibre monoliths.

Stabilisation of low softening point petroleum pitch fibres by iodine treatment

A method using iodine has been developed for the stabilisation of low softening point (SP) pitch fibres that avoids air stabilisation in the production of carbon fibres (CF). The interaction between iodine and petroleum pitches has been studied by following the changes in the hydrogen content, aromatic or aliphatic, during the heat treatment of iodine-treated pitch fibres. Two low SP petroleum pitches were used and the iodine-treated pitch fibres were analysed by TGA, DSC, DRIFT, XPS and SEM. The results confirm that using this novel method pitches with low SP can be used to prepare CF with two advantages, compared with conventional methods. The stabilisation time is considerably reduced and treatments to increase the SP, usually required when low SP pitches are used to prepare CF, can be avoided.

Activation of polymer blend carbon nanofibres by alkaline hydroxides and their hydrogen storage performances

In the present work we study the hydroxide activation (NaOH and KOH) of phenol-formaldehyde resin derived CNFs prepared by a polymer blend technique to prepare highly porous activated carbon nanofibres (ACNFs). Morphology and textural characteristics of these ACNFs were studied and their hydrogen storage capacities at 77 K (at 0.1 MPa and at high pressures up to 4 MPa) were assessed, and compared, with reported capacities of other porous carbon materials. Phenol-formaldehyde resin derived carbon fibres were successfully activated with these two alkaline hydroxides rendering highly microporous ACNFs with reasonable good activation process yields up to 47 wt.% compared to 7 wt.% yields from steam activation for similar surface areas of 1500 m2/g or higher. These nano-sized activated carbons present interesting H2 storage capacities at 77 K which are comparable, or even higher, to other high quality microporous carbon materials. This observation is due, in part, to their nano-sized diameters allowing to enhance their packing densities to 0.71 g/cm3 and hence their resulting hydrogen storage capacities.

Asymmetric hybrid capacitors based on activated carbon and activated carbon fibre–PANI electrodes

Composites consisting of polyaniline (PANI) coatings inside the microporosity of an activated carbon fibre (ACF) were prepared by electrochemical and chemical methods. Electrochemical characterization of both composites points out that the electrodes with polyaniline show a higher capacitance than the pristine porous carbon electrode. These materials have been used to develop an asymmetric capacitor based on activated carbon (AC) as negative electrode and an ACF–PANI composite as positive electrode in H2SO4 solution as electrolyte. The presence of a thin layer of polyaniline inside the porosity of the activated carbon fibres avoids the oxidation of the carbon material and the oxygen evolution reaction is produced at more positive potentials. This capacitor was tested in a maximum cell voltage of 1.6 V and exhibited high energy densities, calculated for the unpackaged active materials, with values of 20 W h kg−1 and power densities of 2.1 kW kg−1 with excellent cycle lifetime (90% during the first 1000 cycles) and high coulombic efficiency.

Activated Carbon Fibre Monoliths for Hydrogen Storage

Porous adsorbents are currently investigated for hydrogen storage application. From a practical point of view, in addition to high porosity developments, high material densities are required, in order to confine as much material as possible in a tank device. In this study, we use different measured sample densities (tap, packing, compacted and monolith) for analyzing the hydrogen adsorption behavior of activated carbon fibres (ACFs) and activated carbon nanofibres (ACNFs) which were prepared by KOH and CO2 activations, respectively. Hydrogen adsorption isotherms are measured for all of the adsorbents at room temperature and under high pressures (up to 20 MPa). The obtained results confirm that (i) gravimetric H2 adsorption is directly related to the porosity of the adsorbent, (ii) volumetric H2 adsorption depends on the adsorbent porosity and importantly also on the material density, (iii) the density of the adsorbent can be improved by packing the original adsorbents under mechanical pressure or synthesizing monoliths from them, (iv) both ways (packing under pressure or preparing monoliths) considerably improve the storage capacity of the starting adsorbents, and (v) the preparation of monoliths, in addition to avoid engineering constrains of packing under mechanical pressure, has the advantage of providing high mechanical resistance and easy handling of the adsorbent.