Stabilisation of low softening point petroleum pitch fibres by iodine treatment

A method using iodine has been developed for the stabilisation of low softening point (SP) pitch fibres that avoids air stabilisation in the production of carbon fibres (CF). The interaction between iodine and petroleum pitches has been studied by following the changes in the hydrogen content, aromatic or aliphatic, during the heat treatment of iodine-treated pitch fibres. Two low SP petroleum pitches were used and the iodine-treated pitch fibres were analysed by TGA, DSC, DRIFT, XPS and SEM. The results confirm that using this novel method pitches with low SP can be used to prepare CF with two advantages, compared with conventional methods. The stabilisation time is considerably reduced and treatments to increase the SP, usually required when low SP pitches are used to prepare CF, can be avoided.

Stabilisation of low softening point petroleum pitch fibres by HNO3

This paper deals with the stabilisation of low softening point pitch fibres obtained from petroleum pitches using HNO3 as oxidising agent. This method presents some advantages compared with conventional methods: pitches with low softening point (SP) can be used to prepare carbon fibres (CF), the stabilisation time has been reduced, the CF yields are similar to those obtained after general methods of stabilisation, and the initial treatments to increase SP when low SP pitches are used to prepare CF, are avoided. The parent pitches were characterised by different techniques such as diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), elemental analysis and solvent extraction with toluene and quinoline. The interaction between HNO3 and the pitch fibres, as well as the changes occurring during the heat treatment, have been followed by DRIFTS.

Isotropic petroleum pitch as a carbon precursor for the preparation of activated carbons by KOH activation

Results show that it is possible to activate a low softening point isotropic petroleum pitch, without intermediate pre-treatments, by chemical activation with KOH. The chemical activation is carried out by direct heat treatment of a mixture of the isotropic pitch and KOH. It produces activated carbons (ACs) with micropore volumes as high as 1.12 cm3/g, and BET surface areas around 3000 m2/g. The activating agent/precursor ratios studied (from 1/1 to 4/1; wt./wt.) show, as expected, that increasing the ratio enhances the adsorption characteristics of the resulting AC.

New insights on the direct activation of isotropic petroleum pitch by alkaline hydroxides

The paper provides interesting evidences that a low softening point isotropic petroleum pitch can be used as a good carbon precursor for the preparation of activated carbons. The activation is carried out by KOH and/or NaOH and the resulting activated carbons present well developed porosity. Such hydroxide activations can be done directly on the pristine petroleum pitch (P) or on the pitch that has been submitted to an air stabilisation followed by a N2 heat treatment (TAN). In general, KOH activation produces better results than NaOH, both in terms of porosity and yield, the results obtained for the activation of TAN being impressive because of the good porosity developments and high yields reached. The different treatments carried out over the petroleum pitch precursor clearly show that they significantly influence the extent of microporosity development. This is due to different changes occurring in the porous structure of the precursor as a function of the treatment carried out. The efficiency of the activation process increases as the mesophase content of the precursor decreases, as well as the mesophase formation during the activation process is avoided.

Production of nanoTiC–graphite composites using Ti-doped self-sintering carbon mesophase powder

This work reports the synthesis of nanoTiC–graphite composites using mesophase pitch containing titanium as TiC or TiO2 nanoparticles. NanoTiC–graphite composites have been prepared using Ti-doped self-sintering mesophase powders as starting materials without using any binders or a metal carbide-carbon mixing stage. The effect of manufacture variables on the graphite compacts properties was studied. Graphites were characterised using XRD and Raman spectroscopy, SEM and TEM, as well as by their mechanical, electrical and thermal properties. The presence of TiC promotes graphitisation producing materials with larger crystal sizes. The kind of titanium source and mesophase content of the starting pitch affects to the final properties. Mesophase pitch with higher amount of mesophase content produces graphites with higher degree of graphitisation. The incorporation of TiC nanoparticles to the graphites composites improved thermal conductivity more than four times, and mechanical properties are not significantly modified by the presence of TiC.

Functionalization of carbon nanotubes using aminobenzene acids and electrochemical methods. Electroactivity for the oxygen reduction reaction

Functionalized carbon nanotubes (CNTs) using three aminobenzene acids with different functional groups (carboxylic, sulphonic, phosphonic) in para position have been synthesized through potentiodynamic treatment in acid media under oxidative conditions. A noticeable increase in the capacitance for the functionalized carbon nanotubes mainly due to redox processes points out the formation of an electroactive polymer thin film on the CNTs surface along with covalently bonded functionalities. The CNTs functionalized using aminobenzoic acid rendered the highest capacitance values and surface nitrogen content, while the presence of sulfur and/or phosphorus groups in the aminobenzene structure yielded a lower functionalization degree. The oxygen reduction reaction (ORR) activity of the functionalized samples was similar to that of the parent CNTs, independently of the functional group present in the aminobenzene acid. Interestingly, a heat treatment in N2 atmosphere with a very low O2 concentration (3125 ppm) at 800 °C of the CNTs functionalized with aminobenzoic acid produced a material with high amounts of surface oxygen and nitrogen groups (12 and 4% at., respectively), that seem to modulate the electron-donor properties of the resulting material. The onset potential and limiting current for ORR was enhanced for this material. These are promising results that validates the use of electrochemistry for the synthesis of novel N-doped electrocatalysts for ORR in combination with adequate heat treatments.

Spectroscopic, calorimetric, and catalytic evidences of hydrophobicity on Ti-MCM-41 silylated materials for olefin epoxidations

Hydrophobic Ti-MCM-41 samples prepared by post-synthesis silylation treatment demonstrate to be highly active and selective catalysts in olefins epoxidation by using organic hydroperoxides as oxidizing agents in liquid phase reaction systems. Epoxide yields show important enhancements with increased silylation degrees of the Ti-mesoporous samples. Catalytic studies are combined and correlated with spectroscopic techniques (e.g. XRD, XANES, UV-Visible, 29Si MAS-NMR) and calorimetric measurements to better understand the changes in the surface chemistry of Ti-MCM-41 samples due to the post-synthesis silylation treatment and to ascertain the role of these trimethylsilyl groups incorporated in olefin epoxidation. In such manner, the effect of the organic moieties on solids, and both water and glycol molecules contents on the catalytic activity and selectivity are analyzed in detail. Results show that the hydrophobicity level of the samples is responsible for the decrease in water adsorption and, consequently, the negligible formation of the non-desired glycol during the catalytic process. Thus, catalyst deactivation by glycol poisoning of Ti active sites is greatly diminished, this increasing catalyst stability and leading to practically quantitative production of the corresponding epoxide. The extended use of these hydrophobic Ti-MCM-41 catalysts together with organic hydroperoxides for the highly efficient and selective epoxidation of natural terpenes is also exemplified.

Novel synthesis of a micro-mesoporous nitrogen-doped nanostructured carbon from polyaniline

Nanostructured carbons with relatively high nitrogen content (3–8%) and different micro and mesoporosity ratio were prepared by activation of polyaniline (PANI) with a ZnCl2–NaCl mixture in the proportion of the eutectic (melting point 270 °C). It was found that the activated carbons consisted of agglomerated nanoparticles. ZnCl2 plays a key role in the development of microporosity and promotes the binding between PANI nanoparticles during heat treatment, whereas NaCl acts as a template for the development of mesoporosity of larger size. Carbons with high micropore and mesopore volumes, above 0.6 and 0.8 cm3/g, respectively, have been obtained. Furthermore, these materials have been tested for CO2 capture and storage at pressures up to 4 MPa. The results indicate that the nitrogen groups present in the surface do not seem to affect to the amount of CO2 adsorbed, not detecting strong interactions between CO2 molecules and nitrogen functional groups of the carbon, which are mainly pyridinic and pyrrolic groups.

Fabrication of Mg foams for biomedical applications by means of a replica method based upon spherical carbon particles

Interest in Mg foams is increasing due to their potential use as biomaterials. Fabrication methods determine to a great extent their structure and, in some cases, may pollute the foam. In this work Mg foams are fabricated by a replica method that uses as skeleton packed spheres of active carbon, a material widely utilized in medicine. After Mg infiltration, carbon particles are eliminated by an oxidizing heat treatment. The latter covers Mg with MgO which improves performance. In particular, oxidation retards degradation of the foam, as the polarization curves of the Mg foam with and without oxide indicate. The sphericity and regularity of C particles allows control of the structure of the produced open-cell foams.