Thermogravimetric analysis of the pyrolysis of several materials used in the preparation of commercial cigarettes

Comunicación presentada en forma de póster en el "12th Mediterranean Congress of Chemical Engineering", Barcelona (Spain), November 15-18, 2011

Steam reforming of ethanol over bimetallic RhPt/La2O3: Long-term stability under favorable reaction conditions

Recently, the steam reforming of biofuels has been presented as a potential hydrogen source for fuel cells. Because this scenario represents an interesting opportunity for Colombia (South America), which produces large amounts of bioethanol, the steam reforming of ethanol was studied over a bimetallic RhPt/La2O3 catalyst under bulk mass transfer conditions. The effect of temperature and the initial concentrations of ethanol and water were evaluated at space velocities above 55,000 h−1 to determine the conditions that maximize the H2/CO ratio and reduce CH4 production while maintaining 100% conversion of ethanol. These requirements were accomplished when 21 mol% H2O and 3 mol% C2H5OH (steam/ethanol molar ratio = 7) were reacted at 600 °C. The catalyst stability was assessed under these reaction conditions during 120 h on stream, obtaining ethanol conversions above 99% during the entire test. The effect of both H2 and air flows as catalyst regeneration treatments were evaluated after 44 and 67 h on stream, respectively. The results showed that H2 treatment accelerated catalyst deactivation, and air regeneration increased both the catalyst stability and the H2 selectivity while decreasing CH4 generation. Fresh and spent catalyst samples were characterized by TEM/EDX, XPS, TPR, and TGA. Although the Rh and Pt in the fresh catalyst were completely reduced, the spent samples showed a partial oxidation of Rh and small amounts of carbonaceous residue. A possible Rh–Pt–Rh2O3 structure was proposed as the active site on the catalyst, which was regenerated by air treatment.

Titania–Silica Materials for Enhanced Photocatalysis

Mesoporous titania–organosilica nanoparticles comprised of anatase nanocrystals crosslinked with organosilica moieties have been prepared by direct co-condensation of a titania precursor, tetrabuthylortotitanate (TBOT), with two organosilica precursors, 1,4-bis(triethoxysilyl) benzene (BTEB) and 1,2-bis(triethoxysilyl) ethane (BTEE), in mild conditions and in the absence of surfactant. These hybrid materials show both high surface areas (200–360 m2 g−1) and pore volumes (0.3 cm3 g−1) even after calcination, and excellent photoactivity in the degradation of rhodamine 6G and in the partial oxidation of propene under UV irradiation, especially after the calcination of the samples. During calcination, there is a change in the TiIV coordination and an increase in the content of Si[BOND]O[BOND]Ti moieties in comparison with the uncalcined materials, which seems to be responsible for the enhanced photocatalytic activity of hybrid titania–silica materials as compared to both uncalcined samples and the control TiO2.

Preparation, characterisation and testing of CuO/Ce0.8Zr0.2O2 catalysts for NO oxidation to NO2 and mild temperature diesel soot combustion

CuO/ceria-zirconia catalysts have been prepared, deeply characterised (N2 adsorption–desorption isotherms at −196 °C, XRD, Raman spectroscopy, XPS, TEM and H2-TPR) and tested for NO oxidation to NO2 in TPR conditions, and for soot combustion at mild temperature (400 °C) in a NOx/O2 stream. The behaviour has been compared to that of a reference Pt/alumina commercial catalyst. The ceria-zirconia support was prepared by the co-precipitation method, and different amounts of copper (0.5, 1, 2, 4 and 6 wt%) were loaded by incipient wetness impregnation. The results revealed that copper is well-dispersed onto the ceria-zirconia support for the catalysts with low copper loading and CuO particles were only identified by XRD in samples with 4 and 6% of copper. A very low loading of copper increases significantly the activity for the NO oxidation to NO2 with regard to the ceria-zirconia support and an optimum was found for a 4% CuO/ceria-zirconia composition, showing a very high activity (54% at 348 °C). The soot combustion rate at 400 °C obtained with the 2% CuO/ceria-zirconia catalyst is slightly lower to that of 1% Pt/alumina in terms of mass of catalyst but higher in terms of price of catalyst.

Preferential oxidation of CO in excess of H2 on Pt/CeO2–Nb2O5 catalysts

A series of CeO2–Nb2O5 mixed oxides with different Nb content, as well as the pure oxides, have been synthesized by co-precipitation with excess urea. These materials have been used as supports for platinum catalysts, with [Pt(NH3)4](NO3)2 as precursor. Both supports and catalysts have been characterized by several techniques: N2 physisorption at 77 K, X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy, UV–vis spectroscopy, scanning electron microscopy, transmission electron microscopy, temperature-programmed reduction and temperature-programmed desorption (CO and H2), and their catalytic behaviour has been determined in the PROX reaction, both with an ideal gas mixture (CO, O2 and H2) and in simulated reformate gas containing CO2 and H2O. Raman spectroscopy analysis has shown the likely substitution of some Ce4+ cations by Nb5+ to some extent in supports with low niobium contents. Moreover, the presence of Nb in the supports hinders their ability to adsorb CO and to oxidize it to CO2. However, an improvement of the catalytic activity for CO oxidation is obtained by adding Nb to the support, although the Pt/Nb2O5 catalyst shows very low activity. The best results are found with the Pt/0.7CeO2–0.3Nb2O5 catalyst, which shows a high CO conversion (85%) and a high yield (around 0.6) after a reduction treatment at 523 K. The effect of the presence of CO2 and H2O in the feed has also been determined.

Superior performance of gold supported on doped CeO2 catalysts for the preferential CO oxidation (PROX)

Herein, the preferential oxidation of CO in excess hydrogen (PROX reaction) was studied over Au catalysts supported on ceria and Y or Nb doped ceria. Both supports and catalysts have been extensively characterized by a number of advanced techniques; XRD, N2-adsortion, Raman spectroscopy, XPS, and H2-TPR. The catalytic results showed that when an ideal mixture of H2 and CO is used for the PROX reaction the gold supported on pure ceria behaves better than the others samples. However, when a typical reformate gas composition containing CO2 and H2O is used, the gold supported on Nb doped sample behaves better than gold supported in pure ceria. It is suggested that niobium hampers the strong adsorption of CO2 and H2O in the active sites, thus improving the catalytic performance in real reformate gas.

Influence of the metal precursor on the catalytic behavior of Pt/Ceria catalysts in the preferential oxidation of CO in the presence of H2 (PROX)

The effect of the metal precursor (presence or absence of chlorine) on the preferential oxidation of CO in the presence of H2 over Pt/CeO2 catalysts has been studied. The catalysts are prepared using (Pt(NH3)4)(NO3)2 and H2PtCl6, as precursors, in order to ascertain the effect of the chlorine species on the chemical properties of the support and on the catalytic behavior of these systems in the PROX reaction. The results show that chloride species exert an important effect on the redox properties of the oxide support due to surface chlorination. Consequently, the chlorinated catalyst exhibits a poorer catalytic activity at low temperatures compared with the chlorine-free catalyst, and this is accompanied by a higher selectivity to CO2 even at high reaction temperatures. It is proposed that the CO oxidation mechanism follows different pathways on each catalyst.

High performance of Cu/CeO2-Nb2O5 catalysts for preferential CO oxidation and total combustion of toluene

Copper-based catalysts supported on niobium-doped ceria have been prepared and tested in the preferential oxidation of CO in excess of H2 (PROX) and in total oxidation of toluene. Supports and catalysts have been characterized by several techniques: N2 adsorption, ICP-OES, XRF, XRD, Raman Spectroscopy, SEM, TEM, H2-TPR and XPS, and their catalytic performance has been measured in PROX, with an ideal gas mixture (CO, O2 and H2) with or without CO2 and H2O, and in total oxidation of toluene. The effects of the copper loading and the amount of niobium in the supports have been evaluated. Remarkably, the addition of niobia to the catalysts may improve the catalytic performance in total oxidation of toluene. It allows us to prepare cheaper catalysts (niobia it is far cheaper than ceria) with improved catalytic performance.

Platinum–tin/carbon catalysts for ethanol oxidation: Influence of Sn content on the electroactivity and structural characteristics

Carbon-supported Pt–Sn catalysts commonly contain Pt–Sn alloy and/or Pt–Sn bimetallic systems (Sn oxides). Nevertheless, the origin of the promotion effect due to the presence of Sn in the Pt–Sn/C catalyst towards ethanol oxidation in acid media is still under debate and some contradictions. Herein, a series of Ptx–Sny/C catalysts with different atomic ratios are synthesized by a deposition process using formic acid as the reducing agent. Catalysts structure and chemical compositions are investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) and their relationship with catalytic behavior towards ethanol electro-oxidation was established. Geometric structural changes are producing by highest Sn content (Pt1–Sn1/C) promoted the interaction of Pt and Sn forming a solid solution of Pt–Sn alloy phase, whereas, the intermediate and lowest Sn content (Pt2–Sn1/C and Pt3–Sn1/C, respectively) promoted the electronic structure modifications of Pt by Sn addition without the formation of a solid solution. The amount of Sn added affects the physical and chemical characteristics of the bimetallic catalysts as well as reducing the amount of Pt in the catalyst composition and maintaining the electrocatalytic activities at the anode. However, the influence of the Sn oxidation state in Pt–Sn/C catalysts surfaces and the alloy formation between Pt and Sn as well as with the atomic ratio on their catalytic activity towards ethanol oxidation appears minimal. Similar methodologies applied for synthesis of Ptx–Sny/C catalysts with a small change show differences with the results obtained, thus highlighting the importance of the conditions of the preparation method.

Dimeric assemblies of lanthanide-stabilised dilacunary Keggin tungstogermanates: A new class of catalysts for the selective oxidation of aniline

In this work we demonstrate the efficiency of some dimeric [Ln4(H2O)6(β-GeW10O38)2]12− anions composed of lanthanide-stabilised dilacunary Keggin tungstogermanate fragments (ββ-Ln4, Ln = Dy, Ho, Er, Tm) as heterogeneous catalysts for the organic phase oxidation of aniline with hydrogen peroxide. The results obtained evidence total conversion of aniline at room temperature, as well as full selectivity towards nitrosobenzene, and the catalysts are able to retain both their activity and selectivity after several runs. Peroxopolyoxometalate intermediaries have been identified as the catalytically active species during the aniline-to-nitrosobenzene oxidation process.

Three-way catalysts: past, present and future

In this article, the past and the state-of-the-art in Three-Way Catalyst (TWC) technology are reviewed. The main chemical reactions occurring in a gasoline engine are discussed and also the main reactions taking place in a TWC placed in the tailpipe, namely CO and hydrocarbons oxidation and nitrogen oxides reduction to molecular nitrogen. The main components of a TWC (substrates, noble metals and cerium oxides) and their role in the different chemical reactions occurring in a TWC are described. Finally, the problem of diesel vehicles gas aftertratment is described, and the current state-of-the art in catalytic converters for these vehicles are commented.

Single-walled carbon nanotube buckypapers as electrocatalyst supports for methanol oxidation

This work studies the use of various single-walled carbon nanotube (SWCNT) buckypapers as catalyst supports for methanol electro-oxidation in acid media. Buckypapers were obtained by vacuum filtration from pristine and oxidized SWCNT suspensions in different liquid media. Pt–Ru catalysts supported on the buckypapers were prepared by multiple potentiostatic pulses using a diluted solution of Pt and Ru salts (2 mM H2PtCl6 + 2 mM RuCl3) in acid media. The resulting materials were characterized via SEM, TEM, EDX and ICP-OES analysis. Well dispersed rounded nanoparticles between 2 and 15 nm were successfully electrodeposited on the SWCNT buckypapers. The ruthenium content in the bimetallic deposits was between 32 and 48 at. %, while the specific surface areas of the catalysts were in the range of 72–113 m2 g−1. It was found that the solvent used to prepare the SWCNT buckypaper films has a strong influence on the catalyst dispersion, particle size and metal loading. Cyclic voltammetry and chronoamperometry experiments point out that the most active electrodes for methanol electro-oxidation were prepared with the buckypaper supports that were obtained from SWCNT dispersions in N-methyl-pyrrolidone.

Sulfur resistance of Pt-W catalysts

The sulfur resistance of low-loaded monometallic Pt catalysts and bimetallic Pt-W catalysts during the partial selective hydrogenation of styrene, a model compound of Pygas streams, was studied. The effect of metal impregnation sequence on the activity and selectivity was also evaluated. Catalysts were characterized by ICP, TPR, XRD, and XPS techniques. Catalytic tests with sulfur-free and sulfur-doped feeds were performed. All catalysts showed high selectivities (>98%) to ethylbenzene. Activity differences between the catalysts were mainly attributed to electronic effects due to the presence of different electron-rich species of Pt0 and electron-deficient species of Ptδ+. Pt0 promotes the cleavage of H2 while Ptδ+ the adsorption of styrene. The catalyst successively impregnated with W and Pt (WPt/Al) was more active and sulfur resistant than the catalyst prepared with an inverse impregnation order (PtW/Al). The higher poison resistance of WPt/Al was attributed to both steric and electronic effects.

Desilication of TS-1 zeolite for the oxidation of bulky molecules

A series of modified TS-1 samples have been produced by desilication of the original TS-1 (4 wt.% Ti) using a chemical treatment with NaOH. Desilicated TS-1 zeolites exhibit a large BET surface area together with a well-developed mesoporosity. The hierarchical catalysts from desilication of TS-1 zeolite show a good catalytic activity for the oxidation of small molecules and a significantly higher activity for the oxidation of bulky molecules.

Evaluation of hectorites, synthesized in different conditions, as soot combustion catalysts after impregnation with copper

Two microporous hectorites were prepared by conventional and microwave heating, and a delaminated mesoporous hectorite by an ultrasound-assisted synthesis. These three hectorites were impregnated with copper. The characterization techniques used were XRD, N2 adsorption, TEM and H2 reduction after selective surface copper oxidation by N2O (to determine copper dispersion). The catalytic activity for soot combustion of the copper-free and the copper-containing hectorites was tested under a gas mixture of 500 ppm NOx/5% O2/N2 (and 5% O2/N2 in some cases), evaluating their stability through three consecutive soot combustion experiments. The delaminated hectorite showed the highest surface area (353 m2/g) allowing the highest dispersion of copper. This copper-containing catalyst was the most active for soot combustion among those prepared and tested in this study. We have also concluded that the Cu/hectorite-catalyzed soot combustion mechanism is based on the activation of the O2 molecule and not on the NO2-assisted soot combustion.